• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.177-182
• /
• 2017

The properties of electroless Ni-B thin film on diamond powder with different parameters (temperature, pH, surfactant etc.) were studied. The surface morphology, structure and composition distribution of the Ni-B film were observed by field effect scanning electron microscope (FE-SEM), energy-dispersive spectrometer (EDS), X-ray diffraction (XRD) and Auger electron spectroscopy (AES). The growth rate of Ni-B film was increased with increase of bath temperature. The B content in Ni-B film was reduced with increase of bath pH. As a result the structure of Ni-B film was changed from amorphous to crystalline structure. The PVP in solution plays multi-functional roles as a dispersant and a stabilizer. The Ni-B film deposited with adding 0.1 mM-PVP was strongly introduced an amorphous structure with higher B content (25 at.%). Also the crystallite size of Ni-B film was reduced from 12.7 nm to 5.4 nm.

• Journal of the Korean Ceramic Society
• /
• v.30 no.4
• /
• pp.279-288
• /
• 1993

A study on calcination and reduction of AUC(ammonium uranyl carbonate, (NH4)4UO2(CO3)3) has been carried out by using TG-DTA in N2, air and H2 atmospheres, respectively. Phases of various intermediate obtained during thermal analysis of AUC in different atmospheres were confirmed by XRD. Powder characteristics of each intermediate were investigated by measuring particle size and specific surface area, and also observed by SEM. As a results, regardless of applied atmosphere AUC was calcined into amorphous UO3, which was converted to $\alpha$-U3O8 Via $\alpha$-UO3 in both H2 and N2 atmosphere, but directly into $\alpha$-UO3 in air atmosphere. Further reduction of U3O8 was only detectable in hydrogen atmosphere. During calcination and reduction, average particle size was reduced to less than 30% of original value without morphology change. Specific surface area was dramatically increased with release of NH3, CO2 and H2O from AUC powder and reached maximum value around 25$0^{\circ}C$, and then gradually decreased with the increase of temperature due to sintering effect of uranium oxides such as UO3 and U3O8. It was also found that the change of average crystallite size and pore size were closely related to the changes of specific surface area of uranium oxides.

• Korean Journal of Materials Research
• /
• v.24 no.4
• /
• pp.186-193
• /
• 2014

A thin Cu seed layer for electroplating has been employed for decades in the miniaturization and integration of printed circuit board (PCB), however many problems are still caused by the thin Cu seed layer, e.g., open circuit faults in PCB, dimple defects, low conductivity, and etc. Here, we studied the effect of heat treatment of the thin Cu seed layer on the deposition rate of electroplated Cu. We investigated the heat-treatment effect on the crystallite size, morphology, electrical properties, and electrodeposition thickness by X-ray diffraction (XRD), atomic force microscope (AFM), four point probe (FPP), and scanning electron microscope (SEM) measurements, respectively. The results showed that post heat treatment of the thin Cu seed layer could improve surface roughness as well as electrical conductivity. Moreover, the deposition rate of electroplated Cu was improved about 148% by heat treatment of the Cu seed layer, indicating that the enhanced electrical conductivity and surface roughness accelerated the formation of Cu nuclei during electroplating. We also confirmed that the electrodeposition rate in the via filling process was also accelerated by heat-treating the Cu seed layer.

• Korean Journal of Materials Research
• /
• v.25 no.5
• /
• pp.247-252
• /
• 2015

The effect of precursor concentration on the structural, morphological, and optical properties of $TiO_2$nano-flowers was investigated in this study. An increase in crystallite size was observed with an increase in the concentration of the precursor (titanium butoxide). The FE-SEM micrographs of the as-prepared samples show a three-dimensional flower-like morphology. The flowers consist of several nanorods coming out of a single core and have very sharp edges. Also, the variation in the aspect ratio of the nanostructure was observed with the concentration of the precursor. The photocatalytic properties of the samples show that the sample that has a high aspect ratio (AR~9) has a much better photocatalytic activity compared to the nano-crystal with a low aspect ratio (AR~6.1). It is believed that the excellent photocatalytic performance and short time synthesis of $TiO_2$nano-flowers using the microwave hydrothermal method can have potential applications in the field of photocatalysis.

• Particle and aerosol research
• /
• v.6 no.1
• /
• pp.29-35
• /
• 2010

Transition metals such as V, Fe, and Ni were used to synthesize doped zinc oxide nanoparticles from mixed liquid precursors by using the flame spray pyrolysis (FSP). The effects of dopants on the powder properties such as morphology, specific surface area, crystal structure, and light adsorption were analyzed by TEM, BET, XRD, and UV-Vis diffuse reflection spectrum (DRS), respectively. The results showed that hexagonal wurtzite structured ZnO:M (M = V, Fe, Ni) nanoparticles were successfully synthesized by the FSP. The transition metal-doping resulted in the decrease in its particle size and crystallite size. The UV-vis absorption spectra of ZnO:M nanoparticles were also red-shifted. ZnO:V showed the highest MB degradation of 99.4% under the UV irradiation after 3 hrs.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.1
• /
• pp.23-27
• /
• 2003

Structural properties of Cu-Ni alloy films, such as preferred orientation, crystallite size, in-ter-planar spacing, cross-sectional morphology, and electrical resistivity, are investigated in terms of tar-get configurations that are used in the film deposition by means of magnetron co-sputtering. Two different target configurations are considered in this study: a dual-type configuration in which two separate tar-gets (Cu and Ni) and different bias types (RF and DC) are used and a Ni-on-Cu type configuration in which Ni chips are attached to a Cu target. The dual-type configuration appears to have some advantages over the Ni-on-Cu type regarding the accurate control of atomic composition of the deposited Cu-Ni alloy. However, the dual-type-produced film exhibits a porous and columnar structure, the relatively large internal stress, and the high electrical resistivity, which are mainly due to the relatively low mobility of adatoms. The affects of thermal treatment and deposition conditions on the structural and electrical properties of dual-type Cu-Ni films are also discussed.

• Journal of Powder Materials
• /
• v.28 no.5
• /
• pp.375-380
• /
• 2021

In this study, we investigate the effect of the duration of mechanical alloying on the microstructures and mechanical properties of ODS ferritic/martensitic steel. The Fe(bal.)-10Cr-1Mo pre-alloyed powder and Y₂O₃ powder are mechanically alloyed for the different mechanical alloying duration (0 to 40 h) and then constantly fabricated using a uniaxial hot pressing process. Upon increasing the mechanical alloying time, the average powder diameter and crystallite size increased dramatically. In the initial stages within 5 h of mechanical alloying, inhomogeneous grain morphology is observed along with coarsened carbide and oxide distributions; thus, precipitate phases are temporarily observed between the two powders because of insufficient collision energy to get fragmented. After 40 h of the MA process, however, fine martensitic grains and uniformly distributed oxide particles are observed. This led to a favorable tensile strength and elongation at room temperature and 650℃.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.167-172
• /
• 2013

Titanium dioxides nanoparticles coated aluminum oxide powders were fabricated by pulsed laser deposition (PLD) with Nd : YAG laser at 266 nm. The Pulse laser energy is 100 mJ/pulse. During the irradiation of the focused laser on the $TiO_2$ target, Ar gas is supplied into the chamber. The gas pressure is varied in a range of $1{\times}10^{-2}$ to 100 Pa. Titanium dioxides nanoparticles deposited aluminum oxide powders were characterized by using energy dispersive X-ray spectroscopy (EDX), high resolution transmission electron microscopy (HR-TEM), in order to understand the effect of Ar background gas on surface morphology and properties of the powders. The coated $TiO_2$ nanoparticles had nanosized spherical shape and the crystallite sizes of 10~30 nm. The morphology of coated $TiO_2$ nanoparticles is not affected by gas pressure. However, the particle size and crystallinity slightly increased with the increase of gas pressure. According to this technique, the size and crystallinity of nanoparticles can be easily controlled by controlling pressure during the laser irradiation.

• Polymer(Korea)
• /
• v.34 no.6
• /
• pp.522-526
• /
• 2010

Bacterial cellulose is produced by the bacterium Gluconacetobacter xylinus, which forms a nanofibrous pellicle in its culture medium. We studied properties of the bacterial cellulose such as crystallinity, viscosity, morphology, and mechanical properties according to the carbon source. Static cultures of Gluconacetobacter sp. V6 were performed in three kinds of media: standard Hestrin-Schramm medium, and modified medium with either glycerol or molasses as carbon sources. Cell growth and cellulose yield were increased in the glycerol and molasses media. The culture in the glycerol medium improved the physical properties of cellulose such as crystallinity, intrinsic viscosity, and breaking stress. However, the culture in the molasses medium decreased crystallinity, crystallite size, and intrinsic viscosity of cellulose. In summary, the cellulose yield was remarkably improved in the molasses medium, but with inferior structural properties.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11a
• /
• pp.110-114
• /
• 2010

Li-incorporated mesoporous $TiO_2$ materials with various pore-sized istributions were synthesized by using triblockcopolymers via a sol-gel process in a queous solution. The properties of the se materials were characterized by HR-TEM, XRD, and BET analysis. All particles have spherical morphology with a diameterrange of $1-3{\mu}m$. The mesoporous $TiO_2$ materials calcined at $400^{\circ}C$ and their specific surface area, average pore size and crystallite sizes were 210 $m^2g^{-1}$, 6.4 nm and 8.8 nm respectively. The Li-incorporated mesoporous $TiO_2$ were tested for $CO_2$ adsorption and its adsorption capacity is 90mg/g. The Li-incorporated mesoporous $TiO_2$ ar eobserved to be thermally stable, recyclable and greens or bent for $CO_2$ capture. The effect of bimetallic $ZrLiTiO_2$ is also studied for $CO_2$ adsorption.