• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.524-528
• /
• 2007

The results of evaluating steel corrosion in concrete containing chloride content of various levels indicated that the more chloride content in concrete leads to the lower potential and higher corrosion current density. However, the open circuit potential of steel varied with time and exposure condition, and the corelation between the open circuit potential and corrosion current density was not obvious. In order to determine the critical threshold content of chloride of steel corrosion in concrete, the concept of average corrosion current density was employed. The range of critical chloride content in portland cement concretes was about $1.56{\sim}1.77%$($Cl^-$, %, wt of cement content) along with water-cement ratio, and higher water-cement ratio resulted in reduction in critical threshold chloride content.

• Advances in concrete construction
• /
• v.11 no.4
• /
• pp.285-298
• /
• 2021

This study focused on experimental evaluation of mechanical properties of pervious concrete mixtures with the aim of achieving higher values of strength while considering the associated costs. The effectiveness of key parameters, including cement content, water to cement ratio (W/C), aggregate to cement ratio (A/C), and sand replacement was statistically analyzed using paired-samples t-test, Taguchi method and one-way ANOVA. Taguchi analysis determined that in general, the role of W/C was more significant in increasing strength, both compressive and flexural, than cement content and A/C. It was found that increase in replacing percent of coarse aggregate with sand could undermine specimens to percolate water, though one-way ANOVA analysis determined statistically significant increases in values of strength of mixtures. Cost analysis revealed that higher strengths did not necessarily correspond to higher costs; in addition, increasing the cement content was not an appropriate scenario to optimize both strength and cost. In order to obtain the optimal values, response surface method (RSM) was carried out. RSM optimization helped to find out that W/C of 0.40, A/C of 4.0, cement content of about 330 kg/m3 and replacing about 12% of coarse aggregate with sand could result in the best values for strength and cost while maintaining adequate permeability.

• Economic and Environmental Geology
• /
• v.45 no.3
• /
• pp.307-315
• /
• 2012

In this paper, a laboratory model test was conducted to evaluate grouting efficiency of ordinary portland cement(OPC) and micro cement used in MIS(Micro-Injection Process System). For this research, a injection equipment was developed for pressure permeation which can evenly simulate various grouting tests in a laboratory and suggested a standard for the production of the test specimen. Using the injection device, the laboratory injection tests of grouts were prepared with water/cement ratio of 1:1, 2:1, 3:1, 4:1, and 5:1. The analysis of injection test for pressure permeation showed that the efficiency of injection increases linearly as the water/cement ratio increases. Comparison of efficiency of the injection indicates that MIS with a relatively smaller average diameter shows more efficient injection than the OPC. In the low ratio of water/cement as 2:1~1:1, the injection efficiency of OPC was especially poor. Also, a nonlinear grout volume-injection time is represented by a hyperbolic model and grout volume predicted by hyperbolic model was compared with the value measured. From the comparison, it shows that the hyperbolic model has the potential of evaluating the efficiency of grouting.

• Journal of Forest and Environmental Science
• /
• v.37 no.1
• /
• pp.79-89
• /
• 2021

Cement bonded boards of 10 mm in thickness were produced from the mixture of Gmelina arborea sawdust and corn cob particles. The strength and dimensional stability of cement bonded composites produced from these two mixtures were examined. A total of thirty experimental boards were produced at density level of 1,000 kg/㎥ with cement to fibre ratio of 2.5:1 and 3:1 and five (5) blending proportions of G. arborea sawdust to corn cob particles of 100:0; 75:25; 50:50; 25:75 and 100:0. The effect of the cement to fibre ratio and blending proportion on the Water Absorption (WA), Thickness Swelling (TS), Modulus of Rupture (MOR), and Modulus of Elasticity (MOE) were determined. The result indicates that as the mixing ratio of cement to fibre and blending proportion of maize cob (75%) to G. arborea (25%) increased, the thickness swelling, water absorption decreased, whereas the MOR and MOE increased. It also shows that most dimensionally stable and flexural strength boards were produced at the highest level of mixing ratios (3:1) and blending proportion of G. arborea to corn cob 25:75. However, the analysis of variance shows that TS and WA were significantly different, whereas, MOE and MOR were not significantly affected by mixing ratios and blending proportions. Finding of this study has shown that maize cob particles are suitable for cement bonded board production.

• Journal of the Korea Concrete Institute
• /
• v.14 no.5
• /
• pp.789-795
• /
• 2002

To evaluate the bind rate and behavior of two types chloride ion-one is the chloride ion added in mixture when un-washed sea sand is used as fine aggregate, one is the chloride ion admitted in the new version of concrete standard specification, pore solution extracted in cement paste were analyzed. The results are follow. 1 As passing the time, the chloride concentration in the pore solution decreases with the Increase in the chloride content absorbed by the hydrate products. As compared with chloride contents in mixing water, the bound ratio of chloride at 49 days is 64∼90％. 2. The bound ratio of chloride in cement paste considering evaporable water as pore solution is obtained. In case of Pl∼P3(added chloride content wt of cement 0.046∼0.16 ％), the bound ratio of chloride is 91.8∼93.5 ％. P4(added chloride wt of cement 0.3％) is 89.1％, but P5(added chloride wt of cement 0.617％) bound is only 77％. 3. The bound ratio of chloride to wt of cement is 0.015∼0.475％ with adding chloride. In case chloride added over 0.091 ％ wt of cement, the bound chloride content increases 1.7∼1.8 times in spite of added chloride increase twice. The bound ratio of chloride to wt of cement decreased with the increase in the chloride content. 4. The more increase added chloride content, the more increase the bound ration of chloride. But the absolute value of chloride content in pore solution increased.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2002.05a
• /
• pp.57-60
• /
• 2002

Recently, the coal ash production has been increased by increase of consumption of electric power. So it is important to find a reclaimed place and treatment utility for treating coal ash. Accordingly, in this study we performed an experimental study to compare and analyze the Properties of concrete according to W/C and bottom ash replacement ratio. As a result of this study, it was found that the bleeding content was decreased according to decrease of W/C and increase of bottom ash replacement ratio, and the compressive strength of concrete using bottom ash was similar to plain concrete(replacement ratio 0%).

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.185-186
• /
• 2020

This study In order to reduce the amount of cement that generates a large amount of carbon dioxide and attempts to find a recycling method to solve environmental problems by using biomass fly ash. Experiments were conducted according to replacement ratio of biomass fly ash based on GGBFS, The test items are flowability, air content, unit volume weight, water absorption, flexural strength and compressive strength. As a result of the experiment, as increased replacement ratio of biomass fly ash, the flowability and air content was increased. As increased replacement ratio, the density was decreased and water absorption was increased. The compressive strength tended to decrease as increased replacement ratio. The flexural strength tended to increased as increased replacement ratio.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.61-64
• /
• 1997

As construction technology advances, most of concrete structures are becoming larger and taller. Therefore, high strength and quality concrete is necessary for them. So, the proposal of using belite cement is investigated to satisfy high flowing, low heat, and high strength. In this study, the compressive strength, tensile strength, and modulous of elasticity of concrete using belite cement was considered according to the mix proposition condition as a water-cement ratio, unit cement content, and sand percentage.

• Computers and Concrete
• /
• v.10 no.1
• /
• pp.49-57
• /
• 2012

Nano-particle-reinforced cement mortars have been the basis of research in recent years and a significant growth is expected in the future. Therefore, optimization and quantification of the effect of processing parameters and mixture ingredients on the performance of cement mortars are quite important. In this work, the effects of nano-silica, water/binder ratio, sand/binder ratio and aging (curing) time on the compressive strength of cement mortars were modeled by means of artificial neural network (ANN). The developed model can be conveniently used as a rough estimate at the stage of mix design in order to produce high quality and economical cement mortars.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.161-162
• /
• 2022

The purpose of this study is to determine the viscosity of the polymer-cement composites(PCCs) for crack repair of RC structures and to investigate its compaction. According to the study on the viscosity and compaction property of PCCs for crack repair, the viscosity of PCCs varies greatly depending on the polymer type and polymer cement ratio, and by mixing silica fume into PCCs, appropriate viscosity and excellent flow can be controlled without separation of cement and water. As a result of this study, basic data on the viscosity, fluidity, and compaction properties of PCCs for crack repair of RC structure can be obtained.