• KCI Concrete Journal
• /
• 제14권4호
• /
• pp.161-169
• /
• 2002

The mechanical properties of fiber reinforced porous concrete for use as a planting material were investigated in this study. Changes in physical and mechanical properties, subsequent to the addition of carbon fiber and silica fume, were studied. The effects of recycled aggregate were also evaluated. The applicability as planting work concrete material was also assessed. The results showed that there were no remarkable changes in the void and strength characteristics following the increase in proportion of recycled aggregate. Also, the mixture with 10% silica fume was found to be the most effective for strength enforcement. The highest flexural strength was obtained when the carbon fiber was added with $3\%$. It was also noticed that PAN-derived carbon fiber was superior to Pitch-derived ones in view of strength. The evaluation of its usage for vegetation showed that the growth of plants was directly affected by the existence of covering soil, in case of having the similar size of aggregate and void.

• 비파괴검사학회지
• /
• 제10권2호
• /
• pp.38-42
• /
• 1990

The specific strength of the fiber reinforced composite material is closely related to the anisotropy of the material. For the quantitative characterization of the anisotropy in the composite material, applied was CODF concept which was extensively used in the metallic material. As the results, the anisotropy of the material could be quantitatively analysed from the measurement of the phase velocities of the angular dependent $SH_o$ waves.

• Journal of Advanced Marine Engineering and Technology
• /
• 제18권3호
• /
• pp.63-67
• /
• 1994

A main property for fiber reinforced thermoplastic composite material in compression molding is the flow of fibers. This flow is so effective a long direction of acting force that this study examined for the inclined angel of 30$^{\circ}$, 45$^{\circ}$ and 6$^{\circ}$. Below the near softing temperature of plastic, the fiber has been fractured at a point so that the fiber strength is smaller then the local hydrostatic stress in the mold. It has been found that the position of fracture is changing accrding to the incling angle. In case of the above softing temperature, the larger the inclined is, the farther the flow of fiber move. Also the plastic flow has been progresed with the cicular are type.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 봄 학술발표회 논문집
• /
• pp.418-421
• /
• 1996

Carbon Fiber Sheet is very attractive for the upgrading damaged reinforced concrete due to its good tensile strength, handabilbity and resistance to corrosion. This paper discusses the applicability of continous carbon fiber sheet for a reinforcement of existeing reinforced concrete structure located in Pusan. Examples of site data and actual concrete rehabilitation project at slab structure related to construction method used carbon fiber sheet will be given.

• 대한기계학회논문집A
• /
• 제30권12호
• /
• pp.1518-1525
• /
• 2006

Finite element analyses of structures made of the fiber reinforced composites require an adequate method to characterize the high anisotropic behavior induced by one or several layers of fiber cords with different spatial orientation embedded in a rubber matrix. This paper newly proposes a continuum based rebar element considering change of the orientation of the fiber during deformation of the composite. The mechanical behavior of the embedded fiber is modeled using two-node bar elements in order to consider the relative deformation and spatial orientation of the embedded fiber. For improvement of the analysis accuracy, the load-displacement curve of fiber is applied to the stiffness matrix of fiber. A finite element program is constructed based on the total Lagrangian formulation considering both geometric and material nonlinearity. Finite element analyses of the tensile test are carried out in order to evaluate the validity of the proposed method. Analysis results obtained with the proposed method provides realistic representation of the fiber reinforced rubber composite compared to results of other two models by the Halpin-Tsai equation and a rebar element in ABAQUS/Standard.

• 한국세라믹학회지
• /
• 제46권3호
• /
• pp.301-305
• /
• 2009

The novel carbon coating process for interlayer of fiber reinforced ceramic composites between fiber and matrix was performed by carbonizing phenolic resin solution that coated on fiber surface in $N_2$ atmosphere at $600^{\circ}C$ to improve the strength and fracture toughness of CMC(ceramic matrix composite). 160 nm carbon layer was coated on fiber surface with 5 vol% of phenolic resin solution. Since the process temperature ($600^{\circ}C$) is lower than chemical vapor deposition($900{\sim}1000^{\circ}C$), the strength and toughness could be preserved. Furthermore the coating thickness uniformity was improved to 8% of deviation along the stacking sequence. Therefore, prevention from fiber degradation during coating process and controlling coating thickness uniformity along the preform depth were achieved by coating with phenolic resin carbonizing method.

• 한국생산제조학회지
• /
• 제21권3호
• /
• pp.421-424
• /
• 2012

Carbon Fiber reinforced composite material can be designed for the optimized performances of structural member that have achieve appropriate mechanical properties with cross-sectional shape, fiber direction, stacking sequence and thickness. So there are needed extensive databases each optimal design of CFRP structural member by impact through the preparation of different shape, interface number, thickness and stacking angle. When pressure is applied to structural member, compression, bending and torsion is shown on the corresponding member. For the effective utilization of fiber reinforced composite material as main structural member, optimized design technology should be established to maximize mechanical properties for compression, bending and torsion. In this paper, CFRP prepreg sheet with different stacking angle is manufactured in CFRP and hybrid(Al+CFRP) with circular cross-section. Strength and stiffness is gotten respectively by flexure test. CFRP structure and hybrid structure can be compared with each other. The best design guideline can be analyzed by use of this study result.

• Composites Research
• /
• 제34권1호
• /
• pp.57-62
• /
• 2021

조선해양산업에서 친환경 선박 및 경량화 기자재에 관한 관심이 높아짐에 따라 파이프 등의 기자재에 복합재료를 적용하고 있다. 본 연구에서는 친환경 및 내열/난연 성능을 요구하는 파이프 단열재 커버에 적용하기 위해 친환경 소재인 바잘트 섬유강화 퓨란복합재료(BFC, basalt fiber reinforced furan composite)를 제조하였다. BFC 소재의 낮은 물성을 강화시키기 위해 후경화 조건의 최적화 연구를 수행하였고, BFC 소재의 기계적강도, 내열/난연 특성 강화, 친화경 특성에 대한 실험과 평가를 진행하였다. 최종적으로 연구 결과 조선해양기자재인 파이프 단열재 커버에 BFC 소재의 적용이 가능함을 확인하였다.

• Composites Research
• /
• 제24권3호
• /
• pp.12-16
• /
• 2011

경량복합소재의 고속인장시험을 수행하여 변형률속도에 따른 강도변화를 측정하고자 한다. 준 정적 시험인 경우 섬유강화 복합소재의 인장시험은 ASTM D3039에 따른 시편 형상이 사용되지만 고속 인장시험인 경우 표준화된 시편 형상에 대한 연구가 진행되어 있지 않다. 본 연구에서는 ASTM D638에 나타난 시편 형상을 기본으로 몇 가지 변형된 형태의 시편을 가지고 고속인장 시험을 수행하여 변형률 속도에 따른 경량복합소재의 강도 변화를 측정하였다. 낙하방식의 고속인장 시험기를 제작하여 변형률 속도 15/s, 100/s에서 시편의 형상에 따른 섬유강화 복합소재의 인장거동을 측정하였으며 시편의 폭이 6mm, 8mm, 10mm인 경우에 대하여 시험을 수행하였다. 측정 결과 시편의 폭이 8mm인 경우 섬유강화 복합소재의 강도를 정확하게 평가할 수 있는 것으로 나타났다.

• 한국환경복원기술학회지
• /
• 제16권2호
• /
• pp.127-135
• /
• 2013

This study was carried out to verify the suitability of GRS(Glass-fiber Reinforced Slag) as natural type landscape stone according to the material property and structural safety performance standards. The structural safety performance of the GRS panel showed 12.4MPa and 16.2MPa each in flexural strength at 2 and 3% content of glass fiber while the flexural strength at 4 and 5% of glass fiber content showed 26.9MPa, and 30.2MPa, respectively, all satisfying the standards. In addition, air-dried gravity was found to be 1.82~1.89 in measuring range at 2~5% level of glass fiber content, satisfy the existing standards 1.8~2.3. In structural safety performance, the range of flexural strength consequent on glass fiber content was surveyed to be 12.8~30.2MPa, all satisfying the performance standards, while 10MPa and more while the compressive strength range was found to be 41.5~53.3MPa, all satisfying the performance standards, 40~60MPa. This study judged the suitability of only the items for a property of matter of landscape stone GRS by applying the natural-form landscape stone GFRC material standard, but in case an installation constructed with GRS material comes into existence later, there should be comprehensive performance guidelines through the research on durability, landscape performance and environmental and ecological performance.