• Tribology and Lubricants
• /
• 제24권5호
• /
• pp.255-263
• /
• 2008

Adhesion tests were conducted to investigate the adhesion characteristics between mold and thermoplastic polymer film. Coating of anti-sticking layer (ASL), a kind of polymer material, imprint pressure, and separation velocity were considered as the process conditions. A piece of fused silica without patterns on its surface was used as a mold and the thermoplastic polymer films were made on Si substrate by spin-coating the commercial polymer solution such as mr-I PMMA and mr-I 7020. The ASL was derived from (1H, 1H, 2H, 2H - perfluorooctyl) trichlorosilane($F_{13}$-OTS) and coated on the fused silica mold in vapor phase. The pull-off force was measured in various process conditions and the surfaces of the mold and the polymer film were observed after separation. It was found that the adhesion characteristics between the mold and the thermoplastic polymer film and the release performance of ASL were changed according to the process conditions. The ASL was effective to reduce the pull-off force and the damage of polymer film. In cases of the mold coated with ASL, the pull-off force did not depend on imprint pressure and separation velocity.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2005년도 학술발표논문집
• /
• pp.97-101
• /
• 2005

High strength concretes utilizing EVA with micro particles were prepared by varying polymer/binder mass ratio and curing conditions with a constant water/binder mass ratio of 0.3. The EVA modified concretes on the compressive and flexural strength, microstructure, ultrapulse modulus in curing condition(dry and water curing) were studied. Also, scanning electron microscope analysis(SEM) was performed to reveal the presence of polymer film and cement hydrates in the concrete. The compressive strength of the EVA modified concretes cured at water conditions ere higher than that of the EVA modified concretes cured at dry conditions. But, the flexural strength of the specimens cured at dry conditions were higher than that of the specimens cured at water conditions. Due to the interaction of the cement hydrates and polymer film, an interpenetrating network originated in which the aggregates were embedded. The curing of the polymer modified concrete involves two step of cement hydrates and polymer modification, and cement hydrates was promoted in water conditions and polymer film formation take place when water evaporates and was thereby was favored in dry conditions. By SEM analysis, influences of polymer modification was strengthening of the transition zone between the aggregate and the paste, and the porosity of transition zone decreases. By spring analysis, it could known that polymer film affects in porosity decrease and strengthening of transition zone.

• Rapid Communication in Photoscience
• /
• 제2권1호
• /
• pp.24-27
• /
• 2013

A polymeric photobase generator containing oxime-urethane groups is applied to a fluorescence micropatterning material. Polymer bearing oxime-urethane groups was prepared by copolymerization of methyl methacrylate with methacryloyloxyethyl benzophenoneoxime urethane (MBU). The reaction of amino groups in the irradiated copolymer film with dansyl chloride (Dns-Cl) was monitored by using UV absorption, IR absorption and fluorescence spectroscopy. The fluorescence spectrum of the Dns-Cl-treated irradiated copolymer film shows a strong fluorescence with a fluorescence maximum wavelength at 510 nm. A blue fluorescent micropattern with a line width of $2{\sim}3{\mu}m$ was obtained. Treatment of the irradiated copolymer film with Dns-Cl and rhodamine B mixture led to the formation of green, red, and orange-colored fluorescence micropatterns. Thus, various colored micropatterns on a single polymer film can be obtained by selective excitation of each dye molecules.

• 한국전기전자재료학회논문지
• /
• 제29권12호
• /
• pp.759-763
• /
• 2016

We demonstrate the utilization of ion gel gate dielectrics for operating non-volatile transistor memory devices based on polymer semiconductor thin films. The gating process in typical electrolyte-gated polymer transistors occurs upon the penetration and escape of ionic components into the active channel layer, which dopes and dedopes the polymer film, respectively. Therefore, by controlling doping and dedoping processes, electrical current signals through the polymer film can be memorized and erased over a period of time, which constitutes the transistor-type memory devices. It was found that increasing the thickness of polymer films can enhance the memory performance of device including (i) the current signal ratio between its memorized state and erased state and (ii) the retention time of the signal.

• 한국입자에어로졸학회지
• /
• 제6권2호
• /
• pp.61-67
• /
• 2010

In this paper, we describe a new method to form polymer thin films, in which carbon nanotubes (CNTs) are homogeneously distributed so that they can strengthen the mechanical property of resulting polymer film. To do so, we first homogeneously mixed CNTs with polymer in a DMF solvent. With the assistance of ultrasonic nebulizer, the polymer/CNT solution was then aerosolized into micro-sized droplets and finally turned into solidified polymer/CNT composite particles by gas-phase drying process. As the results of SEM and TEM analysis, CNTs were found to be homogeneously immobilized in the polymer matrix particles due to rapid drying process in the gas phase. For comparison purpose, (i) the polymer/CNTs composite particles prepared by aerosol processing method and (ii) polymer/CNTs sheets prepared by simple solution-evaporation method were employed to form polymer/CNTs composite thin films using a hot press. As the result, the aerosol processing of composite particles was found to be a much more effective method to form homogeneously distributed-CNTs in the polymer matrix thin film.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2009년도 추계학술발표회 논문집
• /
• pp.79-84
• /
• 2009

Understanding the polymer adsorption in particle/binder/solvent system is important to achieve successful film products. While most of the reported work has dealt with the suspension microstructure, a few studies have focused on film formation. We investigated the effect of adsorption on film formation through measurement of adsorption amount in suspension and stress development in drying film with respect to mixing time ($t_m$). All of the adsorption amount (PVA), characteristic stress ($\sigma_{ch}$) exhibited similarities expressed by the form of $1-e^{t_m/{\tau}}$. The porous and non-unifonn dried film at short tm became close-packed and uniform with longer $t_m$. We found that polymer adsorption plays the key role in film fonnation as it introduces steric repulsion in suspension and suppresses the flocculation during solvent evaporation. We also found that the mixing time for the saturated polymer adsorption is the important variable to acquire the consolidated and uniform film microstructure.

• 폴리머
• /
• 제25권4호
• /
• pp.594-601
• /
• 2001

표면을 개질시켜 극성기를 도입한 다음 열융착시키는 방법으로 접착제를 사용하지 않고도 폴리에틸렌 필름과 알루미늄 판을 직접 접합시킬 수 있는지를 살펴보았다. 폴리에틸렌 필름은 산소 및 아크릴산 플라즈마로 처리하여 극성기를 도입하였으며, 알루미늄 판은 끓는 물로 처리하거나 diaminocyclohexane 플라즈마로 처리하여 극성기를 도입하였다. 폴리에틸렌 필름의 표면만을 개질시킬 경우에도 상당히 높은 접착력을 얻을 수 있었으며, 알루미늄 판의 표면까지 개질시킬 경우에는 접착시험시 폴리에틸렌 필름이 끊어질 정도로 높은 접착력을 얻을 수 있었다. 특히, 아크릴산플라즈마로 처리한 폴리에틸렌 필름과 diaminocyclohexane 플라즈마로 처리한 알루미늄 판을 접합시킬 경우에는 필름 표면의 카르복실기와 판 표면의 아민기가 반응하여 아마이드 그룹을 형성하는 화학적 결합에 대한 가능성도 보여주었다.

• 폴리머
• /
• 제38권6호
• /
• pp.801-808
• /
• 2014

광경화 아크릴고분자 필름에서 이온이동에 관한 연구를 하였다. 고분자에 결합된 아민기와 카르복실산 작용기의 함량을 조절하여 수소이온과 수산화이온의 이동에 적합한 필름을 제조하였다. 수소이온 이동 검출을 위해 p-methylred(PMR) 유도체를 사용하였고 수산화이온 검출을 위해 페놀프탈레인 유도체를 합성하여 각각 고분자에 도입하였다. 수소이온의 이동은 아민기의 함량이 많을수록 빠르게 진행되었고 수산화이온은 카르복실산의 함량이 높을수록 빠르게 이동하였다. 수소이온 이동은 필름표면과 내부로 빠르게 진행하였고 PMR 포함 필름의 흡수스펙트럼을 통해 관찰되었다. 산 용액에 감응하는 필름을 사용하여 색상변화의 가역성을 관찰하였고 연속 50회를 실시하는 동안 정확히 재현되었다. 구리(II) 이온은 카르복실산 작용기의 함량이 높은 필름에서 빠르게 이동하였다. 로다민이 도입된 필름에서 구리이온의 배위로 로다민의 고리열림 반응이 진행되었고 광흡수 및 발광특성 측정을 통해 구리이온의 이동을 추적하였다.

• Transactions on Electrical and Electronic Materials
• /
• 제6권3호
• /
• pp.106-109
• /
• 2005

We have investigated the generation of pretilt angle for a nematic liquid crystal (NLC) alignment with in-situ photoalignment method on polyimide (PI) surfaces using polymer films. Especially, we studied in-situ photoalignment changing heating temperature from $50^{\circ}C\;to\;120^{\circ}C$ on the polymer film. The LC aligning capabilities and pretilt angle on the polymer substrates were better than those on the glass substrate using in-situ photoalignment method. It is considered that this increase in pretilt angle may be attributed to the roughness of the micro-groove substrate induced by the in-situ photoalignment. As temperature of heated subtrate and UV exposure time increase, pretilt angle of the cell used polymer film increased. It is considered that the heating temperature of substrate is attributed to generate pretilt angle. Also, electro-optical performances of the in-situ photoaligned TN cell using the polymer substrate are almost the same as that of the TN cell using the glass substrate.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.205-206
• /
• 2008

The transparent conductive film was prepared by bar coating method of poly (3, 4-ethylenedioxythiophene) (PEDOT) and poly (sodium 4-stylenesulfonate) grafted multi-walled carbon nanotubes (MWNT-PSS) nanocomposites solution on the polyethylene terephthalate (PET) film. In this case, multi-wall carbon nanotubes was treated by chemical methods to obtain water soluble MWNT-PSS and then blending with PEDOT. The non-covalent bonding of polymer to the MWNT surface was confirmed by Fourier transform infrared (FT-IR), thermal gravimetric analysis (TGA) and Transmission electro microscope (TEM) investigation also showed a polymer-wrapped MWNT structure. Furthermore, the electrical, transmission properties of the transparent conductive film were investigated and compared with control samples are raw PEDOT films.