• Journal of the Korean Electrochemical Society
• /
• v.14 no.3
• /
• pp.184-190
• /
• 2011

$LiMn_2O_4$ with mesoporous hollow sphere shape was synthesized by precipitation method with silica template. The synthesized $LiMn_2O_4$ has nanosized first particle and mesoporous hollow sphere shape. Silica template was removed by chemical etching method using NaOH solution. When the concentration of NaOH solution was increased, first particle size of manganese oxide was decrease and confirmed mesoporous hollow shpere shape. X-ray diffraction(XRD) patterns revealed that the synthesized samples has spinel structure with Fd3m space group. In case the ratio of silica and maganese salt increased, the size of first particles was decreased. The tetragoanal $LiMn_2O_4$ with micron size was synthesized at ratio of silica and manganese salt over 1 : 9. The prepared samples were assembled as cathode materials of Li-ion battery with 2032 type coin cell and their electrochemical properties are examined by charge-discharge and cyclic performance. Electrochemical measurements show that the nano-size particles had lower capacity than micron-size particles. But, cyclic performance of nano-size particles had better than that of micron-size particles.

• Resources Recycling
• /
• v.12 no.1
• /
• pp.33-40
• /
• 2003

Mn was extracted by using a nitric acid from the reduced ferromanganese dust and the basic experiments were taken to refine the manganese nitrate solution by means of precipitation of Ca, Mg oxalate. The dust was generated in AOD process producing a medium-low carbon ferromanganese and collected in the bag filter. Manganese oxide content in the dust was about 90% and its phase was confirmed as $Mn_3$$O_4$. $Mn_3$$O_4$ in the dust was reduced to MnO by roasting with activated charcoal. The main impurities in the extracted solution prepared by leaching the reduced dust with nitric acid were Na, K, Fe, Si, Ca, Mg etc. Among them, Fe was removed by controlling pH of the solution more than 4 and precipitating $Fe(OH)_3$, simultaneously silicious material solved in the solution was removed by co-precipitation with the ferric hydroxide. Addition of 150 g reduced dust into 4N HNO3 solution 1$\ell$ was appropriate to control the pH of the solution to pH 4. To differ greatly the solubilities of manganese oxalate and calcium or magnesium oxalate in a solution containing a high concentration of Mn, pH of 4 or less and addition of ($NH_4$)$_2$$C_2$$O_4$ in equivalent with Ca and Mg are recommended. At this time, the higher temperature was the shorter the precipitation reaction time was needed.

• Journal of Convergence for Information Technology
• /
• v.10 no.12
• /
• pp.183-190
• /
• 2020

This study evaluated the possibility of Hoangtonogak Plus extracts as a bioactive ingredients for cosmetic products. Methanol(MN) and hot-water(WN) extracts were analysed by DPPH/ABTS radical scavenging activity, FRAP value for anti-oxidant activity, MTT assay for cell viability, inhibition of NO production and iNOS protein expression for anti-inflammatory effect, paper disc diffusion method for anti-microbial activity against Staphylococcus aureus, Staphylococcus epidermidis and Escherichia coli.. The contents of total polyphenol of MN and WN extracts were 2.92±0.01 mgGAE/g and 1.67±0.02 mgGAE/g, respectively. DPPH, ABTS and FRAP values of MN extracts were higher than WN at each concentration. No significant cytotoxicity was observed in RAW264.7 cells. Furthermore, NO production of MN and WN at 1 mg/mL concentration was measured as 11.69 μM, 20.4 μM, respectively. In addition, MN extracts showed anti-microbial effect only on S. epidermidis. Also MN extracts suppressed iNOS protein level in a concentration-dependent manner. According to our results, the MN extracts demonstrated its potential as a natural source of antioxidant with anti-microbial and anti-inflammatory properties.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.7
• /
• pp.506-510
• /
• 2012

In this study, lead-free $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ ceramics were fabricated by conventional mixed oxide method. Structural and electrical properties of lead-free $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ ceramics with the variation of sintering temperature were investigated. As results of x-ray diffraction analysis, all specimens showed a typical polycrystalline perovskite structure without presence of the second phase. Sintered density increased with an increases of sintering temperature and the specimen sintered at $1,020^{\circ}C$ showed the maximum value of 4.5 $g/cm^3$. The average grain size of the $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ specimen sintered at $1,020^{\circ}C$ is about 0.83 ${\mu}m$. Electromechanical coupling factor, relative dielectric constant and dielectric loss of $(Na_{0.465}K_{0.465}Bi_{0.07})(Nb_{0.93}Ti_{0.07})O_3-0.08MnO_2$ specimens sintered at $1,020^{\circ}C$ were 0.252, 741 and 0.043% respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.8
• /
• pp.665-670
• /
• 2009

Lead-free piezoelectric ($Na_{1/2}K_{1/2}$)$NbO_3$ ceramics doped with CuO and $MnO_2$ were fabricated using the conventional oxide-mixing technique. With increasing content of CuO and $MnO_2$, the dielectric constant(${\varepsilon}_{33}$) and mechanical quality factor($Q_m$) value increased, while electromechanical coupling factor($K_p$) and piezoelectric constant($d_{33}$) decreased. The piezoelectric and dielectric properties ($Na_{1/2}K_{1/2}$)$NbO_3$ ceramics doped with CuO 2.461 wt% and $MnO_2$ 0.538 wt% at sintered temperature $1050\;^{\circ}C$ were attained ${\varepsilon}_{33}$ = 403, $K_p$ = 15, $Q_m$ = 122 and $d_{33}$ = 36 pC/N. Based on response surface methodology results using design of experiment, it was concluded that ($Na_{1/2}K_{1/2}$)$NbO_3$ doped with CuO 0.477 wt% and $MnO_2$ 0.269 wt% has possibility composition of being used for piezoelectric transformer.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.2
• /
• pp.23-33
• /
• 1991

Mn - Zn Ferrite has the natural characteristics of incongruent melting and the zinc oxide evaporation while the crystal is being grown. As a result of these, it comes into existence to be a non-uniform distribution of cations along the crystal growth axis and also Pt particles are usually precipitated into the crystals in Bridgman method since the melt zone is maintained for a long time in the crucible. These have bad effects on the magnetic properties of ferrites. But, to overcome these faults and then acquire the better single crystals. new modified growth method was developed and the growth factors were investigated as following: melt height in the crucible, surface tension and density of melt, the behavior of melt at interface, the shapes of crucible and solid -liquid interface, powder feeding rate, and the crystal growing speed. In additon, when we analyzed the compositional fluctuations of grown crystals, they were supressed within 1.5 mol% $Fe_20_3$, 2 mol% MnO, ZnO respectively with comparing to initial composition of crystal and the microstructures of crystals on the(110) plane were observed by optical microscope through the chemical etching technique and the magnetic properties were determined.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.652-658
• /
• 1997

The phase stability in the interface of Sr-doped LaMnO3(LSM)/Gd-doped CeO2(CGO) was examined in this study in order to check the feasibility of using LSM as the cathode material in a low-temperature SOFC(solid oxide fuel cell) using CGO as the electrolyte. For the purpose, CGO powders of Ce0.82Gd0.18O0.91 and two LSM powders having different compositions, La0.9Sr0.1MnO3(LSM10) and La0.5Sr0.5MnO3(LSM50), were synthesized using Pechini method. Then, specimens having the LSM/CGO interface were prepared, heat-treated at 130$0^{\circ}C$ for up to 3 days, and analyzed by XRD and STEM/EDX. Face-centered cubic CGO powders of less than 10 nm size were obtained by calcination of polymeric precursor formed in the process at 45$0^{\circ}C$. Higher calcination temperature of $700^{\circ}C$ was necessary for monoclinic LSM10 and cubic LSM50 powders. LSM powders were coarser than CGO and observed to be in the range of 50~100 nm. No trace of LSM-CGO interaction product was found in the XRD pattern. Also it was known from the concentration profile in the vicinity of the interface that interdiffusion was occurred over only a small penetration depth of ~100 nm order.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.235-240
• /
• 2000

Screen-printing and doctor blade method were investigated and proposed as an electrode coating process for high power capacitor. CV measured from the amorphous $MnO_2$ electrode prepared by screen-printing shows closer to ideal capacitor characteristics. Specific capacitances calculated from CVs with potential scan rate of 50mV/s were 5.8, 81.8, and 172.0 F/g for electrode thickness of $140{\mu}m,\;24{\mu}m,\; 3{\mu}m$, respectively. Assumed that utilization of active $MnO_2$ in electrode of screen-printing is $100\%$, those were $3.4\%$ in one of paste method and $47.6\%$ in one of doctor blade method. The screen-printing can be good technique to coat thin film on current collector for high power application.

• Journal of the Korean Ceramic Society
• /
• v.20 no.4
• /
• pp.315-323
• /
• 1983

Effect of NiO and $MnO_2$ addtivies on the dielectric piezoelectrics and polarization-reversal properties of $(Pb_{0.936} La_{0.064})$$(Zr_{0.60}Ti_{0.40})O_3$ ceramics have been investigated. The specimens were prepared by the mixed oxide techni-que and atmosphere sintering method. The room temperature X-ray diffraction studies show that perfect perovskite solution with tetragonal structure was obtained from PLZT and its additives. The dielectric constant and dissipation factor decreased with the addition of both NiO and $MnO_2$ The Curie of Curie temperature was not observed but they displayed broadened maxima. The planar coupling factor was improved by addition of NiO and also increased with increasing sintering time carried out at 105$0^{\circ}C$ Addition of $MnO_2$ yielded a markedly high mechanical quality factor. The space-charge field decreased with the addition of NiO but increased with the addition of $MnO_2$ The planar coupling factor and space-charge field showed same dependence on the additivies. The tetragonality Curie temperature and planar coupling factor of $(Pb_{0.936} La_{0.064})$$(Zr_{0.60}Ti_{0.40})O_3$ were higher than those of $(Pb_{0.936} La_{0.064})$$(Zr_{0.568}NU_{0.032}Ti_{0.40})_{0.984}O_3$ but the grain size lattic parameter dielectric constant dissipation factor mechanical quality factor and space-charge field of the former were lower than those of the latter.

• Transactions of the Korean hydrogen and new energy society
• /
• v.14 no.3
• /
• pp.268-275
• /
• 2003

The water-splitting process by the metal oxides using solar heat is one of the hydrogen production method. The hydrogen production process using the metal oxides (NiFe2O4/NiAl2O4,CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite) was carried out by two steps. The first step was carried out by the CH4-reduction to increase activation of metal oxides at operation temperature. And then, it was carried out the water-splitting reaction using the water at operation temperature for the second step. Hydrogen was produced in this step. The production rates of H2 were 110, 160, 72, 29, 17, $21m{\ell}/hr{\cdot}g-_{Metal\;Oxide}$ for NiFe2O4/NiAl2O4, CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite respectively in the second step. CoFe2O4/CoAl2O4 had higher H2 production rate than the other metal oxides.