• Journal of Korean Society of Steel Construction
• /
• v.30 no.2
• /
• pp.115-126
• /
• 2018

Internationally representative steel design standards have forbidden or limited the application of high-strength steels to tubular joints, partly because of concerns about their unique material characteristics such as high yield ratio. Most of design standards stipulate that for steels whose yield strengths exceed 355 or 360 MPa, the strength equations cannot be utilized or strength reduction factor below 1.0 should be multiplied. However, the mechanical background behind these limitations is not clear. Experimental testing of high-strength steel CHS (circular hollow section) X-joints recently conducted by the authors also clearly indicated that the current limitations might be unduly conservative. As a continuing work, extensive, test-validated numerical analyses were made to investigate the behavior of high-strength steel CHS X-joint under axial compression. Three steel grades covering ordinary to very high strength steels were considered in the analysis. Again it was found that the high strength penalty to the joint strength in current standards is too severe and needs to be relaxed. The high-strength steel joints under the effects of chord stress generally showed higher strength than the ordinary steel joints and their strengths were conservatively predicted by current standards. It is also emphasized that current format of the CHS X-joint strength equation does not reflect observed behavior and needs to be recast.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.2
• /
• pp.63-67
• /
• 2011

We investigated effects of bonding conditions on the peel strength of rigid printed circuit board (RPCB)/ flexible printed circuit board (FPCB) joints bonded using a thermo-compression bond method, The electrodes on the FPCB were coated with Sn by a dipping process. We confirmed that the bonding temperature and bonding time strongly affected the bonding configuration and strength of the joints. Also, the peel strength is affected by dipping conditions; the optimum dipping condition was found to be temperature of $270^{\circ}C$ and time of 1s. The bonding strength linearly increased with increasing bonding temperature and time until $280^{\circ}C$ and 10s. The fracture energy calculated from the F-x (Forcedisplacement) curve during a peel test was the highest at bonding temperature of $280^{\circ}C$.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.187-189
• /
• 2006

최근 유연솔더에서 무연솔더로 전환함에 따라서 PCB의 도금이 솔더접합부의 각도에 미치는 영향이 중요하게 되었다. 현재 PCB 도금은 Sn, Au, OSP 등으로 다양하게 진행되고 있다. 그러나 PCB 도금이 솔더접합부의 강도에 미치는 영향에 대한 연구는 아직 미비하다. 따라서 본 연구에서는 PCB 도금(Sn, Au, OSP)이 무연솔더(Sn-3.0Ag-0.5Cu) 접합부의 초기 전단강도에 미치는 영향과 열사이클시험 후 솔더접합부의 전단강도에 미치는 영향에 대해서 연구하였다.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.982-986
• /
• 1998

baking 전후의 금선의 접합강도 변화를 연구하였다. 금선을 이용하여 Si 칩의 AI 패드와 은도금된 리드프레임 사이를 thermosonic 방법으로 본딩하였다. 본딩된 금선을 $175^{\circ}C$에서 시간을 변화시키면서 baking 처리하였다. 접합강도는 와이어 풀 테스트, 볼 전단 테스트, stud 풀 테스트로 평가하였다. 와이어 풀 접합강도는 baking 처리를 거쳐도 크게 변화하지 않았지만 파괴 유형이 baking 전에는 볼목 파괴에서 baking 후 스티치 파괴로 바뀌었다. 본딩과 baking 중 금선의 결정립이 크게 성장하였는데 이런 결정립 크기 변화와 금선 접합 부위의 기하학적인 모양에 따라 파괴 유형이 바뀌었다.

• Journal of the Korea Concrete Institute
• /
• v.14 no.6
• /
• pp.961-972
• /
• 2002

Flat plate structures under lateral load are susceptible to the brittle shear failure of plate-column connection. To prevent such brittle failure, strength and ductility of the connection should be ensured. However, according to previous studies, current design methods do not accurately estimate the strength of plate-column connection. In the present study, parametric study using nonlinear finite element analysis was performed for interior connections. Based on the numerical results, a design method for the connection was developed. At the critical sections around the connection coexist flexural moment and shear developed by lateral and gravity loads, and maximum allowable eccentric shear stresses were proposed based on the interactions between the flexural moment and shear, The proposed method can precisely predict the strength of the connection, compared with the current design provisions. The predictability of the proposed method was verified by the comparisons with existing experiments and nonlinear numerical analyses.

• Journal of Korean Society of Steel Construction
• /
• v.27 no.5
• /
• pp.447-454
• /
• 2015

The researches on circular hollow section(CHS) connections have been conducted continuously because of development of material properties and complex local behavior of the connections. The purpose of this study is that the effects of material strength and chord wall slenderness on chord plastification and strength of CHS X-joint truss connection under compression on branch member were evaluated. To this end, finite element analyses were performed for various connections, using ANSYS Mechanical APDL program. Based on the analysis results, the design strength of the connections according to chord plastification limit state in KBC were examined. Finally, special considerations for CHS X-joint connection design were suggested.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2011.04a
• /
• pp.328-331
• /
• 2011

준정적 횡하중을 재하 받는 철근콘크리트 보-기둥 접합부의 전단강도에 대한 주요 영향요인을 Bayesian parameter estimation의 신뢰성 이론 접목을 통해 검토하였다. 이와 같은 연구 scope의 수행을 위해 철근콘크리트 보-기둥의 실험 database가 구축되었다. 실험 database는 일정한 criteria을 적용하여 구축되었으며, 포함된 시편들은 최종적으로 접합부 내의 전단파괴가 지배하는 경우들이다. 포함된 시편들의 상세는 ACI (American Concrete Institute) 352R-02를 기준으로 평가되어졌다. 보-기둥 접합부의 전단강도에 영향 요인을 편중되지 않게 평가하고자, Bayesian parameter estimation의 신뢰성 이론을 적용하였다. Bayesian parameter estimation의 적용을 통해 전단강도에 영향이 적은 변수 (not informative parameter)를 순차적으로 제거 (stepwise removal process)함으로 주요 영향요인의 우선 순위를 확인할 수 있었다. 검토된 8개의 변수들 중에서, 횡하중을 재하 받는 철근콘크리트 보-기둥의 전단강도는 주로 콘크리트 압축강도, in-plane geometry, 종방향 보의 주철근 그리고 접합부 내의 구속철근 순으로 영향을 줌을 알 수 있었다.

• Composites Research
• /
• v.36 no.6
• /
• pp.441-447
• /
• 2023

Recently, as demand for high-strength, lightweight materials has increased, there has been great interest in joining with metals. In the case of mechanical bonding, such as bolting and riveting, chemical bonding using adhesives is attracting attention as stress concentration, cracks, and peeling occur. In this paper, surface treatment was performed to improve the adhesive strength, and the change in adhesive strength was analyzed. For the adhesive strength test were conducted with Carbon Fiber Reinforced Plastic(CFRP), CR340(Steel), and Al6061(Aluminum), and laser and plasma surface treatment were used. After plasma surface treatment, the adhesive strength improved by 7.3% and 39.2% in CFRP-CR340 and CFRP-Al6061, respectively. CR340-Al6061 was improved by 56.2% in laser surface treatment. Surface free energy(SFE) was measured by contact angle after plasma treatment, and it is thought that the adhesion strength was improved by minimizing damage through a chemical reaction mechanism. For laser surface treatment, it is thought that creates a rough bonding surface and improves adhesive strength due to the mechanical interlocking effect. Therefore, surface treatment is effect to improve adhesive strength, and based on this paper, the long-term fatigue test will be conducted to prevent fatigue failure, which is a representative cause of actual structural damage.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.1
• /
• pp.97-105
• /
• 2006

The reinforced concrete flat plate system provides architectural flexibility, clear space, reduced building height, simple formwork, which consequently enhance constructibility. One of the serious problem in the flat plate system is brittle punching shear failure due to transfer of shear force and unbalanced moments in column-slab connection. Since the use of high strength concrete recently has become in practice for reinforced concrete structures, it is highly desired to establish the structural design method for flat plate construction using high strength concrete. In this paper, interior column-slab connection constructed with high strength concrete were tested under lateral and gravity loads to evaluate their strength and behavior. The test parameters were slab reinforcement ratio and the gravity load levels.

• Journal of the Korean Society for Precision Engineering
• /
• v.12 no.10
• /
• pp.113-120
• /
• 1995

여러가지 두꺼운 복합재료 구조물은 3차원 압축 부하 상태에 노출되는 경우가 발생한다. 이런 경우에 있어 서의 복합재료 압축 강도는 압축 평균 응력을 이용하면 예측이 가능할지도 모른다. 이번 연구 에서는 압축 평균 응력을 이용하여 탄소섬유 강화 복합재료들의 압축 강도를 예측하는 모델을 개발 하고자 한다. 이 모델은 압축강도에 영향을 주는 요소, 초기 misalignment를 고려하였고, 탄소섬유와 수지사이에 접합강도가 임계값을 초과할때 복합재료의 파괴가 일어난다고 가정한다. 또 여라가지 문헌들을 통하여 유압이 접합강도에 미치는 점들을 보여준다. 본 모델을 이용한 예측값들은 가해지는 유압에 따라 증가되며, 실험값들과 비교 분석될 것이다.