• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.4
• /
• pp.265-271
• /
• 2003

Ferroelectric lanthanum-substituted Bi$_4$Ti$_3$O$_{12}$(BLT) thin films were fabricated by spin-coating onto a Pt/Ti/SiO$_2$/Si substrate by metalorganic decomposition technique. The grain size in BLT thin films were prepared with controlled by various drying process. The effect of grain size on the crystallization and ferroelectric properties were investigated by x-ray diffraction and field emission scanning electron microscope. The dependence of crystallization and electrical properties are related to the grain size in BLT thin films with different drying temperature. The remanent polarization of BLT thin film increases with the increasing grain size. The value of 2P$_{r}$ and E$_{c}$ of BLT thin film dried at 45$0^{\circ}C$ were 25.9 $\mu$C/$\textrm{cm}^2$ and 85 kV/cm, respectively. The BLT thin film with larger grain size has better fatigue properties. The fatigue properties revealed that small grained film showed more degradation of switching charge than large grained films.lms.s.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.101-102
• /
• 2006

PZT thin films, which are the representative ferroelectric materials in ferroelectric random access memory (FRAM), have some serious problem such as the imprint, retention and fatigue which ferroelectric properties are degraded by repetitive polarization. BL T thin film capacitors were fabricated by plasma etching, however, the plasma etching of BLT thin film was known to be very difficult. In our previous study, the ferroelectric materials such as PZT and BLT were patterned by chemical mechanical polishing (CMP) using damascene process to top electrode/ferroelectric material/bottom electrode. It is also possible to pattern the BLT thin film capacitors by CMP, however, the CMP damage was not considered in the experiments. The properties of BLT thin films were changed by the change of polishing pressure although the removal rate was directly proportional to the polishing pressure in CMP process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.9
• /
• pp.764-769
• /
• 2002

The effect of excess Bi contents on the ferroelectric properties of B $i_{3.25}$ L $a_{0.75}$ $Ti_3$ $O_{12}$ (BLT) thin films has been investigated. Bismuth lanthanum titanate thin films with excess Bi contents were prepared onto Pt/Ti/ $SiO_2$/Si substrate by metalorganic decomposition (MOD) technique. The structure and morphology of the films were analyzed using X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. From the XRD analysis, BLT thin films show polycrystalline structure and the layered-perovskite phase was obtained over 10% excess of Bi contents. As a result of ferroelectric characteristics related to the Bi content of the BLT thin film, the remanent polarization and dielectric constant decreased with increasing over Bi content of 10% excess. The BLT film with Bi content of 10% excess was measured to have a dielectric constant of 326 and dielectric loss of 0.024. The BLT thin films showed little polarization fatigue test up to 3.5$\times$10$^{9}$ bipolar switching cycling.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.371-374
• /
• 2002

Bismuth lanthanum titanate thin films with excess Bi contents were prepared onto Pt/Ti/$SiO_2$/Si substrate by metalorganic decomposition (MOD) technique. The structure and morphology of the films were analyzed using X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. From the XRD analysis, BLT thin films show polycrystalline structure and the layered-perovskite phase was obtained over 10% excess of Bi contents. As a result of ferroelectric characteristics related to the Bi content of the BLT thin film, the remanent polarization and dielectric constant decreased with increasing over Bi content of 10 % excess. The BLT film with Bi content of 10% excess was measured to have a dielectric constant of n9 and dielectric loss of 1.85[%]. The BLT thin films showed little polarization fatigue test up to 3.5 x $10^{9}$ bipolar switching cycling.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.23-26
• /
• 2003

The BLT thin film and MgO buffer layer were fabricated using a metalorganic decomposition method and the DC sputtering technique. The MgO thin film was deposited as a buffer layer on $SiO_2/Si$ and BLT thin films were used as a ferroelectric layer. The electrical of the MFIS structure were investigated by varying the MgO layer thickness. TEM showsno interdiffusion and reaction that suppressed by using the MgO film as abuffer layer. The width of the memory window in the C-Y curves for the MFIS structure decreased with increasing thickness of the MgO layer Leakage current density decreased by about three orders of magnitude after using MgO buffer layer. The results show that the BLT and MgO-based MFIS structure is suitable for non-volatile memory FETs with large memory window.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.3
• /
• pp.130-132
• /
• 2013

$Bi_{3.25}La_{0.75}Ti_3O_{12}$(BLT) thin films were prepared on the Pt(150 nm)/Ti(50 nm)/$SiO_2$/Si substrate using the rf magnetron sputtering method. The BLT thin films were annealed at temperatures ranging from $600^{\circ}C$ to $750^{\circ}C$ using the rapid thermal annealing. The structure and surface morphology of the thin films were characterized by x-ray diffraction and field emission scanning electron microscopy. The hysteresis loop of the BLT thin films showed that the remanent polarization (2Pr) of the film annealed at $700^{\circ}C$ was 10.92 ${\mu}C/cm^2$. The fatigue characteristic of the BLT thin film annealed at $700^{\circ}C$ was shown change polarization up to $1.2{\times}10^9$ switching cycles. We confirmed the excellent remnant polarization (Pr) and fatigue properties compared with other fabrication methods and suggested a good method for BLT thin films fabrications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.486-491
• /
• 2002

We have fabricated $Bi_{3.25}La_{0.75}Ti_3O_12$ (BLT) thin films on the Pt/Ti/$SiO_2$/Si substrates using a metalorganic decomposition (MOD) method with annealing temperature from $550^{\circ}C$ to $750^{\circ}C$. The structural properties of BLT films examined by x-ray diffraction (XRD). From XRD analysis. BLT thin films show polycrystalline structure. The layered-perovskite phase was obtained by spin-on films at above $600^{\circ}C$ for 1h. Scanning electron microscopy (SEM) showed uniform surface composed of rodlike grains. The grain size of BLT films increased with increasing annealing temperature. The BLT film annealed at $650^{\circ}C$ was measured to have a dielectric constant of 279, dielectric loss of 1.85(%), remanent polarization of $25.66\mu C/\textrm{cm}^2$, and coercive field of 84.75 kV/cm. The BLT thin films showed little polarization fatigue test up to $3.5{\times}10^9$ bipolar cycling at 5 V and 100 kHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.305-309
• /
• 2002

We have successfully fabricated a Metal-Ferroelectric-Insulator-Semiconductor (MFIS) structure using Bi$\sub$4-x/La$\sub$x/Ti$_3$O$\sub$12/ (BLT) ferroelectric thin film and SiO$_2$/Nitride/SiO$_2$ (ONO) stacked buffer layers for single transistor type ferroelectric nonvolatile memory applications. BLT films were deposited on 15 nm-thick ONO buffer layer by sol-gel spin-coating. The dielectric constant and the leakage current density of prepared ONO film were measured to be 5.6 and 1.0 x 10$\^$-8/ A/$\textrm{cm}^2$ at 2MV/cm, respectively, It was interesting to note that the crystallographic orientations of BLT thin films were strongly effected by pre-bake temperatures. X-ray diffraction patterns showed that (117) crystallites were mainly detected in the BLT film if pre-baked below 400$^{\circ}C$. Whereas, for the films pre-baked above 500$^{\circ}C$, the crystallites with preferred c-axis orientation were mainly detected. From the C-V measurement of the MFIS capacitor with c-axis oriented BLT films, the memory window of 0.6 V was obtained at a voltage sweep of ${\pm}$8 V, which evidently reflects the ferroelectric memory effect of a BLT/ONO/Si structure.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.6
• /
• pp.258-261
• /
• 2011

A ferroelectric $(Bi,La)_4Ti_3O_{12}$ (BLT) thin film fabricated by the pulsed-DC sputtering method was evaluated on a cell structure to check its compatibility to high density ferroelectric random access memory (FeRAM) devices. The BLT composition in the sputtering target was $Bi_{4.8}La_{1.0}Ti_{3.0}O_{12}$. Firstly, a BLT film was deposited on a buried Pt/$IrO_x$/Ir bottom electrode stack with W-plug connected to the transistor in a lower place. Then, the film was finally crystallized at $700^{\circ}C$ for 30 seconds in oxygen ambient. The annealed BLT layer was found to have randomly oriented and small ellipsoidal-shaped grains (long direction: ~100 nm, short direction: ~20 nm). The small and uniform-sized grains with random orientations were considered to be suitable for high density FeRAM devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.186-189
• /
• 2003

The MFIS capacitors were fabricated using a metalorganic decomposition method. Thin layers of $ZrO_2$ and $CeO_2$ were deposited as a buffer layer on Si substrate and BLT thin films were used as a ferroelectric layer. The electrical and structural properties of the MFIS structure were investigated. X -ray diffraction was used to determine the phase of the BLT thin films and the quality of the $ZrO_2$ and $CeO_2$ layer. AES show no interdiffusion and the formation of amorphous $SiO_2$ layer is suppressed by using the $ZrO_2$ and $CeO_2$ film as buffer layer between the BLT film and Si substrate. The width of the memory window in the C-V curves for the $BLT/ZrO_2/Si$ and $BLT/CeO_2/Si$ structure is 2.94 V and 1.3V, respectively. The experimental results show that the BLT-based MFIS structure is suitable for non-volatile memory FETs with large memory window.