• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.9
• /
• pp.754-760
• /
• 2008

A two-photon induced photoreduction process suggests a possibility for fabricating complicated metallic microstructures which can be applied to 3-D micro-circuits and optical devices, etc. The process employs the photoreduction of silver ions in a metallic solution which is composed of metallic salt ($AgNO_3$) and watersoluble polymer ((poly(4-styrenesulfonique acid) 18wt. % in $H_2O$, $(C_8H_8O_3S)_n$)). In this process, the improvement of the resolution and the uniformity of fabricated metallic structures are important issues. To address these problems, continuous forming window (CFW) is obtained from a parametric study on the conditions of laser power and scanning velocity and the direct seed generation (DSG) method is proposed. Silver nano particles are uniformly generated in a metallic solution through the DSG method, which enables the decrease of a laser power to trigger the photoreduction of silver ions as well as the increase of metal contents in a metallic solution. So the two-photon induced photoreduction property of a metallic solution is improved. Through this work, precise silver patterns are fabricated with a minimum line width of 400 nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.7
• /
• pp.510-514
• /
• 2013

In order to prevent heat loss that occurs through the glass, low-emissivity (Low-E) coating methods with good insulating properties and high transmittance were used. InGaZnO/Ag/InGaZnO (IGZO/Ag/IGZO) multilayer thin films have been deposited on XG glass substrate by RF magnetron sputtering. Depending on the different thickness of Ag in multilayer films, the structural and optical properties of Low-E multilayer films were analyzed. By XRD analysis results, the multilayer thin films were observed to be amorphous structure regardless of Ag thickness. According to the AFM results, surface morphology of the multilayer films was observed and compared. Using UV-VIS spectroscopy, low emissivity property has been observed clearly with the transmittance of higher than 85% at visible range and lower than 30% at IR range.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.2
• /
• pp.232-239
• /
• 2015

In this paper, we study the dry transfer technology utilizing PDMS (Polydimethylsiloxane) stamp of a large single-layer graphene grown on Cu-foil as catalytic metal by using Chemical Vapor Deposition (CVD). By changing the surface property of the target substrate through $UV/O_3$ treatment, we can transfer the graphene on the target substrate while minimizing mechanical damages of graphene layer. Multi-layer (1~4 layers) graphene was stacked on $SiO_2/Si$ wafer successfully by repeating thetransfer method/process and then optical transmittance and sheet resistance of graphene layers have been measured as a quality assessment.

• ETRI Journal
• /
• v.38 no.6
• /
• pp.1179-1189
• /
• 2016

A chemorheological analysis of a no-flow underfill was conducted using curing kinetics through isothermal and dynamic differential scanning calorimetry, viscosity measurement, and solder (Sn/27In/54Bi, melting temperature of $86^{\circ}C$) wetting observations. The analysis used an epoxy system with an anhydride curing agent and carboxyl fluxing capability to remove oxide on the surface of a metal filler. A curing kinetic of the no-flow underfill with a processing temperature of $130^{\circ}C$ was successfully completed using phenomenological models such as autocatalytic and nth-order models. Temperature-dependent kinetic parameters were identified within a temperature range of $125^{\circ}C$ to $135^{\circ}C$. The phenomenon of solder wetting was visually observed using an optical microscope, and the conversion and viscosity at the moment of solder wetting were quantitatively investigated. It is expected that the curing kinetics and rheological property of a no-flow underfill can be adopted in arbitrary processing applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.315.1-315.1
• /
• 2014

The use of cellulose papers has recently attracted much attention in various device applications owing to their natural advantageous properties of earth's abundance, bio-friendly, large-scale production, and flexibility. Conventional metal oxides with novel structures of nanorods, nanospindles, nanowires and nanobelts are being developed for emerging electronic and chemical sensing applications. In this work, both ZnO (n-type) nanorod arrays (NRAs) and CuO (p-type) nanospindles (NSs) were synthesized on cellulose papers and the p-n junction property was investigated using the electrode of indium tin oxide coated polyethylene terephthalate film. To synthesize ZnO and CuO nanostructures on cellulose paper, a simple and facile hydrothermal method was utilized. First, the CuO NSs were synthesized on cellulose paper by a simple soaking process, yielding the well adhered CuO NSs on cellulose paper. After that, the ZnO NRAs were grown on CuO NSs/cellulose paper via a facile hydrothermal route. The as-grown ZnO/CuO NSs on cellulose paper exhibited good crystalline and optical properties. The fabricated p-n junction device showed the I-V characteristics with a rectifying behaviour.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.2
• /
• pp.15-18
• /
• 2007

The sub micron sized spherical $MgB_2$ powders were synthesized by spray reaction method. $MgB_2$ tapes with Al addition were fabricated by Powder in Tube (PIT) method. The superconducting property and microstructure of Al doped $MgB_2$ tapes were characterized by X-ray diffraction, optical microscopy and transport measurement under magnetic field. The $J_c$ value of $MgB_2$ tapes was increased with 10 vol. % Al addition. The $J_c$ value of 5,500 A/$cm^2$ and 11,000 A/$cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol. % of Al added $MgB_2$ tape without heat treatment, respectively. The $J_c$ value of 8,000 A/$cm^2$ and 33,000 A/$cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol. % of Al added $MgB_2$ tape with heat treatment, respectively. The $J_c$-B curves show enhancement in $J_c$ (B), which suggests that the microstructure and transport properties of $MgB_2$ tapes have been improved with Al addition.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.3
• /
• pp.99-104
• /
• 2013

The simple and cost-effective microfabrication method of photosensitive glass (PSG) using metal patterning and blank exposure was proposed. Conventional photolithography for micromachining of PSG needs a costly quartz mask which has high transmittance as an optical property. However, in this study the process was improved through the combination of micro-patterned Ti thin film and blank UV exposure without quartz mask. The effect of UV exposure time as well as the DHF etching condition was investigated. UV exposure test was performed within the range from 3 min to 9 min. The color and etch result of PSG exposed for 5 min were the most clear and effective to etch more precisely, respectively. The etching results of PSG in diluted hydrofluoric acid (DHF) with a concentration of 5, 10, 15 vol% were compared. The effect on the side etch was insignificant while the etch rate was proportional as the concentration increased. 10 vol% DHF results not only high etch rate of 75 ${\mu}m/min$ also lower side etch value after PSG etching. This method facilitates the microfabrication of PSG with various patterns and high aspect ratio for applying to advanced applications.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.629-636
• /
• 2014

For surface modification, bulk metallic glass coatings were fabricated using metallic glass powder and a mixture of a self-fluxing alloy or/and hard metal alloys with a heat-resisting property using a high velocity oxy-fuel coating thermal spraying process. Microstructural analyses and mechanical tests were carried out using X-ray diffraction, a scanning electron microscope, an atomic force microscope, a three-dimensional optical profiler, and nanoindenation. As a result, the monolithic metallic glass coating was found to consist of solid particle and lamellae regions that included many pores. Second phase-reinforced composite coatings with a self-fluxing alloy or/and hard metal alloy additives were employed with in-situ $Cr_2Ni_3$ precipitate or/and ex-situ WC particles in an amorphous matrix. The mechanical behaviors of the solid particles and lamella regions showed large hardness and elastic modulus differences. The mechanical properties of the particle regions in the metallic glass composite coatings were superior to those of the lamellae regions in the monolithic metallic glass coatings, but indicated similar trends in matrix region of all the coating layers.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.306.1-306.1
• /
• 2016

ZnO semiconductor material has been widely utilized in various applications in semiconductor device technology owing to its unique electrical and optical features. It is a promising as solar cell material, because of its low cost, n-type conductivity and wide direct band gap. In this work ZnO/Si heterojunctions were fabricated by using pulsed laser deposition. Vacuum chamber was evacuated to a base pressure of approximately $2{\times}10^{-6}Torr$. ZnO thin films were grown on p-Si (100) substrate at oxygen partial pressure from 5mTorr to 40mTorr. Growth temperature of ZnO thin films was set to 773K. A pulsed (10 Hz) Nd:YAG laser operating at a wavelength of 266 nm was used to produce a plasma plume from an ablated a ZnO target, whose density of laser energy was $10J/cm^2$. Thickness of all the thin films of ZnO was about 300nm. The optical property was characterized by photoluminescence and crystallinity of ZnO was analyzed by X-ray diffraction. For fabrication ZnO/Si heterojunction diodes, indium metal and Al grid patterns were deposited on back and front side of the solar cells by using thermal evaporator, respectively. Finally, current-voltage characteristics of the ZnO/Si structure were studied by using Keithly 2600. Under Air Mass 1.5 Global solar simulator with an irradiation intensity of $100mW/cm^2$, the electrical properties of ZnO/Si heterojunction photovoltaic devices were analyzed.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.114.2-114.2
• /
• 2017

Transparent film heaters (TFHs) based on Joule heating are currently an active research area. However, TFHs based on an indium tin oxide (ITO) monolayer have a number of problems. For example, heating is concentrated in part of the device. Also, heating efficiency is low because it has high sheet resistance ($R_S$). Resistance of indium zinc oxide (IZO) is similar to ITO and it can be used to flexible applications due to its amorphous structure. To solve these problems, our study introduced hybrid layers of IZO/Ag/IZO deposited by magnetron sputtering, and the electrical, optical, and thermal properties were estimated for various thickness of the metal interlayer. It was found that the sheet resistance of the multilayer was mainly dependent on the thickness of the Ag layers. The $R_S$ of IZO(40)/Ag/IZO(40nm) multilayer was 5.33, 3.29, $2.15{\Omega}/{\Box}$ for Ag thickness of 10, 15, and 20nm, respectively, while the $R_S$ of an IZO monolayer(95nm) was $59.58{\Omega}/{\Box}$. The optical transmittance at 550nm for the IZO(95nm) monolayer is 81.6%, and for the IZO(40)/Ag/IZO(40nm) multilayers with Ag thickness 10, 15 and 20nm, is for 72.8, 78.6, and 63.9%, respectively. The defrost test showed that the film with the lowest RS had the highest heat generation rate (HGR) for the same applied voltage. The results indicated that IZO(40)/Ag(15)/IZO(40nm) multilayer has the best suitable property, which is a promising thin film heater for the application in vehicle windshield.