• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.3
• /
• pp.267-272
• /
• 2011

We analyzed the wear characterization of $Si_3N_4$ ceramics according to the amount of added $SiO_2$ nanocolloid. The test specimen was prepared by hot-press sintering at 35 MPa and 2123 K in an $N_2$ gas atmosphere for 1 h. A wear test was performed with a block-on-ring tester, and the test conditions were as follows: (1) the ring with a diameter of 35 mm had a rotational speed of 50 rpm; (2) the load was 9.8 N; and (3) the temperature was $25^{\circ}C$. The test results show that $Si_3N_4$ ceramics have a friction coefficient of about 1.0 and a wear loss of about 0.02 mm. Of the specimens used this study, the test specimen with 1.3 wt% of added $SiO_2$ nanocolloid has the best wear resistance because it has the lowest friction coefficient and the smallest wear loss. This specimen also has the highest Vickers hardness and bending strength. In this study, the friction coefficient is inversely proportional to the hardness and bending strength.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.5
• /
• pp.625-630
• /
• 2013

The friction behavior of a 60-${\mu}m$-thick anodic aluminum oxide (AAO) film having cylindrical nanopores of 45-nm diameter was investigated as a function of impregnated oil viscosity ranging from 3.4 to 392.6 cSt. Reciprocating ball-on-flat sliding friction tests using a 1-mm-diameter steel ball as the counterpart were carried out with normal load ranging from 0.1 to 1 N in an ambient environment. The friction coefficient significantly decreased with an increase in the oil viscosity. The boundary lubrication film remained effectively under all test conditions when high-viscosity oil was impregnated, whereas it was easily destroyed when low-viscosity oil was impregnated. Thin plastic deformed layer patches were formed on the worn surface with high-viscosity oil without evidence of tribochemical reaction and transfer of counterpart material.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.10a
• /
• pp.45-45
• /
• 2003

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.552-555
• /
• 2004

The reliability issue of the probe tip/recording media interface is one of the most crucial concerns in the Atomic Force Microscope (AFM)-based recording technology. In this work, the tribological characteristics of the probe/media interface were investigated by performing wear tests using an AFM. The ranges of applied normal load and sliding velocity for the wear test were 10 to 50nN and 2 to 20$\mu$m/s respectively. The damage of the probe tip was quantitatively as well as qualitatively characterized by Field Emission Scanning Probe Microscope (FESEM) analysis and calculated based on Archard s wear equation. It was shown that the wear coefficient of the probe tip was in the order of 10$^{-4}$ ~ 10$^{-3}$ , and significant contamination at the end of the probe tip was observed. Thus in order to implement the AFM-based recording technology, tribological optimization of the probe/media interface must be achieved.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.54-54
• /
• 2008

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.5
• /
• pp.189-195
• /
• 2003

Atomic Force Microscope (AFM) has been widely used in micro/nano-scale studies and applications for. the last few decade. In this work, wear characteristics of silicon-based AFM tip was investigated. AFM tip shape was observed using a high resolution SEM and the wear coefficient was approximately calculated based on Archard's wear equation. It was shown that the wear coefficient of silicon and silicon nitride were in the range of ${10}^{-1}$~${10}^{-3}$ and ${10}^{-3}$~${10}^{-4}$, respectively. Also, the effect of relative humidity and sliding distance on adhesion-induced tip wear was discussed. It was found that the tip wear has more severe for harder test materials. Finally, the probable wear mechanism was analyzed from the adhesive and abrasive interaction point of view.

• Tribology and Lubricants
• /
• v.35 no.5
• /
• pp.286-293
• /
• 2019

In friction and wear tests that use friction force microscopy (FFM), the wear debris transfer to the tip apex that changes tip radius is a crucial issue that influences the friction and wear performances of films and coatings with nanoscale thicknesses. In this study, FFM tests are performed for bilayer $MoS_2$ film to obtain a better understanding of how geometrical and chemical changes of tip apex influence the friction and wear properties of nanoscale molecular layers. The critical load can be estimated from the test results based on the clear distinction of the failure area. Scanning electron microscopy and energy-dispersive spectroscopy are employed to measure and observe the geometrical and chemical changes of the tip apex. Under normal loads lower than 1000 nN, the reuse of tips enhances the friction and wear performance at the tip-sample interface as the contact pair changes with the increase of tip radius. Therefore, the reduction of contact pressure due to the increase of tip radius by the transfer of $MoS_2$ or Mo-dominant wear debris and the change of contact pairs from diamond/$MoS_2$ to partial $MoS_2$ or Mo/$MoS_2$ can explain the critical load increase that results from tip reuse. We suggest that the wear debris transfer to the tip apex should be considered when used tips are repeatedly employed to identify the tribological properties of ultra-thin films using FFM.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.354-359
• /
• 2001

CNTs were added to Ultra-high molecular weight polyethylene (UHMWPE) to improve the tribological properties of UHMWPE. CNTs which have a diameter of about 10-50nm, while their length is about 3-5nm were produced by the catalytic decomposition of tile C$_2$H$_2$ using a tube furnace. UHMWPE/CNTs composites were fabricated by hot pressing method. It is shown that friction coefficient was increased and wear resistance was improved as CNTs were added to UHMWPE because of excellent mechanical properties of CNTs located on UHMWPE surface.

• Tribology and Lubricants
• /
• v.27 no.6
• /
• pp.344-350
• /
• 2011

Friction and wear behavior of tungsten oxide nanorods (TONs) was investigated using friction force microscopy(FFM) employing colloidal probes instead of conventional sharp tips. Vertically well-ordered TONs with 40 nm diameter, 130 nm length and 100 nm pitch width were synthesized on an anodic aluminium oxide substrate using two step electrochemical anodizing processes. The colloidal probe (diameter 20 ${\mu}m$) attached at the free end of tipless cantilever was oscillated(scanned) against a stationary surface of vertically aligned TONs with various scan speeds (1.2 ${\mu}m/s$, 3.0 ${\mu}m/s$ and 6.0 ${\mu}m/s$) and sliding cycles (100, 200 and 400) under normal load of 800 nN. The friction force and wear depth decreased with the increase of the scan speed. Plastically deformed thin layers were formed and sparsely deposited on the worn nonorod surface. The lower wear rate of the TONs with the longer oscillating cycles was attributed to the decreased real contact pressure due to the increase of real contact area between the colloidal probe and the TONs.

• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.11
• /
• pp.228-233
• /
• 2002

In this work, a new non-photolithographic micro-fabrication technique is presented. The motivation of this work is to overcome the demerits of the most commonly used photolithographic techniques. The micro-fabrication technique presented in this work is a two-step process which consists of mechanical scribing followed by chemical etching. This method has many advantages over other micro-fabrication techniques since it is simple, cost-effective, rapid, and flexible. Also, the technique can be used to obtain a metal structure which has sub-micrometer width patterns. In this paper, the concept of this method and its application to microsystem technology are described.