• 한국전기전자재료학회논문지
• /
• 제21권6호
• /
• pp.575-579
• /
• 2008

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ of by RF magnetron sputtering. Target was ZnO ceramic mixed with 2 wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-3}$, mobilities from 0.194 to $2.3\;cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4\;{\Omega}cm$. p-type sample has density of $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. XPS spectra show that Ols has O-O and Zn-O structures and Al2p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.408-409
• /
• 2007

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ by RF magnetron sputtering. Target was ZnO ceramic mixed with 2wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}\;to\;4.04{\times}10^{18}cm^{-3}$, mobilities from 0.194 to $2.3cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4{\Omega}cm$. P-type sample has density of $5.40cm^{-3}$ which is smaller than theoretically calculated value of $5.67cm^{-3}$. XPS spectra show that O1s has O-O and Zn-O structures and A12p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• 센서학회지
• /
• 제21권4호
• /
• pp.263-269
• /
• 2012

Al doped ZnO(AZO) thin films were deposited at different substrate temperatures by a continuous composition spread(CCS) method. Various compositions of Al doped ZnO thin films deposited at substrate temperatures between 0 and $250^{\circ}C$ were explored to find excellent electrical and optical properties. The AZO thin film deposited at $100^{\circ}C$ had the lowest resistivity, $9{\times}10^{-4}{\Omega}$ cm and its average transmittance at the 400 to 700 nm wavelength region was 92 %. Optimized composition of the AZO thin film which had the lowest resistivity and high transmittance was 3.13 wt% Al doped ZnO.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.27-29
• /
• 2005

ZnO and phosphorus doped ZnO thin films (ZnO:P) are deposited by pulsed laser deposition grown on (001) $Al_{2}O_{3}$. ZnO/ZnO:P/ZnO/$Al_{2}O_{3}$ (multi-layer) structure was used for phosphorus doped ZnO fabrication. This multi-layer structure thin film was annealed at $400^{\circ}C$ for 40 min. The electron concentration of that was changed from $10^{19}$ to $10^{16}/cm^{-3}$ after annealing. ZnO thin films with encapsulated structure showed the enhanced structural and optical properties than phosphorus doped ZnO without encapsulated layer. In this study, encapsulated ZnO structure was suggested to enhance electrical, structural and optical properties of phosphorus doped ZnO thin film and it was identified that encapsulated structure could be used to fabricate high quality phosphorus doped ZnO thin film.

• 한국전기전자재료학회논문지
• /
• 제21권9호
• /
• pp.789-794
• /
• 2008

Zinc oxide (ZnO) has been widely studied for its practical applications such as transparent conduction electrodes for flat panel displays and solar cells. Especially, ZnO films show good chemical stability against hydrogen plasma, absence of toxicity, abundance in nature, and then suitable for photovoltaic applications. However, the fabrication process of thin film solar cells require a high substrate temperature and/or post heat treatment. Therefore, the layers have to withstand high temperatures, requiring an excellent stability without degrading their electronic and optical properties. In this paper, we investigated the stability of zinc oxide (ZnO) films doped with aluminum and hydrogen. Doped ZnO films were prepared by r.f. magnetron sputter and followed by heat treatment at different temperatures and for various times.

• 한국결정성장학회지
• /
• 제18권1호
• /
• pp.50-55
• /
• 2008

졸-겔 공정을 이용하여 유리기판 위에 Al-doped ZnO(AZO) 박막을 제조하였고, AZO 박막의 특성에 대하여 Al 전구체 종류 및 post-annealing 온도가 미치는 영향에 대하여 고찰하였다. AZO 박막 제조용 졸은 zinc acetate, EtOH, MEA 등을 사용하여 제조하였고, Al doping 을 위한 전구체로는 aluminum nitrate 와 aluminum chloride 를 사용하였다. Sol 내의 Zn 농도는 0.5 mol/l 로 하였고, Al doping 양은 Zn 대비 1 at%로 고정하였다. 유리기판 위에 졸을 spin-coating 한 후 $550^{\circ}C$에서 2 시간 동안 열처리한 후, $N_2$와 $H_2$의 비가 9 : 1인 환원 분위기 내에서 $300^{\circ}C,\;400^{\circ}C,\;500^{\circ}C$인 온도에서 2시간 동안 post-annealing을 진행하였다. 제조된 AZO 박막의 구조적, 전기적, 광학적 특성은 XRD, FE-SEM, AFM, Hall effect measurement system 및 UV-Visible spectroscopy를 이용하여 분석하였다. Al 전구체로서 aluminum nitrate 를 사용한 경우가 aluminum chloride 를 사용하여 제조한 AZO 박막보다 우수한 광학적, 전기적 특성을 나타내었으며, post-annealing 온도가 증가함에 따라 비저항과 투과율은 감소하였다. $500^{\circ}C$에서 post-annealing한 AZO 박막의 전기비저항 값은 $2{\times}10^{-3}{\Omega}{\cdot}cm$이었고, 투과율은 $300^{\circ}C$에서 91%로 가장 높게 나타났다.

• 한국전기전자재료학회논문지
• /
• 제24권6호
• /
• pp.491-496
• /
• 2011

Al-doped ZnO film on glass substrate is deposited by ALD in low temperature, using 4-step process (DEZ-$H_2O$-TMA-$H_2O$). To find out the optimal film condition for TCO material, we fabricate Al-doped ZnO films by increasing Al doping concentration at $100^{\circ}C$, so that the Al-doped film of 5 at% shows the lowest resistivity ($1.057{\times}10^{-2}{\Omega}{\cdot}cm$) and the largest grain size (38.047 nm). Afterwards, the electrical and physical characteristics in Al-doped films of 5 at% are also compared in accordance with increasing deposition temperature. All the films show the optical transmittance over 80% and the film deposited at $250^{\circ}C$ demonstrates the superior resistivity ($1.237{\times}10^{-4}{\Omega}{\cdot}cm$).

• 한국세라믹학회지
• /
• 제43권9호
• /
• pp.532-536
• /
• 2006

The annealing temperature effect of transparent conducting oxide film grown on glass substrate for solar cell application was studied in this paper. Using pulsed DC magnetron sputtering with 1 at% Al-doped ZnO target, TCO films were deposited on coming 7059 glass at room temperature. Al:ZnO thin films were annealed at 200, 400, Al $600^{\circ}C$ for 10 min and annealing resulted in lower biaxial compressive stress of about 1GPa and increased average crystallite size in all films. The as-grown film shows the resistivity of $1{\times}10^{-2}{\Omega}{\cdot}cm$ and transmittance under 80%, whereas the electrical and optical properties of film annealed at $400^{\circ}C$ are enhanced up to $5{\times}10^{-4}{\Omega}{\cdot}cm$ and 85%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.82-83
• /
• 2008

AI doped ZnO (AZO) films, and intentionally Zn added AZO (ZAZO) films were prepared on Corning glass by rf magnetron sputtering, and the electrical, optical, and structural properties of the as-deposited films together with the air annealed films were investigated. The resistivity of the AZO films increased with increasing substrate temperature and having minimum resistivity at $150^{\circ}C$. At the high temperature, the ZAZO films showed improved electrical properties better than the AZO films due.to increase in both the carrier concentration and.the Hall mobility. Upon air annealing at $500^{\circ}C$, the resistivity of both AZO and ZAZO films increased substantially, but the relative amount of degradation was smaller for films deposited at $450^{\circ}C$ than the films deposited at $150^{\circ}C$.

• 한국반도체및디스플레이장비학회:학술대회논문집
• /
• 한국반도체및디스플레이장비학회 2006년도 춘계학술대회
• /
• pp.164-167
• /
• 2006

In this paper, we prepared Al doped ZnO thin films by using facing targets sputtering method. Al doped ZnO thin film was deposited with different working pressure on flexible substrate. We prepared Al doped ZnO thin film at room temperature, because the flexible substrate has weak thermal resistance. From the results, we could obtain thin film with a resistivity of $8.4{\times}10^{-4}{\Omega}cm$, an average transmittance of over 80% and a film thickness of 200nm.