• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.3
• /
• pp.152-158
• /
• 2016

The bonding characteristics of MLCCs (multi layer ceramic capacitor, C1608) lead-free solder (SAC305) joints were evaluated through thermal shock test ($-40^{\circ}C{\sim}125^{\circ}C$, total 1,800 cycle). After the test, IMCs( intermetallic compounds) growth and cracks were verified, also shear strengths were measured for degradation of solder joints. In addition, The thermal stress distributions at solder joints were analyzed to compare the solder joints changes before and after according to thermal shock test by FEA (finite elements analysis). We considered the effects of IMCs growth at solder joints. As results, the bonding characteristics degradation was occurred according to initial crack, crack propagations and thermal stress concentration at solder-IMCs interface, when the IMCs grown to solder inside.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.17 no.1
• /
• pp.137-143
• /
• 2008

Thermal fatigue life prediction for solder joints becomes the most critical issue in present microelectronic packaging industry. And lead-free solder is quickly becoming a reality in electronic manufacturing fields. This trend requires life prediction models for new solder alloy systems. This paper describes the life prediction models for SnAgCu and SnPb solder joints, based upon non-linear finite element analysis (FEA). In case of analyses of the SnAgCu solder joints, two kinds of shapes are used. As a result, it is found that the SnAgCu solder has longer fatigue life than the SnPb solder in temperature cycling analyses.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.194-195
• /
• 2009

본 연구에서는 고속전단 강도에 표면 처리의 변화가 미치는 영향에 대해 연구하고자 하였다. 표면 처리를 ENIG, ENEPIG, OSP로 하여 고속전단시험을 수행하였다. 고속전단 결과 SAC105의 전단 강도 값은 ENIG가 가장 작았고, ENEPIG가 가장 높았다. SAC305의 전단 강도 값은 ENIG가 가장 작았고, OSP와 ENEPIG는 비슷한 값을 나타냈다.

• Journal of Welding and Joining
• /
• v.20 no.5
• /
• pp.106-112
• /
• 2002

In the present study, the wettability and interfacial tension between (bare Cu, electroless Ni/cu, immersion Au/Ni/Cu) substrates and indium solder were investigated as a function of soldering temperature, types of flux. The wettability of In solder increased with soldering temperature and solid content of flux. The wettability of In solder was affected by the substrate metal finish used, i.e., nickel, gold and copper. On the bare Cu substrate, In solder wet better than any of the substrate metal finishes tested. Intermetallic compound formation between liquid solder and substrate reduced the interfacial energy and improved wettability. For the identification of intermetallic compounds, X-Ray Diffraction(LRD) were employed. Experimental results showed that the intermetallic compounds, such as Cu11In9 and In27Ni10 are observed f3r different substrates respectively. The wetting kinetics is investigated by measuring wetting time with the wetting balance technique. The activation energy of wetting calculated for the In solder/cu substrate and In solder/electroless Au/Ni/Cu substrate are 36.13 and 27.36 kJ/mol, respectively.

• Journal of Welding and Joining
• /
• v.20 no.1
• /
• pp.91-96
• /
• 2002

Three different kinds of substrate used in this study : bare Cu, electroless Ni/Cu substrate with a Nilayer thickness of $5\mu\textrm{m}$, immersion Au/electroless Ni/Cu substrate with the Au and Ni layer of $0.15\mu\textrm{m}$ and $5\mu\textrm{m}$ thickness, respectively. The wettability and interfacial tension between various substrate and Sn-3.5Ag solder were examined as a function of soldering temperature, types of flux. The wettability of Sn-3.5Ag solder increased with soldering temperature and solid content of flux. The wettability of Sn-3.5Ag solder was affected by the substrate metal finish used, i.e., nickel, gold and copper. Intermetallic compound formation between liquid solder and substrate reduced the interfacial energy and decreased wettability.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.179-180
• /
• 2009

본 연구에서는 ENIG, ENEPIG 의 Pad 표면처리가 고속전단시험에 미치는 영향에 대해 연구하고자 하였다. Pad의 표면처리를 ENIG와 ENEPIG로 하여 고속전단시험을 수행하여 그에 따른 Shear force와 Shear energy를 측정하였다. 고속전단시험결과 ENEPIG 표면처리 시편이 ENIG의 표면처리시편보다 shear force와 shear energy의 값이 높게 나타났다.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.4
• /
• pp.7-15
• /
• 2000

The purpose of this work is to evaluate the solderahility and characteristics of solder joints. Bridge defect of solder joint was examined in natural atmosphere and $N_2$ condition. Consequently, wettability was excellent for each of Sn-Pb plated Cu specimen, Sn plated Cu specimen, and Cu polished in $N_2$ condition. The wetting time in $N_2$ condition was shorter than that of natural atmosphere condition, showing the decreasing values of about 0.2~0.45 seconds. The max. wetting force under the $N_2$ condition was more increasing that of natural atmosphere condition, showing the increasing values of about 1.8~2.8 N. With the result of wetting balance test, the wetting time ($t_2$) and wetting farce according to increasing amount of $N_2$ from 10 1/min to 30 1/min, the wetting time ($t_2$) was reduced about 0.25 second and wetting force was increased about 2.3 N. In non-cleaning flux, when $N_2$ gas is applied, it is compensated to decrease of wettability. In the case of using the $N_2$ gas, the wettability was improved. The reason for improving wettability is due to preventing the formation of dross. The generation rate of bridge in $N_2$ condition decreased than that of natural atmosphere, and when the specimen had a fine pitch, the rate of bridge defects was considerably decreased in $N_2$ condition, showing the decreasing rate of 25~75%.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.6
• /
• pp.443-453
• /
• 2017

In flip chip technology, the conventional solder bump has been replaced with a copper (Cu) pillar bump owing to its higher input/output (I/O) density, finer pitch, and higher reliability. However, Cu pillar bump technology faces several issues, such as interconnect shorting and higher low-k stress due to stiffer Cu pillar structure when the conventional reflow process is used. Therefore, the thermal compression bonding (TCB) process has been adopted in the flip chip attachment process in order to reduce the package warpage and stress. In this study, we investigated the package warpage induced during the TCB process using a numerical analysis. The warpage of the TCB process was compared with that of the reflow process.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.4
• /
• pp.1-9
• /
• 2011

Understanding the void characterization in the solder joints has become more important because of the application of lead free solder materials and its reliability in electronic packaging technology. According to the JEDEC 217 standard, it describes void types formed in the solder joints, and divides into some categories depending on the void position and formation cause. Based on the previous papers and the standards related to the void, reliability of the BGA solder joints is determined by the size of void, as well as the location of void inside the BGA solder ball. Prior to reflow soldering process, OSP(organic surface preservative) finished Cu electrode was exposed under $85^{\circ}C$/60%RH(relative humidity) for 168 h. Voids induced by the exposure of $85^{\circ}C$/60%RH became larger and bigger with increasing aging times. The void position has more influence on mechanical strength property than the amount of void growth does.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.1
• /
• pp.47-54
• /
• 2021

For the bonding of smaller PCB solder bumps of less than 100 microns, an experiment was performed to make up a tin plating solution and find plating conditions in order to produce a bump pattern through tin electroplating, replacing the previous PCB solder bumps process by microballs. After SR patterning, a Cu seed layer was formed, and then, through DFR patterning, a pattern in which Sn can be selectively plated only within the SR pattern was formed on the PCB substrate. The tin plating solution was made based on methanesulfonic acid, and hydroquinone was used as an antioxidant to prevent oxidation of divalent tin ions. Triton X-100 was used as a surfactant, and gelatin was used as a grain refiner. By measuring the electrochemical polarization curve, the characteristics of organic additives in Triton X-100 and gelatin were compared. It was confirmed that the addition of Triton X-100 suppressed hydrogen generation up to -1 V vs. NHE, whereas gelatin inhibited hydrogen generation up to -0.7 V vs. NHE. As the current density increased, there was a general tendency that the grain size became finer, and it was observed that it became finer when gelatin was added.