• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.1012-1018
• /
• 1996

To investigate the final structures and reactions of silicides a somewhat thick Ti monolayer Co monolayer and Co/Ti bilayer films were deposited on single Si(100) wafer by electron beam evaporation followed by heat treatment using RTA system in N2 ambient. TiO2 film formed between Ti and TiSi2 layers due to oxgen or moisture in the Ti monolayer sample. The final layer structure obtained after the silicidation heat-treatment of the Co/Ti bilayer sample turned out to be TiSi2/CoSi2/Ti-Co-Si alloy/CoSi2/Si sbustrate. This implies that imperfect layer inversion occurred due to the formation of Ti-Co-Si intermediate phase.

• Journal of the Korean Vacuum Society
• /
• v.7 no.3
• /
• pp.208-213
• /
• 1998

Silicidation of the Co/Ti/Si bilayer system in which Ti is used as epitaxy promoter for $CoSi_2$has recently received much attention. The Co/Ti bilayer on the spacer oxide of gate electrode must be thermally stable at high temperatures for a salicide transistor to be fabricated successfully. In the $SiO_2$substrate was rapid-thermal annealed. The Sheet resistances of the Co/Ti bilayer increased substantially after annealing at $600^{\circ}C$, which is due to the agglomeration of the Co layer to reduce the interface energy between the Co layer and the $SiO_2$substrate. In the bilayer system insulating Ti oxide stoichiometric Ti oxide and silicide were not found after annealing.

• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.579-583
• /
• 1998

Silicide layer structures, agglomeration of silicide layers, and dopant redistributions for the Co/Ti bilayer sputter-deposited on the P-doped polycrystalline Si substrate and subjected to rapid thermal annealing were investigated and compared with those on the single Si substrate. The $CoSi_2$ phase transition temperature is higher and agglomeration of the silicide layer occurs more severely for the Co/Ti bilayer on the doped polycrystalline Si substrate than on the single Si substrate. Also, dopant loss by outdiffusion is much more significant on the doped polycrystalline Si substrate than on the single Si substrate. All of these differences are attributed to the grain boundary diffusion and heavier doping concentration in the polycrystalline Si. The layer structure after silicidation annealing of Co/ Tildoped - polycrystalline Si is polycrystalline CoSi,/polycrystalline Si, while that of Co/TiI( 100) Si is Co- Ti- Si/epi- CoSi,/(lOO) Si.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.484-492
• /
• 1998

The formation mechanism of the epitaxial cobalt silicide from Co/Ti/OOO) Si structure has been investigated. The transition temperature of CoSi to CoSi, was found to increase with increasing the Ti interlayer thickness, which may be owing to the occupation of the tetrahedral sites by Ti atoms in the CoSi crystal structure as well as the blocking effect of the Ti interlayer on the diffusion of Co. Also, the Co- Ti-O ternary compound formed at the metal! Si interface at the begining of silicidation, which seems to play an important role in epitaxial growth of Co silicide. The final layer structures obtained after a rapid thermal annealing of the Cot Ti/( 100) Si bi-layer structure turned out to be Ti oxide/Co- Ti-Si/epi-$CoSi_2$/OOO)

• Korean Journal of Materials Research
• /
• v.13 no.2
• /
• pp.88-93
• /
• 2003

Co/Ti bilayer structure in Co salicide process helps to the improvement of device speed by lowering contact resistance due to the epitaxial growth of $CoSi_2$layers. We investigated the epitaxial growth and interfacial mass transport of $CoSi_2$layers formed from $150 \AA$-Co/Ti structure with two step rapid thermal annealing (RTA). The thicknesses of Ti layers were varied from 20 $\AA$ to 100 $\AA$. After we confirmed the appropriate deposition of Ti film even below $100\AA$-thick, we investigated the cross sectional microstructure, surface roughness, eptiaxial growth, and mass transportation of$ CoSi_2$films formed from various Ti thickness with a cross sectional transmission electron microscopy XTEM), scanning probe microscopy (SPM), X-ray diffractometery (XRD), and Auger electron depth profiling, respectively. We found that all Ti interlayer led to$ CoSi_2$epitaxial growth, while $20 \AA$-thick Ti caused imperfect epitaxy. Ti interlayer also caused Co-Ti-Si compounds on top of $CoSi_2$, which were very hard to remove selectively. Our result implied that we need to employ appropriate Ti thickness to enhance the epitaxial growth as well as to lessen Co-Ti-Si compound formation.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.120-125
• /
• 2007

The microstructure, mechanical properties and melting range of Ni-Cr-Mo based alloys were investigated to develop Be-free Ni-Cr-Mo base dental alloys for Porcelain-Fused-to-Metal Firing(PFM). All as-cast alloys showed dendritic structure. Rockwell hardness of 20Cr7Mo was increased with addition of Si and Ti. On the contrary, it was decreased with addition of Co. The duplex alloying elemental addition such as 3Co + xTi, 2Si + xCo and 2Si + xTi to 20Cr7Mo resulted in much increase of hardness. Rockwell hardness and compressive strength for 20Cr3CoSiTi or 17Cr6CoSiTi alloy that add Si-Ti had similar values compared to the commercial alloys. Melting range for 20Cr3CoSiTi and 17Cr6CoSiTi alloy that add Si-Ti showed similar or lower than commercial alloys. In conclusion, 20Cr3CoSiTi and 17Cr6CoSiTi alloys can be applied for commercial use.

• Korean Journal of Materials Research
• /
• v.6 no.12
• /
• pp.1192-1198
• /
• 1996

배선 재료나 salicide 트랜지스터에 적용될 것으로 기대되는 Cu 배선과 Co 단일층 및 Co/Ti 이중층을 사용하여 형성된 코발트 실리사이드간의 열적 안정성에 대하여 조사하였다. 40$0^{\circ}C$열처리후 Cu3Si 막이 CoSi2층과 Si 기판 사이에 형성되었는데, 이것은 Cu 원자의 확산에 기인한 것이다. $600^{\circ}C$에서의 열처리 후에 형성된 최종막의 구조는 각각 Cu/CoSi2/Cu3Si/Si과 TiO2/Co-Ti-Si 합금/CoSi2/Cu3Si/Si였으며, 상부에 형성된 TiO2층은 산소 오염에 의한 것으로 밝혀졌다.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.324-332
• /
• 1995

전자빔 증착법을 사용하여 Ti과 Co를 Si(100) 단결정, 다결정 Si 및 Si$O_{2}$기판에 증착한 후 90$0^{\circ}C$에서 20초 급속 열처리하여, Co/Ti 이중박막으로부터의 실리사이드화 반응을 조사하였다. 단결정 시편의 경우 Ti의 두께를 5~6mm로 최소화함으로서 두께가 균일하고 기판과의 계면이 평탄하며 비저항이 낮고 열적 안정성이 높은 Co$Si_{2}$ 에피박막을 형성할 수 있었다. 그러나 다결정 시편에는 두께와 계면이 불균일하고 열적으로도 불안정한 다결정의 Co$Si_{2}$와 그 위에 두개의 Co-Ti-Si혼합층이 형성되었다. 한편 Si$O_{2}$ 우에 증착된 Co/Ti은 열처리를 하여도 확산하지 않고 그대로 남아 있어서, Co/Ti 이중박막의 Si$O_{2}$와의 반응성이 미약함을 보여 주었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.61-61
• /
• 2000

Device의 고성능화를 위하여 소자의 고속화, 고집적화가 가속됨에 따라 SALICIDE Process가 더욱 절실하게 요구되고 있다. 이러한 SALICIDE Process의 재료로써는 metal/silicide 중에서 비저항이 가장 낮은 TiSi2(15-25$\mu$$\Omega$cm), CoSi2(17-25$\mu$$\Omega$cm)가 일반적으로 많이 연구되어 왔다. 그러나 Ti-silicide의 경우 Co-silicide는 배선 선폭의 감소에 따른 면저항 값의 변화가 작으며, 고온에서 안정하고, 도펀트 물질과 열역학적으로 안정하여 화합물을 형성하지 않는다는 장점이 있으마 Ti처럼 자연산화막을 제거할 수 없어 Si 기판위에 자연산화막이 존재시 균일한 실리사이드 박막을 형성할 수 없는 단점등을 가지고 있다. 본 연구에서는 Ti Capping layer 에 의한 균일한 Co-silicide의 형성을 일반적인 Si(100)기판과 SCl 방법에 의하여 chemical Oxide를 성장시킨 Si(100)기판의 경우에 대하여 연구하였다. 스퍼터링 방법에 의해 Co를 150 증착후 capping layer로써 TiN, Ti를 각각 100 씩 증착하였다. 열처리는 RTP를 이용하여 50$0^{\circ}C$~78$0^{\circ}C$까지 4$0^{\circ}C$ 구간으로 N2 분위기에서 30초 동안 열처리를 한후, selective metal strip XRD, TEM의 분석장비를 이용하여 관찰하였다. lst RTP후 selective metal strip 후 면저항의 측정과 XRD 분석결과 낮은 면저항을 갖는 CoSi2로의 상전이는 TiN capping과 Co 단일박막이 일반적인 Si(100)기판과 interfacial oxide가 존재하는 Si(100)기판위에서 Ti capping의 경우보다 낮은 온도에서 일어났다. 또한 CoSi에서 CoSi2으로 상전이는 일반적인 Si(100)기판위에서 보다 interfacial Oxide가 존재하는 Si(100)기판 위에 TiN capping과 Co 단일박막의 경우 열처리 후에도 Oxide가 존재하는 불균인한 CoSi2박막을 관찰하였으며, Ti capping의 경우 Oxise가 존재하지 않는 표면과 계면이 더 균일한 CoSi2 박막을 형성 할 수 있었다.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.335-340
• /
• 2000

We investigated the role of the capping layers in the formation of the cobalt silicide in Co/Si systems with TiN and Ti capping layers and without capping layers. The Co/Si interfacial reactions and the phase transformations by the rapid thermal annealing (RTA) processes were observed by sheet resistance measurements, XRD, SIMS and TEM analyses for the clean silicon substrate as well as for the chemically oxidized silicon substrate by $H_2SO_4$. We observed the retardation of the cobalt disilicide formation in the Co/Si system with Ti capping layers. In the case of Co/$SiO_2$/Si system, cobalt silicide was formed by the Co/Si reaction due to with the dissociation of the oxide layer by the Ti capping layers.