• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.659-674
• /
• 2000

A large increase in the use of thin film coating of hydroxyapatite(HA) in implant dentistry is driven by the desire to take advantage of the excellent biocompatibility and high strength of HA coating. The purpose of this study was to evaluate the effects of HA-coated implants by ion Beam Assisted Deposition(IBAD) method in comparison to the sand-blasted and machined surfaces. Osteoblast culture test, removal torque test and histomorphometric analysis were performed and the following results obtained; 1. Examination of the osteoblast cultures displayed no difference in the secretion of alkaline phosphatase between the various specimen, but IBAD with pure HA specimen showed low alkaline phosphatase secretion(p<0.05). 2. Removal torque tests showed HA-coated implants by IBAD method to be similar in high value to the implants with sand-blasted surface than the implants with machined surface. And the ovariectomized group showed low mechanical test value than the normal group(p<0.05). 3. Histomorphometrical comparisons were performed on undecalcified ground sections. HA-coated implants by IBAD method demonstrated the highest mean bone-to-metal contact ratio on all threads and 3-best consecutive threads, and the implants with sand-blasted surface and implants with machined surface was in the next consecutive order(p<0.05). HA-coated implants showed slightly higher bone-to- metal contact ratio than sand-blasted implants, but no statistically significant difference was obtained between the two materials. The ovariectomized group showed lower value of bone-to-metal contact ratio than the normal group, but no statistically significant difference was obtained between the two groups. 4. Evaluation of bone volume on all threads and 3-best consecutive threads showed no statistically significant difference among the different surface treatment groups, but showed lower bone volume in ovariectomized group than in the normal group(p<0.05). According tn these results, thin film coated implants with HA showed high bone contact ratio, bone volume and removal torque strength in the short term, but long term observation is needed.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.1
• /
• pp.41-52
• /
• 2009

The surface treatment of titanium implant could bring out the biochemical bonding between bone and implant. The purpose of this study was to evaluate the biomechanical bone response of Mg-ion implanted implants with plasma source ion implantation method. Twelve New Zealand white rabbits were included in this study. Each rabbit received one control fixture (blasted with resorbable blasting media, RBM) and three types of Mg ion implanted fixtures in tibiae. The implants were left in place for 6 weeks before the rabbits were sacrificed. Removal torque value and resonance frequency analysis (ISQ) were compared. The repeated measured analysis of variance was used with $P{\leq}0.05$ as level of statistical significance. ISQ was not different among all groups. However, the ISQ was increased after 6 weeks healing. The group had lowest ISQ value showed the greatest increment. Mg-1 implants with 9.4% retained ion dose showed significantly higher removal torque value than that of the other implants. From this results, it is concluded that the Mg-1 implants has stronger bone response than control RBM surface implant.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.164-173
• /
• 2009

Purpose: The purpose of this study was to evaluate the effect of abutment material on screw-loosening before and after cyclic loading. Among the different materials of abutments, zirconia and metal abutment were used. Material and methods: Two types of implant systems: external butt joint(US II, Osstem Implant, Korea) and internal conical joint(GS II, Osstem Implant, Korea) were used. In each type, specimens were divided into two different kinds of abutments: zirconia and metal(n=5). The implant was rigidly held in a special holding to device ensure fixation. Abutment was connected to 30 Ncm with digital torque gauge, and was retightened in 30 Ncm after 10 minutes. The initial removal torque values were measured. The same specimens were tightened in 30 Ncm again and held in the cycling loading simulator(Instron, USA) according to ISO/FPIS 1480. Cycling loading tests were performed at loads 10 to 250 N, for 1 million cycles, at 14 Hz,(by subjecting sinusoidal wave from 10 to 250 N at a frequency of 14 Hz for 1 million cycles,) and then postload removal torque values were evaluated. Results: 1. In all samples, the removal values of abutment screw were lower than tightening torque values(30 Ncm), but the phenomenon of the screw loosening was not observed. 2. In both of the implant systems, initial and postload removal torque of zirconia abutment were significantly higher than those of metal abutment(P<.05). 3. In both of the implant systems, the difference in removal torque ratio between zirconia abutment and metal abutment was not significant(P>.05). 4. In metal abutments, the removal torque ratio of GS II system(internal conical joint system) was lower than that of US II system(external butt joint system)(P<.05). 5. In zirconia abutments, the difference in removal torque ratio between the two implant systems was not significant(P>.05). Conclusion: Zirconia abutment had a good screw joint stability in the condition of one million cycling loading.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.1
• /
• pp.71-83
• /
• 2001

The purpose of this study was to compare the effects of various surface treatments by measuring removal torque on bone healing around titanium implants. 40 Screw-shaped cp titanium implants with length of 4mm, outer diameter of 3.75mm, and pitch-height of 0.5mm were used Group 1 was left as machined(control), Group 2 was blasted with $50{\mu}m\;Al_2O_3$, group 3 was blasted and etched in etching solution($NH_4OH : H_2O_2:H_2O= 1 : 1 : 5$) at $90^{\circ}C$ for 1 minute group 4 was blasted and oxidated under pure oxygen at $800^{\circ}C$. The implant surface roughness was analyzed with SEM and CLSM(Confocal Laser Scanning Microscope) and implants were placed in proximal tibial metaphysis of 10 New Zealand White rabbits. After 3 months of healing period, removal torque of each implant was measured to compare bone healing around implant. The results obtained were as follows 1. In SEM view, blasting increased the roughness of the surface, but etching of that rough surface decreased the roughness due to the removal of the tip of the peak. Oxidation also decreased the roughness due to formation of needle-like oxide grains on the implant surface. 2. The Sa value from CLSM was least in the machined group($0.47{\mu}m$), greatest in blasted group($1.25{\mu}m$), and the value decreased after etching($0.91{\mu}m$) and oxidation($0.94{\mu}m$). 3. The removal torque of etched group(24.5Ncm) was greater than that of machined group(16.7Ncm) (P<0.05), and was greatest in the oxidated group(40.3Ncm) and the blasted group(34.7Ncm).

• The Journal of Korean Academy of Prosthodontics
• /
• v.56 no.3
• /
• pp.179-187
• /
• 2018

Purpose: The purpose of this study was to investigate the effect of heat applied to disintegrate cement on the removal torque value and fracture strength of titanium abutment and abutment screw. Materials and methods: Implants, titanium abutments and abutment screws were prepared for each 20 piece. Implant abutments and screws were classified as the control group in which no heat was applied and the experimental group was heated in a vacuum furnace to $450^{\circ}C$ for 8 minutes and cooled in air. The abutments and screws were connected to the implants with 30 Ncm tightening torque at interval 10 minutes and the removal torque value was measured 15 minutes later. And the fracture strength of abutment screw was measured using universal testing machine. Results: The mean removal torque value was $27.84{\pm}1.07Ncm$ in the control group and $26.55{\pm}1.56Ncm$ in the experimental group and showed statistically significant difference (P < .05). The mean fracture strength was $731.47{\pm}39.46N$ in the control group and $768.58{\pm}46.73N$ in the experimental group and showed statistically no significant difference (P > .05). Conclusion: The heat applied for cement disintegration significantly reduced the removal torque value of the abutment screw and did not significantly affect fracture strength of the abutment screw. Therefore, in the case of applying heat to disintegrate cement it is necessary to separate the abutment screw or pay attention to the reuse of the heated screw. However further studies are needed to evaluate the clinical reuse of the heated screw.

• The korean journal of orthodontics
• /
• v.36 no.5
• /
• pp.324-330
• /
• 2006

Objective: The purposes of this study were to evaluate the differences between sand blasted, large grit and acid-etched (SLA) treated mini-implants and smooth surface orthodontic mini-implants in relation to the removal torque as well as the histologic analysis. Methods: Custom-made, screw-shaped, titanium implants with a length of 9.5 mm and an outer diameter of 1.8 mm were divided into 2 groups; the SLA group (20 SLA treated orthodontic mini-implants) and the smooth surface group (20 smooth surface mini-implants), and placed In the tibia metaphysis of 10 rabbits. Each rabbit had 4 mini-implants placed, 2 in each tibia. The right tibia were implanted with the SLA group mini-implants and the left tibia had the smooth group mini-implants placed. Each mini-implant group were immediately applied with a continuous traction force of 150 g using a Ni-Ti coil spring. The rabbits were sacrificed 6 weeks post-surgically. Subsequently, the legs were stabilized, the Ni-Ti coil springs were removed and the mini-implants were removed under reverse torque rotation with a digital torque gauge. Results: 6 weeks after placement, the SIA group presented a higher mean removal torque value (8.29 Ncm) than the smooth group (3.34 Ncm) and histologic analysis revealed a higher new bone formation aspect along the screw in the SLA group. Conclusion: Results of this study indicates that SLA treated mini-implants may endure higher orthodontic forces without loosening.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.5
• /
• pp.309-315
• /
• 2018

The purpose of this study is to assess the mechanical properties of the ceramic abutment with washer. In this study, ceramic abutment were used, tested with $30^{\circ}$ compression load, shear fatigue, adaptation accuracy test(rotation angle, contact interval), removal torque force test, torsional breaking force test. The $30^{\circ}$ compression load was 729 N, the shear fatigue load was 275 N, adaptation accuracy test of rotation angle was within $3^{\circ}$, contact interval within $10{\mu}m$, and removal torque force test value is $18.88N{\cdot}cm$, torsional breaking force test value is $35.52N{\cdot}cm$. Ceramic abutment with a washer fitted have sufficient mechanical strength and may be substituted for titanium abutment.

• The korean journal of orthodontics
• /
• v.37 no.6
• /
• pp.400-406
• /
• 2007

The purpose of this experimental study was to evaluate the effect of immediate orthodontic loading on the stability at the bone-implant interface of titanium miniscrews in a rabbit model. Methods: Forty titanium miniscrews (1.6 mm diameter, 8 mm length) were inserted in the tibiae of 10 rabbits. Twenty test group miniscrews were subjected to continuous orthodontic forces of 200g immediately after implantation for a period of 6 weeks. The remaining 20 control group miniscrews were left unloaded for the same follow-up interval. Removal torque values were recorded using a digital torque gauge. An independent t-test was performed. Results: All the miniscrews were stable, and exhibited no mobility or displacement throughout the experimental period. Histologically, miniscrews were well-integrated into bone. No statistically significant differences in removal torque data were found between the loaded test and the unloaded control groups. Conclusions: These findings suggest that titanium miniscrews can be used as anchoring units for orthodontic tooth movement immediately after insertion.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.38 no.1
• /
• pp.98-104
• /
• 2009

The objective of this study was to characterize quality changes of PET-packaged green tea beverage during 4-week storage at $60^{\circ}C$. Changes in oxygen transmission of the PET bottle package and cap removal torque were also examined. MXD6 blend PET bottle showed stability in the gas barrier. Its cap removal torque was kept stable during the 4 weeks. pH, color value, contents of vitamin C and catechin showed significant changes during the storage while caffeine and amino acid did not change significantly. Four alcohol flavor components (hexanol, linalool, menthol, and ${\alpha}$-terpineol) increased rapidly during the first three weeks while d-limonene did not show significant change. Sensory test showed decrease in astringent flavor lowering the product flavor and acceptability.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.5
• /
• pp.490-499
• /
• 2008

Statement of problem: Bioactive materials must have the ability to spontaneously form a bone like apatite layer on their surface and induce direct biochemical bonding to bone. A simple chemical treatment via alkali and heat has been revealed to induce bioactivity in titanium. Purpose: The purpose of this study was to evaluate the surface characteristics and stability of alkali and heat treated implants. Material and methods: Specimens were divided into three groups; group 1 was the control group with machined surface implants, groups 2 and 3 were treated with alkali solutions and heat treated in the atmosphere and vacuum conditions respectively. The surface characteristics were observed with FESEM, XPS, TF-XRD and AFM. Stability was evaluated with the resonance frequency analysis, periotest and removal torque values. One-way ANOVA and Duncan test were used for statistical analysis. Results: 1. Groups treated with alkali and heat showed similar characteristics. Groups 2 and 3 showed high compositions of Na ions on the surface with sub-micron sized pores compared to group 1. Group 2 showed mixed compositions of anatase and rutile with superior contents of rutile. 2. Resonance frequency analysis : The ISQ of group 2 showed significantly higher values than that of groups 1 and 3 at 12 weeks. The ISQ of groups 1 and 2 showed significant increase after 4 weeks, and the ISQ of group 3 increased significantly after 2 and 4 weeks respectively (P < .05). 3. Periotest: The PTV of groups 1 and 2 showed significant decrease after 4 weeks, and the PTV of group 3 showed significant decrease after 2 and 4 weeks respectively (P < .05). 4. Removal torque analysis: The removal torque value of group 2 was significantly higher than those of groups 1 and 3 at 2, 4 and 8 weeks. The removal torque values of groups 1 and 3 showed increase at 4 and 12 weeks, but the removal torque value of group 2 showed increase after 4 weeks (P < .05). Conclusion: An oxide layer with appropriate crystal structure and amorphous sodium titanate layer can be obtained on titanium implants through alkali and heat treatment in the atmosphere, and even alkali and heat treatment in vacuum conditions, provided a bioactive surface containing sodium. These surface layers can be considered to be effective for enhancement of osseointegration and reduction of healing period for implant treatment.