• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.86.2-86.2
• /
• 2010

In order to improve polymer electrolyte membrane fuel cell (PEMFC) durability, the durability of membrane electrode assemblies (MEA), in which the electrochemical reactions actually occur, is one of the vital issues. Many articles have dealt with catalyst layer degradation of the durability-related factors on MEAs in relation to loss of catalyst surface area caused by agglomeration, dissolution, migration, formation of metal complexes and oxides, and/or instability of the carbon support. Degradation of catalyst layer during long-term operation includes cracking or delamination of the layer which result either from change in the catalyst microstructure or loss of electronic or ionic contact with the active surface, can result in apparent activity loss in the catalyst layer. Membrane degradation of the durability-related factors on MEAs can be caused by mechanical or thermal stress resulting in formation of pinholes and tears and/or by chemical attack of hydrogen peroxide radicals formed during the electrochemical reactions. All of these effects, the mechanical damage of membrane and degradation of catalyst layers are more facilitated by uneven stress or improper MEA fabrication process. In order to improve the PEMFC durability, therefore, it is most important to minimize the uneven stress or improper MEA fabrication process in the course of the fabrication of MEA. We analyzed the effects of the MEA fabrication condition on the PEMFC durability with MEA produced using CCM (catalyst coated membrane) method. This paper also investigated the effects of MEA fabrication condition on the PEMFC durability by adding additional treatment process, hot pressing and pressing, on the MEA produced using CCM method.

• 한국정밀공학회지
• /
• 제27권9호
• /
• pp.58-66
• /
• 2010

This study examines thermal safety on three-way catalyst that dominates 70 % among whole exhaust gas purification device in 2003. Three-way catalyst durability in the Korea requires 5 years/80,000 km in 1988 but require 10 years/120,000 km after 2002. Three-way catalyst durability in the USA requires 7 years/120,000 km but require 10 years/160,000 km after 2004. Three-way catalyst maintains high temperature in interior domain but maintains low temperature on outside surface. Therefore this device shows tensile stress on outside surface. Temperature distribution of three-way catalyst was acquired by thermal flow analysis for predicted thermal flow parameter. Thermal stress analysis for three-way catalysis was performed based on this temperature distribution. Thermal safety of three-way catalyst was estimated by power law dynamic fatigue life estimation and strength reduction methods for thermal stress.

• 융복합기술연구소 논문집
• /
• 제9권1호
• /
• pp.7-12
• /
• 2019

The aim of this study is to improve the durability performance of catalysts for a catalytic combustor and to obtain operating conditions for stable combustion of the catalytic combustor. It was attempted to improve the durability of the catalysts by adding a promoter in order to reduce the cost of replacing Pt catalyst while maintaining stability. The main catalyst used in the study was Pt and the promoters were Ni and La. Pure Pt3/γ-Al₂O₃ catalyst without promoter was promoted to fast sintering states under harsh conditions and catalytic combustion was turned off, whereas the catalysts added La, Ni as promoter were showed relatively slow sintering states. It can be concluded that the promoter La, Ni effectively contributes to the improvement of the durability of the Pt catalyst, and it is possible to get longer durability and more stable duration than the conventional catalytic combustor.

• Korean Chemical Engineering Research
• /
• 제50권4호
• /
• pp.627-631
• /
• 2012

휴대용 고분자전해질 연료전지의 수소발생용으로써 $NaBH_4$는 많은 장점을 갖고 있다. 본 연구에서는 $NaBH_4$ 가수분해 반응용 Co-P-B/Cu 촉매의 내구성에 대해 연구하였다. Co-P-B/Cu 촉매의 내구성 미치는 반응 온도, $NaBH_4$ 농도, NaOH 농도, 촉매 소성온도 등의 영향에 대해 실험하였다. 촉매의 내구성은 가수분해 반응 중에 발생하는 gel 형성에 영향을 받았다. 즉 gel 형성에 의해 촉매 손실률이 증가하였다. $NaBH_4$ 농도가 고농도일 때는 $60^{\circ}C$ 이상에서는 gel 형성이 안 되어 촉매 손실률이 낮았다. 그러나 $40^{\circ}C$ 이하에서는 gel이 형성되어 촉매 손실률이 증가했다. $NaBH_4$ 20 wt%, $40^{\circ}C$에서 NaOH 농도증가에 따라 겔이 형성되어 촉매 손실률이 증가함을 보였다. Co-P-B/Cu 촉매의 높은 온도에서 소성은 내구성을 향상시켰지만 촉매 활성을 감소시켰다.

• Korean Chemical Engineering Research
• /
• 제61권3호
• /
• pp.341-347
• /
• 2023

PEMFC(Proton Exchange Membrane Fuel Cells)에서 PtCo/C 합금 촉매가 성능이나 내구성에서 우수하여 많이 사용되고 있다. 그러나 높은 전압에서(1.0~1.5 V) 평가되는 촉매 지지체 내구성에 관한 연구는 별로 보고 되지 않았다. 본 연구에서는 PtCo/C 촉매와 Pt/C 촉매에 촉매 지지체 가속 열화 프로토콜을 적용한 후 내구성을 비교하였다. 1.0↔1.5V 전압 변화 사이클 반복 후에 촉매 비활성도(Mass activity)와 전기화학적 활성면적(ECSA), 전기이중층 용량(DLC), Pt 용해와 입자 성장 등을 분석하였다. 전압변화 2,000 사이클 후 PtCo/C 촉매는 Pt/C 촉매에 비해 0.9 V에서 촉매 무게당 전류밀도가 1.5배 이상 감소하였다. 이와 같은 결과는 PtCo/C 촉매의 카본지지체의 열화 속도가 Pt/C 촉매보다 높기 때문이었다. Pt/C 촉매는 PtCo/C 촉매보다 촉매층의 ECSA 감소가 1.5배 이상 높았지만 Pt/C 촉매의 카본 지지체 부식이 작아 I-V 성능 감소가 작았다. PtCo/C 촉매의 고전압 내구성 향상을 위해서는 카본 지지체 내구성 향상이 필수적임을 보였다.

• 대한기계학회논문집A
• /
• 제31권12호
• /
• pp.1157-1164
• /
• 2007

Ceramic honeycomb structures have performed successfully as catalyst supports for meeting hydrocarbon, carbon monoxide and nitrous emissions standards for gasoline-powered vehicles. Three-way catalyst converter has to withstand high temperature and thermal stress due to pressure fluctuations and vibrations. Thermal stress constitutes a major portion of the total stress which the ceramic catalyst support experiences in service. In this study, temperature distribution was measured at ceramic catalyst supports. Thermal durability was evaluated by power series dynamic fatigue damage model. Radial temperature gradient was higher than axial temperature gradient. Thermal stresses depended on direction of elastic modulus. Axial stresses are higher than tangential stresses. Tangential and axial stresses remained below thermal fatigue threshold in all engine operation ranges.

• 한국연소학회:학술대회논문집
• /
• 대한연소학회 2003년도 제27회 KOSCO SYMPOSIUM 논문집
• /
• pp.265-272
• /
• 2003

Some catalytic reactors for industrial/generation gas turbines were reviewed and investigated to understand the current status and future prospect for ultra low NOx catalytic gas turbine combustor. Catalytic reactor which was applied to 1${\sim}$10MW class gas turbine has achieved the ultra low emission corresponding to less than 3ppm NOx and 10ppm CO. But the durability and sizing flexibility of catalyst is needed to improve the catalyst performance for commercial gas turbine operation.

• Korean Chemical Engineering Research
• /
• 제62권1호
• /
• pp.7-12
• /
• 2024

고분자 전해질 연료전지(PEMFC) 내구성에 촉매 지지체 내구성이 미치는 영향이 크다. 촉매 지지체의 가속 내구 평가는 높은 전압(1.0~1.5 V)에서 진행되어 촉매층의 촉매와 이오노머 바인더도 같이 열화되어 지지체 내구성 평가에 방해가 된다. 내구성 평가대상인 지지체가 더 열화되는 조건을 찾고자 기존의 프로토콜 (DOE 프로토콜)을 개선하였다. 상대습도를 35% 낮추고 전압변화 횟수를 감소시킨 프로토콜 (MDOE)을 개발하였다. 1.0 ↔ 1.5 V 전압변화 사이클 반복 후에 촉매 비활성도 (MA)와 전기화학적 활성면적 (ECSA), 전기이중층 용량 (DLC), Pt 용해와 입자 성장 등을 분석하였다. 비활성도 감소 40% 도달하는데 MDOE 프로토콜은 500 사이클 밖에 안되어 DOE방법보다 전압변화 횟수를 감소시키면서 카본 지지체 열화를 DOE 프로토콜보다 50% 증가시킬 수 있었다.

• Korean Chemical Engineering Research
• /
• 제51권1호
• /
• pp.35-41
• /
• 2013

Co-P-B/FeCrAlloy 촉매의 $NaBH_4$ 가수분해 특성과 내구성에 대해 연구하였다. 5 wt% $NaBH_4$ 농도에서 활성화 에너지가 25.2 kJ/mol로 귀금속 촉매와 비슷했고, $NaBH_4$ 농도가 증가할수록 활성화 에너지가 증가하였다. 20 wt% 이상의 $NaBH_4$ 농도에서 겔 형성이 수소발생과 촉매 내구성에 많은 영향을 줬다. $NaBH_4$ 농도가 높을 때 반응온도가 높을수록 겔 형성이 안 되므로 촉매 손실률이 낮았다. 수소발생과 촉매 내구성을 모두 고려했을 때 담지체를 $1,000^{\circ}C$에서 열처리하고, 초음파 진동없이 촉매를 담지하고, 촉매 담지 후 소성한 촉매가 우수하였다. 25 wt% $NaBH_4$에서는 촉매를 3회 이상 재사용하기 위해서는 $60^{\circ}C$ 이상의 온도에서 반응시켜야 함을 보였다.

• 상하수도학회지
• /
• 제13권3호
• /
• pp.101-106
• /
• 1999

This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.