• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.377-385
• /
• 2002

Metal-Ferroelectric-Insulator-Semiconductor(MFIS) 구조의 적용하기 위해 R. F. 마그네트론 스퍼터를 이용하여 p-type Si(111) 기판 위에 $ZrO_2$와 $SrBi_2Ta_2O_9$ 박막을 증착하였다. SBT 박막은 $ZrO_2$ 완충층을 삽입함으로써 MFIS 구조의 전기적인 특성이 향상되었다. $ZrO_2$ 박막의 두께를 고정하고 SBT 박막의 두께를 160nm에서 220nm으로 변화시키면서 윈도우 메모리를 3-9V의 범위에서 측정하였다. Pt/SBT(160nm)/$ZrO_2$(20nm)/Si의 조건에서 최대 2.2V 메모리 윈도우 값을 얻을 수 있었으며 이 메모리 윈도우 값은 실제 적용되는 저전압 NDRO-FRAM 구동에 충분한 값이다.

• Bulletin of the Korean Chemical Society
• /
• 제28권9호
• /
• pp.1463-1466
• /
• 2007

Single phases of multi-component oxides films, ZrTiO4 and Ta2Zr6O17, could be synthesized by using the combinatorial approach through surface sol-gel route, coating the appropriate mole ratio of 100 mM zirconium butoxide, tantalum butoxide and titanium butoxide precursors on Pt/Ti/SiO2/Si (100) substrate, following pyrolysis at 450 oC, and annealing them at 770 oC. Both the films and bulks of ZrTiO4 and Ta2Zr6O17 showed very stable dielectric properties in temperature range, ?140 to 60 oC, and frequency range, 100 Hz to 1 MHz, promising their applications in wide range of temperatures and frequencies. The dielectric constants of the films were lower and a little more dependent on frequency than those of the bulks. The reduction of dielectric property in the film was mainly due to the interfacial effects that worked as series and parallel-connected capacitances toward the substantial film capacitance.

• 한국진공학회지
• /
• 제5권2호
• /
• pp.147-155
• /
• 1996

Optical properties of $TiO_2/M/Ag/M/TiO_2$ films have been changed with the diffusion barrier metal M. Optimum opticla properties of $TiO_2/M/Ag/M/TiO_2$ as the transparent heat mirror film, could be obtained with Ti among diffusion barrier metals of Ti, Cu, Zr and Al. $TiO_2/M/Ag/M/TiO_2$ film, which was fabricated by sputtering of 18 nm-thick $TiO_2$ and Ag, and 4nm-thick Ti, showed maximum transimittance of 89% at visible wavelength and infrared reflectance of 97% at wavelength of 3000 nm. Optical properties of this film was not degraded by Xenon-sunshine weather test for 240 hours. For specimens with barrier layers of Cu, Zr, and Al, degradation of optical properties by weather test was increased in a sequence of films with Cu, Zr, and Al barrier layers.

• Bulletin of the Korean Chemical Society
• /
• 제30권1호
• /
• pp.92-96
• /
• 2009

A new precursor [$Zr(acac)_{3}(H_{2}O)_{2}$] was synthesized by Sonochemical technique and used to deposit thin $ZrO_{2}$ film on quartz and ceramic substrate via ultrasonic aerosol assisted chemical vapour deposition (UAACVD) at 300 ${^{\circ}C}$ in oxygen environment followed by annealing of the sample for 2-3 minutes at 500 ${^{\circ}C}$ in nitrogen ambient. The molecular structure of the precursor determined by single crystal X-ray analysis revealed that the molecules are linked through intermolecular hydrogen bonds forming pseudo six and eight membered rings. DSC and TGA/FTIR techniques were used to determine thermal behavior and decomposition temperature of the precursor and nature of evolved gas products. The optical measurement of annealed $ZrO_{2}$ film with tetragonal phase shows optical energy band gap of 5.01 eV. The particle size, morphology, surface structure and composition of deposited films were investigated by XRD, SEM and EDX.

• 한국세라믹학회지
• /
• 제28권1호
• /
• pp.1-10
• /
• 1991

Zirconium dioxide(ZrO2) thin films have been deposited by chemical vapor deposition technique involving the application of gas mixture of ZrCl4, and H2O into silicon wafers. The relationships between the deposition rate and various reaction parameters such as the deposition time, the gas flow rate, the deposition temperature, and the composition of reactant gases were studied. The film was identified as nearly stoichiometric monoclinic ZrO2. The apparent activation energy is about 19Kcal/mole at surface chemical reaction controlled region. The deposition rate is mainly influenced by the H2O-forming reacting between CO2 and H2.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.301-304
• /
• 2002

We investigated the structural and electrical properties of Ce-doped Ba($Zr_{0.2}Ti_{0.8}$)$O_3$(BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/$SiO_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/$O_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 m (RMS at $500^{\circ}C$, Ar:6 scrim, $O_2$:6 sccm). We have found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• 한국전기전자재료학회논문지
• /
• 제16권5호
• /
• pp.361-364
• /
• 2003

It was investigated that the structural and electrical Properties of Ce-doped Ba(Zr$_{x}$Ti$_{1-x}$ )O$_3$ (BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/SiO$_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/O$_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 nm (RMS at 500 $^{\circ}C$, Ar:6 sccm, $O_2$:6 sccm). It was found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권8호
• /
• pp.836-850
• /
• 1996

In this study, we have analyzed structural analysis and measured ferroelectric characteristics of PZT thin films prepared by sol gel process with different sintering conditions and different Zr/Ti mot%. When the Zr mot% of PZT thin film was increased, it was found that the remanent. polarization and coercive field were decreased and increased, respectively. Also, the maxium dielectric constant of PZT(50/50) thin film was 786.8. We got double hysteresis(anti-fcrroelectric) curve from PbZrO$_{3}$ thin film. As heating rate goes up, pyrochlore phase of PZT thin film was decreased and dielectric and ferroelectric characteristics were improved. As a result of variation of sintering temperature and time 500.deg. C-800.deg. C and 5 sec.-8 hours, respectively, we got optimal sintering temperature and time. The optimium sintering temperature and time of conventional furnace method and rapid thermal processing method were 650.deg. C-700.deg. C for 30-60 minutes and 700.deg. C/20 seconds-2 minutes, respectively.

• Transactions on Electrical and Electronic Materials
• /
• 제16권3호
• /
• pp.130-134
• /
• 2015

This research proposes the use of a composition modulated (ZrO₂)_x(Al₂O₃)_1-x film as a charge trapping layer for charge trap flash memory; this is possible when the Zr (Al) atomic percent is controlled to form a variable bandgap as identified by the valence band offsets and electron energy loss spectrum measurements. Compared to memory devices with uniform compositional (ZrO₂)_0.1(Al₂O₃)_0.9 or a (ZrO₂)_0.92(Al₂O₃)_0.08 trapping layer, the memory device using the composition modulated (ZrO₂)_x(Al₂O₃)_1-x as the charge trapping layer exhibits a larger memory window (6.0 V) at the gate sweeping voltage of ±8 V, improved data retention, and significantly faster program/erase speed. Improvements of the memory characteristics are attributed to the special energy band alignments resulting from non-uniform distribution of elemental composition. These results indicate that the composition modulated (ZrO₂)_x(Al₂O₃)_1-x film is a promising candidate for future nonvolatile memory device applications.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제17권2호
• /
• pp.245-251
• /
• 2017

Niobium doped zirconium oxide (Nb-Zr-O:NZO) thin films were fabricated on Si substrates by a sol-gel technique with an annealing temperatures of $500{\sim}1000^{\circ}C$ in air ($N_2:O_2=3:1$) for 20 minutes. It was found that the NZO film is based on tetragonal $ZrO_2$ polycrystalline structure with the Nb 5+ ion state and there is almost no diffusion of Nb or Zr to Si substrate. The relative dielectric constant for the NZO film with the Nb composition of 30 mol% and annealed at $800^{\circ}C$ was around 40. The root mean roughness was 1.02 nm. In addition, the leakage current of NZO films was as low as $10^{-6}A/cm^2$ at 4.4 V.