• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.205-206
• /
• 2006

The microstructural evolutions and shear properties of the pure Sn solder bumps with Ni UBMs were investigated during multiple reflows and high temperature storage(HTS) tests. Only a $Ni_3Sn_4$ IMC was found at the bump/Ni UBM interface after 1 reflow. The layer thickness of these IMCs increased with increasing reflow number and testing time. The solder bumps showed a good reliability during multiple reflows and HTS tests.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.168-170
• /
• 2007

Sn-Bi eutectic solder alloy have is good wetting and physical properties. The results of solder paste properties test, melting point is about $139^{\circ}C$ and spread test is represent spread properties of $7{\sim}16%$. The results of shear strength after as reflowed, thermal shock test, high temperature storage test of 500hr and 1000hr at $100^{\circ}C$. The shear strength value range is from 6000 to 11000gf, pull strength value range is from 2200 to 3300gf.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.53-59
• /
• 2014

The mechanical stability of solder joints in electronic devices with Sn-Ag-Cu is a continuous issue since the material was applied to the industry. Various shock test methods were developed and standardized tests are used in the industry worldwide. Although it is applied for several years, the detailed mechanism of the shock induced failure mechanism is still under investigation. In this study, the effect of external temperature was observed on large Flip-chip BGA components. The weight and size of the large package produced a high strain region near the corner of the component and thus show full fracture at around 200G level shock input. The shock performance at elevated temperature, at $100^{\circ}C$ showed degradation based on board pad designs. The failure mode and potential failure mechanisms are discussed.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.3
• /
• pp.1-7
• /
• 2015

In this study, properties of Pb-free solders for automotive electronics parts were discussed. Lead-free solders for electronics became important after RoHS (Restriction of the use of certain Hazardous Substances) to avoid environmental pollution. Also the growing electronic rate in automotive parts and ELV (End-of Life Vehicles) make Pb-free solder for automotive electronics to be inevitable trend. Definitely, Pb-free solder for automotive electronics should have good wettability, basic strength, but need more reliability than other solders, since it has harsh condition like high temperature, humidity and engine vibration. Thus, shear strength test, thermal shock, drop test and many others are needed to ensure the high reliability. This study describes the properties and requirements of Pb-free solders for automotive electronics.

• Proceedings of the Korean Reliability Society Conference
• /
• 2004.07a
• /
• pp.147-151
• /
• 2004

In this study, an optical fiber assembly directly coupled with a laser diode or a photo diode is designed to confirm high reliable optical coupling efficiency of optical transmitter(Tx) and receiver(Rx). The optical fiber assembly is fabricated by soldering an optical fiber and a Kovar ferrule using a glass solder after inserting an optical fiber through a Kovar ferrule. The Kovar which has good welding characteristics is applied to introduce laser welding technique. The glass solder has excellent thermal characteristics such as thermal shift delamination compared with PbSn, AuSn solder previously used usually. Furthermore, the glass solder doesn't need fiber metalization and this enables low cost fabrication. However, the glass soldering is high temperature process over 35$0^{\circ}C$ and the convex shape after solidification due to surface tension causes the stress concentration on optical fiber. The stress concentration on the optical fiber increases the optical insertion loss and possibility of crack formation. The shape of glass solder was designed referring to 2-D Axi-symmetric FEM simulation. To test the mechanical reliability, mechanical vibration test and shock test were done according to Telcorida GR-468-Core protocol. After each test, the optical loss of the stress distributed fiber assembly didn't exceed 0.5 dB, which passes the test.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.3
• /
• pp.15-20
• /
• 2012

In electronics industry, the coming electronic devices will be expected to be high integration and convergence electronics. And also, it will be expected that the coming electronics will be flexible, bendable and wearable electronics. Therefore, the demands and interests of bonding technology between flexible substrate and chip for mobile electronics, e-paper etc. have been increased because of weight and flexibility of flexible substrate. Considering fine pitch for high density and thermal damage of flexible substrate during bonding process, the micro solder bump technology for high density and low temperature bonding process for reducing thermal damage will be required. In this study, we researched on bonding technology of chip and flexible substrate by using 25um Cu pillar bumps and Sn-Bi solder bumps were formed by electroplating. From the our study, we suggest technology on Cu pillar bump formation, Sn-Bi solder bump formation, and bonding process of chip and flexible substrate for the coming electronics.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.4
• /
• pp.5-8
• /
• 2009

In this paper, a high-quality low-temperature co-fired ceramic (LTCC) solenoid inductor using a solder ball and an air cavity on a silicon wafer for three-dimensional (3-D) system-in-package (SiP) is proposed. The LTCC multi-layer solenoid inductor is attached using Ag paste and solder ball on a silicon wafer with the air cavity structure. The air cavity is formed on a silicon wafer through an anisotropic wet-etching technology and is able to isolate the LTCC dielectric loss which is equivalent to a low k material effect. The electrical coupling between the metal layer and the LTCC dielectric layer is decreased by adopting the air cavity. The LTCC solenoid inductor using the solder ball and the air cavity on silicon wafer has an improved Q factor and self-resonant frequency (SRF) by reducing the LTCC dielectric resistance and parasitic capacitance. Also, 3-D device stacking technologies provide an effective path to the miniaturization of electronic systems.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.1
• /
• pp.21-28
• /
• 2002

Bismuth and Indium added Sn-Cu-Ni solder alloy was investigated for a new lead free solder. The thermal, electrical and mechanical properties were characterized for the Sn-0.7%(Cu+Ni) solder alloy by adding 2~5% Bi and 2~ 10% In. The melting point of solder alloy was in range of 200 to $222^{\circ}C$ and the mushy zone was in range of 20 to $37^{\circ}C$. This alloys could be adapted to middle and high temperature solder materials. A new solder alloy composition. Sn-0.7%(Cu+Ni) -3.5%Bi-2%In is very promising with high performance and effective cost. The melting point was $220^{\circ}C$, the mushy zone range was $25^{\circ}C$, and mechanical, electrical and wetting properties were competitive with those of other lead-free solder except the lower elongation value.

• Journal of Welding and Joining
• /
• v.35 no.3
• /
• pp.7-14
• /
• 2017

The effect of high temperature-moisture on corrosion and mechanical properties for Sn-0.7Cu, Sn-3.0Ag-0.5Cu (SAC305) solders on flexible substrate was studied using Highly Accelerated Temperature/Humidity Stress Test (HAST) followed by three-point bending test. Both Sn-0.7Cu and SAC305 solders produced the internal $SnO_2$ oxides. Corrosion occurred between the solder and water film near flexible circuit board/copper component. For the SAC305 solder with Ag content, furthermore, octahedral corrosion products were formed near Ag3Sn. For the SAC305 and Sn-0.7Cu solders, the amount of internal oxide increased with the HAST time and the amount of internal oxides was mostly constant regardless of Ag content. The size of the internal oxide was larger for the Sn-0.7Cu solder. Despite of different size of the internal oxide, the fracture time during three-point bending test was not significantly changed. It was because the bending crack was always initiated from the three-point corner of the chip. However, the crack propagation depended on the oxides between the flexible circuit board and the Cu chip. The fracture time of the three-point bending test was dependent more on the crack initiation than on the crack propagation.

• ETRI Journal
• /
• v.32 no.3
• /
• pp.414-421
• /
• 2010

The interconnection mechanisms of a smart anisotropic conductive adhesive (ACA) during processing have been characterized. For an understanding of chemorheological mechanisms between the fluxing polymer and solder powder, a thermal analysis as well as solder wetting and coalescence experiments were conducted. The compatibility between the viscosity of the fluxing polymer and melting temperature of solder was characterized to optimize the processing cycle. A fluxing agent was also used to remove the oxide layer performed on the surface of the solder. Based on these chemorheological phenomena of the fluxing polymer and solder, an optimum polymer system and its processing cycle were designed for high performance and reliability in an electrical interconnection system. In the present research, a bonding mechanism of the smart ACA with a polymer spacer ball to control the gap between both substrates is newly proposed and investigated. The solder powder was used as a conductive material instead of polymer-based spherical conductive particles in a conventional anisotropic conductive film.