• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.842-851
• /
• 2009

The long-term reliability of Sn-0.3wt%Ag-0.7wt%Cu solder joints was evaluated and compared with Sn-3.0wt%Ag-0.5wt%Cu under thermal shock conditions. Test vehicles were prepared to use Sn-0.3Ag-0.7Cu and Sn-3.0Ag-0.5Cu solder alloys. To compare the shear strength of the solder joints, 0603, 1005, 1608, 2012, 3216 and 4232 multi-layer ceramic chip capacitors were used. A reflow soldering process was utilized in the preparation of the test vehicles involving a FR-4 material-based printed circuit board (PCB). To compare the shear strength degradation following the thermal shock cycles, a thermal shock test was conducted up to 2,000 cycles at temperatures ranging from $-40^{\circ}C$ to $85^{\circ}C$, with a dwell time of 30 min at each temperature. The shear strength of the solder joints of the chip capacitors was measured at every 500 cycles in each case. The intermetallic compounds (IMCs) of the solder joint interfaces werealso analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results showed that the reliability of Sn-0.3Ag-0.7Cu solder joints was very close to that of Sn-3.0Ag-0.5Cu. Consequently, it was confirmed that Sn-0.3Ag-0.7Cu solder alloy with a low silver content can be replaced with Sn-3.0Ag-0.5Cu.

• Korean Journal of Metals and Materials
• /
• v.48 no.3
• /
• pp.248-255
• /
• 2010

The effect of various alloying elements and melt treatment on the microstructural control of Al-Sn metallic bearing alloy was investigated. The thickness of tin film crystallized around primary aluminum decreased with the addition of 5% Cu in Al-Sn alloy, with tin particles being reduced in size by intervening the Ostwald ripening. With the addition of Si in Al-10%Sn alloy, the tin particles were crystallized with eutectic silicon, resulting in uniform distribution of tin particles. With the addition of Cu and Si in Al-Sn alloy, both the tensile strength and yield strength increased, with the increasing rate of yield strength being less than that of tensile strength. Although the Al-10%Sn-7%Si alloy has similar tensile strength compared with Al-10%Sn-5%Cu, the former showed superior abrasion resistance, resulting from preventing the tin particles from movement to the abrasion surface.

• Journal of Welding and Joining
• /
• v.20 no.1
• /
• pp.91-96
• /
• 2002

Three different kinds of substrate used in this study : bare Cu, electroless Ni/Cu substrate with a Nilayer thickness of $5\mu\textrm{m}$, immersion Au/electroless Ni/Cu substrate with the Au and Ni layer of $0.15\mu\textrm{m}$ and $5\mu\textrm{m}$ thickness, respectively. The wettability and interfacial tension between various substrate and Sn-3.5Ag solder were examined as a function of soldering temperature, types of flux. The wettability of Sn-3.5Ag solder increased with soldering temperature and solid content of flux. The wettability of Sn-3.5Ag solder was affected by the substrate metal finish used, i.e., nickel, gold and copper. Intermetallic compound formation between liquid solder and substrate reduced the interfacial energy and decreased wettability.

• Journal of Korea Foundry Society
• /
• v.17 no.3
• /
• pp.245-251
• /
• 1997

Solderability, interfacial reaction and mechanical properties of joint between Sn-Bi-Ag base solder and Cu-substrate were studied. Solders were subjected to aging treatments to see the change of mechanical properties for up to 30 days at $100^{\circ}C$, and then also examined the changes of microstructure and morphology of interfacial compound. Sn-Bi-Ag base solder showed about double tensile strength comparing to Pb-Sn eutectic solder. Addition of 0.7wt%Al in the Sn-Bi-Ag alloy increase spread area on Cu substrate under R-flux and helps to reduce the growth of intermetallic compound during heat-treatment. According to the aging experiments of Cu/solder joint, interfacial intermetallic compound layer was exhibited a parabolic growth to aging time. The result of EDS, it is supposed that the soldered interfacial zone was composed of $Cu_6Sn_5$.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.4
• /
• pp.23-28
• /
• 2009

We investigated the wafer-level MEMS capping process for which cavity formation in Si wafer was not required. Ni caps were formed by electrodeposition on 4" Si wafer and Ni rims of the Ni caps were bonded to the Cu rims of bottom Si wafer by using epoxy. Then, top Si wafer was debonded from the Ni cap structures by using SnBi layer of low melting temperature. As-evaporated SnBi layer was composed of double layers of Bi and Sn due to the large difference in vapor pressures of Bi and Sn. With keeping the as-evaporated SnBi layer at $150^{\circ}C$ for more than 15 sec, SnBi alloy composed of eutectic phase and Bi-rich $\beta$ phase was formed by interdiffusion of Sn and Bi. Debonding between top Si wafer and Ni cap structures was accomplished by melting of the SnBi layer at $150^{\circ}C$.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.99-102
• /
• 2003

Reactions between 48Sn-52In solder and under bump metallurgies(UBM) such as 100nm $Ti/8{\mu}m$ Cu and 300nm Al/400nm Ni(V)/400nm Cu have been investigated, and the shear strength of 48Sn-52In solder bumps on each UBM has been evaluated. While intermetallic compounds with two different morphologies were continuously thickened on Ti/Cu with repeating the reflow process, the intermetallics on Al/Ni(V)/Cu spalled into the solder with increasing the number of reflow times. The solder bumps on Ti/Cu exhibited higher shear strength than those on Al/Ni(V)/Cu.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.313-316
• /
• 2008

This work sought to examine the suitability of twin roll strip casting for Ag-27%Cu-25%Zn-3%Sn brazing alloy (BAg-7A) and to investigate the mechanical properties and microstructure of the strip. The effect of aging heat treatment on the properties was also studied,. This new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analysis of the Ag-27%Cu-25%Zn-3%Sn strip represented eutectic microstructure of a Cu-rich phase and a Ag-rich matrix regardless of heat treatment. The results of mechanical tests showed tensile strength of 470MPa, a significant enhancement, and an 18% elongation of the twin roll casted strip, due mainly to the solid solution strengthening of Zn atoms (${\sim}20%$) in the Cu-rich phases. Tensile results showed gradually decreasing strengths and increasing elongation with aging heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.73-73
• /
• 2000

Shear strength of BGA solder joints on Cu pad was studied for Cu-contained Sn n.5 a and 2.5wt.% Cu) and Sn-Pb (o.5wt.% Cu) solders, with emphasis on the roles of the C Cu-Sn intermetallic layer thickness and the roughness of the interface between the i intermetallic layer and solder. The shear strength test was performed both for a as-soldered s이der joints with soldering reaction times of 1, 2, 4 min and for aged s이der j joints at 170 C up to 16 days. The Cu addition to both pure Sn and eutectic Sn-Pb s solders increased the intermetallic layer thickness at both soldering and aging t temperatures. The Cu addition also resulted in changes in the roughness of the interface b between the intermetallic layer and solder at as-soldered states. With increasing Cu c content. the interface roughened for Sn-Cu solders whereas it flattened for Sn-Pb-Cu s solders. The shear fractures in all solder joints investigated were confined in the bulk s solder rather than through the intermetallic layer. Therefore, the effect of Cu content in s solders on the shear strength of the solder joints was primarily attributed to its i influence on the micros$\sigma$ucture of bulk solder, such as the size and spatial distributions of CU6Sn5 precipitates. In addition, the critical intermetallic layer thickness for a m maximum shear strength seemed to depend on the Cu content in bulk solder.older.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.21 no.1
• /
• pp.145-153
• /
• 2013

In this study, shear punch-creep (SP-Creep) at Sn-4Ag/Cu pad the joint was tested by using environment-friendly Pb-free solder alloy Sn-4Ag of electronic components. Pb eutectic alloy (Sn-37Pb) joints limited to environmental issues with reflow time (10sec, 30sec, 100sec, 300sec) according to two types of solder alloy joints are compared and evaluated by creep strain rate, rupture time and IMC (Intermetallic Compound) behavior. As the results, reflow time increases with increasing thickness of IMC can be seen at overall 100sec later in case of two solder joints on the IMC thickness of Sn-4Ag solder joints thicker than Sn-37Pb solder joints. In addition, when considering creep evaluation factors, lead-free solder alloy Sn-4Ag has excellent creep resistance more than Pb eutectic alloy. For this reason, the two solder joints, such as in the IMC (Cu6Sn5) was formed. However, the creep resistance of Sn-4Ag solder joints was largely increased in the precipitation strengthening effect of dispersed Ag3Sn with interface more than Sn-37Pb solder joints.

• Korean Journal of Metals and Materials
• /
• v.47 no.8
• /
• pp.500-507
• /
• 2009

Pb-free solder has recently been used in electronics in efforts to meet environmental regulations, and a number of Pb-free solder alloy choices beyond the near-eutectic SnAgCu solder are now available. With increased demand for thin and portable electronics, the high cost of alloys containing significant amounts of silver and their poor mechanical shock performance have spurred the development of low Ag SnAgCu solder, which provides improved mechanical performance at a reasonable cost. Although low Ag SnAgCu solder exhibits significantly higher fracture resistance under high-strain rates, little thermal fatigue data exist for this solder. Therefore, it is necessary to investigate thermal fatigue reliability of low Ag SnAgCu solder under variation of thermal stress in order to allow its implementation in electronic products with high reliability requirements. In this study, the reliability of Sn0.3Ag0.7Cu(SAC0307), a low Ag solder alloy, is discussed and compared with that of Sn3Ag0.5Cu(SAC305). Three sample types and six samples size are evaluated. Mechanical properties and microstructure of the solder joint are investigated under thermal shock cycles. It was observed that the mechanical strength of SAC0307 dropped slightly with thermal cycling relative to that of SAC305. This reveals that the failure mode of SAC0307 is different from that SAC305 under this critical condition.