• Journal of Powder Materials
• /
• v.25 no.3
• /
• pp.240-245
• /
• 2018

This study focuses on the fabrication of a WC/Co composite powder from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere for the recycling of WC/Co hardmetal. Mixed powders are manufactured by mechanically milling the oxide powder of WC-13 wt% Co hardmetal scrap and carbon black with varying powder/ball weight ratios. The oxide powder of WC-13 wt% Co hardmetal scrap consists of $WO_3$ and $CoWO_4$. The mixed powder mechanically milled at a lower powder/ball weight ratio (high mechanical milling energy) has a more rapid carbothermal reduction reaction in the formation of WC and Co phases compared with that mechanically milled at a higher powder/ball weight ratio (lower mechanical milling energy). The WC/Co composite powder is fabricated at $900^{\circ}C$ for 6 h from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere. The fabricated WC/Co composite powder has a particle size of approximately $0.25-0.5{\mu}m$.

• Journal of Powder Materials
• /
• v.9 no.4
• /
• pp.273-279
• /
• 2002

In this study, the WC-10 wt.%Co nanopowders doped by grain growth inhibiter were produced by three different methods based on the spray conversion process. Agglomerated powders with homeogenous distribution of alloying elements and with internal particles of about 100-200 nm in diameter were synthesized. The microstructural changes and sintering behavior of hardmetal compacts were compared with doping method and sintering conditions. The microstructure of hardmetals was very sensitive to doping methods of inhibitor. Nanostructured WC-Co hardmetal powder compacts containing TaC/VC doped by chemical method instead of ball-milling shown superior sintering densification, and the microstructure maintained ultrafine scale with rounded WC particles.

• Journal of Powder Materials
• /
• v.28 no.4
• /
• pp.342-351
• /
• 2021

Because of its unique properties, tungsten is a strategic and rare metal used in various industrial applications. However, the world's annual production of tungsten is only 84000 t. Ammonium paratungstate (APT), which is used as the main intermediate in industrial tungsten production, is usually obtained from tungsten concentrates of wolframite and scheelite by hydrometallurgical treatment. Intermediates such as tungsten trioxide, tungsten blue oxide, tungstic acid, and ammonium metatungstate can be derived from APT by thermal decomposition or chemical attack. Tungsten metal powder is produced through the hydrogen reduction of high-purity tungsten oxides, and tungsten carbide powder is produced by the reaction of tungsten powder and carbon black powder at 1300-1700℃ in a hydrogen atmosphere. Tungsten scrap can be divided into hard and soft scrap based on shape (bulk or powder). It can also be divided into new scrap generated during the production of tungsten-bearing goods and old scrap collected at the end of life. Recycling technologies for tungsten can be divided into four main groups: direct, chemical, and semi-direct recycling, and melting metallurgy. In this review, the current status of tungsten smelting and recycling technologies is discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.285-285
• /
• 2007

Friction material in a piezoelectric system is a important part to affect to moving performance. In this paper, alumina ceramics $(AlO_2)$, silicon carbide (SiC), high speed steel and super-hard alloy (WC, Tungsten Carbide) having a hardness knoop of 1000 to 2000 $kg/mm^2$ were tested as a friction material of AF module. Even though $AlO_2$, SiC and high speed steel were a high-hardness material, $AlO_2$ and SiC were worn by a rough surface, and SiC is rusted in humidity condition. AF module using super-hard alloy has showed a stable moving performance in life time test.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.41-46
• /
• 2014

In this study, cracking susceptibility of laser cladding was investigated according to the processing parameters such as laser power, scan speed and feeding rate with blended powders of stellite#6 and technolase40s (WC+NiCr). The solidification microstructure of clad was composed of Co-based dendrite structures with ${\gamma}+Cr7C3$ eutectic phases at the dendritic boundaries. The crack propagation showed transgranular fracture along dendritic boundaries due to brittle chrome carbide at the eutectic phases. From results of fractography experiments, the fracture surface was typical cleavage brittle fracture in the clad and substrate. The number of clad cracks, caused by a tensile stress after the solidification, increased with increase of laser power, scan speed and feeding rate. Increase of the laser power caused large pores by facilitating WC decarburizing reaction. And the pores affected increase of crack susceptibility. High scan speed caused increment of clad cracks due to thermal stress and WC particle fractures. Also, increase of the feeding rate accompanied an amount of WC particles causing crack initiation and decarburizing reaction.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.06a
• /
• pp.403-404
• /
• 2008

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.88-93
• /
• 2008

Ir-Re thin films with Ti interlayer were deposited onto the tungsten carbide substrate by ion beam assisted DC magnetron sputtering. The Ir-Re films were prepared with targets of having two atomic percent of 7:3 and 5:5. The microstructure and surface analysis of the specimen were conducted by using SEM, XRD and AFM. Mechanical properties such as hardness and adhesion strength of Ir-Re thin film also were examined. The interlayer of pure titanium was formed with 100 nm thickness. The film growth of Ir-30at.%Re was faster than that of Ir-50at.%Re in the same deposition conditions. Ir-Re thin films consisted of dense and columnar structure irrespective of the different target compositions. The values of hardness and adhesion strength of Ir-30at.%Re thin film coated on WC substrate were higher than those of Ir-50at.%Re thin film.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.272-278
• /
• 1999

Tungsten Carbide(WC) Roll is widely used in finishing stands of wire rod mill. This report is about the manufacturing method of WC roll with excellent wear resistance. To enhance wear resistance, WC content has been increased to the maximum extent while binder content such as Co, Ni, Cr has been minimized. Part of WC is replaced with TiC having more wear resistant than WC. WTiC powder has been used to prevent weight unbalance resulting from the difference of specific weight when adding TiC. The roll manufactured by this method, is having more wear resistance than the existing rolls when applying to the final stand of the finishing mill. This report shows that WC is the critical factor of wear resistance in WC rolls and an approprite amount of TiC effects wear resistance and when adding TiC, using WTiC powder is better.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.215-216
• /
• 2002

This paper describes the wear characteristics of WC-Co cemented carbides machined with Wire-cut or Die-sinking EOM. We prepared the specimens with different grades of grinding to remove the affected layer after the EDM. These specimens were experimented by block-on-cylinder type tribometer. The result indicated that although the hardness of the affected layer was lower than that of the bulk, wear resistance was increased. In order to investigate the cause of the increase in wear resistance of the affected layer, the layer was observed and analyzed by SEM and ESCA. We also discussed the mean free path of Co phase.

• Journal of the Korean Society for Precision Engineering
• /
• v.11 no.5
• /
• pp.42-55
• /
• 1994

Presently, abrasive processing is on eof several methods for cutting and grinding brittle materials, and high quality in dimensional accuracy and surface roughness are often required as a structural components, therefore most of them has to be ground. In manufacturing of tungsten-carbide components, grinding by diamond wheel is usually adopted in order to provide configurational and dimensional accuracy to the components. The present study proposes the experi- mental research of optimum condition to the high quality surface grinding of the WC-Co material using diamond abrasive wheel in order to minimize the damage on the ground surface and to pursue the precise dimension by conventional grinding machine. Brief investigation is carried out to decrease the dressing is constant, theoretical grinding effect such as machining precision is changed according to the speed of workpiece. Accordingly, normal and tangential grinding forces, which are Fn, Ft were analyzed for the machining processes of WC-Co material to obtain optimum grinding conditions, 3-point bending test is carried out to check machining damage on the ground surface layer, which is one of sintered brittle materials.