• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.244-249
• /
• 2008

It happened a failure on special bolt which supported main landing gear actuator up-lock rod of 00 aircraft. Fracture was occurred at end of center drilled hole and thread machined on bolt. Metallographic, fractographic, and other characteristics of embrittlement analysis and experiments carried out on the failed bolt to find out the reason. Bolt surface was cadmium electroplated(EP) to give lubrication and provide excellent corrosion resistance. Resultly, Bolt was failed due to cadmium embrittlement occurred during baking treatment as well as center drilled hole. for the failure that are relevant to failure analysis and prevention. For their successful functional application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and is complete with no center drilled hole

• Journal of the Korea Institute of Military Science and Technology
• /
• v.13 no.5
• /
• pp.769-774
• /
• 2010

It happened fractures on special bolt which supported main landing gear actuator up-lock rod of aircraft. Cracks were initiated mainly from the center hole and the external thread of the special bolt. To find out failure root causes, metallographic, fractographic analyses as well as test work were carried out. From the fractographic study by SEM work, fracture occurred by a brittle intergranular type failure. The fracture could be occurred primarily by solid-metal-induced embrittlement due to cadmium embrittler penetrated into the flaw existed after machining work for center hole and thread on the bolt during baking treatment processing to eliminate hydrogen. For its successful application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and make no more drilled center hole on the bolt to prevent same failure.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.19 no.4
• /
• pp.611-634
• /
• 2017

In rapid urbanization, demand for utility tunnel increases more, and tunnel boring machine (TBM) has been used widely. Prediction of TBM penetration rate is important for proper estimation of construction period and cost. Although there are several methods, such as NTNU model and CSM model that require many input parameters, fundamental understanding on correlations between rock properties and TBM penetration rate is critical. In this study, we explored the brittleness indices of hard rocks according to various definitions, and the correlations between the brittleness indices and the TBM penentration rates.

• Tunnel and Underground Space
• /
• v.33 no.1
• /
• pp.29-41
• /
• 2023

The brittleness of rocks plays an important role in determining the fragmentation and failure behavior of rock. However, there is still no standard method to evaluate the brittleness of rock, and previous studies have suggested the several definitions for estimation of brittleness of rock. Even in the process of mechanical rock excavation and drilling, the brittleness of rock is considered as an important property for evaluating the excavation efficiency of mechanical excavators or boreability of rock. The previous studies have been carried out to investigate the correlation between different brittleness of rock and cutting efficiency and boreability of rock. This study introduced a method for calculating the brittleness of rock from punch penetration test, and analyzed the correlation between the brittleness of rock calculated by the uniaxial compressive and Brazilian tensile strengths and that from punch penetration test. From the results of correlation analysis, the relationship between various brittleness was confirmed, and it was found that PSI and BI₃ showed a good correlation with the strength-based brittleness index. In addition, the results indicated that B₃ and B₄ are suitable to represent the brittleness of rock in the field of mechanical rock excavation.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.18 no.5
• /
• pp.469-485
• /
• 2016

The failure of rock mass around deep tunnel, different from shallow tunnel largely affected by discontinuities, is dominated by magnitudes and directions of stresses, and the failures dominated by stresses can be divided into ductile and brittle features according to the conditions of stresses and the characteristics of rock mass. It is important to know the range and the depth of the V-shaped notch type failure resulted from the brittle failure, such as spalling, slabbing and rock burst, because they are the main factors for the design of excavation and support of deep tunnels. The main features of brittle failure are that it consists of cohesion loss and friction mobilization according to the stress condition, and is progressive. In this paper, a three-dimensional numerical model has been developed in order to simulate the brittle behavior of rock mass around deep tunnel by introducing the bi-linear failure envelope cut off, elastic-elastoplastic coupling and gradual spread of elastoplastic regions. By performing a series of numerical analyses, it is shown that the depths of failure estimated by this model coincide with an empirical relation from a case study.

• Journal of the Korean Institute of Gas
• /
• v.19 no.1
• /
• pp.57-63
• /
• 2015

The hydrogen was charged TRIP steel by electrochemical method under 0.5M $H_2SO_4$ electrolyte and 0.5M NaOH electrolyte with hydrogen charging conditions respectively. The degree of hydrogen embrittlement of TRIP steel was evaluated by using micro Vickers hardness tests. These results showed that the degree of hydrogen embrittlement in acidic electrolyte with hydrogen penetration and hydrogen diffusion through the depth of specimen was more sensitive than its alkaine electrolyte between two type electrolytes. However, it was investigated that micro Vickers hardnesses of surface in acidic electrolyte under two electrolyte were higher than those of alkaine electrolyte. It was thought that in case of hydrogen embrittlement in acid-ice electrolyte, hydrogen charging time was more effective than current density, in case of alkaine electrolyte, hydrogen current density was more effective than charaging time.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.3
• /
• pp.284-291
• /
• 2002

An attempt was made to evaluate the degree of aging degradation in thermally aged 2.25Cr-1Mo steel by electrical resistivity measurement. Artificial aging was performed to simulate the microstructural degradation in 2.25Cr-1Mo steel arising from long time exposure at $540^{\circ}C$. Microstructural parameter (amount of solid solution element), mechanical property (ductile-brittle transition temperature) and electrical resistivity were measured to investigate the mutual relationship among these parameters. Depletion of solid solution element(Mo and Cr) in matrix was detected after aging. The ductile-brittle transition temperature(DBTT) increased rapidly in the initial stage of aging and then saturated afterward. On the other hand, the electrical resistivity decreased rapidly in the beginning and then saturated in the later stage of aging.

• Journal of Hydrogen and New Energy
• /
• v.35 no.2
• /
• pp.216-229
• /
• 2024

Pipeline steels for hydrogen transmission may cause hydrogen embrittlement due to absorption and diffusion of hydrogen through metals. Hydrogen pipes exhibited similar mechanical properties to atmospheric conditions in terms of tensile and yield strength in a hydrogen atmosphere. This paper aims to provide relevant information regarding hydrogen embrittlement in hydrogen transmission pipeline.

• Journal of the Korean Institute of Gas
• /
• v.19 no.1
• /
• pp.64-70
• /
• 2015

In order to evaluate the degree of hydrogen embrittlement of TRIP steels charged with hydrogen according to varying the current density and the charging time under acid and alkaline electrolyte conditions were tested by small punch test. The results of SP test showed that the degree of hydrogen embrittlement at acid electrolyte condition was more effective factor compared to that of alkaline electrolyte condition. Therefore, all of the charging time and the charging current density were at the condition of acid electrolyte appeared as the main factor of the degree of hydrogen embrittlement in the condition of acid electrolyte. But, it was considered that the charging time compared to the charging current density at the condition of alkaline electrolyte was more effective factor to raise the degree of hydrogen embrittlement.

• Korean Journal of Materials Research
• /
• v.6 no.3
• /
• pp.253-263
• /
• 1996

고온.고압하에서 장시간 사용되는 고온부재용 구조물은 경년열화현상을 나타낸다 그러므로 구조물의 안정성 측면에서 재질열화의 정도를 정량적으로 평가하는 것이 중요하다. 그러나 실기 구조물에서 채취할 시험편의 크기와 수는 제한이 되기 때문에 새로운 비파괴적인 평가법이 요구되고 있다. 따라서 본 연구에서는 화력발전설비에 이용되는 탄소강과 페라이트강에 대한 열화도의 평가를 위해 입계부식법의 적용 가능성을 조사한다. 시험결과, 재질열화의 정도는 사용시간보다 사용온도에 더 큰 영향을 받았으며, Larson-Miller인자와 열화도([$\Delta$DBTT]SP)사이의 관계는 선형적이었으나, 강종에 따라 다른 기울기를 보였다. 반면, 연성-취성천이온도 ([$\Delta$DBTT]SP)와 격자절단비(Ni/No)와 관계는 강종에 무관하게 선형적인 비례관계를 나타내었다. 또한, [$\Delta$DBTT]SP와 Ni/No 의 관계로부터 입계부식법은 페라이트계 강뿐만아니라 탄소강에 대해서도 유용한 재질열화 평가 방법임을 알 수 있었다.