• Corrosion Science and Technology
• /
• 제21권1호
• /
• pp.53-61
• /
• 2022

Alloys of Fe-(5.3-29.8)%Mn-(1.1-1.9)%Al-(0.4-0.5)%C were oxidized at 550 ℃ to 650 ℃ for 20 h to understand effects of alloying elements on oxidation. Their oxidation resistance increased with increasing Mn level to a small extent. Their oxidation kinetics changed from parabolic to linear when Mn content was decreased and temperature was increasing. Oxide scales primarily consisted of Fe₂O₃, Mn₂O₃, and MnFe₂O₄ without any protective Al-bearing oxides. During oxidation, Fe, Mn, and a lesser amount of Al diffused outward, while oxygen diffused inward to form internal oxides. Both oxide scales and internal oxides consisted of Fe, Mn, and a small amount of Al. The oxidation of Mn and carbon transformed γ-matrix to α-matrix in the subscale. The oxidation led to the formation of relatively thick oxide scales due to inherently inferior oxidation resistance of alloys and the formation of voids and cracks due to evaporation of manganese, decarburization, and outward diffusion of cations across oxides.

• 한국지구과학회지
• /
• 제27권3호
• /
• pp.313-327
• /
• 2006

담양 지역의 음용 지하수 중에 형성된 망간 스케일의 지구화학적 특성을 규명하고자 하였다. 망간 스케일은 MnO 및 $SiO_2$로 구성되어 있고, MnO의 함량은 56.61wt.%에서 68.69wt.%, 그리고 $SiO_2$ 함량은 1.56wt.%에서10.45wt.%로 나타난다. 망간 스케일 중의 Ba와 Mo 함량은 지하수 심도가 증가할수록 증가하여 나타나고 Zn과 Pb는심도가 증가할수록 감소한다. 망간 스케일을 x-선 회절 분석을 한 결과 birnessite, 석영 및 장석이 분석되었다. IR 분석에서 망간 스케일은 OH, $H_2O$ 그리고 birnessite에 의한 흡수 밴드가 관찰된다. SEM 및 EDS 분석에서 망간 스케일은 포도송이 구조, 과립 구조, 구상 구조 및 속이 빈 straw 구조로 되어 있는 것이 관찰된다. 이들 구조들은 고농도의 망간함량에 의해 단순히 과포화로 침전되었을 것으로 생각되며, 혹은 Lepthothrix discophora에 의해 미생물적으로 침전되었을 것으로 생각된다. 이들 구조들의 표면을 EDS로 분석한 결과 Mn의 원자(atomic) 퍼센트가 28에서 44범위로 나타나고 Si, K, Na, Ca, Cl, Cu, Zn 및 Ba 등이 검출된다.

• 대한금속재료학회지
• /
• 제50권4호
• /
• pp.300-309
• /
• 2012

Low-carbon steels and a stainless steel were oxidized isothermally and cyclically between $1050^{\circ}C$ and $1200^{\circ}C$ for up to 100 min in air to find the effect of alloying elements of Si, Mn, Ni, and Cr on their oxidation. The most active alloying element of Si was scattered inside the oxide scale, at the scale-alloy interface and as internal oxide precipitates beneath the oxide scale. Manganese, which could not effectively improve the oxidation resistance, was rather uniformly distributed in the oxide scale. Nickel and chromium tended to present at the lower part of the oxide scale. Excessively thick porous scales formed on the low-carbon steels, whereas thin but non-adherent scales containing $Cr_2O_3$ formed on the stainless steel.

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.386-391
• /
• 2017

Two kinds of steels whose compositions were Fe-34.4Cr-14.5Ni-2.5Mo-0.4W-0.4Mn-0.5Si-(0.009 or 0.35)S (wt.%) were centrifugally cast, and oxidized at $900^{\circ}C$ for 50-350 h in order to find the effect of sulfur on the high-temperature oxidation of Fe-34.4Cr-14.5Ni-2.5Mo-0.4W-0.4Mn-0.5Si-(0.009 or 0.35)S (wt.%) alloys. These alloys formed oxide scales that consisted primarily of $Cr_2O_3$ as the major oxide and $Cr_2MnO_4$ as the minor one through preferential oxidation of Cr and Mn. They additionally formed $SiO_2$ particles around the scale/alloy interface as well as inside the matrices. The high affinity of Mn with S led to the formation of scattered MnS inclusions particularly in the 0.35S-containing cast alloy. Sulfur was harmful to the oxidation resistance, because it deteriorated the scale/alloy adherence so as to accerelate the adherence and compactness of the formed scales.

• 한국결정학회지
• /
• 제14권2호
• /
• pp.79-83
• /
• 2003

Electrolytic MnO₂ (EMD)의 미세구조를 X선 회절 및 투과전자현미경 분석을 통해 연구하였다. 벌크에 대한 X선 회절 실험은 전헝적인 EMD 재료의 분말 회절패턴을 나타내었다. 투과전자현미경 분석은 EMD가 약 0.2㎛크기의 입자로 이루어져 있고, 각각의 입자가다시 10 nm 정도의 결정립으로 이루어진 이중 미세구조를 가짐을 나타내었다. 나노 결정립에 대한 전자빔 마이크로 회절 분석 결과, EMD 입자는 여러 상의 혼합체로서 약 50%의 Ramsdellite, 30%의 ε-MnO₂, 15%의 Pyrolusite 상으로 이루어져 있음을 확인하였다. 한편, X선 분말 회절패턴 상의 약 67°에 위치한 ｛1120｝ 피크와 (0001) 면에 대한 고분해능 이미지는 ε-MnO₂ 상의 존재를 입증하였다.

• 한국표면공학회지
• /
• 제35권4호
• /
• pp.193-198
• /
• 2002

Alloys of XD45 (Ti45A12Nb2Mn-0.8vol%TiB$_2$) and XD47 (Ti47A12Nb2Mn-0.8vol%TiB$_2$) were oxidized between 800 and $1000^{\circ}C$ in air, and their oxidation characteristics were studied. The oxide scales consisted primarily of an outer $TiO_2$ layer, an intermediate $Al_2$$O_3$-rich layer, and an inner mixed layer of ($TiO_2$+$Al_2$$O_3$). Nb tended to present at the lower part of the oxide scale, whereas Mn at the upper part of the oxide scale. The Pt marker tests indicated that the outer oxide layer grew primarily by the outward diffusion of Ti and Mn, and the inner mixed layer by the inward transport of oxygen.

• 한국세라믹학회지
• /
• 제40권2호
• /
• pp.139-145
• /
• 2003

Fe-Cr 합금의 고체산화물 연료전지용 금속접속자로의 적용 가능성을 알아보기 위하여 페라이틱 스틸에 내산화 물질인 Y-Cr계 산화물을 졸 코팅하여 산화 특성을 연구하였다. YCr $O_3$졸 코팅된 페라이틱 스틸은 80$0^{\circ}C$에서 40시간 열처리 후에도 Fe계 산화물은 생성되지 않고, 주상으로 YCr $O_3$그리고 소량의 C $r_2$ $O_3$와 M $n_{1.5}$C $r_{1.5}$ $O_4$산화물 등이 생성되었다. Mn-Cr계 산화물은 금속 성분인 Mn이 내부로부터 확산에 의해 산화가 진행됨에 따라 입자가 성장하였다. 모든 YCr $O_3$졸 코팅된 시편에서의 전기 저항을 나타내는 Log(ASR/T) 값은 -4.57~-4.70Ω$ extrm{cm}^2$K￣$^1$로 코팅되지 않은 금속의 Log(ASR/T), -3.99Ω$\textrm{cm}^2$K￣$^1$보다 작아지므로 금속접속자로의 적용 가능성을 확인할 수 있었다.있었다.

• 대한금속재료학회지
• /
• 제49권2호
• /
• pp.153-160
• /
• 2011

The AISI 216L stainless steel with a composition of Fe-16Cr-6Ni-6Mn-1.7Mo (wt.%) was oxidized at $700{\sim}900^{\circ}C$ in air for 100 h. At $700^{\circ}C$, a thin $Mn_{1.5}Cr_{1.5}O_4$ oxide layer with a thickness of $0.4{\mu}m$ formed. At $800^{\circ}C$, an outer thin $Fe_2O_3$ oxide layer and a thick inner $FeCr_2O_4$ oxide layer with a total thickness of $30{\mu}m$ formed. The non-adherent scale formed at $800^{\circ}C$ was susceptible to cracking. At $900^{\circ}C$, an outer thin $Fe_2O_3$ oxide layer and a thick inner $Mn_{1.5}Cr_{1.5}O_4$ oxide layer formed, whose total thickness was $10{\sim}15{\mu}m$. The scales formed at $900^{\circ}C$ were non-adherent and susceptible to cracking. 216 L stainless steel oxidized faster than 316 L stainless steel, owing to the increment of the Mn content and the decrement of Ni content.

• 한국표면공학회지
• /
• 제54권2호
• /
• pp.43-52
• /
• 2021

The Ni-based superalloy, Inconel 740, was corroded between 800 and 1100℃ for up to 100 hr in air and Ar-0.2%SO₂ gas in order to study its corrosion behavior in air and sulfur/oxygen environment. It displayed relatively good corrosion resistance in both environment, because its corrosion was primarily dominated by not sulfidation but oxidation especially in Ar-0.2%SO₂ gas. Such was attributed to the thermodynamic stability of oxides of alloying elements when compared to corresponding sulfides. The scales consisted primarily of Cr₂O₃, together with some NiAl₂O₄, MnCr₂O₄, NiCrMnO₄, and rutile-TiO₂. Sulfur from SO₂ gas made scales prone to spallation, and thicker. It also widened the internal corrosion zone when compared to air. The corrosion resistance of IN740 was mainly indebted to the formation of protective Cr₂O₃-rich oxides, and suppression of the sulfide formation.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.373-383
• /
• 2021

The effect of Cr addition to high Mn steel on flow-accelerated corrosion (FAC) behavior in a neutral aqueous environment was evaluated. For comparison, two types of conventional ferritic steels (API X70 steel and 9% Ni steel) were used. A range of experiments (electrochemical polarization and impedance tests, weight loss measurement, and metallographic observation of corrosion scale) were conducted. This study showed that high Mn steel with 3% Cr exhibited the highest resistance to FAC presumably due to the formation of a bi-layer scale structure composed of an inner Cr enriched Fe oxide and an outer Mn substituted partially with Fe oxide on the surface. Although the high Mn steels had the lowest corrosion resistance at the initial corrosion stage due to rapid dissolution kinetics of Mn elements on their surface, the kinetics of inner scale (i.e. Cr enriched Fe oxide) formation on Cr-bearing high Mn steel was faster in dynamic flowing condition compared to stagnant condition. On the other hand, the corrosion scales formed on API X70 and 9% Ni steels did not provide sufficient anti-corrosion function during the prolonged exposure to dynamic flowing conditions.