• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.32A no.11
• /
• pp.35-43
• /
• 1995

To obtain high quality of $Ta_{2}O_{5}$ film, two dielectric layers of $Si_{3}N_{4}$ and $Ta_{2}O_{5}$ were subsequently formed on Si wafer. Silicon nitride films were thermally grown in 10 Torr ammonia ambient by R.F induced heating system. The thickness of thermally grown $Si_{3}N_{4}$ film was able to be controlled in the range of tens $\AA$ due to the self-limited growth property. $Ta_{2}O_{5}$ film of 200$\AA$ thickness was then deposited on the as-grown $Si_{3}N_{4}$ film about 25$\AA$ thickness by sputtering method and annealed at $900^{\circ}C$in $O_{2}$ ambient for 1hr. Stoichiometry film was prepared by the annealing in oxygen ambient. Despite the high temperature anneal process, silicon oxide layer was not grown at the interface of the layered films because of the oxidation barrier effect of Si$_{3}$N$_{4}$ film. The fabricated $Ta_{2}O_{5}$/$Si_{3}N_{4}$ film showed low leakage current less than several nA and high dielectric breakdown strength.

• Journal of the Korean Vacuum Society
• /
• v.14 no.2
• /
• pp.97-102
• /
• 2005

NO adsorption can be used in synthesizing oxynitride thin films which have potential application in nanodevices. However, it is very difficult to understand the oxynitridation Process since too many factors are involved in it. In this paper, we present our first-principles molecular dynamics calculation of the NO molecule adsorption on the Si(001) surface as the initial stage of the oxynitridation process. The previous first-principles calculation has argued the NO molecule is dissociated with a very small activation barrier, 0.07eV, which acutally corresponds to 1.60eV considering thermodynamics. This is in clear contrast to the observation that NO is dissociated at temperatures as low as 20K From extensive searches of NO on the Si(001) surface, we have found the new dissociation processes that have the much lower activation energies, less than 0.01 eV. We also present the dissociation and penetration processes with the corresponding activation energies and discuss their experimental implications.

• Korean Journal of Materials Research
• /
• v.25 no.5
• /
• pp.233-237
• /
• 2015

Silicon oxynitride that can be deposited two times faster than general SiNx:H layer was applied to fabricate the passivation protection layer of atomic layer deposition (ALD) $Al_2O_3$. The protection layer is deposited by plasma-enhanced chemical vapor deposition to protect $Al_2O_3$ passivation layer from a high temperature metallization process for contact firing in screen-printed silicon solar cell. In this study, we studied passivation performance of ALD $Al_2O_3$ film as functions of process temperature and RF plasma effect in plasma-enhanced chemical vapor deposition system. $Al_2O_3$/SiON stacks coated at $400^{\circ}C$ showed higher lifetime values in the as-stacked state. In contrast, a high quality $Al_2O_3$/SiON stack was obtained with a plasma power of 400 W and a capping-deposition temperature of $200^{\circ}C$ after the firing process. The best lifetime was achieved with stack films fired at $850^{\circ}C$. These results demonstrated the potential of the $Al_2O_3/SiON$ passivated layer for crystalline silicon solar cells.

• Journal of the Korean Vacuum Society
• /
• v.21 no.6
• /
• pp.348-353
• /
• 2012

We investigated chemical states of a $Sb_2Te_3$ thin film with the polycrystalline phase by using high-resolution x-ray photoelectron spectroscopy with synchrotron radiation. The $Sb_2Te_3$ thin film was formed by sputtering. The rhombohedral phase was confirmed by x-ray diffraction. To remove the surface oxide, we performed $Ne^+$ ion sputtering for 1 hour with the beam energy of 1 kV and post-annealing at $100^{\circ}C$ for 5 min in ultra-high vacuum. We obtained the Te and Sb 4d core-levels spectra with the peaks at the binding energies of 40.4 and 33.0 eV, respectively. The full-width of half maximum of both the Te and Sb $4d_{5/2}$ core-levels is 0.9 eV. The Te and Sb core-levels only show a single chemical state, and we also confirmed the stoichiometry of approximately 2 : 3.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.3
• /
• pp.33-38
• /
• 2021

Recently, rollable and foldable displays are attracting great attention in the flexible display market due to their excellent form factor. To predict and prevent the mechanical failure of the display panels, it is essential to accurately understand the mechanical properties of brittle SiN_x thin films, which have been used as an insulating film in flexible displays. In this study, tensile properties of the ~130 nm- and ~320 nm-thick SiN_x thin films were successfully measured by coating a ~190 nm-thick organic nano-support-layer (PMMA, PS, P3HT) on the fragile SiN_x thin films and stretching the films as a bilayer state. Young's modulus values of the ~130 nm and ~320 nm SiN_x thin films fabricated through the controlled chamber pressure and deposition power (A: 1250 mTorr, 450 W/B: 1000 mTorr, 600 W/C: 750 mTorr, 700 W) were calculated as A: 76.6±3.5, B: 85.8±4.6, C: 117.4±6.5 GPa and A: 100.1±12.9, B: 117.9±9.7, C: 159.6 GPa, respectively. As a result, Young's modulus of ~320 nm SiN_x thin films fabricated through the same deposition condition increased compared to the ~130 nm SiN_x thin films. The tensile testing method using the organic nano-support-layer was effective in the precise measurement of the mechanical properties of the brittle thin films. The method developed in this study can contribute to the robust design of the rollable and foldable displays by enabling quantitative measurement of mechanical properties of fragile thin films for flexible displays.