Self-photoinitiating acrylate (SPIA) which can undergo self-initiation under UV irradiation was synthesized by a Michael addition in the presence of a base catalyst. The SPIA polymerizations were investigated by photo-differential scanning calorimeter (photo-DSC) and surface physical properties such as pendulum hardness and pencil hardness. The results showed that the SPIA can cure upon UV irradiation by itself without a photoinitiator. But we found out that both the curing rate and the conversion were too low for the self-curing reaction of SPIA. In order to improve the SPIA curing properties, we introduced the SPIA/cationic hybrid system and observed the effects of the addition of commercial free radical type monomer and photoinitiator on the curing behaviors. SPIA/cationic hybrid system was the best suitable to improve the SPIA curing properties. The kinetic analysis indicated that the cationic monomer and photoinitiator apparently accelerated the cure reaction and rate of the hybrid SPIA system, mostly due to the synergistic effect of cationic monomer and photoinitiator increasing the mobility of active species and the generation of reactive species (free radical, cation) during the photopolymerization process. The physical properties showed that, unlike typical free radical system, the hybrid systems did not show oxygen inhibition effect because of cationic reaction on the coating surface.

• Journal of Adhesion and Interface
• /
• v.22 no.4
• /
• pp.136-143
• /
• 2021

Polyurea has been investigated as a polymer matrix for composite materials because of its high mechanical strength. Although polyurea has a similar chemical structure to polyurethane, it has much higher strength and durability. In this study, the fabrication of polyurea composites reinforced with carbon nanotube (CNT) and graphene oxide (GO) is demonstrated to enhance the tensile strength of the glass fibers composite. Using FTIR and Raman spectroscopies, the chemical structures of polyurea, CNT, and GO are investigated. As a result, spectroscopy analysis reveals that the chemical structure of CNT, GO, and polyurea is maintained during the fabrication of the composite structure. Scanning electron microscopy reveals the uniform distribution of CNT and GO across the polyurea matrix. The reinforcement of 1 wt% CNT in polyurea enhances the tensile strength of CNT/polyurea composites. In contrast, the reinforcement of GO in polyurea induces the degradation of the tensile strength of GO/polyurea composites.

• Journal of Adhesion and Interface
• /
• v.22 no.4
• /
• pp.118-127
• /
• 2021

In this study, the mechanical properties of vulcanized rubber were evaluated through compounding by controlling filler content to improve the mechanical properties of NBR rubber. Aramid and glass fibers with excellent heat resistance were used as fillers, and ceramics were additionally used in anticipation of a complementary effect, and as for the ceramic materials, needle-shaped and plate-shaped ceramics were used. Each filler was used in an amount of 5.0, 10.0, 15.0, and 20.0 phr in order to investigate the basic properties according to the amount of filler. To confirm the complementary effect through ceramic application, each 10.0 phr fiber and ceramic were mixed with 1:1 ratio to evaluate mechanical properties. As a result, it was confirmed that the decreasing ratio of tensile strength after heat aging was small in the order of aramid fiber, acicular ceramic, glass fiber, and plate ceramic in the case of applying the filler alone. In addition, the mechanical characteristics of vulcanized rubber using composite filler based on fibers and ceramics were evaluated, and it was confirmed that the composite filler had a complementary effect on thermal aging.

• Journal of Adhesion and Interface
• /
• v.20 no.1
• /
• pp.1-8
• /
• 2019

Fabrication of monolayer is important method for enhancing physical and chemical characteristics such as light shielding and antireflection while maintaining thin film properties. In previous studies, monolayers were fabricated by various methods on small substrates, but processes were complicated and difficult to form monolayers with large area. We used rod coating equipment with a small amount of coating liquid to form a HCP (hexagonal closed packing) coating of PMMA beads on PET(poly(ethylene terephthalate)) substrate with $20cm{\times}20cm$ size. We observed that changes in morphologies of monolayers by using the solvents with different boiling points and vapor pressures, by adapting surfactants on particles and by applying plasma treatment on substrates. The coverage was increased by 20% by optimizing the coating conditions including meniscus of beads, control of the attraction - repulsion forces and surface energy. This result can potentially be applied to optical films and sensors because it is possible to make a uniform and large-scale monolayer in a simple and rapid manner when it is compared to the methods in previous studies.

• Journal of Adhesion and Interface
• /
• v.22 no.2
• /
• pp.31-38
• /
• 2021

In this study, a nonionic reactive emulsifier with aromatic and acryl group was synthesized by using polyoxyethylene(10) dodecylphenyl ether with 3-butenoic acid. The synthesized nonionic reactive emulsifier was confirmed by ¹H-NMR and FT-IR. In addition, the reactive emulsifier synthesized in the preparation of aqueous acrylic adhesives base emulsion was used and the properties of the solid content, conversion, particle size distribution, peel strength and high temperature holding force were compared to those of nonionic emulsifiers without aromatic group. The particle size was distributed from 370 nm to 698 nm, and the peel strength were measured in the range of 1.507~1.802 kg_f. The high temperature holding force of prepared adhesives base emulsion were measured in the range of 0.50~2.00 mm. Especially, in the result of synthesized nonionic reactive emulsifier with aromatic group, it was confirmed that high temperature holding force results were the most excellent than the case of using other nonionic reactive emulsifiers, and it can be useful for water-based acryl pressure sensitive adhesive.

• Journal of Adhesion and Interface
• /
• v.22 no.2
• /
• pp.57-62
• /
• 2021

Recently, the atomically thin two-dimensional transition-metal dichalcogenides (TMDs) have received considerable attention for the application to next-generation semiconducting devices, owing to their remarkable properties including high carrier mobility. However, while a technique for growing graphene is well matured enough to achieve a wafer-scale single crystalline monolayer film, the large-area growth of high quality TMD monolayer is still a challenging issue for industrial application. In order to enlarge the size of single crystalline MoS₂ monolayer, here, we systematically investigated the effect of process parameters in molten-salt-assisted chemical vapor deposition method. As a result, with optimized process parameters, we found that single crystalline monolayer MoS₂ can be grown as large as 420 ㎛.

• Journal of Adhesion and Interface
• /
• v.22 no.2
• /
• pp.63-68
• /
• 2021

Unsaturated Polyester Resin (UPR) is in general used as a resin to prepare for composite materials with reinforcing materials such as glass fibers. UPR, a thermosetting resin, is used in industry to prepare for sheet molding compound (SMC) molding prepreg that has excellent productivity and is advantageous for mass production among various molding methods of composite materials. The fiber-reinforced composite material using UPR as a matrix material is light and has the advantage of excellent physical properties, but it is weak against impact and is fragile. Four types of polyurethane were synthesized and added to UPR resin to overcome the shortcomings.

• Journal of Adhesion and Interface
• /
• v.21 no.4
• /
• pp.143-155
• /
• 2020

Hydrophobic Organic-Inorganic (O-I) hybrid materials prepared by sol-gel process have been widely used at functional coating fields such as coatings for anti-corrosion, anti-icing, self-cleaning, anti-reflection. The key point for fabricating hydrophobic surface is to optimize the surface energy and roughness of the coating films. There are typical processes to control the surface energy and roughness which are 'In situ fabricating', 'Pre-fluorinating/Post-roughening', 'Pre-roughening/ Post-fluorinating'. In this study, particle-binder process was used for in-situ fabrication of hydrophobic coating films. Various O-I hybrid compounds prepared using several kinds of alkoxysilane compounds were used as a binder for silica nanoparticles at particle-binder process. To study effect of fluorine content and weight ratio of particle : binder on the hydrophobicity and surface morphology, Hydrophobic coating films were prepared onto glass substrate at various content of fluorine content of O-I hybrid binder and weight ratio of particle : binder. The coating films prepared using O-I hybrid binder (GPTi-HF10) having 10 wt% of fluorine content showed the highes water contact angle (107.52±1.6°). The coating films prepared at 1:3 weight ratio of GPTi-HF10 : silica nanoparticle exhibited the highest water contact angle (130.84±1.99°).

• Journal of Adhesion and Interface
• /
• v.23 no.2
• /
• pp.44-52
• /
• 2022

Epoxy resin has the disadvantage of being easily destroyed by instantaneous impact due to its high crosslinking density despite its high glass transition temperature (T_g) and excellent properties. To compensate for this, in this study, polyol was synthesized by ring opening polymerization of propylene glycol (PPG) diamine, Jeffamine D 2000 and propylene carbonate, and urethane modified epoxy was synthesized using this. The properties of the synthesized urethane modified epoxy were confirmed by FT-IR, H-NMR. To confirm the degree of improvement in impact resistance as an adhesive, a urethane modified epoxy adhesive was prepared by mixing a digylcidyl ether bisphenol A (DGEBA) with curing agent and curing accelerator. Properties test of urethane modified epoxy were shear strength, tensile strength and impact strength. As a result, excellent results were obtained in all test when the ratio of DGEBA : urethane modified epoxy was 8:2.

• Journal of Adhesion and Interface
• /
• v.23 no.2
• /
• pp.25-32
• /
• 2022

There has been a growing demand for water based-type PSA due to environmental regulations for solvent-type PSA. And accordingly, there is a growing expectation as well for tackifiers used to compensate for the problem of deterioration of physical properties. Therefore, In this study, water-based tackifiers were synthesized by changing the contents of hard and functional acrylic monomers CHMA, IBOA, and AA. And these were added to the pressure-sensitive adhesive at 10 phr and their physical properties were compared. Tackiness slightly decreased as CHMA increased and IBOA decreased. Since the intermolecular bonding force increased due to the increase in AA content, the lower the AA content showed better results. Peel strength increased as the tackifiers were added because the fluidity of the polymer chain increased. And higher AA content showed better results because more hydrogen bonds were formed. The holding power tended to decrease as CHMA increased because the content of IBOA relatively decreased which has a large influence on the holding power. And higher AA content showed better results.