Abstract
The magnetic properties of the amorphous $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ alloys, fabricated by a single roll rapid quenching technique and annealed at $400~650^{\circ}C$, have been investigated. The optimum annealing temperature is $550^{\circ}C$ for the amorphous $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy. The properties of the nanocrystalline $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy show the relative permeability of $1.1{\times}10^{4}$ and the coercive force of 0.22 Oe at 1 kHz. When annealed at $600^{\circ}C$, the nanocrystalline $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$ alloy shows the relative permeability of $1.0{\times}10^{4}$ and the coercive force of 0.19 Oe at 1 kHz. From the X-ray measurement, it is found that the remarkably improved soft magnetic properties are the effect of the formation of $\alpha$-Fe(Si) grain. By the results of FMR exper-imeIlt, the optimum annealing condition is just below temperature which the peak-to-peak line width of FMR spectrum increase rapidly.
초급냉법중 단롤법으로 제작한 $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ 비정질 합금을 $400~650^{\circ}C$에서 열처리하여 자기적 특성을 조사하였다. $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ 비정질 합금의 최적 열처리 온도는 $550^{\circ}C$이며, 이온도에서 열처 리된 시료의 상대 투자율과 항자력은 1 kHz에서 각각 $1.1{\times}10^{4}$, 0.22 Oe이다. $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$의 경우는 $600^{\circ}C$에서 열처리 했을때 상대 투자율과 항자력이 각각 $1.0{\times}10^{4}$, 0.19 Oe로 가장 우수한 연자성 특성을 보였다. X-선 실험결과, 이러한 연자성 특성의 향상은 $\alpha$-Fe(Si) 결정립의 형성에 의한 것임을 확인 할 수 있었으며, 강자성 공명 실험에 의하면 최적 열처리 조건은 공명 흡수선의 반치폭이 급격히 증가하기 직전의 온도임을 알 수 있었다.