• 한국재료학회지
• /
• 제8권7호
• /
• pp.584-590
• /
• 1998

$(Fe_{0.98}Mn_{0.02})_xSi_2(x{\leq$}1) 조성으로, 용융법으로 제조한 $\alpha$-$Fe_2Si_5$상의 잉곳을 730~85$0^{\circ}C$에서 4~20시간 열처리하거나, 기계적 합금화로 제조한 $\varepsilon$-FeSi과 Si상으로 구성된 분말을 760~85$0^{\circ}C$에서 10분간 가압통전소결하므로써 $\beta$-$FeSi_2$기지상에 Si이 분산된 미세조직을 얻을 수 있었다. 조성, 열처리 온도와 소결 온도에 따라 Si 분상의 크기와 간격이 각기 0.05~0.27$\mu\textrm{m}$와 0.2~0.6$\mu\textrm{m}$ 범위에서 변화하였다. 이와 같은 Si 분산상에 의해 $\beta$-$FeSi_2$의 격자 열전도도가 감소되어 성능지수가 향상될 수 있을 것으로 기대된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 추계학술대회 논문집
• /
• pp.5-7
• /
• 1988

Effect of isothermal aging on the crystallization of $Fe_{78}B_{13}Si_{9}$ metallic glass has been investigated by electrical resistivity, X-ray measurements, bending test, thermal analysis and transmission electron microscopy. Amorphous $Fe_{78}B_{13}Si_{9}$ alloy was annealed isothermally for 5 to 1200 mon. between 300 C and 540 C. It has been found that close relation between relative resistivity and X-ray diffraction pattern showed. The crystalline peak of $\alpha$-(Fe, Si) and Fe$_2$B are detected by X-ray experiment. The crystalline phases observed by TEM show $\alpha$-(Fe, Si) and Fe$_3$B with dendritic and cylindrical morphology, respectively. It has been also found that the embrittleness of aged samples rapidly increased with the crystallization and was shown before the crystallization.th the crystallization and was shown before the crystallization.

• 한국자기학회지
• /
• 제5권4호
• /
• pp.281-286
• /
• 1995

Hexaferrite $Ba_{0.25}Sr_{0.75}Fe_{12}O_{19}$에 $SiO_{2}$를 첨가한 쉬트자석의 자기적 성질의 변화를 연구하기 위해 X-선 회절 실험, 뫼스바우어 분광실험, 자기모멘트 측정실험 등을 하였다. 쉬트자석은 Dr. Blade 방법에 의해 제조되었고, 결정구조는 마그네토플럼바이트 M-type 육방결정구조이다. 첨가제 농도에 따른 격자상수의 변화는 거의 없으나, $SiO_{2}$가 2.0 wt.% 이상부터 ${\alpha}-Fe_{2}O_{3}$ 의 상이 나타나기 시작했다. 이성질체 이동값은 Fe이온들이 3가 임을 나타낸다. $SiO_{2}$의 증가에 따라 Curie 온도는 감소함을 보였다. 이것은 $Si^{4+}$가 12k-site $Fe^{3+}$의 자리를 차지함으로써 Fe-O-Fe의 초교환상호작용에 의한 원자간 거리와 양이온 사이의 각이 변함에 따른 것이다. ${\alpha}-Fe_{2}O_{3}$의 상은 $Si^{4+}$가 12k-site $Fe^{3+}$의 자리를 차지함으로 치환된 $Fe^{3+}$에 의해 나타난 것이다. 자기모멘트측정으로 부터 $SiO_{2}$를 첨가한 $Ba_{0.25}Sr_{0.75}Fe_{12}O_{19}$ 쉬트자석은 보자력 $H_{c}$, 포화자화 $M_{s}$, 잔류자화 $M_{r}$이 양이온 치환보다는 미세구조변화에 더 의존함을 알았다.

• Applied Microscopy
• /
• 제25권3호
• /
• pp.90-98
• /
• 1995

In the Fe-Si system, a mixture of a($Fe_{2}Si_5$) - and ${\epsilon}$(FeSi)-composition powders was sintered and heat-treated subsequently at various temperatures and time to get thermoelectric ${\beta}$-phase($FeSi_2$) compacts. The different transformational sequences depending on the heat treating temperature were found through the investigation into phase transformation and microstructural development. That is, a rapid eutectoid decomposition of ${\alpha}{\to}{\beta}+Si$ occurred together with a accompanying slow reaction between the dispersed Si formed by above decomposition and the preexisted ${\epsilon}$ phase at temperatures below $830^{\circ}C$. The unreacted Si and the micropores formed due to the density change upon the transformation coarsened as heat treating time elapsed. At temperatures above $880^{\circ}C$, however, transformation was proceeded by a peritectoid reaction of ${\alpha}+{\epsilon}{\to}{\beta}$. It took at least 200min. to achieve 90% volume fracion of transformed ${\beta}$ phase, and the growth of micro-pores was also observed in this transformational sequence with prolonged heat treating time.

• 한국주조공학회지
• /
• 제30권2호
• /
• pp.76-82
• /
• 2010

Effect of reaction time and sludge formation on the thickness of die soldering reaction layer has been studied in Al-9Si-0.3Mg casting alloy. Ternary ${\alpha}_{bcc}-Al_8Fe_2Si$ and ${\alpha}_{hcp}-Al_8Fe_2Si$ intermetallic compounds formed at the interface of SKD61 tool steel by interaction diffusion of Al, Fe and Si atoms after 0.5hr and 6hr immersion time, respectively. Binary ${\eta}-Fe_2Al_5$ additionally formed at the interface of SKD61 tool steel after 10hr immersion time. Thickness of soldering reaction layer in die surface increased as immersion time increased from 0.5hr to 24hr. Sludge formation was ascertained in the samples which were immersed in the melts more than 10hr. Reaction of die soldering after sludge formation was more accelerated than that of before sludge formation due to a decrease in Fe content, followed by higher diffusion rate of Al in the melt by sludge formation.

• 한국주조공학회지
• /
• 제33권2호
• /
• pp.55-62
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-4wt%Mg-0.9wt%Si system alloy has been studied. According to the analysis of cooling curve for Al-4wt%Mg-0.9wt%Si-0.3wt%Fe-0.3/0.5wt%Mn alloy, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}-Al_5FeSi$ phases crystallized above eutectic temperature of $Mg_2Si$. Therefore, these phases affected both the fluidity and shrinkage behaviors of the alloy during solidification. As Fe and Mn contents of Al-4wt%Mg-0.9wt%Si system alloy increased from 0.1 wt% to 0.4 wt% and from 0.3 wt% to 0.5 wt% respectively, the fluidity of the alloy decreased by 26% and 33%. When Fe content of the alloy increased from 0.1 wt% to 0.4 wt%, 23% decrease of macro shrinkage and 19% increase of micro shrinkage appeared. Similarly, Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, 11% decrease of macro shrinkage and 14% increase of micro shrinkage appeared. Judging from the castability of the alloy, Al-4wt%Mg-0.9wt%Si alloy with low content of Fe and Mn, 0.1 wt% Fe and 0.3 wt% Mn, is recommendable.

• Advanced Composite Materials
• /
• 제18권4호
• /
• pp.339-350
• /
• 2009

Al-Fe-V-Si alloys reinforced with SiC particles were prepared by multi-layer spray deposition technique. Both microstructures and mechanical properties including hardness and tensile properties development during hot exposure process of Al-8.5Fe-1.3V-1.7Si, Al-8.5Fe-1.3V-1.7Si/15 vol% $SiC_P$ and Al-10.0Fe-1.3V-2Si/15 vol% $SiC_P$ were investigated. The experimental results showed that an amorphous interface of about 3 nm in thickness formed between SiC particles and the matrix. SiC particles injected silicon into the matrix; thus an elevated silicon concentration was found around $\alpha-Al_{12}(Fe,\;V)_3Si$ dispersoids, which subsequently inhibited the coarsening and decomposition of $\alpha-Al_{12}(Fe,\;V)_3Si$ dispersoids and enhanced the thermostability of the alloy matrix. Moreover, the thermostability of microstructure and mechanical properties of Al-10.0Fe-1.3V-2Si/15 vol% $SiC_P$ are of higher quality than those of Al-8.5Fe-1.3V-1.7Si/15 vol% $SiC_P$.

• 한국재료학회지
• /
• 제14권3호
• /
• pp.218-223
• /
• 2004

P-type $\beta$-FeSi$_2$ with a nominal composition of $Fe_{0.92}Mn_{0.08}Si_2$ powders has been produced by mechanical alloying process. As-milled powders were spray dried and consolidated by atmospheric plasma thermal spraying as a rapid sintering process. As-milled powders were of metastable state and fully transformed to $\beta$-$FeSi_2$ phase by subsequent isothermal annealing. However, as-thermal sprayed $Fe_{0.92}Mn_{0.08}Si_2$ consisted of untransformed mixture of $\alpha$-$Fe_2Si_{5}$ and $\varepsilon$-FeSi phases. Isothermal annealing has been carried out to induce transformation to the thermoelectric semiconducting $\beta$-$FeSi_2$ phase. Isothermal annealing at $845^{\circ}C$ in vacuum gradually led to the thermoelectric semiconducting $\beta$-$FeSi_2$ phase transformation, but some residual metallic $\alpha$ and $\varepsilon$ phases were unavoidable even after prolonged annealing. Thermoelectric properties of $\beta$-$FeSi_2$ materials before and after isothermal annealing were evaluated. Seebeck coefficient increased and electric conductivity decreased with increasing annealing time due to the phase transition from metallic phases to semiconducting phases. Thermoelectric properties showed gradual increment, but overall properties appeared to be inferior to those of vacuum hot pressed specimens.

• 한국분말재료학회지
• /
• 제1권1호
• /
• pp.66-71
• /
• 1994

Optical microstructures and mechanical properties of Na gas atomized Al-20Si-5Fe alloying powder and its hot extrudates were studied on 3 different types of powder size distribution. This powder showed the size distribution of 10~210 $\mu\textrm{m}$. Also the microstructures of $\alpha$-Al, primary and eutectic Si and needle shaped intermetallic compounds were observed by optical microscope. These needle shaped intermetallic compounds were identified as ${\delta}Al_4FeSi_2$- by XRD and EDX analysis. The ultimate tensile strength(UTS) of these alloy extrudates was increased from 324 to 390 MPa with decreasing powder size range from 120~210 $\mu\textrm{m}$ to 10~64 $\mu\textrm{m}$. A value of Micro-vic-kers hardness was simillar to the result of UTS. These extrudates showed better wear resistance than those of Al-20Si-2X(X : Ni, Cr, Zr), although they are insensitive to the size distribution. These results indicate that the presentation of ${\delta}Al_4FeSi_2$ intermetallic compounds contributed to the wear resistance improvement.

• 한국자기학회지
• /
• 제3권2호
• /
• pp.130-134
• /
• 1993

초급냉법중 단롤법으로 제작한 $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ 비정질 합금을 $400~650^{\circ}C$에서 열처리하여 자기적 특성을 조사하였다. $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ 비정질 합금의 최적 열처리 온도는 $550^{\circ}C$이며, 이온도에서 열처 리된 시료의 상대 투자율과 항자력은 1 kHz에서 각각 $1.1{\times}10^{4}$, 0.22 Oe이다. $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$의 경우는 $600^{\circ}C$에서 열처리 했을때 상대 투자율과 항자력이 각각 $1.0{\times}10^{4}$, 0.19 Oe로 가장 우수한 연자성 특성을 보였다. X-선 실험결과, 이러한 연자성 특성의 향상은 $\alpha$-Fe(Si) 결정립의 형성에 의한 것임을 확인 할 수 있었으며, 강자성 공명 실험에 의하면 최적 열처리 조건은 공명 흡수선의 반치폭이 급격히 증가하기 직전의 온도임을 알 수 있었다.