• Journal of Powder Materials
• /
• v.16 no.5
• /
• pp.316-325
• /
• 2009

Fe based (Fe$_{68.2}$C$_{5.9}$Si$_{3.5}$B$_{6.7}$P$_{9.6}$Cr$_{2.1}$Mo$_{2.0}$Al$_{2.0}$) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The experiment results show that the as-prepared Fe amorphous powders less than 90 $\mu$m in size has a fully amorphous phase and its weight fraction was about 73.7%. The as-atomized amorphous Fe powders had a complete spherical shape with very clean surface. Differential scanning calorimetric results of the as-atomized Fe powders less than 90 $\mu$m showed that the glass transition, T$_g$, onset crystallization, T$_x$, and super-cooled liquid range $\Delta$T=T$_x$-T$_g$ were 512, 548 and 36$^{\circ}C$, respectively. Fe amorphous powders were mixed and deformed well with 10 wt.% Cu by using AGO-2 high energy ball mill under 500 rpm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.3
• /
• pp.133-138
• /
• 2017

We evaluated the structural, electrical and optical properties of tungsten (W)-doped $Ge_8Sb_2Te_{11}$ thin films. In a previous work, GeSbTe alloys were doped with different materials in an attempt to improve thermal stability. 200 mm thick $Ge_8Sb_2Te_{11}$ and W-doped $Ge_8Sb_2Te_{11}$ films were deposited on p-type Si (100) and glass substrates using a magnetron co-sputtering system at room temperature. The fabricated films were annealed in a furnace in the $0{\sim}400^{\circ}C$ temperature range. The structural properties were analyzed using X-ray diffraction (X'pert PRO, Phillips). The results showed increased crystallization temperature ($T_c$) leading to thermal stability in the amorphous state. The optical properties were analyzed using an UV-Vis-IR spectrophotometer (Shimadzu, U-3501, range : 300~3,000 nm). The results showed an increase in the crystalline material optical energy band gap ($E_{op}$) and an increase in the $E_{op}$ difference (${\Delta}E_{op}$). This is a good effect to reduce memory device noise. The electrical properties were analyzed using a 4-point probe (CNT-series). This showed increased sheet resistance ($R_s$), which reduces programming current in the memory device.

• Korean Journal of Materials Research
• /
• v.15 no.2
• /
• pp.89-92
• /
• 2005

The induction melting was employed to prepare Nb-doped $CoSb_3$ skutterudites and their thermoelectric properties were investigated. Single phase $\delta-CoSb_3$ was successfully obtained by induction melting and subsequent annealing at $400^{\circ}C$ for 2 hrs in vacuum. The positive signs of Seebeck coefficients for all the specimens revealed that Nb atoms acted as p-type dopants by substituting Co atoms. Electrical conductivity decreased and then increased with increasing temperature, indicating mixed conduction behavior. Electrical conductivity increased by Nb doping, and it was saturated at high temperature. Maximum value of the thermoelectric power factor was shifted to higher temperature with increasing the amount of Nb doping, mainly originated from the high Seebeck coefficient around mixed conduction temperature and high electrical conductivity.

• Journal of the Korean Ceramic Society
• /
• v.45 no.5
• /
• pp.290-296
• /
• 2008

$AB'_{0.5}B"_{0.5}O_3$ type complex perovskite structures which have been reported as proton conductors over $600^{\circ}C$ were studied. The $AB'_{0.5}B"_{0.5}O_3$ type complex perovskite structure is known to be more easily synthesized and has better stability than normal $ABO_3$ perovskite structure. And it is stable at about $800^{\circ}C$ in the $CO_2$ atmosphere, whereas the $BaCeO_3$ perovskite is easily decomposed into carbonate. In addition, this $AB'_{0.5}B"_{0.5}O_3$ type complex perovskite structure could simply produce oxygen vacancies within their structure not by introducing additional doping oxides but by just controling the molar ratio of $B'^{+3}$ and $B"^{+5}$ metal ions in the B site. Hence it is easy to design the structure which shows highly sensitive electrical conductivity to humidity. In this study, the single phase boundary of $BaR_{0.5+x}Ta_{0.5-x}O_{3-{\delta}}$(R = rare earth) complex perovskite structures and it's phase stability were investigated with changes in composition, x. And the humidity dependance of electrical conductivity at different $P_{H2O}$ conditions was investigated.

• Journal of Advanced Marine Engineering and Technology
• /
• v.32 no.1
• /
• pp.82-93
• /
• 2008

The flowfield behind two cylinders and flow-induced noise generated from the cylinders in various arrangement are numerically investigated based on the finite difference lattice Boltzmann model with 21 velocity bits. which is introduced a flexible specific heat ${\gamma}$ to simulate diatomic gases like air. In an isolated cylinder with two type of mesh. some flow parameters such as Strouhal number $S_t$ and acoustic pressure ${\Delta}p$ simulated from the solution are given and quantitatively compared with those provided the previous works. The effects of the center-to-center pitch ratio $L_{cc}/d=2.0$ in staggered circular cylinders as shown in Fig. 1 and angles of incidence ${\alpha}=30^{\circ}(T_{cc}/d=0.5)$, $45^{\circ}(T_{cc}/d =0.707)$ and $60^{\circ}\;(T_{cc}/d=0.866)$, respectively, are studied. Our analysis focuses on the small-scale instabilities of vortex shedding, which occurs in staggered arrangement. With the results of drag $C_d$ and lift $C_l$ coefficients and vorticity contours. the mechanisms of the interference phenomenon and its interaction with the two-dimensional vortical structures are present in the flowfields under $Re\;{\le}\;200$. The results show that we successively capture very small pressure fluctuations, with the same frequency of vortex shedding, much smaller than the whole pressure fluctuation around pairs of circular cylinders. The upstream cylinder behaves like an isolated single cylinder, while the downstream one experiences wake-induced flutter. It is expected that, therefore, the relative position of the downstream cylinder has significant effects on the flow-induce noise, hydrodynamic force and vortex shedding characteristics of the cylinders.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.340-340
• /
• 2002

In an effort to develop alternative single buffer layer technology for YBa$_2$Cu$_3$O$_{7-{\delta}}$ (YBCO) coated conductors, we have investigated both LaMnO$_3$, (LMO) and La$_2$Zr$_2$O$_{7}$ (LZO) as potential buffer layers. High-quality LMO films were grown directly on textured Ni and Ni-W (3%) substrates using rf magnetron sputtering. Highly textured LZO buffers were grown on textured Ni substrates using sol-gel alkoxide processing route. YBCO films were then grown on both LMO and LZO buffers using pulsed laser deposition. Detailed X-ray studies have shown that YBCO films were grown on both LMO and LZO layers with a single epitaxial orientation. A high J$_{c}$ of over 1 MA/cm$^2$ at 77 K and self-field was obtained on YBCO films grown on both LMO-buffered Ni or Ni-W substrates, and also on LZO-buffered Ni substrates. We have identified LaMnO$_3$ as a good diffusion barrier layer for Ni and it also provides a good template for growing high current density YBCO films. Similarly we have also demonstrated the growth of high J$_{c}$ YBCO films on all solution buffers. We will discuss in detail about our buffer deposition processes. processes.s.s.s.s.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.6C
• /
• pp.277-285
• /
• 2009

A series of undrained cyclic triaxial tests were carried out to investigate the cyclic shear stress strength characteristics of sands with respect to the silt content. Silty sand was collected around the basin of Nak-Dong River and remolded in laboratory with the range of silt content 0~50% in sand located. As results, with the change of silt content cyclic shear stress ratio (CSR) at N=10 showed the maximum value at 5% and the minimum at 20% in all relative density. The development tendency of the pore water pressure analyzed by the relationship cyclic ratio and pore water pressure ratio is unrelated the change of CSR varying silt content. Comparing the results of the void ratio and skeleton void ratio after consolidation, CSR varying silt content was much affected by skeleton void ratio which is known to affect shear behavior of silty sand.

• Journal of Pharmaceutical Investigation
• /
• v.31 no.4
• /
• pp.289-295
• /
• 2001

Carvedilol is an antihypertensive and antianginal compound that combines nonselective beta-adrenoceptor blocking and vasodilation properties and is devoid of intrinsic sympathomimetic activity. The purpose of the present study was to evaluate the bioequivalence of two carvedilol tablets, $Dilatrend^{TM}$ (Chong Kun Dang Pharmaceutical Co., Ltd.) and $Carvelol^{TM}$ (Dae Won Pharmaceutical Co., Ltd.), according to the prior and revised guidelines of Korea Food and Drug Administration (KFDA). The carvedilol release from the two carvedilol tablets in vitro was tested using KP VII Apparatus II method with various different kinds of dissolution media (pH 1.2, 4.0, 6.8 buffer solution, water and blend of PSB80 into water). Eighteen normal male volunteers, $24.22{\pm}1.86$ years in age and $64.81{\pm}4.56\;kg$ in body weight, were divided into two groups and a randomized $2{\times}2$ cross-over study was employed. After one tablet containing 25 mg of carvedilol was orally administered, blood was taken at predetermined time intervals and the concentrations of carvedilol in serum were determined using HPLC method with fluorescence detector. The dissolution profiles of two carvedilol tablets were very similar at all dissolution media. Besides, the pharmacokinetic parameters such as $AUC_t$, $C_{max}$ and $T_{max}$ were calculated and ANOVA test was utilized for the statistical analysis of the parameters using non-transformed and logarithmically transformed $AUC_t$ and $C_{max}$. The results showed that the differences in $AUC_t$, $C_{max}$ and $T_{max}$ between two tablets based on the $Dilatrend^{TM}$ were 2.23%, -2.00% and 0.00%, respectively. Minimum detectable differences $({\Delta})$ at ${\alpha}=0.05$ and $1-{\beta}=0.8$ were less than 20% (e.g., 13.55% and 17.61% for $AUC_t$ and $C_{max}$, respectively). The powers $(l-{\beta})$ at ${\alpha}=0.05$, ${\Delta}=0.2$ for $AUC_t$ and $C_{max}$ were 98.08% and 88.81%, respectively. The 90% confidence intervals were within ${\pm}20%$ (e.g., $-5.69{\sim}10.16$ and $-12.30{\sim}8.30$ for $AUC_t$ and $C_{max}$, respectively). There were no sequence effect between two tablets in logarithmically transformed $AUC_t$ and $C_{max}$. The 90% confidence intervals using logarithmically transformed were within the acceptance range of log(0.8) to log(1.25) (e.g., $0.95{\sim}1.11$ and $0.89{\sim}1.09$ for $AUC_t$ and $C_{max}$, respectively). Two parameters met the criteria of prior and revised KFDA guideline for bioequivalence, indicating that $Carvelol^{TM}$ tablet is bioequivalent to $Dilatrend^{TM}$ tablet.

• Geophysics and Geophysical Exploration
• /
• v.9 no.1
• /
• pp.50-59
• /
• 2006

The risk of fault reactivation in the Gippsland Basin was calculated using the FAST (Fault Analysis Seal Technology) technique, which determines fault reactivation risk by estimating the increase in pore pressure required to cause reactivation within the present-day stress field. The stress regime in the Gippsland Basin is on the boundary between strike-slip and reverse faulting: maximum horizontal stress $({\sim}\;40.5\;Mpa/km)$ > vertical stress (21 Mpa/km) ${\sim}$ minimum horizontal stress (20 MPa/km). Pore pressure is hydrostatic above the Campanian Volcanics of the Golden Beach Subgroup. The NW-SE maximum horizontal stress orientation $(139^{\circ}N)$ determined herein is broadly consistent with previous estimates, and verifies a NW-SE maximum horizontal stress orientation in the Gippsland Basin. Fault reactivation risk in the Gippsland Basin was calculated using two fault strength scenarios; cohesionless faults $(C=0;{\mu}=0.65)$ and healed faults $(C=5.4;\;{\mu}=0.78)$. The orientations of faults with relatively high and relatively low reactivation potential are almost identical for healed and cohesionless fault strength scenarios. High-angle faults striking NE-SW are unlikely to reactivate in the current stress regime. High-angle faults oriented SSE-NNW and ENE-WSW have the highest fault reactivation risk. Additionally, low-angle faults (thrust faults) striking NE-SW have a relatively high risk of reactivation. The highest reactivation risk for optimally oriented faults corresponds to an estimated pore pressure increase (Delta-P) of 3.8 MPa $({\sim}548\;psi)$ for cohesionless faults and 15.6 MPa $({\sim}2262\;psi)$ for healed faults. The absolute values of pore pressure increase obtained from fault reactivation analysis presented in this paper are subject to large errors because of uncertainties in the geomechanical model (in situ stress and rock strength data). In particular, the maximum horizontal stress magnitude and fault strength data are poorly constrained. Therefore, fault reactivation analysis cannot be used to directly measure the maximum allowable pore pressure increase within a reservoir. We argue that fault reactivation analysis of this type can only be used for assessing the relative risk of fault reactivation and not to determine the maximum allowable pore pressure increase a fault can withstand prior to reactivation.

• Journal of dental hygiene science
• /
• v.14 no.2
• /
• pp.191-197
• /
• 2014

The purpose of this study was to evaluate the tooth whitening efficacy of 2.9% hydrogen peroxide strip with primer gel of alkaline condition and containing metallic salts as catalyst in-vitro. Hydroxyapatite (HAP) disk was made by compressing and sintering 0.3 g of mixture of HAP powder and polyvinyl alcohol. This HAP disk was stained using modified Stookey's methods. Main bleaching materials were 2.9% hydrogen peroxide strips and the primer gel containing metallic salts as catalyst and pH controller. Stained HAP disks were allocated to each control or experimental groups by color grade. Stained HAP disks were treated for 30 minutes in $37^{\circ}C/80%$ incubator for wetting, then each primer gel according to control or each test group was spread and strips were attached. After 30 minutes for each group strips were detached and HAP disks were washed, dried then color was measured by colorimeter. Efficacy was evaluated by comparing ${\Delta}L$ values of HAP disks at baseline and after treated. Among some kinds of metallic salts for as catalyst, ferric chloride showed best improvement of efficacy and it was statistically significant (p<0.05) compared to control group. Evaluating whitening efficacy according to various pH of primer, efficacy using primer of alkaline condition was increased significantly (p<0.05) compared to control and primers of acidic or neutral conditions. Evaluating whitening efficacy for time course, efficacy of test group for 30 minutes was similar to that of control for 120 minutes. It can be concluded that 2.9% hydrogen peroxide strips using with primer of alkaline condition and containing ferric chloride showed significantly increased whitening efficacy compared to the case of strips only.