• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.2
• /
• pp.142-153
• /
• 2004

Statement of problem: Increasing demand of esthetic restorations made lots of kinds of ceramic materials. Among them, zirconia has been being focused by many dentists. But, mechanical properties of zirconia were still unclear. Purpose : The purposes of this study were to analyze the flexural strength of various zirconia ceramics which had been currently used for clinic i.e., In-Ceram Zirconia(Vita Zahnfabrik, Bad $S\"{a}ckingen$, Germany), Celay Zirconia(Vita Zahnfabrik, Bad $S\"{a}ckingen$, Germany) and CAD/CAM Zirconia (Adens Zi-Ceram. Seoul , Korea). Material and methods: The four point bending test(ASTM Cl161) was used to measure the flexural strength of a specimen before and after circular heat treatment and fatigue loading. Results : 1. The average value of flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia in dry condition were 806.5 MPa, 669.9 MPa, 605.6 MPa, respectively. There was a statistically significant difference in strength among the types (P<0.05). 2. After thermocycling, the average flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia were 791.2 MPa, 604.2 MPa, 605.4 MPa, respectively. CAD/CAM Zirconia showed statistically significant higher strength(P<0.05). The others showed no significant difference after thermocycling(P>0.05). 3. After fatigue loading in wet condition. the average flexural strengths of CAD/CAM Zirconia, Celay Zirconia, In-Ceram Zirconia were 806.0 MPa, 674.9 MPa, 601.7 MPa, respectively. There was a significant difference in strength among the types(P<0.05). 4. There was no statistically significant difference in strength of the specimens according to experimental methods except for before and after thermocycling in Celay Zirconia(P>0.05). Conclusion: Besides high esthetic quality, zirconia had sufficiently high mechanical strength.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.6
• /
• pp.701-713
• /
• 2000

In this study, the 4-point bending test been performed in order to estimate effect of grinding on fatigue characteristics quantitatively for as-welded specimen, grinding specimen & TIG-dressing specimen for non load-carrying fillet welded joints subjected to pure bending. As a result of fatigue tests, fatigue strength at $2{\times}106$cycles of grinding specimen and TIG-dressing specimen has been increased compared with as-welded specimen and satisfied the grade of fatigue strength prescribed in specifications of domestics and AASHTO & JSSC. As a result of beachmark test, fatigue cracks on all specimens have occurred at several points where stress

• Textile Coloration and Finishing
• /
• v.28 no.4
• /
• pp.246-252
• /
• 2016

In comparison to metal alloys, braided composite features a high impact resistance and crash energy absorption potential, and also it still remained competitive stiffness and strength properties. Braiding angle is one of the most important parameters which affect the mechanical behaviors of braided composite. This paper presents transverse low velocity impact failure behavior analysis on the carbon 3D triaxial braided composite tube with the braiding angle of $20^{\circ}$, $50^{\circ}$ and $80^{\circ}$. The flexural behaviour of 3D triaxial braided composite tube under bending loads was studied by conducting quasistatic three point bending test. Also, the low velocity impact responses of the braided composite tubes were also tested to obtain load-displacement curves and energy absorption. Consequently, the increase of the braided angle, the peak load also increases owing to the bigger bending stiffness.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.11a
• /
• pp.165-168
• /
• 2000

로켓엔진에서 노즐은 추력을 발생하고, 단위 면적당 열 전달이 최대가 되는 곳으로 구조적으로 가장 취약한 부분이다. 이런 가혹한 조건에서 사용되어질 수 있는 4D 탄소/탄소 복합재를 제조하였으며. 초밀도화시, 탄화압력은 100bar 와 900bar 에서 각각 시행되었다. 만들어진 시편의 밀도는 1.5~l.9g/$cm^3$ 이었다. 실제 로켓을 모사할 수 있는 지상연소시험을 통해 밀도에 따른 삭마율을 계산한 결과, 밀도가 높을수록 삭마율은 감소하였다. 또한 3-point bending test를 통해 굽힘강도(flexural strength)를 측정하였으며, 굽힘강도를 개선시켜주었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.9
• /
• pp.5844-5853
• /
• 2014

This paper presents the results of experimental investigations on the shear failure behaviors of reinforced concrete beams using ductile fiber reinforced cementitious composite (DFRCC). Total 10 RC beams of $150{\times}300{\times}1,000mm$ size were tested by 4-point bending under the displacement control. The main parameters of the experiment are surface treatment by grinding and preloading to the cracking point in the repair process. The load-displacement curves, diagonal tension cracking load, flexural cracking load, and shear strength were obtained. The test results showed that the DFRCC can be used effectively for restoring the shear strength approximately 99% to the original value under the condition that the appropriate thickness and surface treatment like grinding are assured. For further research, the specimens taken from real deteriorated structures will need to be tested after being repaired with DFRCC.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1997.06a
• /
• pp.13-17
• /
• 1997

The densification of $Al_2$O$_3$/15v/o ZrO$_2$ (Zirconia Toughened Alumina: ZTA) to the 99% of theoretical density was attempted by controlling the processing parameters affecting the each processing step i.e., milling, spray-drying, forming and pressureless sintering. The ZTA processed under the identical conditions showed a large variation in the green and sintered densities, and the mechanical properties. The deviation of 4-point bending strength was more than 100MPa for the ZTA with ~99% of theoretical density. Moreover, the relative green and sintered densities were deviated greatly from the average value. This low reproducibility could be caused by the variation of spray-dried granule properties. Thus, the effect of yield strength and morphology of spray-dried ZTA granule on the green and sintered densities and the mechanical properties needs to be studied in detail. The objective of this work is to fine out the optimum condition of compaction pressure and compaction method depending on the properties of spray-dried granules.

• Computers and Concrete
• /
• v.19 no.6
• /
• pp.631-639
• /
• 2017

This study experimentally investigated the flexural capacity of a concrete beam reinforced with a newly developed GFRP bar that overcomes the lower modulus of elasticity and bond strength compared to a steel bar. The GFRP bar was fabricated by thermosetting a braided pultrusion process to form the outer fiber ribs. The mechanical properties of the modulus of elasticity and bond strength were enhanced compared with those of commercial GFRP bars. In the four-point bending test results, all specimens failed according to the intended failure mode due to flexural design in compliance with ACI 440.1R-15. The effects of the reinforcement ratio and concrete compressive strength were investigated. Equations from the code were used to predict the deflection, and they overestimated the deflection compared with the experimental results. A modified model using two coefficients was developed to provide much better predictive ability, even when the effective moment of inertia was less than the theoretical $I_{cr}$. The deformability of the test beams satisfied the specified value of 4.0 in compliance with CSA S6-10. A modified effective moment of inertia with two correction factors was proposed and it could provide much better predictability in prediction even at the effective moment of inertia less than that of theoretical cracked moment of inertia.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.172-175
• /
• 2003

Mechanically-alloyed NiAl powder was sintered by Spark-Plasma Sintering (SPS) process. Densification and behavior mechanical property were determined from the experimental results and analysis ,such as changes in linear shrinkage, shrinkage rate, microstructure, and phase during sintering process, Victors hardness, and transver.ie-rupture-strength (TRS). Above 97% relative density was obtained after sintering at 115$0^{\circ}C$ for 5 min. Crystallite size determined by the Scherrer method was approximately 50 nm. From the X-ray diffraction analysis it was confirmed that the sintered bodies were composed mainly of NiAl phase together with Ni$_3$Al phase. Measured Vickers hardness and TRS value were 555$\pm$10 $H_v$ and 1393$\pm$75 MPa , respectively.

• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.373-378
• /
• 2011

The composite added with surface-coated chopped carbon fiber showed the microstructure of a 3 dimensional discretional arrangements. The fiber reinforced reaction bonded silicon carbide composite, containing the 50 vol% carbon fiber, showed the porosity of < 1 vol%, 3-point bending strength value of 250MPa and fracture toughness of 4.5 $MPa{\cdot}m^{1/2}$. As the content of carbon fiber was increased from 0 vol% to 50 vol% in the composite, fracture strength was decreased due to the increase of carbon fiber, which has a less strength than SiC and molten Si. On the other hand, the fracture toughness was increased with increasing the amount of carbon fiber. According to the polished microstructure, carbon fiber was shown to have a random 3 dimensional arrangement. Moreover, the fiber pull-out phenomenon was observed with the fractured surface, which can explain the increased fracture toughness of the composite containing high content of carbon fiber.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.5 s.48
• /
• pp.617-628
• /
• 2000

In this study, the 4-point bending test has been performed in order to estimate the effect of TIG-dressing on fatigue strength and fatigue characteristics quantitatively for non load-carrying fillet welded joints subjected to pure bending. As a result of fatigue tests, fatigue strength of as-welded specimens has been satisfied the grade of fatigue strength prescribed in specifications of domestics and AASHTO & JSSC, and fatigue strength at $2{\times}106cycles$ of TIG-dressing specimens has been increased compared with as-welded specimens. As the result of beachmark tests, fatigue cracks have been occurred at several points, where the radius of curvature and flank angle in the weld bead toes are low, and grown as semi-elliptical cracks, then approached to fracture. As a result of finite element analysis, stress concentration factor in weld bead toes has been closely related to the flank angel and radius of curvature, and between these, the radius of curvature has more largely affected in stress concentration factor than flank angle. As a result of fracture mechanics approaches, the crack correction factor of test specimens has been largely affected on stress gradient correction factor in case a/t is below 0.4. From the relations between stress intensity factor range estimated from FEM analysis and fatigue crack growth rate, fatigue life has been correctly calculated.