• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.290-293
• /
• 2001

The SrBi$_2$Nb$_2$O$_{9}$ (SBN) thin films were deposited on p-type(100) Si substrates by rf magnetron sputtering to confirm the Possibility of Pt/SBN/Si structure for the application of nondestructive read out ferroelectric random access memory (NDRO- FRAM). The SBN thin films were deposited by co-sputtering method with Sr$_2$Nb$_2$O$_{7}$ (SNO) and Bi$_2$O$_3$ ceramic targets. The SBN thin films deposited at room temperature were annealed at $700^{\circ}C$ for 1hr in $O_2$ ambient. The structural and electrical properties of SBN with different power ratios of targets were measured by x-ray diffraction(XRD), scanning electron microscopy(SEM), capacitance-voltage(C-V), and current-voltage(I-V). The C-V curves of the SBN films showed hysteresis curves of a clockwise rotation showing ferroelectricity. When the Power ratio of the SNO/Bi$_2$O$_3$ targets was 120 W/100 W, the SBN thin films had excellent electrical properties. The memory window of SBN thin film was 1.8 V-6.3 V at applied voltage of 3 V-9 V and the leakage current density was 1.5 $\times$ 10$^{-7}$ A/$\textrm{cm}^2$ at applied voltage of 5 V The composition of SBN thin films was analysed by electron probe X-ray micro analyzer(EPMA) and the atomic ratio of Sr:Bi:Nb with pawer ratio of 120 W/100 W was 1:3:2.

• Journal of the Korean Ceramic Society
• /
• v.37 no.10
• /
• pp.1008-1013
• /
• 2000

SrTi $O_3$(001) 단결정 기판 위에 졸-겔 스핀코팅으로 $SrBi_2(Ta,Nb)_2O_9$ 박막을 도포하고 그 결정화 과정을 고온 X-선 회절분석 (HTXRD)으로 추적하면서 Pt(111)/Ti/ $SiO_2$/Si 위에 성장한 박막과 비교하였다. SrTi $O_3$(001) 단결정 기판 위에 도포된 $SrBi_2Nb_2O_{9}$ 박막은 fluorite-like phase와 같은 transient phase를 거치지 않고 곧바로 순수한 $SrBi_2Nb_2O_9$ 상으로 결정화가 시작되었으며 결정화가 시작되는 온도인 ${\sim}540^{\circ}C$부터 c축 배향성장하였다. 또한 $SrB i_2(Ta,Nb)_2O_9$ 박막은 Ta/Nb 비에 관계없이 $SrTiO_3$(001) 위에서 모두 $(00{\ell})$로 배향되었으며, 코팅 횟수가 늘어나 필름의 두께가 증가함에 따라 c축 배향성은 미세한 감소를 보였다. $SrBi_2Nb_2O_9/SrTiO_3$단면을 TEM으로 관찰한 결과 $SrBi_2Nb_2O_9$은 대체로 불규칙한 크기의 다결정체로 되어 있었으나 계면 부근에서는 [001]$_{SBN}$//[001]$_{SrTi}$ $O_3$/, [100]$_{SBN}$//[100]$_{SrTi}$ $O_3$/라는 결정학적 관계를 가지며 에피탁샬 성장했음을 알 수 있었다.있었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.4 s.37
• /
• pp.339-343
• /
• 2005

Pt-$SrBi_2Nb_2O_9(SBN)-Pt-Y_2O_3-Si$ gate field effect transistors (MFMISFETs) have been fabricated and the SBN thin films are rapid thermal annealed in oxygen plasma. The grain size of the SBN becomes 4 times much larger than that of furnace annealed SBN films even at the same annealing temperature of $700^{\circ}C$, remnant polarization value of Pt-SBN-Pt is improved by 2 times. Using the rapid grain growth of SBN for the MFM-ISFET, memory window and programming characteristics of on/off states are fairly well improved.

• Transactions of the Korean hydrogen and new energy society
• /
• v.21 no.5
• /
• pp.375-382
• /
• 2010

A layered perovskite photocatalysts, $SrBi_2Nb_2O_9$ (SBN), was synthesized by the conventional solid-state reaction method and characterized by X-ray diffraction (XRD) and UV-visble spectrophotometry. The results showed that the structure of $SrBi_2Nb_2O_9$ is orthorhombic. Diffuse reflectance spectra for calcined and attrition-milled SBN showed the main absorption edges were less 400 nm, that is ultraviolet region. SBN under micron-sized powder was deposited on the $Al_2O_3$ by room temperature powder spray in vacuum process, so called aerosol deposition (AD), and nano-grained $SrBi_2Nb_2O_9$ photocatalytic thick film was fabricated. AD-deposited SBN thick films were characterized by XRD, scanning electron microscopy (SEM) and UV-visable spectrophotometry, Moreover, it was found that several nano-sized SBN film by AD process can improve the photocatalytic activity under visable reflectance.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.186-187
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition conditions. Thickness of SBN thin films was about 250[nm] in 70/30 of $Ar/O_2$ ratio. The thickness and deposition rate of SBN thin films were increased with increase of RF power. The capacitance of SBN thin films were increased with the increase of deposition temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.549-552
• /
• 2002

$(SrBi_2Nb_2O_9)_{0.5}-(Bi_3TiNbO_9)_{0.5}$ ceramics were fabricated by the mixed-oxide method, and the structural and electrical properties with variation of ball-milling time were investigated. All SBN-BTN specimens showed the typical polycrystalline X-ray diffraction patterns without the presence of the second phase. The SBN-BTN specimen sintered at $1200^{\circ}C$ and ball-milled for 168h showed the average grain size of $16{\mu}m$. The dielectric constant and dielectric loss of the SBN-BTN specimen sintered at $1150^{\circ}C$ and ball-mill for 72h were 225, 0.4% at 1KHz, respectively.

• Journal of the Semiconductor & Display Technology
• /
• v.8 no.2
• /
• pp.11-14
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various $Ar/O_2$ ratio. We investigated the effect of deposition condition(specially $Ar/O_2$ ratio) on the structural properties of SBN thin film. As $Ar/O_2$ ratio was increased, the peaks in the XRD pattern became more sharp. Also, the peaks(008)(115)(220) in 80/20 of $Ar/O_2$ ratio were suddenly appeared. The optimum of the rougness showed about 4.33 nm in 70/30 of $Ar/O_2$ ratio. The crystallinity of SBN thin films were increased with the increase of $Ar/O_2$ ratio. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70/30 of $Ar/O_2$ ratio. The capacitance of SBN thin films were increased with the increase of $Ar/O_2$ ratio.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.185-186
• /
• 2008

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/SiO2/Si) using RF sputtering method at various substrate temperature. The optimum conditions of RF power and Ar/O2 ratio were 60[W] and 70/30, respectively. The rougness showed about 4.33[nm]. Deposition rate of SBN thin films was about 4.17[nm/min]. The capacitance of SBN thin films were increased with the increase of substrate temperature.

• Korean Journal of Materials Research
• /
• v.12 no.12
• /
• pp.962-966
• /
• 2002

The $SrBi_2$$Nb_2$$O_{9}$ (SBN) thin films were deposited with $SrNb_2$$O_{6}$ / (SNO) and $Bi_2$$O_3$ targets by co-sputtering method. For the growth of SBN thin films, we adopted the various power ratios of two targets; the power ratios of the SNO target to $Bi_2$$O_3$ target were 100 W : 20 W, 100 W : 25 W, and 100 W : 30 W during sputtering the SBN films. We found that the electrical properties of SBN films were greatly dependent on Bi content in films. The $Bi_2$Pt and $Bi_2$$O_3$ phase as second phases occurred at the films with excess Bi content greater than 2.4, resulting in poor ferroelectric properties. The best growth condition of the SBN films was obtained at the power ratio of 100 W : 25 W for the two targets. At this condition, the crystallinity and electrical properties of the films were improved at even low annealing temperature as $700^{\circ}C$ for 1h in oxygen ambient and the Sr, Bi and Nb component in the SBN films were about 0.9, 2.4, and 1.8 respectively. From the P-E and I-V curves for the specimen, the remnant polarization value ($2P_{r}$) of the SBN films was obtained about 6 $\mu$C/c $m^2$ at 250 kV/cm and the leakage current density of this thin film was $2.45$\times$10^{-7}$ $A/cm^2$ at an applied voltage of 3 V.V.

• Korean Journal of Materials Research
• /
• v.12 no.6
• /
• pp.464-469
• /
• 2002

$SrBi_2Nb_2O_9(SBN)$ thin films were grown on Pt/Ti/Si and p-type Si(100) substrates by rf-magnetron co-sputtering method using two ceramic targets, $SrNb_2O_6\; and \;Bi_2O_3$. The structural and electrical characteristics have been investigated to confirm the possibility of the SBN thin films for the applications to destructive and nondestructive read out ferroelectric random access memory(FRAM). For the optimum growth condition X-ray diffraction patterns showed that SBN films had well crystallized Bi-layered perovskite structure after $700^{\circ}C$ heat-treatment in furnace. From this specimen we got remnant polarization $(2P_r)$ of about 6 uC/$\textrm{cm}^2$ and coercive voltage $(V_c)$ of about 1.5 V at an applied voltage of 5 V. The leakage current density was $7.6{\times}10^{-7}$/A/$\textrm{cm}^2$ at an applied voltage of 5V. And for the NDRO-FRAM application, properties of SBN films on Si substrate has been investigated. From transmission electron microscopy (TEM) analysis, we found the furnace treated sample had a native oxide about 2 times thicker than the RTA treated sample and this thick native oxide layer had a bad effect on C-V characteristics of SBN/Si thin film. After $650^{\circ}C$ RTA process, we got the improved memory window of 1.3 V at an applied voltage of 5 V.