• Journal of the Korean institute of surface engineering
• /
• v.39 no.6
• /
• pp.245-249
• /
• 2006

In this study, ternary Ti-Mo-N and new quaternary Ti-Mo-Si-N coatings were synthesized on steel substrates(AISI D2) and Si wafers by a hybrid coating system of arc ion plating (AIP) using Ti target and d.c. magnetron sputtering technique using Mo and Si targets in $N_2/Ar$ gaseous mixture. Ternary Ti-Mo-N coatings were substitutional solid-solution of (Ti, Mo)N and showed maximum hardness of approximately 30 GPa at the Mo content of ${\sim}10$. %. The Ti-Mo-Si-N coating with the Si content of 8.8 at. % was a composite consisting of fine (Ti, Mo)N crystallites and amorphous $Si_3N_4$ phase. The hardness of the Ti-Mo-Si(8.8 at. %)-N coatings exhibited largely increased hardness value of ${\sim}48$ GPa due to the microstructural evolution to the fine composite microstructure and the refinement of (Ti, Mo)N crystallites. The average friction coefficient of the Ti-Mo-Si-N coatings largely decreased with increase of Si content. The microstructures of Ti-Mo-Si-N coatings were investigated with instrumental analyses of XRD, XPS, and HRTEM in this work.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.3
• /
• pp.110-114
• /
• 2006

In this work, comparative studies on microstructure and mechanical properties between $Mo_2N$ and Mo-Si-N coatings were conducted. Ternary Mo-Si-N coatings were deposited on AISI D2 steel substrates by a hybrid method, where AIP technique was combined with a magnetron sputtering technique. Instrumental analyses of XRD, HRTEM, and XPS revealed that the Mo-Si-N coatings must be a composite consisting of fine $Mo_2N$ crystallites and amorphous $Si_3N_4$. The hardness value of Mo-Si-N coatings significantly increased from 22 GPa of $Mo_2N$ coatings to about 37 GPa with Si content of 10 at.% due to the refinement of $Mo_2N$ crystallites and the composite microstructure characteristics. The average friction coefficient of the Mo-Si-N coatings gradually decreased from 0.65 to 0.4 with increasing Si content up to 15 at.%. The effects of Si content on microstructure and mechanical properties of Mo-N coatings were systematically investigated.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.6
• /
• pp.279-282
• /
• 2007

Cr-Mo-Si-C-N coatings were deposited on steel and Si wafer by a hybrid system of AIP and sputtering techniques using Cr, Mo and Si target in $Ar/N_2/CH_4$ gaseous mixture. Instrumental analyses of XRD and XPS revealed that the Cr-Mo-Si-C-N coatings must be a composite consisting of fine(Cr, Mo and Si)(C and N) crystallites and amorphous $Si_3N_4$ and SiC. The hardness value of Cr-Mo-Si-C-N coatings significantly increased from 41 GPa of Cr-Mo-C-N coatings to about 53 GPa with Si content of 9.3 at.% due to the refinement of (Cr, Mo and Si)(C and N) crystallites and the composite microstructure characteristics. A systematic investigation of the microstructures and mechanical properties of Cr-Mo-Si-C-N coatings prepared with various Si contents is reported in this paper.

• Journal of the Korean Vacuum Society
• /
• v.6 no.2
• /
• pp.143-150
• /
• 1997

In this study, doffusion barrier properties of 1000 $\AA$ thick molybdenum compound(Mo, Mo-N, $MoSi_2$, Mo-Si-N) films were investigated using sheet resistance measurement, X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), Scanning electron mircoscopy(SEM), and Rutherford back-scattering spectrometry(RBS). Each barrier material was deposited by the dc magnetron sputtering and annealed at 300-$800^{\circ}C$ for 30 min in vacuum. Mo and MoSi2 barrier were faied at low temperatures due to Cu diffusion through grain boundaries and defects in Mo thin film and the reaction of Cu with Si within $MoSi_2$, respectively. A failure temperature could be raised to $650^{\circ}C$-30 min in the Mo barrier system and to $700^{\circ}C$-30 min in the Mo-silicide system by replacing Mo and $MoSi_2$ with Mo-N and Mo-Si-N, respectively. The crystallization temperature in the Mo-silicide film was raised by the addition of $N_2$. It is considered that not only the $N_2$, stuffing effect but also the variation of crystallization temperature affects the reaction of Cu with Si within Mo-silicide. It is found that Mo-Si-N is the more effective barrier than Mo, $MoSi_2$, or Mo-N to copper penetraion preventing Cu reaction with the substrate for $30^{\circ}C$min at a temperature higher than $650^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.683-690
• /
• 1996

In this study, the diffusion barrier properties of $1000 \AA$ thick molybdenum compounds (Mo, Mo-N, $MoSi_2$, Mo-Si-N) were investigated using sheet resistance measurements, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning electron microscopy (SEM), and Rutherford backscattering spectrometry (RBS). Each barrier material was deposited by the dc magnetron sputtering, and annealed at 300-$800^{\circ}C$ for 30min in vacuum. Mo and $MoSi_2$ barrier were failed at low temperature due to Cu diffusion through grain bound-aries and defects of Mo thin film and the reaction of Cu with Si within $MoSi_2$ respectively. A failure temperature could be raised to $650^{\circ}C$-30min in the Mo barrier system and to $700^{\circ}C$-30min in the Mo-silicide system by replacing Mo and $MoSi_2$ with Mo-N and Mo-Si-N, respectively. The crystallization temperature in the Mo-silicide film was raised by the addition of $N_2$. It is considered that not only the N, stuffing effect but also the variation of crystallization temperature affects the reaction of Cu with Si within Mo-silicide. It was found that Mo-Si-N is more effective barrier than Mo, $MoSi_2$, or Mo-N to copper penetration preventing Cu reaction with the substrate for 30min at a temperature higher than $650^{\circ}C$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.86-87
• /
• 2008

4성분계 Cr-MO-Si-N코팅은 하이브리드 시스템에 아르곤, 질소 가스를 주입하여 스테인리스 기판과 실리콘 웨이퍼에 증착시킨다. XRD, XPS, HRTEM을 이용해 Cr-MO-Si-N코팅의 성분을 분석하고 Si의 함량이 12.1at.%일때 50GPa의 강도가 나오고 이것은 33GPa의 강도Cr-MO-N코팅보다 크게 향상된 것이다.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.240-244
• /
• 2006

In this paper, magnetic properties and annealing behavior of spin valve structures using Mo(MoN) layers as underlayers were studied varying the thickness of the underlayers. The spin valve structure was consisted of Si substrate/$SiO_2(2,000{\AA})/Mo(MoN)(t{\AA})/NiFe(21\;{\AA})/CoFe(28\;{\AA})/Cu(22\;{\AA})/CoFe(18\;{\AA})/IrMn(65\;{\AA})/Ta(25\;{\AA})$. Also, MoN films were deposited on Si substrates and their thermal annealing behavior was analyzed. The resistivity of the MoN film increased as the $N_2$ gas flow rate was increased. After annealing at $600^{\circ}C$, XRD results did not show peaks of silicides. XPS results indicated MoN film deposited with 5 sccm of $N_2$ gas flow rate was more stable than the film deposited with 1 sccm of $N_2$ gas flow rate. The variations of MR ratio and magnetic exchange coupling fold were small for the spin valve structures using Mo(MoN) underlayers up to thickness of45 ${\AA}$. MR ratio of spin valves using MoN underlayers deposited with various $N_2$ gas flow rate was about 7.0% at RT and increased to about 7.5% after annealing at $220^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased to about 3.5%. Variation of $N_2$ gas flow rate up to 5 sccm did not change the MR ratio and $H_{ex}$ appreciably.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.04a
• /
• pp.103-104
• /
• 2007

Cr-Mo-Si-N 코팅막은 AISI D2 모재와 Si 모재위에 $Ar/N_2$ 혼합기체를 사용하여 AIP (arc ion plating) 방법과 마그네트론 스퍼터링 (DC magnetron sputtering) 방법을 결합시킨 하이브리드 코팅시스템을 이용하여, 증착하였다. XRD, HRTEM, XPS 등의 분석장비를 이용하여 Cr-Mo-Si-N 코팅의 미세구조를 관찰하였다. Cr-Mo-Si-N 코팅의 경도는 Si함량이 12.1 at.%에서 약 50 GPa의 최고치를 나타냈으며, 평균 마찰계수는 Si 함량이 증가할수록 감소하였다.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.17 no.2
• /
• pp.204-209
• /
• 2017

We have investigated a Mo/Au gate scheme for use in AlGaN/GaN-on-Si HFETs. AlGaN/GaN-on-Si HFETs were fabricated with Ni/Au or Mo/Au gates and their electrical characteristics were compared after thermal stress tests. While insignificant difference was observed in DC characteristics, the Mo/Au gate device exhibited lower on-resistance with superior pulsed characteristics in comparison with the Ni/Au gate device.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.95-98
• /
• 2007

In this paper, the magnetic properties and the annealing behavior of spin valve structures with Mo(MoN) underlayers were studied for various underlayer thickness. The spin valve structure was Si substrate/Mo(MoN)$(t{\AA})/NiFe(21{\AA})/CoFe(28{\AA})/Cu(22{\AA})/CoFe(18{\AA})/IrMn(65{\AA})/Ta(25 {\AA})$. Mo and MoN films were deposited on Si substrates and their thermal annealing behavior was analyzed. The deposition rate of the MoN thin film was decreased and tile resistivity of the MoN thin films were increased as the $N_2$ gas flow was increased. The variations of MR ratio and magnetic exchange coupling field of spin valve structure were smaller with MoN underlayers than that with Mo underlayers up to thickness of $51{\AA}$. MR ratio of spin valves with Mo underlayers was 2.86% at room temperature and increased up to 2.91 % after annealing at $200^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased about 2.16%. The MR ratio of spin valves structure with MoN underlayers for $N_2$ gas flow 1 sccm was 5.27% at room temperature and increased up to 5.56% after annealing at $200^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased about 4.9%.