• Corrosion Science and Technology
• /
• v.6 no.2
• /
• pp.50-55
• /
• 2007

The smaller size and higher integration of advanced electronic package systems result in severe electrochemical reliability issues in microelectronic packaging due to higher electric field under high temperature and humidity conditions. Under these harsh conditions, electronic components respond to applied voltages by electrochemical ionization of metal and the formation of a filament, which leads to short-circuit failure of an electronic component, which is termed electrochemical migration. This work aims to evaluate electrochemical migration susceptibility of the pure Sn, Sn-3.5Ag, Sn-3.0Ag-0.5Cu solder alloys in $Na_{2}SO_{4}$. The water drop test was performed to understand the failure mechanism in a pad patterned solder alloy. The polarization test and anodic dissolution test were performed, and ionic species and concentration were analyzed. Ag and Cu additions increased the time to failure of Pb-free solder in 0.001 wt% $Na_{2}SO_{4}$ solution at room temperature and the dendrite was mainly composed of Sn regardless of the solders. In the case of SnAg solders, when Ag and Cu added to the solders, Ag and Cu improved the passivation behavior and pitting corrosion resistance and formed inert intermetallic compounds and thus the dissolution of Ag and Cu was suppressed; only Sn was dissolved. If ionic species is mainly Sn ion, dissolution content than cathodic deposition efficiency will affect the composition of the dendrite. Therefore, Ag and Cu additions improve the electrochemical migration resistance of SnAg and SnAgCu solders.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.4 s.37
• /
• pp.307-313
• /
• 2005

Electromigration behavior in the Sn96.5Ag3.0Cu0.5 solder lines was investigated and compared Sn96.5Ag3.0Cu0.5 with eutectic SnPb. Measurements were made for relevant parameters for electromigration of the solder, such as drift velocity, threshold current density, activation energy, as well as the product of diffusivity and effective charge number (DZ$\ast$). The threshold current density were measured to be $2.38{\times}10^4A/cm^2$ at $140^{\circ}C$ and the value represented the maximum current density which the SnAgCu solder can carry without electromigration damage at the stressing temperatures. The electromigration energy was measured to 0.56 eV in the temperature range of $110-160^{\circ}C$. The measured products of diffusivity and the effective charge number, DZ$\ast$ were $3.12{\times}10^{-10} cm^2/s$ at $110^{\circ}C$, $4.66{\times}10^{-10} cm^2/s$ at $125^{\circ}C$, $8.76{\times}10^{-10} cm^2/s$ at $140^{\circ}C$, $2.14{\times}10^{-9}cm^2/s$ at $160^{\circ}C$ SnPb solder existed incubation stage, while SnAgCu did not have incubation stage. It was thought that the diffusion mechanism of SnAgCu was different from that of SnPb.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.869-873
• /
• 2002

$Cu_2ZnSnS_4$ (CZTS) thin film is one of the candidate materials for the solar cell. It has an excellent optical absorption coefficient as well as appropriate 1.4~1.5eV band gap. The purpose of this study is replacing a half of high-cost Indium(In) atoms with low-cost Zinc(Zn) atoms and the other half with low-cost Tin(Sn) atoms in the lattice of CIS. In annealing process of thin films deposited with mixture target, the thin films were appeared the peeling. The resistivity was decreased. Thin films were deposited on ITO glass substrates using a compound target which were made by $CU_2S$, ZnS, $SnS_2$ powder were sintered in the atmosphere of Al at room temperature by rf magnetron sputtering We investigated potentialities of a low-cost material for the solar cell by measuring of thin film composition, the structure and optical properties. We could get an appropriate $Cu_2ZnSnS_4$ composition A (112) preferred orientation was appeared without annealing temperature as shown in the diffraction peaks of the CIS cells and was available for photovoltaic thin film materials. The band gap increased from 1.4 to 1.7eV as the composition ratio of Zn/Sn.. The optical absorption coefficient of the thin film was above $10^4cm^{-1}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.2
• /
• pp.81-85
• /
• 2017

$SnO_2/Ag/Nb_2O_5/SiO_2/SnO_2$ multilayer films were prepared on glass substrate by sequential using RF/DC magnetron sputtering at room temperature. The influence of top $SnO_2$ layer thickness on optical and electrical properties of the multilayer films was investigated. Experimentally measured results exhibit transmittances over 84.3 ~ 85.8% at 550 nm wavelength. As the top $SnO_2$ layer thickness increased from 40 to 55 nm, the sheet resistance (Rs) increased from 5.81 to $6.94{\Omega}/sq$. The Haacke's figure of merit (FOM) calculated for the samples with various $SnO_2$ layer thicknesses was a maximum at 45 nm ($35.3{\times}10^{-3}{\Omega}^{-1}$).

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.2
• /
• pp.43-48
• /
• 2017

Conductive $Sn_xO_y$ thin films were fabricated via RF reactive sputtering using SnO:Sn (80:20 mol%) composite target. The composite target was used to produce a chemically stable composition of $Sn_xO_y$ thin film while controlling structural defects by chemical reaction between tin and oxygen. During sputtering pressure, RF power, and substrate temperature were fixed, and oxygen partial pressure was varied from 0% to 12%. Annealing process was carried out at $300^{\circ}C$ for 1 hour in vacuum. Except $P_{O2}=0%$ sample, all samples showed the transmittance of 80~90% and amorphous phase before and after annealing. Electrically stable p-type $Sn_xO_y$ thin film with high transmittance was only obtained from the oxygen partial pressure at 12%. The carrier concentration and mobility for the $P_{O2}=12%$ were $6.36{\times}10^{18}cm^{-3}$ and $1.02cm^2V^{-1}s^{-1}$ respectively after annealing.

• Nano
• /
• v.13 no.11
• /
• pp.1850130.1-1850130.12
• /
• 2018

A novel strontium titanate/binary metal sulfide ($SrTiO_3/SnCoS_4$) heterostructure was synthesized by a simple two-step hydrothermal method. The visible-light-driven photocatalytic performance of $SrTiO_3/SnCoS_4$ composites was evaluated in the degradation of methyl orange (MO) under visible light irradiation. The photocatalytic performance of $SrTiO_3/SnCoS_4-5%$ is much higher than that of pure $SrTiO_3$, $SnCoS_4$, $SrTiO_3/SnS_2$ and $SrTiO_3/CoS_2$. The $SrTiO_3/SnCoS_4$ composite material with 5 wt.% of $SnCoS_4$ showed the highest photocatalytic efficiency for MO degradation, and the degradation rate could reach 95% after 140 min irradiation time. The enhanced photocatalytic activity was ascribed to not only the improvement of visible light absorption efficiency, but also the construction of a heterostructure which make it possible to effectively separate photoexcited electrons and holes in the two-phase interface.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.953-954
• /
• 2006

Ti-Cu-Ni-Sn quaternary amorphous alloys of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$ composition were prepared by mechanical alloying in a planetary high-energy ball-mill (AGO-2). The amorphization of all three alloys was found to set in after milling at 300rpm speed for 2h. A complete amorphization was observed for $Ti_{50}Cu_{32}Ni_{15}Sn_3$ and $Ti_{50}Cu_{25}Ni_{20}Sn_5$ after 30h and 20h of milling, respectively. Differential scanning calorimetry analyses revealed that the thermal stability increased in the order of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$.

• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.372-377
• /
• 2011

In this study, we reported the microstructure and properties of Ag-$SnO_2$ contact materials fabricated by a controlled milling process with subsequent consolidation. The milled powders were consolidated to bulk samples using a magnetic pulsed compaction process. The nano-scale $SnO_2$ phases were distributed homogeneously in the Ag matrix after the consolidation. The relative density and hardness of the Ag-$SnO_2$ contact materials were 95~96% and 89~131 Hv, respectively.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.11
• /
• pp.1967-1972
• /
• 2007

Photophysical properties of a newly-synthesized porphyrin derivative, trans-bis(ferrocene carboxylato)- (5,10,15,20-tetraphenylporphyrinato)tin(IV) [Sn(TPP)(FcCOO)2] were investigated by means of steady-state and fs-time resolved laser spectroscopic techniques, and compared with those of a standard molecule, trans-dichloro( 5,10,15,20-tetraphenyl-porphrinato)tin(IV) [Sn(TPP)Cl2]. The fluorescence spectrum of Sn(TPP)- (FcCOO)2 was observed to exhibit dual emission bands originating from the S2-state and the S1-state, which was greatly quenched as compared to those of Sn(TPP)Cl2. The fs-time resolved fluorescence and transient absorption spectroscopic measurements revealed that the fluorescence quenching is due to formation of the long-lived charge transfer state by intramolecular electron transfer from ferrocene to the S2-excited SnTPP in addition to the enhanced non-radiative deactivation processes.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.154.1-154
• /
• 2000