• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 춘계학술발표대회 개요집
• /
• pp.278-281
• /
• 2002

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2001년도 추계학술발표대회 개요집
• /
• pp.162-164
• /
• 2001

• Journal of Welding and Joining
• /
• 제20권2호
• /
• pp.90-94
• /
• 2002

FC-BGA has advantages over other interconnection methods including high I/O counts, better electrical performance, high throughput, and low profile. But, FC-BGA has a lot of reliability issues. The 2nd level solder joint reliability of the FC-BGA with large chip on laminate substrate was studied in this paper. The purpose of this study is to discuss solder joint failures of 2nd level thermal cycling test. This work has been done to understand the influence of the structure of package, the properties of underfill, the properties and thickness of bismaleimide tiazine substrate and the temperature range of thermal cycling on 2nd level solder joint reliability. The increase of bismaleimide tiazine substrate thickness applied to low modulus underfill was improve of solder joint reliability. The resistance of solder ball fatigue was increased solder ball size in the solder joints of FC-BGA.

• 마이크로전자및패키징학회지
• /
• 제21권1호
• /
• pp.1-6
• /
• 2014

고출력 LED 패키지의 열적 경로(thermal path)를 줄이기 위해 플립칩 본딩법에 대한 연구가 활발히 진행되고 있다. 본 연구에서는 Au-Sn 열압착 본딩 및 Sn-Ag-Cu(SAC) 리플로우 본딩을 이용하여 본딩 특성 및 열적특성을 비교 평가 하였다. Au-Sn 열압착 본딩은 50 N에서 $300^{\circ}C$의 접합온도로 본딩하였고, SAC 솔더는 솔더페이스트를 인쇄한 후 리플로우법으로 피크온도 $255^{\circ}C$에서 30 sec에서 본딩하였다. SAC 솔더를 사용한 LED 패키지의 전단강도는 $5798.5gf/mm^2$로 Au-Sn 열압착 본딩의 $3508.5gf/mm^2$에 비해 1.6배 높았다. 파단면과 단면분석 결과 Au-Sn, SAC 솔더 모두 LED 칩 내부에서 파단이 일어나는 것을 관찰하였다. 반면 Au-Sn 열압착 본딩 샘플의 열저항은 SAC솔더 접합 샘플에 비해 낮았으며, SAC 솔더 접합부 내부의 기공에 의해 열저항이 커짐을 알 수 있었다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.456-462
• /
• 2002

In the present work, a low cost and fine pitch bumping process by electroless Ni/immersion Au UBM (under bump metallurgy) and stencil printing for the solder bump on the Al pad is discussed. The Chip used this experimental had an array of pad 14x14 and zincate catalyst treatment is applied as the pretreatment of Al bond pad, it was shown that the second zincating process produced a dense continuous zincating layer compared to first zincating. Ni UBM was analyzed using Scanning electron microscopy, Energy dispersive x-ray, Atomic force microscopy, and X-ray diffractometer. The electroless Ni-P had amorphous structures in as-plated condition. and crystallized at 321 C to Ni and Ni$_3$P. Solder bumps are formed on without bridge or missing bump by stencil print solder bump process.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.21-23
• /
• 2006

The microstructural investigation and thermo-mechanical reliability evaluation of the Sn-3.0Ag-0.5Cu solder bumped flip chip package were carried out during the thermal shock test of the package. In the initial reaction, the reaction product between the solder and Cu mini bump of chip side was Cu6Sn5 layer, while the two phases which were (Cu,Ni)6Sn5 and (Ni,Cu)3Sn4 were formed between the solder and Ni-P layer of the package side. The cracks were occurred at the corner solder joints after the thermal shocks of 400 cycles. The primary failure mechanism of the solder joints in this type of package was confirmed to be thermally activated solder fatigue failure.

• 한국정밀공학회지
• /
• 제31권10호
• /
• pp.865-871
• /
• 2014

Paradigm shift to 3-D chip stacking in electronic packaging has induced a lot of integration challenges due to the reduction in wafer thickness and pitch size. This study presents a hybrid bonding technology by self-alignment effect in order to improve the flip chip bonding accuracy with ultra-thin wafer. Optimization of Cu pillar bump formation and evaluation of various factors on self-alignment effect was performed. As a result, highly-improved bonding accuracy of thin wafer with a $50{\mu}m$ of thickness was achieved without solder bridging or bump misalignment by applying reflow process after thermo-compression bonding process. Reflow process caused the inherently-misaligned micro-bump to be aligned due to the interface tension between Si die and solder bump. Control of solder bump volume with respect to the chip dimension was the critical factor for self-alignment effect. This study indicated that bump design for 3D packaging could be tuned for the improvement of micro-bonding quality.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2010년도 춘계학술발표대회 초록집
• /
• pp.78-78
• /
• 2010

모바일 정보통신기기를 중심으로 패키지의 초소형화, 고집적화를 위해 플립칩 공법의 적용이 증가되고 있고 있으며 접속피치의 미세화에 따라 솔더 및 언더필을 사용하는 C4 공법보다 ACA(Anisotropic Conductive Adhesive), NCA (Non-conductive Adhesive) 등의 접착제를 이용하는 칩본딩 공법에 대한 요구가 증가하고 있다. 특히, NCA 공법의 경우 산업 현장의 대량생산에 대응하기 위해서는 접착제의 속경화 특성이 요구되어 진다. 일반적으로 접착제의 경화거동은 DSC(Differential Scanning Calorimeter)를 사용해 확인하지만, 수초 이내에 경화되는 접착제의 경우는 적용되기 어렵다. 본 연구에서는 이러한 전자패키지용 접착제의 속경화 거동을 효과적으로 평가할 수 있는 방법을 조사 하였다. 실험에서 사용된 접착제는 에폭시계 레진 기반에 이미다졸계 경화제를 사용한 기본적인 포뮬레이션을 사용하였고, 경화시간은 160^{\circ}C에서 1분 이내에 경화되는 특성을 가지고 있다. 경화 거동을 확인하기 위해서 isothermal DSC와 DEA(Dielectric Analysis)의 두가지 방법을 사용해 비교하였다. 두 실험 방법 모두 $160^{\circ}C$를 유지하며 경화 거동을 확인하였고, DoC(Degree of Cure)의 측정오차를 비교 분석하였다. DEA는 이온 모빌리티 변화에 따른 유전손실율을 측정하는 방법으로 80~90% 이후의 경화도는 측정되지 않았지만, 수초 이내에 경화되는 속경화 특성을 평가하기에 적합한 것으로 확인되었다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2000년도 특별강연 및 춘계학술발표대회 개요집
• /
• pp.170-173
• /
• 2000

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.203-205
• /
• 2006