• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.469-471
• /
• 2001

Dry grinding of a mixture of CaCO$_3$ and Ca(H$_2$PO$_4$)$_2$.$H_2O$ was conducted using a planetary ball mill in order to investigate solid state reaction for a synthesis of hydroxyapatite(Ca$_{10}$(PO$_4$)$_{6}$(OH)$_2$, HAp) through mechanochemical treatment method. The raw materials, which are composed of waste oyster and calcium biphosphate Ca(H$_2$PO$_4$)$_2$.$H_2O$, were mixed and then treated mechanochemically. The synthesis of hydroxyapatite(Ca$_{10}$(PO$_4$)$_{6}$(OH)$_2$, HAp) from the mixture was almost completed by about 60 minute grinding. The formation of HAp monophase in the ground mixture was characterized through X-ray diffraction (XRD) analysis. Moreover, the formation of HAp monophase depending on the grinding time was improved by increasing the grinding time.ime.ime.

• Journal of Haehwa Medicine
• /
• v.19 no.2
• /
• pp.153-158
• /
• 2011

Objective : To investigate the therapeutic effects of HangAm-Plus (HAP) on advanced gastric cancer patient. Methods : A 53 year old male patient diagnosed with advanced gastric cancer (T3N3M1) was admitted to EWCC (East-West Cancer Center) on Nov. 20008. He had refused to go through the standard cancer regimen after having total gastrectomy on Jul 2008. The patient was treated with HAP (3,000 mg/day) for the period of 11 months from Nov 27th, 2008 to Oct 10th, 2009. Computed tomography (CT) and endoscopy were used to evaluate the disease progression of the patient. Results : HAP treatment was well tolerated by the patient. Patient has shown 25 months of stable disease condition up until now. Conclusion : This case study supports HAP's potential efficacy in treating advanced gastric cancer patients.

• Carbon letters
• /
• v.16 no.4
• /
• pp.233-240
• /
• 2015

Electrochemical synthesis was employed to prepare a novel hydroxyapatite/graphene (HAP/Gr) composite powder suitable for medical applications as a hard tissue implant (scaffold). The synthesis was performed in a homogeneous dispersion containing Na₂H₂EDTA·2H₂O, NaH₂PO₄ and CaCl₂ with a Ca/EDTA/PO₄³⁻ concentration ratio of 0.25/0.25/0.15M, along with 0.01 wt% added graphene nanosheets, at a current density of 137 mA cm⁻² and pH value of 9.0. The field emission scanning electron microscopy and transmission electron microscopy observations of the composite HAP/Gr powder indicated that nanosized hydroxyapatite particles were uniformly placed in the graphene overlay. Raman spectroscopy, Fourier transform infrared spectroscopy and X-ray diffraction confirmed graphene incorporation in the HAP/Gr powder. The electrochemically prepared HAP/Gr composite powder exhibited slight antibacterial effect against the growth of the bacterial strain Staphylococcus aureus.

• Ocean and Polar Research
• /
• v.36 no.2
• /
• pp.189-197
• /
• 2014

The pearl-spot damsel, Chromis notata, is one of the important fishery species in Korea. While C. notata has been commonly harvested in southern Korea, the increasing number of C. notata in higher latitudes has crucial ecological, economic and evolutionary implications under conditions where the climate is rapidly changing. Here we examined the morphological and genetic characteristics of C. notata to assess patterns of geographical variations among the groups from three different sites. The groups were clearly distinguishable in the analysis of morphological characteristics. On the other hand, the groups were genetically indistinguishable. All individuals fell within a single clade in the neighbor-joining tree but appeared scattered in the haplotype network. Several haplotypes are shared among the sampling sites (Jejudo-Ulleungdo; Hap 9, Wangdolcho-Ulleungdo; Hap 28, Hap 33, Hap 34). Although control region markers did not elucidate the spatial patterns in genetic characteristics, Wangdolcho and Ulleungdo groups appear to exhibit a more robust gene flow between the two groups than with Jejudo group. Integrative approaches such as those combining morphological and genetic analyses minimize potential errors caused by limited perspectives of each analysis and can provide useful information for discovering functional DNA regions attributable to morphological characteristics expressions.

• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.264-271
• /
• 2006

RF sputtering process was applied to produce thin hydroxyapatite(HAp) films on Ti-6Al-4V alloy substrates. The effects of different heat treatment conditions on the chemical composites between HAp thin films and Ti-6Al-4V alloy substrates were studied. After deposition, the HAp thin films were heat treated for 1h at $400^{\circ}C,\;600^{\circ}C\;and\;800^{\circ}C$ under the atmosphere, and analyzed O/M, FESEM-EDX and ESCA, respectively. Experimental results represented that interface of HAp thin films and Ti-6Al-4V alloy substrates was composed Ti-OH, TiO, TiN, $Al_2O_3,\;V_2O_3,\;VO_2$. pyrophosphate and decreased carbide followed by the increase of heat treatment temperature.

• Journal of Microbiology and Biotechnology
• /
• v.18 no.5
• /
• pp.975-982
• /
• 2008

We investigated whether transplantation of osteogenically differentiated bone marrow-derived mesenchymal stem cells (BMMSCs) and the use of an hydroxyapatite (HAp) scaffold can enhance the in vivo bone formation efficacy of human BMMSCs. Three months after implantation to the subcutaneous dorsum of athymic mice, transplantation of osteogenically differentiated human BMMSCs increased the bone formation area and calcium deposition to 7.1- and 6.2-folds, respectively, of those of transplantation of undifferentiated BMMSCs. The use of the HAp scaffold increased the bone formation area and calcium deposition to 3.7- and 3.5-folds, respectively, of those of a polymer scaffold. Moreover, a combination of transplantation of osteogenically differentiated BMMSCs and HAp scaffold further increased the bone formation area and calcium deposition to 10.6- and 9.3-folds, respectively, of those of transplantation of undifferentiated BMMSCs seeded onto polymer scaffolds. The factorial experimental analysis showed that osteogenic differentiation of BMMSCs prior to transplantation has a stronger positive effect than the HAp scaffold on in vivo bone formation.

• Korean Journal of Materials Research
• /
• v.16 no.11
• /
• pp.715-718
• /
• 2006

Porous hydroxyapatite (HAp) scaffolds have been prepared by using the slurry including HAp and magnesia based on the replication of polymer sponge substrate. The influence of MgO content in slurry on the pore morphology and size, density, porosity, and mechanical strength of porous HAp scaffolds was investigated. The obtained scaffolds with average pore sizes ranging 150 to 300 mm had open, relatively uniform, and interconnected porous structure regardless of MgO content. As the MgO content increased, the pore network frame of scaffolds became to be relatively stronger, even though the pore size was not much changed. The compressive strength of the scaffolds increased rapidly with the increase of MgO content because of increasing the pore wall thickness and density of the scaffolds. As a result, the porosity, density, and compressive strength of the porous HAp scaffolds prepared by the sponge method were significantly affected by the addition of MgO.

• The Journal of Korean Medicine Ophthalmology and Otolaryngology and Dermatology
• /
• v.34 no.4
• /
• pp.228-236
• /
• 2021

Objective : The purpose of this study is to report the clinical effectiveness of herbal decoction(Samul-tang hap Soyo-san.) on whole body nummular eczema. Method : A patient suffering from nummular eczema received herbal decoction(Samul-tang hap Soyo-san), acupuncture, and electronic-moxibustion treatment. The effectiveness of treatment was evaluated by EASI, DLQI, photography and subjective evaluation of the patient's improvement of symptoms. Results : After treatment, eczema lesions were remarkably improved. Compared to its peak, EASI improved by 69% and DLQI by 53%. According to photo and symptom changes, purulent exudates were stopped and pruritus was decreased. Conclusion : This study suggests that Samul-tang hap Soyo-san could show effectiveness on nummular eczema.

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.570-575
• /
• 2018

Hydroxyapatites (HAps) were synthesized using the powdered waste of fishery products, i.e., fish scales and crab shells, as starting materials. HAp was synthesized by a wet-chemistry method followed by calcination at 600 and $800^{\circ}C$. Calcined crabshell powder revealed a single HAp phase and fine powder, while calcined fish-scale powder showed a ${\beta}-TCP$ secondary phase, even at the higher calcination temperature. Dense HAp pellets were obtained from the crab-shell powder by spark plasma sintering at $1000^{\circ}C$ for 10 min under applied pressures of 40 and 80 MPa in a vacuum state, giving sample densities of 2.93 and $3.06g/cm^3$, respectively. The estimated grain size of HAp was $448{\pm}96$ and $283{\pm}59nm$ for applied pressures of 40 and 80 MPa, respectively. In contrast, the HAp obtained using the pressureless sintering technique showed excessive grain growth without further densification.

• Journal of Korean Society of Water and Wastewater
• /
• v.31 no.6
• /
• pp.577-586
• /
• 2017

One of the major sources causing eutrophication and algal blooms of lakes or streams is phosphorus which comes from point and nonpoint pollution sources. HAP (hydroxyapatite) crystallization using granular alkaline materials can achieve the decrease of phosphorus load from wastewater treatment plants and nonpoint pollution control facilities. In order to induce HAP crystal formation, continuous supply of calcium and hydroxyl ions is required. In this research, considering HAP crystallization, several types of lime-based granular alkaline materials were prepared, and the elution characteristics of calcium and hydroxyl ions of each were analyzed. Also, column tests were performed to verify phosphorus removal efficiencies of granular alkaline materials. Material_1 (gypsum+cement mixed material) achieved the highest pH values in the column tests consistently, also, Material_2 (gypsum+slag mixed material) and Material_3 (calcined limestone material) achieved over pH 9.0 for 240 hours (10 days) and proved the efficiencies of long-term ion supplier for HAP crystallization. In the column tests using Material_3, considerable pH increase and phosphorus removal were carried out according to each linear velocity and filtration depth. T-P removal efficiencies were 87.0, 84.0, 68.0% and those of PO4-P 100.0, 97.0, 80.0% for linear velocity of 1.0, 2.5, 5.0 m/hr respectively. Based on the column test results, the applicability of phosphorus removal processes for small-scale wastewater treatment plants and nonpoint pollution control facilities was found out.