Evaluation of Microstructure and Ductile-Brittle Transition Temperature in Thermally aged 2.25Cr-1Mo Steel by Electrical Resistivity Measurement

전기비저항을 이용한 2.25Cr-1Mo 강 열화재의 미세조직 및 연성-취성천이온도 평가

  • Byeon, Jai-Won (Research Institute of Engineering and Technology, Korea University) ;
  • Kwun, S.I. (Research Institute of Engineering and Technology, Korea University)
  • 박재원 (고려대학교 공학기술연구소) ;
  • 권숙인 (고려대학교 공학기술연구소)
  • Published : 2002.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

An attempt was made to evaluate the degree of aging degradation in thermally aged 2.25Cr-1Mo steel by electrical resistivity measurement. Artificial aging was performed to simulate the microstructural degradation in 2.25Cr-1Mo steel arising from long time exposure at $540^{\circ}C$. Microstructural parameter (amount of solid solution element), mechanical property (ductile-brittle transition temperature) and electrical resistivity were measured to investigate the mutual relationship among these parameters. Depletion of solid solution element(Mo and Cr) in matrix was detected after aging. The ductile-brittle transition temperature(DBTT) increased rapidly in the initial stage of aging and then saturated afterward. On the other hand, the electrical resistivity decreased rapidly in the beginning and then saturated in the later stage of aging.

전기비저항법을 이용하여 2.25Cr-1Mo 강의 경년열화도를 평가하고자 하였다. 2.25Cr-1Mo 강이 $540^{\circ}C$에서 장시간 노출되었을 때 일어나는 미세조직 변화를 모사하기 위해 인공 열화를 실시하였으며 열화에 따른 미세조직 인자 (고용원소의 함량), 기계적 성질 (연성-취성 천이온도 ), 전기비저항을 측정하여 이들간의 상호관계를 구하고자 하였다. 열화재에서는 기지내의 고용 원소 (Mo 와 Cr)의 고갈이 나타났다. 연성-취성 천이온도는 열화 초반부에 급격히 증가 후 포화되는 경향을 보인 반면 전기비저항은 열화 초반부에 급격히 감소 후 포화되는 경향을 보였다. 즉, 열화 시간에 따른 연성-취성 천이온도의 변화 경향과 전기비저항의 변화는 서로 반대적으로 변화하는 관계를 나타내었다.

Keywords

References

  1. N. S. Cheruvu, 'Degradation of Mechanical Properties of Cr-Mo-V and 2.25Cr-1Mo Steel Components After Long-Term Service at Elevated Temperatures,' Metall. Trans., Vol. 20A, pp. 87-97, (1989)
  2. Z. Qu and K. H. Kuo, 'Embrittlement of 2.25CrMoV Steel Bolts After Long Exposure at $540^{\circ}C$,' Metall. Trans., Vol. 12A, pp. 1333-1337, (1981)
  3. J. C. Murza and C. J. McMahon, 'The Effects of Composition and Microstructure on Temper Embrittlement in 2.25Cr-1Mo steel,' J. Eng. Mater. Technol., Vol. 102, pp. 369-375, (1980) https://doi.org/10.1115/1.3224826
  4. N. Gape, A Chatterjee, T. Mukherjee and D. S. Sanna, 'Influence of Long-Term Aging and Superimposed Creep Stress on the Microstructure of 2.25Cr-1Mo Steel,' Metall. Trans., Vol. 24A, pp. 315-326, (1993)
  5. Y. J. Lee, 'Assessment of Creep Damage in Weldment of 1Cr-0.5Mo Steels,' Ph. D. Thesis, Monash University, (1989)
  6. Y. Watanabe and T. Shoji, 'The Evaluation on In-Service Materials Degradation of Low-Alloy Steels by the Electrochemical Method,' Metall. Trans., Vol. 22A, pp. 2037-2103, (1991)
  7. 변재원, '고온 열화 손상된 니켈기 초내열합금과 2.25Cr-1Mo 강의 미세조직 및 기계적 성질에 대한 벼파펴평가', 고려대학교 박사학위논문, (2001)
  8. 변재원, 표승우, 권숙인, '전기비저항, 바크하우젠노이즈 빛 탄화물 분석법을 이용한 2.25Cr-1Mo 강의 열화도 평가', 대한기계학회 추계학술대회 논문집 A, pp. 210-215, (2001)
  9. 김정표, 배봉국, 김동중, 석창성, '전기비저항법을 이용한 재료열화 평가', 대한기계학회추계학술대회 논문집 A, pp. 129-136, (2001)
  10. 남승훈, 유광민, 김엄기, '전기비저항을 이용한 1Cr-1Mo-0.25V강의 인성열화도 평가‘, 바파괴검사학회지, Vol. 18, No. 1, pp. 10-16, (1998)
  11. K. M. Yu, S. H. Nahm and Y. I. Kim, 'Toughness Degradation Evaluation of 1Cr-1Mo-0.25V Steel by Electrical Resistivity,' J. Mat. Sci. Letters, Vol. 18, pp. 1175-1176, (1939)
  12. 남승훈, 유광민, 류제천, '전기비저항을 이용한 금속합금 열화도 평가기술‘, 비파괴검사학회지, Vol. 21, No. 5, pp. 532-541, (2001)
  13. N. Maeda, T. Gato, T. Kamimura, T. Naito, S. Kumano and Y. Nakao, 'Changes in Electromagnetic Properties During Thermal Aging of Duplex Stainless Steel,' Int, J. Pres. Ves. & Piping, Vol. 71, pp. 7-12, (1997)
  14. 변재원, 권숙인, '보자력 및 잔류자화를 이용한 2‘25Cr - 1Mo 강의 경년열화도 평가-미세조직적 접근', 비파괴검사학회지, Vol. 22, No. 1, pp. 65-73, (2002)
  15. K. S. Ryu, S. H. Nahm, Y. B. Kim, K. M. Yu and D. Son., ''Dependence of Magnetic Properties on isothermal Time for 1Cr-1Mo -0.25V Steel,' J. Magn. Magn. Mater., Vol. 222, pp. 128-132, (2000)
  16. 변재원, 권숙인, 박은수, 박익근, '인공 열화 열처리된 2.25Cr-1Mo 강의 미세조직 변화 에 대한 초음파 비파괴평가', 한국열처리공학회지, Vol. 14, No. 2, pp. 110-117, (2001)
  17. 변재원, 권숙인, 박은수, 박익근, '초음파 속도를 이용한 니켈기 초내열 합금의 크리프 손상 평가’, 대한금속 . 재료학회지, Vol. 39, No. 2, pp. 1367-1374, (2001)
  18. 변재원, 송진헌, 김용환, 권숙연, 김정석, 박은수, 전채홍, 박기성, 김승태, '초음파법에의한 가스터빈 정익 블레이드재의 경년열화도 평가‘, 비파괴검사학회 추계학술대회논문집, pp. 236-241, (2001)
  19. D. D. Pollock, ‘Electrical Conduction in Solids,' Am. Soc. Metals, pp. 89' Metals Park, Ohio, (1985)
  20. A. M. Adbel-Latif, J. M. Corbett and D. M. R. Taplin, 'Analysis of Carbides Formed During Accelerated Aging of 2.25Cr-1Mo Steel,' Met. Sci., Vol. 16, pp. 90-96, (1982)
  21. V. A. Biss and T. Wacla, ‘Microstructural Changes in 1Cr-0.5Mo Steel after 20 Years of Service,' Metall. Trans., Vol. 16A, pp. 109-114, (1985)
  22. K. E. Stahlkopf, R E. Smith, W. L. Server and R. A. Wullaert, ASTM STP 601, pp. 291-307, ASTM, Baltimore, (1975)
  23. J. Miyake and M. E. Fine, 'Electrical Conductivity versus Strength in a Precipitation Hardened Alloy,' Acta Metall. Mater., Vol. 40, pp. 733-741, (1992) https://doi.org/10.1016/0956-7151(92)90015-7