• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.675-682
• /
• 2011

Recently, in retrofit of RC structures using FRP (Fiber Reinforced Polymer), researches about Near-Surface-Mounted Rertofit (NSMR) method have been widely performed. In NSMR, FRP bar is normally inserted in the slit formed in the cover concrete and then bonded by using epoxy mortar. In this paper, the bond characteristic of NSMR using FRP plate instead of bar was studied experimentally. Fracture behavior is observed from bond test using the parameters of embedment length, shear key, and FRP plate layer. In addition, an equation to predict the splitting strength of NSMR using FRP is proposed using the test result. The results showed that when the longer embedment length and more layers of FRP are used, the higher bond strength is achieved. There was a good co-relationship between the test and calculated results using the proposed equation.

• Magazine of the Korea Concrete Institute
• /
• v.2 no.3
• /
• pp.89-95
• /
• 1990

Possibility for the evaluation of fracture properties of mortar and concrete by splitting tensile test was stud¬ied. Splitting tensile tests were conducted to obtain the fracture loads for several sizes of cylindrical specimens of mortar and concrete with initial notch. From the results, fracture energy and fracture toughness by SEL were obtained and compared with the values by Rooke and Cartwright, and r.E.Moo The values by SEL method converged effectively. SEL method was shown to be a good method to obtain fracture properties of mortar and concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.1
• /
• pp.151-157
• /
• 2008

It is difficult for existing beams to ensure the sufficient embedding depth due to constructional cause. Owing to these problems, currently FRP-Rod embedding repair method run parallel with a section increasing method in many case. In this study, anchor pin was adopted to solving the problems of the sliding of FRP-Rod and the unified behaviors of the repaired beam without increasing the section. In the experiments, split failure of covering concrete and slippage of the FRP-Rod were not occurred. it was confirmed that FRP-Rod shown the integrate behaviors with RC beam till the repaired beams destroyed.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.861-867
• /
• 2015

The Compact Tension (CT) type test was performed in order to evaluate the fracture toughness performance of glass fiber-reinforced laminated timber. Glass fiber textile and sheet Glass fiber reinforced plastic were used as reinforcement. The reinforced laminated timber was formed by inserting and laminating the reinforcement between laminated woods. Compact tension samples are produced under ASTM D5045. The sample length was determined by taking account of the end distance of 7D, and bolt holes (12 mm, 16 mm, 20 mm) had been made at the end of artificial notches in advance. The fracture toughness load of sheet fiberglass reinforced plastic reinforced laminated timber was increased 33 % in comparison to unreinforced laminated timber while the glass fiber textile reinforced laminated timber was increased 152 %. According to Double Cantilever Beam theory, the stress intensity factor was 1.08~1.38 for sheet glass fiber reinforced plastic reinforced laminated timber and 1.38~1.86 for glass fiber textile reinforced laminated timber, respectively. That was because, for the glass fiber textile reinforced laminated timber, the fiber array direction of glass fiber and laminated wood orthogonal to each other suppressed the split propagation in the wood.

• Journal of the Korean Geotechnical Society
• /
• v.19 no.2
• /
• pp.171-178
• /
• 2003

Wing and secondary cracks are unique types of cracks observed in rock masses subjected to uniaxial and biaxial compressive loading conditions. In this study, morphological features of wing and secondary cracks developed in gypsum specimens are investigated in the macro and micro scales. Along the path of wing crack, microtensile cracks are observed. Microtensile cracks coalesce with pores and show branch phenomenon. From the onset of the wing crack, multiple initiations of microtensile cracks are observed. Microtensile cracks show tortuous propagation paths and relatively constant aperture of the cracks during the propagation. It is shown that microtensile cracks propagate by splitting failure. At the micro scale, microfsults are observed in the path of the secondary cracks. Along the path of the secondary cracks, separation of grains and conglomerate grains, oblique microfaults, and irregular aperture of microfault are observed. These features show that the secondary cracks are produced in shear mode. The measured sizes of fracture process zone across the propagation direction near the tip of wing and secondary cracks range from 10$\mu{m}$ to 20$\mu{m}$ far wing cracks and from 100$\mu{m}$ to 200$\mu{m}$ for secondary cracks, respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.315-322
• /
• 2016

Block-glued glulam is a structural material that can be used as a construction member of a large-section wooden building, which is produced by edgewise bonding of two or more glulam beam elements. The edgewise bonding performance of the block-glued glulam was examined through delamination test and block shear strength test. According to the test results, the block-glued glulam that was manufactured with 1.5 MPa of compressive pressure after applying $500g/m^2$ of Resorcinol adhesive showed the best edgewise bonding performance. The block-glued glulam produced in a good edgewise bonding condition was compared with a control glulam with the same section modulus for bending strength performance. The modulus of elasticity (MOE) in bending was similar to that of the control glulam. The modulus of rupture (MOR) of the block-glued glulam was higher by 27% than that of the control glulam. No interfacial failure or cohesive failure were observed in the edgewise bonding layer.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.3
• /
• pp.1-8
• /
• 2008

The lateral strength test of bending type was done to investigate the lateral capacity of the double bolt connection of domestic larix glulam according to bolt spacing. In the shear specimen, which is bolted connection in the inserted plate type, the hole of bolt was made, changing the diameter of bolt (12 mm and 16 mm), the number of bolt (single bolt : control and double bolt), the direction of bolt row (in parallel to grain : Type-A and in perpendicular to grain : Type-B) and the bolt spacing (Type-A : 4 d and 7 d and Type-B : 3 d and 5 d). Lateral capacity and failure mode of bolt connection were compared according to conditions. In prototype design (KBCS, 2000), the reduction factor of the allowable shear resistance that the bolt spacing is reduced was calculated. The results were as follows. 1) Bearing stress per bolt in the single and double bolt connection of Type-A was directly proportional to bolt diameter and bolt spacing. Bearing stress of Type-B decreased as bolt diameter was increased, and decreased by 2~10% when bolt diameter was increased. 2) In the single bolt connection and the double bolt connection of Type-A, the splitted failure was formed in the edge direction. When the bolt spacing was 3 d in Type-B, bolt was yielded more in the part of tension than in the part of compression, and the splitted failure started at the bolt in the part of tension. In the 5 d spacing specimen, the bolt in the part of tension was yielded similarly to bolt in the part of compression, and the splitted failure started in the part of compression. 3) In the prototype design, the reduction factor was calculated by non-dimensionizing the yielding load in the standard of bolt spacing (Type A : 7 d and Type B : 5 d). In 12 mm bolt connection, the reduction factor of bolt spacing 4 d (type-A) and single bolt connection was 0.87 and 0.55, respectively, and the reduction factor of bolt spacing 3 d (Type-B) and single bolt connection was 0.91 and 0.55, respectively. In 16 mm bolt connection, the reduction factor of bolt spacing 4 d (type-A) and single bolt connection was 0.96 and 0.76, respectively, and the reduction factor of bolt spacing 3 d (Type-B) and single bolt connection was 0.91 and 0.77, respectively.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.37-43
• /
• 2013

Recently, experimental and analytical researches have been performed in order to find interface failure between FRP plate and concrete in near surface-mounted (NSM) retrofit using FRP plate. As a result, it was found that the bond strength between concrete and NSM FRP plate had a close relationship with shape of FRP, concrete compressive strength and bond length. However, research need is increasing about another factors such as suitable space of FRP plate and group effect. In this study, therefore, a bond test was performed with aforementioned factors and compared with a previous equation to verify its suitability for predicting bond strength of NSM FRP plate. From the test, it was found that the bond strength increased according to the increase of space of NSM FRP plates even if its bond length was same. The splitting failure of concrete governed when space of FRPs was too narrow and it changed to FRP's tensile failure with increase of the space. From the evaluation of test specimens using previous equation, it was found that the bond strength could be predicted properly with consideration of group effect.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.868-875
• /
• 2015

In order to replace existing slit type steel plate on the wooden structure joint, the FRP-reinforced laminated plates were produced. Four types of FRP-reinforced laminated plates were produced according to the type of reinforcement and adhesive, and before applying to the joint, the adhesion performance test according to KSF 3021 and KSF 2160 and the Compact Tension (CT) type fracture toughness test specified in ASTM D5045-99 were carried out. As a result of adhesion performance test, all GFRP textile, GFRP sheet, and GFRP Textile-Sheet type FRP-reinforced laminated plates satisfied the requirement of soaking delamination percentage with smaller than 5% based on KS standard. However, aramid type specimen satisfied the standard as the soaking delamination percentage of 4.8% but it did not satisfied the standard as the water proof soaking delamination percentage of 70%. As a result of fracture toughness test, the volume ratio of reinforcement to timber became 23% so that the strength of FRP-reinforced laminated plates increased by two to four times in comparison to the control specimen. It was confirmed that the GFRP Textile-Sheet type specimen was most resistant to the fracture most since the ratio of stress intensity factor compared with that of the control increased to 61% owing to the parallel arrangement of glass fiber to the load. As a result of tensile shear strength test using FRP-reinforced laminated plates and nonmetal dowels, it is about 12% lower than metal connectors.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.4
• /
• pp.93-101
• /
• 2008

Bearing strength test was investigated to determine the bearing properties of domestic larix glulam according to the load direction (in parallel to grain and in perpendicular to grain), the fastener (bolt and drift-pin), and the direction of laminae. The specimen was 5 ply glulam. The diameters of fastener are 12, 16 and 20 mm. The results were as follows. 1) In according to the diameter of bolt and drift-pin, the average of maximum bearing strength in parallel to grain loading was similar to that in perpendicular to grain loading. The average of maximum bearing strength was 1.50~2.31 times higher in parallel to grain loading than in perpendicular to grain loading. The average of maximum bearing strength in parallel to grain loading was lowered by 20% with increasing the diameter from 16 mm to 20 mm, but that in perpendicular to grain loading didn't show a clear tendency. 2) The average of bearing stiffness in parallel to grain loading was the highest at 16 mm in diameter. The average of bearing stiffness is similar to the shearing stiffness in drift-pin connection with increasing diameter. 3) In parallel to grain loading, the failure mode of specimens was the splitting along the grain in decreasing diameter. The failure mode in perpendicular to grain loading was the splitting along the grain. In this case, split occured more in specimens using bolt than in those using drift-pin. 4) The 5% offset yield strength in parallel to grain loading was similar to the predicted bearing strength of KBCS, NDS. In perpendicular to grain loading, the NDS's equation can be applied to predict the bearing strength.