Recently, the interest of UHSC (ultra-high-strength concrete) is increased for skyscrapers and long span bridges. Thus, the autogenous shrinkage of UHSC which mainly affect to reduce durability should be studied and in this paper, the experimental test for estimating behavior of autogenous shrinkage of UHSC is performed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.29-32
• /
• 2006

The techniques related to ultra-high strength concrete(UHSC) became the key issue in recent days since requirements of the high-rise building which story is over than 100 gradually increases. Therefore, for the development of 150MPa UHSC this research is generally categorized by 4 parts: development of pre-mixed binders, evaluation for the fire performance of coarse aggregate, optimization of the mixture proportion, and mock-up test. Finally, based on the optimized mixture and its laboratory tests, mock-up test for wall and column specimens were carried out to simulate and evaluate the UHSC in real situation. The mechanical properties of core specimens were compared with the cylinder specimens made in laboratory. For instance, it showed the reasonable the results that the strength at the age of 91 days is 183MPa.

• Steel and Composite Structures
• /
• v.38 no.2
• /
• pp.121-139
• /
• 2021

Ultra-high strength concrete (UHSC) encased steel columns are receiving growing interest in high-rise buildings owing to their economic and architectural advantages. However, UHSC encased steel columns are not covered by the modern fire safety design code. A total of 14 fire tests are conducted on UHSC (120 MPa) encased steel columns under constant axial loads and exposed to ISO-834 standard fire. The effect of load ratio, slenderness, stirrup spacing, cross-section size and concrete cover to core steel on the fire resistance and failure mode of the specimens are investigated. The applicability of the tabulated method in EC4 (EN 1994-1-2-2005) and regression formula in Chinese code (DBJ/T 15-81-2011) to fire resistance of UHSC encased steel columns are checked. Generally, the test results reveal that the vertical displacement-heating time curves can be divided into two phases, i.e. thermal expansion and shortening to failure. It is found that the fire resistance of column specimens increases with the increase of the cross-section size and concrete cover to core steel, but decreases with the increase of the load ratio and slenderness. The EC4 method overestimates the fire resistance up to 186% (220 min), while the Chinese code underestimates it down to 49%. The Chinese code has a better agreement than EC4 with the test results since the former considers the effect of the load ratio, slenderness, cross section size directly in its empirical formula. To estimate the fire resistance precisely can improve the economy of structural fire design of ultra-high strength concrete encased steel columns.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.13-16
• /
• 2006

This paper investigates the shrinkage behavior of Ultra High Strength(UHSC) having three water-to-cementitious material ratio, 0.20, 0.16, 0.12. All of mixtures have same design compressive strength. Free shrinkage test for autogenous and drying shrinkage using $100{\times}100{\times}400$ prismatic specimen was conducted. On all mixture, Effects of fly ash and blast-furnace slag on each shrinkage test results were also investigated. The largest portion of autogenous shrinkage was observed in UHSC12 (w/b=0.12) and the measured strain was as high as 80% of the total drying shrinkage strain. The autogenous shrinkage of UHSC decreased as the amount of fly ash increased as demonstrated in the literature. However, the results of the effect of blast-furnace slag on autogenous shrinkage were somewhat different from previous researches.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.5A
• /
• pp.565-575
• /
• 2009

In recent years, there have been numerous explosion-related accidents due to military and terrorist activities. Such incidents caused not only damages to structures but also human casualties, especially in urban areas. To protect structures and save human lives against explosion accidents, better understanding of the explosion effect on structures is needed. In an explosion, the blast load is applied to concrete structures as an impulsive load of extremely short duration with very high pressure and heat. Generally, concrete is known to have a relatively high blast resistance compared to other construction materials. However, normal strength concrete structures require higher strength to improve their resistance against impact and blast loads. Therefore, a new material with high-energy absorption capacity and high resistance to damage is needed for blast resistance design. Recently, Ultra High Strength Concrete(UHSC) and Reactive Powder Concrete(RPC) have been actively developed to significantly improve concrete strength. UHSC and RPC, can improve concrete strength, reduce member size and weight, and improve workability. High strength concrete are used to improve earthquake resistance and increase height and bridge span. Also, UHSC and RPC, can be implemented for blast resistance design of infrastructure susceptible to terror or impact such as 9.11 terror attack. Therefore, in this study, the blast tests are performed to investigate the behavior of UHSC and RPC slabs under blast loading. Blast wave characteristics including incident and reflected pressures as well as maximum and residual displacements and strains in steel and concrete surface are measured. Also, blast damages and failure modes were recorded for each specimen. From these tests, UHSC and RPC have shown to better blast explosions resistance compare to normal strength concrete.

• Journal of the Korea Concrete Institute
• /
• v.19 no.2
• /
• pp.209-216
• /
• 2007

This study reports on the structural characteristics of slab-column connections using fiber-reinforced ultra-high-strength concrete (UHSC). Compression tests were performed on two slab-column and four isolated column specimens. In the column load tests, slab loads were also applied on the slab-column specimens so that the actual confinement condition at the slab-column joint was considered. The main parameter investigated was the "puddling" of fiber-reinforced UHSC. This paper also investigates the effects of some parameters, such as confinement of slab concrete, steel fibers, and concrete strength of the joint, related to the ability of the slab-column specimens and isolated column specimens without the surrounding slab to transmit axial loads from the UHSC columns through slab-column connections. Furthermore, the ACI Code (2005) and the CSA Standard (2004) are compared to the experimental results. The beneficial effects of the puddling of fiber-reinforced UHSC on the transmission of column loads through slab-column connections are demonstrated.

• Journal of the Korea Concrete Institute
• /
• v.26 no.3
• /
• pp.377-384
• /
• 2014

Recently, the trend toward larger architectural structures continues and accelerates demand for Ultra High Strength Concrete (UHSC) which satisfies structural performance. However, UHSC has weakness in fire and the performance tests are required. In this paper, the change of mechanical properties of 100 MPa grade UHSC exposed to high temperatures ($20^{\circ}C{\sim}800^{\circ}C$) was observed to develop high temperature material model of UHSC: residual compressive strength, modulus of elasticity, property of stress-strain on monotonous loading and property of stress-strain on cyclic loading. In addition, TG/DTA and SEM Images analyses were performed to investigate chemical and physical characteristics of UHSC, and the results of this research were compared with those of previous studies. As a result, UHSC at the heating temperature of $300^{\circ}C$ showed a sharp decrease of residual compressive strength and modulus of elasticity. And It was shown that UHSC had a plastic behavior at more than $400^{\circ}C$ on the cyclic loading and revealed a same tendency in both monotonous and cyclic loading of all heating temperatures. In addition, through TG/DTA and SEM images analyses compared with those from previous studies, it was shown that the deterioration of concrete inner tissue, water evaporation and chemical reaction caused the decrease of residual compressive strength and modulus of elasticity.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.365-368
• /
• 2008

This research is related to 240MPa ultra-high strength concrete(UHSC) with extremely loss W/B ratio. For this development, High flow cement is mainly used which has a short reaction rate due to the high blaine and high early strength, which can make greater fluidity in case of very low W/C ratio. It made the best mixture using the mineral admixtures silica fume, slag powder and special admixture. For dispersibility and homogeneity of cement binder, cement of premix type is produced using omni-mixer. Moreover, it ensures the fluidity of ultra-high strength concrete(UHSC). For having a good fire performance, we made an experiment special coarse aggregate. As a result, we got 180MPa in case of water curing, 200MPa in case of steam curing and uniform UHSC of 240MPa in case of a special curing method.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.641-650
• /
• 2010

The concrete cracking from the restrained stress caused by the shrinkage may play significant cause of deterioration of concrete structures by allowing the permeation of sulphate and chloride ions which in turn triggers corrosion of steel reinforcement. In particular, the cracking becomes more critical as water binder ratio (W/B) is reduced and concrete strength increases. Therefore, it needs to evaluate correctly the comprehensive shrinkage behavior of concrete with high strength: high-strength concrete (HSC), ultra-highstrength concrete (UHSC). The unrestrained shrinkage tests, however, cannot estimate the net shrinkage effectively which affects cracking after full development of strength and stiffness because it does not consider the degree of restraint, strength development, stress relaxation, and so on. Therefore, in this study, both free and restrained shrinkage tests with variables of W/B (W/B of 30, 25 and 16%) and admixtures (fly ash (FA) and granulated blast-furnace slag (BFS)) for HSC, very-high-strength concrete (VHSC) and UHSC were performed. The test results indicated that the autogenous shrinkage and total shrinkage at drying condition were reduced as W/B increased and FA, BFS were added, and the cracking behavior was suppressed as W/B increased and FA was added.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05a
• /
• pp.79-82
• /
• 2005

This study reports on the structural characteristics of slab-column connections using an ultra-high-strength-fiber-reinforced concrete from new and retrospective data. The parameters investigated were the ' puddling ' of ultra-high-strength-fiber-reinforced concrete and the use of high-strength concrete in the slab. The effects of these parameters on the punching shear capacity, negative moment cracking, and stiffness of the two-way slab specimens are investigated. Furthermore, the ACI Code (2002), the CSA Standard (1994), the BS Standard (1985) and the CEB-FIP Code (1990) predictions are compared to the experimental results obtained from some slab-column connections tested in this experiment and those tested by other investigators. The beneficial effects of the ultra-high-strength-fiber-reinforced concrete puddling and of the use of high-strength concrete are demonstrated. It is also concluded that the punching shear strength of slab-column connections is a function of the flexural reinforcement ratio.