• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.140-143
• /
• 2001

A study has been made on the recovery of nitric acid and valuable metals such as Cu, Sn, Pb from the spent nitric etching solutions. The nitric acid was extracted effectively by TBP but the heavy metals such as Fe, Cu, Sn, Pb were not extracted by TBP from the spent nitric etching solutions. From the experimental results, 95% of nitric acid in spent etching solution was extracted at O:A ratio of 3:1 with five stage by 60% TBP and 98% of nitric acid was stripped from the loaded organic phase at O:A ratio of 1:1 with four stages by distilled water. After extracting nitric acid, Cu was recovered as a metal by electrowinning effectively and Sn was successfully removed by precipitation method by adjusting the pH of raffinate solution. Finally, Pb was recovered by cementation with iron scrap at $65^{\circ}C$. Parameters controlling the cementation process, such as temperature, pH and the effect of the additives were investigated.

• Electrical & Electronic Materials
• /
• v.10 no.7
• /
• pp.645-650
• /
• 1997

We manufactured CoNbZr/Cu/CoNbZr multi-layer films by rf magnetron sputtering methods and formed the patterns on the deposited multi-layer films. In this study, we fabricated a new etchant for forming the patterns by the wet etching with etchant and we searched for the best etching conditions and the etchant composition. Cu was etched selectively independent on the concentration of iron chloride solution, but amorphous CoNbZr thin film did not. The etchant was achieved by iron chloride solution(17.5 mol%) mixed with HF (20 mol%) during 150 sec, which etched CoNbZr/Cu/CoNbZr multi-layer films at the same time. Also, the etchant etched CoNbZr/Cu/CoNbZr multi-layer films by the three-step. It was shown that the cross-section had the isotropic structure and excellent etching characteristics with the above etchant.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.1033-1036
• /
• 2003

In this paper, Si anisotropic etching characteristics of tetramethylammonium hydroxide (TMAH)/ ammonium persulfate (AP) solutions were investigated to realize the optimum structure of a diaphragm for the piezoresistive pressure sensor application. Due to its low toxicity and its high compatibility with the CMOS processing, TMAH was used as Si anisotropic etchants. The variations of Si etch rate on the etching temperature, TMAH concentration, and etching time were obtained. With increasing the etching temperature and decreasing TMAH concentrations, the Si etch rate is increased while a significant non-uniformity exists on the etched surface because of formation of hillocks on the <100> surface. With the addition of AP to TMAH solution, the Si etch rate is increased and an improvement in flatness on the etching front is observed. The Si etch rate is also maximized with increasing the number of addition of AP to TMAH solution per one hour. The Si square diaphragms of 20${\mu}{\textrm}{m}$ thickness and 100~400${\mu}{\textrm}{m}$ one-side length were fabricated successfully by applying optimum Si etching conditions of TMAH/AP solutions.

• The Journal of Korean Academy of Prosthodontics
• /
• v.23 no.1
• /
• pp.83-95
• /
• 1985

The purpose of this study was to evaluate microstructures on the etched surface of 11 base metal alloys for dental restorations and to observe the relationship between the etching pattern and beryllium. For this purpose, the following experiments were done; 11 base metal alloys were etched in (1) 10% $H_2SO_4$, (2) 10% $H_2SO_4$, 9 parts+methanol 1 part (3) Conc. $HNO_3$ 25%+glacial acetic acid 25%+$H_2O$ 50% (4) Conc. $HNO_3$ 5% (5) 2% glacial acetic acid added to Conc. $HNO_3$ 1% solution, with their etching conditions varied. Etched surface of alloys were examined under the scanning electron microscope. Results were as follows; 1. Almost all of Ni-Cr-Be alloys showed gooed etchd surface in $H_2SO_4$, solution, while some of those alloys which contains no beryllium showed good etched surface in $HNO_3$ solution. 2. Main components of etching solution can vary etching pattern of alloys. 3. Gamma prime phase relief, which can be found in all Ni-Cr-Be alloys, can't be found in any alloy that contains no beryllium.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.3
• /
• pp.149-157
• /
• 1993

In the study of TAB(Tape Automated Bonding)technologies, Cu-Cr sputtered seed layer has been used to improve the adhesion between Polyimide and Cu film and electrical properties. But the Cu electrodeposit on Cu-Cr film had poor adhesion or powder-like form due to the surface Cr oxides on the Cu-Cr film. By means of activating the Cu-Cr film with the oxalic acid and phosphoric acid, the Cu film with the improved adhesion could be coated on the Cu-Cr sputtered film in CuSO4 solution. The etching rate was compared with increasing the Cr content of the sputtered Cu-Cr film, and anodic polarization curve in FeCl3 solution was investigated. With increasing the Cr content, the etching rate was reduced. The clean etching cross section could be obtained with increasing the concentration of FeCl3 solution. But above the 13 w/o Cr content, Cu-Cr sputtered film could not bed etched cleanly only with FeCl3 solution and additives were needed.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1252-1254
• /
• 2005

Recently, PDP barrier ribs require the formation of complex structure so that they are usually formed by etching method. For producing the fine ribs structure, during the etching process the metal ions of matrix (glass) of barrier materials should be understood on the etching mechanism with etching condition. We analyzed the quantity of Pb, Si, and B ions from the etch solution as a function of etching time.

• Journal of the Semiconductor & Display Technology
• /
• v.19 no.2
• /
• pp.77-81
• /
• 2020

Silicon wafer etching in micro electro mechanical systems (MEMS) fabrication is challenging to form 3-D structures. Well known Si-wet etch of silicon employs potassium hydroxide (KOH), tetramethylammonium hydroxide (TMAH) and sodium hydroxide (NaOH). However, the existing silicon wet etching process has a fatal disadvantage that etching of the back side of the wafer is hard to avoid. In this study, a wet etching bath for 150 mm wafers was designed to prevent back-side etching of silicon wafer, and we demonstrated the optimized process recipe to have anisotropic wet etching of silicon wafer without any damage on the backside. We also presented the design of wet bath for 300 mm wafer processing as a promising process development.

• Journal of Sensor Science and Technology
• /
• v.30 no.1
• /
• pp.10-14
• /
• 2021

Wet etching is more economical than dry etching and provides a uniform etching depth regardless of wafer sizes. Typically, potassium hydroxide (KOH) and tetra-methyl-ammonium hydroxide (TMAH) solutions are widely used for the wet etching of silicon. However, there is a limit to the wet etching process when a material deposited on an unetched surface reacts with an etching solution. To solve this problem, in this study, an apparatus was designed and manufactured to physically block the inflow of etchants on the surface using a rubber O-ring. The proposed apparatus includes a heater and a temperature controller to maintain a constant temperature during etching, and the hydrostatic pressure of the etchant is considered for the thin film structure. A corrugation membrane with a diameter of 800 ㎛, thickness of 600 nm, and corrugation depth of 3 ㎛ with two corrugations was successfully fabricated using the prepared device.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.9
• /
• pp.803-809
• /
• 2005

Cerium ammonium nitrate (CAN) and nitric acid was used an etchant and an additive for Ru etching and polishing. pH and Eh values of the CAN and nitric acid added chemical solution satisfied the Ru etching condition. The etch rate increased linearly as the concentration of CAN increased. Nitric acid added solution had the high etch rate. But micro roughness of etched surfaces was not changed before and after etching, The removal rate of Ru film was the highest in $1wt\%$ abrasive added slurry, and not increased despite the concentration of alumina abrasive increased to $5wt\%$. Even Ru film was polished by only CAN solution due to the friction. The highest removal rate of 120nm/min was obtained in 1 M nitric acid and $1wt\%$ alumina abrasive particles added slurry. The lowest micro roughness value was observed in this slurry after polishing. From the XPS analysis of etched Ru surface, oxide layer was founded on the etched Ru surface. Therefore, Ru was polished by chemical etching of CAN solution and oxide layer abrasion by abrasive particles. From the result of removal rate without abrasive particle, the etching of CAN solution is more dominant to the Ru CMP.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.4
• /
• pp.51-56
• /
• 2012

In order to fabricate through-Si-vias for thermal vias by using wet etching process, anisotropic etching behavior of Si substrate was investigated as functions of concentration and temperature of TMAH solution in this study. The etching rate of 5 wt%, 10 wt%, and 25 wt% TMAH solutions, of which temperature was maintained at $80^{\circ}C$, was $0.76{\mu}m/min$, $0.75{\mu}m/min$, and $0.30{\mu}m/min$, respectively. With changing the temperature of 10 wt% TMAH solution to $20^{\circ}C$ and $50^{\circ}C$, the etching rate was reduced to $0.067{\mu}m/min$ and $0.233{\mu}m/min$, respectively. Through-Si-vias of $500{\mu}m$-depth could be fabricated by etching a Si substrate for 5 hours in 10 wt% TMAH solution at $80^{\circ}C$ after forming same via-pattern on each side of the Si substrate.