• Journal of Sensor Science and Technology
• /
• v.28 no.1
• /
• pp.41-46
• /
• 2019

In order to develop novel thermal imaging materials for microbolometer applications, $[(Ni_{0.3}Mn_{0.7})_{1-x}Cu_x]_3O_4$ ($0.18{\leq}x{\leq}0.26$) thin films were fabricated using metal-organic decomposition. Effects of Cu content on the electrical properties of the annealed films were investigated. Spinel thin films with a thickness of approximately 100 nm were obtained from the $[(Ni_{0.3}Mn_{0.7})_{1-x}Cu_x]_3O_4$ films annealed at $380^{\circ}C$ for five hours. The resistivity (${\rho}$) of the annealed films was analyzed with respect to the small polaron hopping model. Based on the $Mn^{3+}/Mn^{4+}$ ratio values obtained through x-ray photoelectron spectroscopy analysis, the hopping mechanism between $Mn^{3+}$ and $Mn^{4+}$ cations discussed in the proposed study. The effects of $Cu^+$ and $Cu^{2+}$ cations on the hopping mechanism is also discussed. Obtained results indicate that $[(Ni_{0.3}Mn_{0.7})_{1-x}Cu_x]_3O_4$ thin films with low temperature annealing and superior electrical properties (${\rho}{\leq}54.83{\Omega}{\cdot}cm$, temperature coefficient of resistance > -2.62%/K) can be effectively employed in applications involving complementary metal-oxide semiconductor (CMOS) integrated microbolometer devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.538-548
• /
• 2003

We studied effects by Re$_2$O$_3$(R=Dy, Gd, Ho) addition on the properties of Mn-Zn ferrite. The doping concentration range from 0.05 wt% to 0.25 wt%. All samples were prepared by standard fabrication of ceramics. With increasing the rare earth oxides, specific density and initial permeability increased on the whole. But, the tendencies such as upper result had the measured value on limitation and characteristics saturated or decreased properties after that. In case of excessive addition of additive beyond some level, initial permeability properties of ferrite have gone down in spite of anomalous grain. With increasing the content of additive, both the real and imaginary component of complex permeability and the magnetic loss (tan$\delta$) increased. Because the increased rate of real component had higher than imaginary component, magnetic loss increased none the less for increasing the real component related with magnetic permeability. But, the magnetic loss of ferrite doped with the rare earth oxides was lower than that of Mn-Zn ferrite at any rate. The small amount of present rare earth oxides in Mn-Zn ferrite composition led to enhancement of resistivity in bulk, and more so in the grain boundary. It was seem to be due to the formation of mutual reaction such as between iron ions and rare earth element ions.

• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.453-457
• /
• 2005

Piezoelectric properties of $Pb(Mn_{1/3}Nb_{2/3})O_3-PbZrO_3-PbTiO_3$ ceramics were investigated with $Al_2O_3$ content $(0.0-1.0 wt\%)$. The constituent phases, microstructure, electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants were analyzed. Diffraction peaks for (002) and (200) planes were identified by X-ray diffractometer for all the specimens doped with $Al_2O_3$, indicating the MPB (morphotropic phase boundary) composition of tetragonal structures. The highest sintered density of $7.8 g/cm^3$ was obtained for $0.2wt\%\;Al_2O_3-doped$ specimen. Grain size increased by doping $Al_2O_3$ up to $0.3 wt\%$, and it decreased by more doping. Electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants increased by doping $Al_2O_3$ up to $0.2wt\%$, and it decreased by more doping. This might result from the formation of oxygen vacancies due to defects in $O^{2-}$ ion sites and the substitution of $Al^{3+}$ ions.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.113-117
• /
• 2005

Multiferroic $HoMnO_3$ single crystal was prepared using 4-point focused floating zone furnace, and polycrystalline $HoMn_{1-x}\;^57Fe_xO_3$ (x=0.00, 0.01, 0.02, 0.05) powders have been prepared by solid state reaction. Their magnetic and crystallographic properties are studied using MPMS, PPMS, and $M\ddot{o}ssbauer$ spectroscopy. The crystal structure found to be a hexagonal and a magnetic easy-axis is (110) direction. As the external applied magnetic field increases, temperature of the dielectric constant anomaly is decreased. $HoMn_{0.95}\;^{57}Fe_{0.05}O_3$ shows huge quadrupole splitting value from the $M\ddot{o}ssbauer$ spectra.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.296-301
• /
• 2018

In this study, an experiment is performed to recover the Li in $Li_2CO_3$ phase from the cathode active material NMC ($LiNiCoMnO_2$) in waste lithium ion batteries. Firstly, carbonation is performed to convert the LiNiO, LiCoO, and $Li_2MnO_3$ phases within the powder to $Li_2CO_3$ and NiO, CoO, and MnO. The carbonation for phase separation proceeds at a temperature range of $600^{\circ}C{\sim}800^{\circ}C$ in a $CO_2$ gas (300 cc/min) atmosphere. At $600{\sim}700^{\circ}C$, $Li_2CO_3$ and NiO, CoO, and MnO are not completely separated, while Li and other metallic compounds remain. At $800^{\circ}C$, we can confirm that LiNiO, LiCoO, and $Li_2MnO_3$ phases are separated into $Li_2CO_3$ and NiO, CoO, and MnO phases. After completing the phase separation, by using the solubility difference of $Li_2CO_3$ and NiO, CoO, and MnO, we set the ratio of solution (distilled water) to powder after carbonation as 30:1. Subsequently, water leaching is carried out. Then, the $Li_2CO_3$ within the solution melts and concentrates, while NiO, MnO, and CoO phases remain after filtering. Thus, $Li_2CO_3$ can be recovered.

• Journal of the Korean Ceramic Society
• /
• v.44 no.11
• /
• pp.645-649
• /
• 2007

The $La_{0.7}Sr_{0.3}MnO_3$ was deposited on $SiO_2/Si$ substrate by RF magnetron sputtering. The oxygen gas flow rate was changed from 0 to 80 sccm and the substrate temperature was $350^{\circ}C$. The oxygen gas flow rate was changed to control the growth orientation and crystalline state of the film. Relatively high TCR (temperature coefficient of resistance) value (-2.33%/K) was obtained when comparing with the reported values of the films prepared by using high substrate anneal temperature. The decrease in the sheet resistance and TCR value were observed when grain size of the film increased with the increase of oxygen gas flow rate.

• Nuclear Engineering and Technology
• /
• v.46 no.1
• /
• pp.117-124
• /
• 2014

The effect of various process variables on the powder properties of recycled $U_3O_8$ from MnO-$Al_2O_3$ doped large grain $UO_2$ pellets and the effect of those recycled $U_3O_8$ powders on the sintered density and grain size of MnO-$Al_2O_3$ doped large grain $UO_2$ pellets have been investigated. The evolution of morphology, size, and BET surface area of the recycled $U_3O_8$ powders according to the respective variation of the thermo-mechanical treatment variables of oxidation temperature, powder milling, and sequential cyclic heat treatment of oxidation and then reduction was examined. The correlation between the BET surface area of recycled $U_3O_8$ powder and the sintered pellet properties of MnO-$Al_2O_3$ doped pellets showed that the pellet density and grain size of doped pellets were increased and then saturated by increasing the BET surface area of the recycled $U_3O_8$ powder. The density and grain size of the pellets were maximized when the BET surface area of the recycled $U_3O_8$ powder was in the vicinity of $3m^2/g$. Among the process variables applied in this study, the cyclic heat treatment followed by low temperature oxidation was a potential process combination to obtain the sinter-active $U_3O_8$ powder.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.2
• /
• pp.160-171
• /
• 2013

$LiNi_{1/3}Co_{1/3}Mn_{1/3}O_2$ powder for cathode materials in lithium rechargeable batteries was treated by atmospheric plasma containing hydrogen to investigate the relationship between charge/discharge performance and physical/chemical changes of materials. Hydrogen plasma at atmosphere pressure was irradiated on the surface of active materials, and the change for their crystal structure, surface morphology, and chemical composition were observed by XRD, SEM-EDS and titration method, respectively. The crystal structure and surface morphology of $H_2$ plasma-treated powders were not changed but their chemical compositions were slightly varied. For charge/discharge test, $H_2$ plasma affected initial capacity and rate capability of active materials but continuous cycling was not subject to plasma treatment. Therefore, it was observed that $H_2$ plasma treatment affected the surface of materials and caused the change of chemical composition.

• Korean Journal of Metals and Materials
• /
• v.47 no.3
• /
• pp.188-194
• /
• 2009

Recently, new extraction technology for manganese nodule has been developed as alternative noble metallic resources. It is important to understand thermodynamic behaviors of phosphorus in low basic slag system from the viewpoint of the refining processing optimization. Thermodynamic behaviors of phosphorus in the $FeO-MnO-CaO-SiO_2-MgO_{satd.}$ slag system were investigated at 1723 K with various oxygen potential and slag composition of low basicity. The experimental results for dependence of phosphorus on oxygen potential and slag basicity indicated that the dissolution mechanism of phosphorus into slag of low basicity could be derived as follows; $[P]+5/4O_2+(O^{2-})=({PO_{3.5}}^{2-})$ Present experimental results implied that stability of phosphorus in slag would be depended on both of $O^{2-}$ (basicity) and content of $Ca^{2+}$ in molten slag. The thermodynamic effect of FeO, MnO and $Na_2O$ on low basicity on phosphate capacity was discussed.

• Clean Technology
• /
• v.21 no.3
• /
• pp.153-163
• /
• 2015

The effects of H₂O and residue SO₂ in flue gases on the activity of the Fe/zeolite catalysts for low-temperature NH₃-SCR of NO were investigated. And the addition effect of Mn, Zr and Ce to Fe/zeolite for low-temperature NH₃-SCR of NO in the presence of H₂O and SO₂ was investigated. Fe/zeolite catalysts were prepared by liquid ion exchange and promoted Fe/zeolite catatysts were prepared by liquid ion exchange and doping of Mn, Zr and Ce by incipient wetness impregnation. Zeolite NH₄-BEA and NH₄-ZSM-5 were used to adapt the SCR technology for mobile diesel engines. The catalysts were characterized by BET, X-ray diffraction (XRD), SEM/EDS, TEM/EDS. The NO conversion at 200 ℃ over Fe/BEA decreased from 77% to 47% owing to the presence of 5% H₂O and 100 ppm SO₂ in the flue gas. The Mn promoted MnFe/BEA catalyst exhibited NO conversion higher than 53% at 200 ℃ and superior to that of Fe/BEA in the presence of H₂O and SO₂. The addition of Mn increased the Fe dispersion and prevented Fe aggregation. The promoting effect of Mn was higher than Zr and Ce. Fe/BEA catalyst exhibited good activity in comparison with Fe/ZSM-5 catalyst at low temperature below 250 ℃.