• 한국결정성장학회지
• /
• 제11권4호
• /
• pp.154-159
• /
• 2001

(Li,Al)$MnO_2(OH)_2$:Co 화합물의 합성르 수열법에 의해 행하였다. 출발원료는 $MnO_2$, LiOH.$H_2$O, $Co_3O_4$, $Al(OH)_3$이 사용되었으며, 단일상의 (Li,Al)$MnO_2(OH)_2$:Co 화합물을 얻을 수 있는 최적의 합성조건은 다음과 같았다. 반응온도 : $200^{\circ}C$ 반응시간 ; 3일간, 반응장치 ; 시이소형, 수열용매 ; 3M-KOH, (Li,Al)$MnO_2(OH)_2$:Co 의 원자비 = 1:2.1:2.5~2:0.5~1. 수열합성된 단사의 (Li,Al)$MnO_2(OH)_2$:Co 화합물은 결정성이 우수하였으며, 청색안료로써 천연 오수에 필적하는 발색효과를 나타내었다. 합성된 (Li,Al)$MnO_2(OH)_2$:Co 화합물의 형태는 육각 판싱이였으며, 입자의 크기는 0.5~1 $\mu\textrm{m}$의 미립자이였다.

• 한국분말재료학회지
• /
• 제25권4호
• /
• pp.296-301
• /
• 2018

In this study, an experiment is performed to recover the Li in $Li_2CO_3$ phase from the cathode active material NMC ($LiNiCoMnO_2$) in waste lithium ion batteries. Firstly, carbonation is performed to convert the LiNiO, LiCoO, and $Li_2MnO_3$ phases within the powder to $Li_2CO_3$ and NiO, CoO, and MnO. The carbonation for phase separation proceeds at a temperature range of $600^{\circ}C{\sim}800^{\circ}C$ in a $CO_2$ gas (300 cc/min) atmosphere. At $600{\sim}700^{\circ}C$, $Li_2CO_3$ and NiO, CoO, and MnO are not completely separated, while Li and other metallic compounds remain. At $800^{\circ}C$, we can confirm that LiNiO, LiCoO, and $Li_2MnO_3$ phases are separated into $Li_2CO_3$ and NiO, CoO, and MnO phases. After completing the phase separation, by using the solubility difference of $Li_2CO_3$ and NiO, CoO, and MnO, we set the ratio of solution (distilled water) to powder after carbonation as 30:1. Subsequently, water leaching is carried out. Then, the $Li_2CO_3$ within the solution melts and concentrates, while NiO, MnO, and CoO phases remain after filtering. Thus, $Li_2CO_3$ can be recovered.

• 공업화학
• /
• 제35권1호
• /
• pp.1-7
• /
• 2024

NO, CO 및 CH₄의 동시 산화를 위한 4 종의 Mn-M/Al₂O₃ (M = Cu, Fe, Co, Ce) 촉매를 제조하여 산화 활성을 비교하고, 동시 산화활성이 가장 높은 Mn-Cu/Al₂O₃ 촉매에 대해 XRD, Raman, XPS, O₂-TPD 분석을 수행하였다. XRD 분석 결과, Mn-Cu/Al₂O₃ 촉매에서는 담지된 Mn과 Cu는 복합산화물로 존재하였다. Raman 및 XPS 분석을 통해 Mn-Cu/Al₂O₃ 촉매는 Mn-O-Cu 결합의 형성 과정에서 Mn 이온과 Cu 이온 간의 전자 수수가 일어남을 알 수 있었다. XPS O 1s 및 O₂-TPD 분석을 통해 Mn-Cu/Al₂O₃ 촉매는 Mn/Al₂O₃ 촉매에 비해 이동성이 우수한 흡착산소 종이 증가했음을 알 수 있었다. Mn-Cu/Al₂O₃ 촉매의 높은 동시 산화 활성은 이러한 결과에 기인한다고 판단된다. Mn-Cu/Al₂O₃ 촉매 상에서 NO는 CO와 CH₄ 산화를 촉진하지만, NO 산화는 억제되었다. 이는 NO로부터 산화된 NO₂가 CO 및 CH₄의 산화제로 사용되었기 때문이라고 추측된다. CO와 CH₄의 산화 반응은 경쟁하지만 촉매 활성 온도가 다르기 때문에 그 효과가 두드러지지 않았다.

• 한국재료학회지
• /
• 제23권4호
• /
• pp.219-226
• /
• 2013

Activated magnetite ($Fe_3O_{4-{\delta}}$) has the capability of decomposing $CO_2$ proportional to the ${\delta}$-value at comparatively low temperature of $300^{\circ}C$. To enhance the $CO_2$ decomposition capability of $Fe_3O_{4-{\delta}}$, $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$ and $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$ were synthesized and then reacted with $CO_2$. $Fe_{1-x}Co_xC_2O_4{\cdot}2H_2O$ powders having Fe to Co mixing ratios of 9:1, 8:2, 7:3, 6:4, and 5:5 were synthesized by co-precipitation of $FeSO_4{\cdot}7H_2O$ and $CoSO_4{\cdot}7H_2O$ solutions with a $(NH_4)_2C_2O_4{\cdot}H_2O$ solution. The same method was used to synthesize $Fe_{1-x}Mn_xC_2O_4{\cdot}2H_2O$ powders having Fe to Mn mixing ratios of 9:1, 8:2, 7:3, 6:4, 5:5 with a $MnSO_4{\cdot}4H_2O$ solution. The thermal decomposition of synthesized $Fe_{1-x}Co_xC_2O_4{\cdot}2H_2O$ and $Fe_{1-x}Mn_xC_2O_4{\cdot}2H_2O$ was analyzed in an Ar atmosphere with TG/DTA. The synthesized powders were heat-treated for 3 hours in an Ar atmosphere at $450^{\circ}C$ to produce activated powders of $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$ and $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$. The activated powders were reacted with a mixed gas (Ar : 85 %, $CO_2$ : 15 %) at $300^{\circ}C$ for 12 hours. The exhaust gas was analyzed for $CO_2$ with a $CO_2$ gas analyzer. The decomposition of $CO_2$ was estimated by measuring $CO_2$ content in the exhaust gas after the reaction with $CO_2$. For $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$, the amount of $Mn^{2+}$ oxidized to $Mn^{3+}$ increased as x increased. The ${\delta}$ value and $CO_2$ decomposition efficiency decreased as x increased. When the ${\delta}$ value was below 0.641, $CO_2$ was not decomposed. For $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$, the ${\delta}$ value and $CO_2$ decomposition efficiency increased as x increased. At a ${\delta}$ value of 0.857, an active state was maintained even after 12 hours of reaction and the amount of decomposed $CO_2$ was $52.844cm^3$ per 1 g of $(Fe_{0.5}Co_{0.5})_3O_{4-{\delta}}$.

• 한국전기전자재료학회논문지
• /
• 제29권5호
• /
• pp.298-302
• /
• 2016

In this work, $LiMn_2O_4$ and $LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ cathode materials are mixed by some specific ratios to enhance the practical capacity, energy density and cycle performance of battery. At present, the most used cathode material in lithium ion batteries for EVs is spinel structure-type $LiMn_2O_4$. $LiMn_2O_4$ has advantages of high average voltage, excellent safety, environmental friendliness, and low cost. However, due to the low rechargeable capacity (120 mAh/g), it can not meet the requirement of high energy density for the EVs, resulting in limiting its development. The battery of $LiMn_2O_4-LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ (50:50 wt%) mixed cathode delivers a energy density of 483.5 mWh/g at a current rate of 1.0 C. The accumulated capacity from $1^{st}$ to 150th cycles was 18.1 Ah/g when the battery is cycled at a current rate of 1.0 C in voltage range of 3.2~4.3 V.

• 한국세라믹학회지
• /
• 제41권10호
• /
• pp.735-741
• /
• 2004

단순화한 연소법에 의해 합성한 $LiMn_{1.92}Co_{0.08}O_4$와 $LiNi_{0.7}Co_{0.3}O_2$의 혼합물의 전기화학적 성질을 알아보기 위하여, 30분 동안 milling하여 $LiMn_{1.92}Co_{0.08}O_4$-x wt$\%$ $LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41, and 47) 조성의 혼합물을 제조하였다. x=9 조성의 전극이 비교적 큰 초기방전용량(109.9mAh/g at 0.1C)과 좋은 싸이클 성능을 가지고 있었다. 싸이클링에 따른 혼합물 전극의 방전용량 감소는 주로 $LiNi_{0.7}Co_{0.3}O_2$의 퇴화에 기인한다고 생각된다. $LiNi_{0.7}Co_{0.3}O_2$의 퇴화는 $LiMn_{1.92}Co_{0.08}O_4$로부터 용해된 Mn이 $LiNi_{0.7}Co_{0.3}O_2$ 입자를 둘러싸서(coating) 일어나는 것으로 판단된다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.552-555
• /
• 1995

The magnetic properties of Mg-Mn ferrites were investigated in the composition range of $Mg_{a}Mn_{b}Fe_{c}O_{4\pm\delta}$ (a+b+c=3) with the addition of $Al_{2}O_{3}$. In $MgO-MnO-Fe_{2}O_{3}$ ternary system, the spinel single phase existed within the composition range of MgO-50 mol%, MnO-70 mol% and $Fe_{2}O_{3}-60\;mol%$. The saturation magnetic flux density increased with the increase of $Fe_{2}O_{3}$ content and showed the maximum at the stoichiometric composition of $(Mg,Mn)Fe_{2}O_{4}$. In $Mg_{x}Mn_{1-x}Fe_{2}O_{4}(x=0.2~0.8)$ system, the saturation magnetic flux density showed the maximum at $Mg_{0.2}Mn_{0.8}Fe_{2}O_{4}$. The addition of $Al_{2}O_{3}$ resulted in the decrease of saturation magnetic flux density but increased the electrical resistivity.

• 한국가스학회지
• /
• 제4권2호
• /
• pp.27-32
• /
• 2000

본 연구는 염화망간과 수산화나트륨을 이용하여 당량비에 따라 산화망간을 합성하였다. 합성된 산화망간의 결정구조와 비표면적을 측정하였으며, 이산화탄소의 분해 및 흡착에 대하여 연구하였다. 합성된 시료의 결정구조 분석결과 $Mn_3O_4$의 주피크가 나타났으며, 약간의 $MnO_2$와 $Mn_5O_8$도 관찰되었다. 또한 비표면적은 $13.92m^2/g{\~}32.33m^2/g$으로 측정되었다. 산화망간을 이용하여 $450^{\circ}C$에서 이산화탄소의 분해를 실시하였으며, 당량비 0.75에서 가장 잘 분해되었다. 이산화탄소의 화학흡착량을 측정한 결과 2.885cc/g${\~}$19.628cc/g으로 관찰되었으며, 이산화탄소의 흡착을 위한 최적당량비는 1.00이었다.

• 자원리싸이클링
• /
• 제11권1호
• /
• pp.3-8
• /
• 2002

고탄소페로망간을 중저탄소페로망간으로 제조하는 AOD공정에서 발생되는 분진은 약 90%가 $Mn_3$$O_4$이므로, 이를 이용하여 soft ferrite의 원료인 고순도 $Mn_3$$O_4$분말을 제조하기 위해서는 침출한 액의 Mn을 더욱 정제하여야 한다. 분진을 활성탄으로 배소하여 MnO로 환원시키고, 상온의 4N 염산수용액에 180g/L의 환원된 분진을 첨가하면 용액의 pH가 5이상이 되고 Fe와 Si가 침전으로 제거된 약 10%의 망간침출액이 얻어진다. Mn의 농도가 약 15000 ppm이 되도록 희석한 $70^{\circ}C$의 침출액에 F의 농도가 3000ppm이 되도록 $NH_4$F를 첨가하면 Ca가 침전하여 약14 ppm이하로 제거된다. Ca를 침전시킨 상징액에(NH$ 1.5M_4$)$_2$$CO_3$수용액을 2L/min으로 Mn의 당량만큼 첨가하면 미립의 고순도 $MnCO_3$가 침전한다. 침전을 여과하고 건조한 후에 $1000^{\circ}C$에서 2 시간 소성하면 median size가 $8.2mu$m인$ Mn_3$O$_4$를 얻을 수 있다. 제조된 산물은 99%이상의 순도로 soft ferrite용 Mn$O_3$$_4$분말의 규격을 만족한다.

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1174-1179
• /
• 2001

상온용 NTC 서미스터로는 주로 Mn-Co-Ni 산화물계가 사용된다. 본 연구에서는 Mn-Co-Ni 산화물게 분말을 이용하여 상온에서 가압성형하여 125$0^{\circ}C$에서 3시간 동안 소결한 후, 100$0^{\circ}C$에서 3시간 유지하여 소결체를 제작하였다. 다양한 조성으로 제조된 서미스터의 전기적 특성을 평가한 결과, MCN622(Mn$_3$O$_4$60wt%, 20wt%, NiO 20wt%)는 가장 낮은 비저항과 상대적으로 높은 B 정수를 나타내었고, MCN721(Mn$_3$O$_4$70wt%, Co$_3$O$_4$20wt%, NiO 10 wt%)는 다는 조성들에 비해 현저히 높은 비저항값을 나타내었다. 또한, 각 조성들의 경시변화는 $\pm$2%이내로서 비교적 안정한 특성을 나타냈다.