• JSTS:Journal of Semiconductor Technology and Science
• /
• v.2 no.3
• /
• pp.213-225
• /
• 2002

Metal-Ferroelectric- Insulator- Silicon (MFIS) structured field effect transistor (FET) device was fabricated and characterized. Important issues to realize ferroelectric gate field effect transistor device were summarized in three sections. The choice of interlayer dielectric was made in the consideration of device functionality and chemical reaction between ferroelectric materials and silicon surface during fabrication process. Also, various ferroelectric thin film materials were taken into account to meet desired memory window and process compatibility. Finally, MFIS structured FET device was fabricated and important characteristics were discussed. For feasible integration of current device as random access memory array cell address schemes were also suggested.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.8
• /
• pp.894-900
• /
• 2006

The electrical characteristics associated with crystal structure changes as a function of La content for $(Pb_{1-x}La_x)(Zr_{0.5}Ti_{0.5})O_3$ thin films were investigated for applications in memory capacitors. Tetragonality of PLZT films decreased with increasing La content. Thin films with La $\geq$ 20 mol% were found to be cubic. Films with La $\geq$ 12 mol% exhibited broader dielectric peaks compared to those of bulk ceramics and behaved as relaxer ferroelectrics. Tetragonal PLZT film with 12 mol% La had a dielectric constant maximum of 1330 at room temperature and a charge storage density of ${\sim}18{\mu}C/cm^2$ at 5 V. Decrease in coercive field and remnant polarization with increase in La content were resulting from less dipolar response caused by the decreased crystal anisotropy. The leakage current densities $<10^{-8}A/cm^2$ up to 5 V bias voltage were observed for the films with La $\geq$ 14 mol%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.8
• /
• pp.694-699
• /
• 2000

S $r_{0.9}$/B $i_{2.1}$/T $a_{2}$/ $O_{9}$ solutions was synthesized by MOD (metalorganic decomposition) method. SBT thin films with 2000$\AA$ thickness were prepared on Ir $O_2$/ $SiO_2$/Si and Pt/Ti/ $SiO_2$/Si substrates using the spin coating process and then investigated the dielectric and electrical properties of them. In the case of using Ir $O_2$bottom electrode the hysteresis loop was saturated at lower temperature than Pt/Ti electrode but the breakdown phenomenon was occurred at low voltage because of the rough surface morphology and porous microstructure of SBT thin films. As the results of the fatigue and imprint characteristics related to the lifetime and reliability of devices after 10$^{10}$ cycles the fatigue rates were about 10% at the Ir $O_2$and Pt/Ti bottom electrodes. Both SBT thin films with Ir $O_2$ and with Pt/Ti bottom electrodes show a slight tendency to imprint after 10$^{9}$ cycles but do not lead to a failure.e.e.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.118-121
• /
• 1999

PLZT thin films were fabricated with different energy density by pulsed laser deposition. PLZT films deposited on Pt/Ti/SiO$_2$/Sr substrate. This PLZT thin films of 5000$\AA$ thickness were crystallized at $600^{\circ}C$, 200mTorr $O_2$ pressure for 2 J/$\textrm{cm}^2$ laser energy density. 14/50/50 PLZT thin film showed a maximum dielectric constant value of $\varepsilon$$_{r}$=1289.9 P-E hysteresis loop of 14/ 50/50 PLZT thin film was slim ferroelectric. Leakage current density of 14/50/50 PLZT thin film was 10/ sup -7/=A/$\textrm{cm}^2$.>.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.278-281
• /
• 1999

PLZT thin films on Pt/Ti/SiO$_2$/Si substrate were fabricated with different Thickness by pulsed laser deposition. 14/50/50 PLZT thin film showed a maximum dielectric constant value of $\varepsilon$$_{t}$=985 at 5000$\AA$, and $\varepsilon$$_{t}$=668 at 2000A. P-EI hysteresis loop of 14/50/50 PLZT thin film was slim ferroelectric. Leakage current density of 14/50/70 PLZT thin film was 10$^{-8}$ A/$\textrm{cm}^2$ at 2000$\AA$.EX>.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.239-244
• /
• 2015

Lead zirconate titanate (PZT) thick films with thickness of $10{\sim}20{\mu}m$ were fabricated on silicon substrate by aerosol deposition method. As-deposited films on silicon were annealed at the temperatures of $700^{\circ}C$. The electrical properties of films deposited by PZT powders were characterized using impedance analyzer and Sawyer-Tower circuit. The PZT powder was prepared by both conventional solid reaction process and sol-gel process. The remanent polarization, coercive field, and dielectric constant of the $10{\mu}m$ thick film with solid reaction process were $20{\mu}C/cm^2$, 30 kV/cm and 1320, respectively. On the other hand, the PZT films by sol-gel process showed a poor dielectric constant of 635. The reason was probably due to the presence of pores produced from organic residue during annealing.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.960-964
• /
• 2004

[ $Ba_2NaNb_5O_{15}$ ](BNN) thin films have been prepared by the ion beam sputter deposition (IBSD) method on Pt coated Si substrate at temperature as low as $600^{\circ}C$ XRD, SEM were used to investigate the crystallization and microstructure of the films. It was found that the films were crack-free and uniform in microstructure. The electric properties of thin films were carried out by observation of D-E hysteresis loop, dielectric constant and leakage current. It was found the deposition rate strongly influenced the phase formation of the films, where the phase of $BaNb_2O_6$ was always formed when the deposition rate was high. However, the single phase (tungsten bronze structure ) BNN thin film was obtained with the deposition rate as low as $22{\AA}/min$. The remanent polarization Pr and dielectric constant are about 1-2 ${\mu}C/cm^2$ and $100\sim200$, respectively. It was also founded the electric properties of thin films were influenced by the deposition rate. The Pr and dielectric constant of films increased with the decrease of deposition rate. The effects of annealing temperature and annealing time to the crystallization behavior of films were studied. The crystallization of thin film started at about $600^{\circ}C$. The adequate crystallization was gotten at the temperature of $650^{\circ}C$ when the annealing time is 0.5 hour or at the temperature of $600^{\circ}C$ when the annealing time is long as 6 hours.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.169-170
• /
• 2006

In this study, ultra thin films of ferroelectric vinylidene fluoride-trifluoroethylene (VF2-TrFE) copolymer were fabricated on degenerated Si (n+, $0.002\;{\Omega}{\cdot}cm$) using by spin coating method. A 1~5 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene (VF2:TrFE=70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers at a spin rate of 2000~5000rpm for 30 seconds. After annealing in a vacuum ambient at $200^{\circ}C$ for 60 min, upper gold electrodes were deposited by vacuum evaporation for electrical measurement. X-ray diffraction results showed that the VF2-TrFE films on Si substrates had $\beta$-phase of copolymer structures. The capacitance on $n^+$-Si(100) wafer showed hysteresis behavior like a butterfly shape and this result indicates clearly that the dielectric films have ferroelectric properties. The typical measured remnant polarization (2Pr) and coercive filed (EC) values measured using a computer controlled a RT-66A standardized ferroelectric test system (Radiant Technologies) were about $0.54\;C/cm^2$ and 172 kV/cm, respectively, in an applied electric field of ${\pm}0.75\;MV/cm$.

• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.325-328
• /
• 1991

In this study, $0.085Ba(La_{1/2}Nb_{1/2})O_3-0.915Pb(Zr_yTi_{1-y})O_3$(y=0.45, 0.50, 0.55, 0.60, 0.65[mol]) transparent electrooptic ceramics were fabricated by two-stage sintering method. Increasing the $PbZrO_3$ contents, dielectric constant was increased and Curie temperature was decreased. In the composition of 0.55[mol] $PbZrO_3$, electromechanical coupling factor was 0.43. From the results of ferroelectric hysteresis loop and transmitted light intensity with electric field, the compositions of 0.65, 0.60, 0.55[mol] $PbZrO_3$ was applicable to electroopticmemory device and the compositions of 0.50, 0.45[mol] $PbZrO_3$ was applicable to linear electrooptic device.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.70-73
• /
• 2001

MFIS(Metal-ferroelectric-insulator- semiconductor) structures using silicon oxynitride(SiON) buffer layers were fabricatied and demonstrated nonvolatile memory operations. Oxynitride(SiON) films have been formed on p-Si(100) by RTP(rapid thermal process) in O$_2$+N$_2$ ambient at 1100$^{\circ}C$. The gate leakage current density of Al/SiON/Si(100) capacitor was about the order of 10$\^$-8/ A/cm$^2$ at the range of ${\pm}$ 2.5 MV/cm. The C-V characteristics of Al/LiNbO$_3$/SiON/Si(100) capacitor showed a hysteresis loop due to the ferroelectric nature of the LiNbO$_3$ thin films. Typical dielectric constant value of LiNbO$_3$ film of MFIS device was about 24. The memory window width was about 1.2V at the electric field of ${\pm}$300 kV/cm ranges.