$ZnO-SnO_2(ZTO)$ was deposited by RF magnetron sputtering using a ceramic target whose Zn atomic ratio to Sn is 2:1 as a target, and the crystal structure variation with thermal treats was investigated. Transparent thin film transistors (TTFT) were fabricated using the ZTO films as active layers. About 100 nm-thick $Si_3N_4$ film grown on 100 nm-thick $SiO_2$ film was adopted as gate dielectrics. The mobility, threshold voltage, $I_{on}/I_{off}$, and interface trap density were obtained from the transfer characteristics of ZTO TTFTs. The effects of substrate temperature, and post-annealing on the property variation of ZTO TTFT were analyzed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.4
• /
• pp.304-308
• /
• 2012

Transparent thin film transistors (TTFT) were fabricated using the rf magnetron sputtered ZnO-$SnO_2$ films as active layers. A ceramic target whose Zn atomic ratio to Sn is 2:1 was employed for the deposition of ZnO-$SnO_2$ films. To study the post-annealing effects on the properties of TTFT, ZnO-$SnO_2$ films were annealed at $200^{\circ}C$ or $400^{\circ}C$ for 5 min before In deposition for source and drain electrodes. Oxygen was added into chamber during sputtering to raise the resistivity of ZnO-$SnO_2$ films. The effects of oxygen addition on the properties of TTFT were also investigated. 100 nm $Si_3N_4$ film grown on 100 nm $SiO_2$ film was used as gate dielectrics. The mobility, $I_{on}/I_{off}$, interface state density etc. were obtained from the transfer characteristics of ZnO-$SnO_2$ TTFTs.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08a
• /
• pp.860-863
• /
• 2007

ZnO nano film for transparent thin film transistors is prepared by injection type source delivery system of atomic layer deposition. By using this delivery system the source delivery pulse time can dramatically be reduced to 0.005s in ALD system. ZnO nanofilms obtained at $150^{\circ}C$ are characterized.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.110.2-110.2
• /
• 2012

We reported on antireflective ZnSnO (ZTO)/Ag bilayer and ZTO/Ag/ZTO trilayer source/drain (S/D) electrodes for all-transparent ZTO channel based thin film transistors (TFTs). The ZTO/Ag bilayer is more transparent (83.71%) and effective source/drain (S/D) electrodes for the ZTO channel/Al2O3 gate dielectric/ITO gate electrode/glass structure than ZTO/Ag/ZTO trilayer because the bottom ZTO layer in the trilayer increasea contact resistance between S/D electrodes and ZTO channel layer and reduce the antireflection effect. The ZTO based all-transparent TFTs with ZTO/Ag bilayer S/D electrode showed a saturation mobility of 4.54cm2/Vs and switching property (1.31V/decade) comparable to TTFT with Ag S/D electrodes.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.23.1-23.1
• /
• 2009

Transparent thin film transistor(TTFT)는 기존의 디스플레이가 가지고 있는 공간적, 시각적 제약을 해소하는 것이 가능하며, 이는 디스플레이 산업 및 기술이 지향하는 대면적, 저가격, 공정의 단순함을 해결해 줄 수 있기 때문에 최근 TTFT에 관한 연구가 급증하고 있다. 산화물 기반의 TFT는 유리, 금속, 플라스틱 등등 그 기판 종류에 상관없이 균일한 제작이 가능하며, 상온 및 저온에서 대면적으로 제작 가능하고, 저렴한 비용으로 제작 가능하다는 장점 때문에 최근 산화물을 기반으로 하는 TFT 연구가 많이 이루어지고 있다. 현재 TTFT 물질로 많이 연구되고 있는 산화물은 ZnO(3.4 eV)나 $InO_x$(3.6 eV), $GaO_x$(4.9 eV), $SnO_x$(3.7 eV)등의 물질과 각각의 조합으로 구성된 재료들이 주로 사용되고 있다. 가장 많은 연구가 이루어진 ZnO 기반의 TFT는 mobility와 switching 속도에서 우수한 특성을 보이나, amorphous ZnO 기반의 TFT의 경우 소자의 안정성이 떨어지는 것으로 보고되고 있다. 따라서 본 연구에서는 ZnO 보다 넓은 bandgap energy를 가질 수 있으며, n-type 특성을 보이고, amorphous 구조로 제작 가능한 IGZO 물질을 사용하여 RF magnetron sputtering 방법으로 박막 증착 온도의 변화를 주어 증착하였고, 증착된 IGZO 박막의 열처리를 통해 이에 따른 특성 변화를 분석하였다. Field emission scanning electron microscope(FESEM)와 surface profiler를 이용하여 IGZO 박막의 표면의 형상과 두께를 확인하였으며, x-ray diffraction(XRD) 분석을 통해 박막의 결정학적 특성을 관찰하였다. TTFT 물질로서 IGZO 박막의 적합성 여부를 확인하기 위하여 TFT를 만든 후 I-V를 측정하였으며, UV-vis를 이용하여 IGZO 박막의 투과율을 분석하여 TTFT로의 응용 가능성을 확인하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.11a
• /
• pp.20.1-20.1
• /
• 2008

• Korean Journal of Materials Research
• /
• v.19 no.1
• /
• pp.24-27
• /
• 2009

Indium Gallium Zinc Oxide (IGZO) thin films were deposited onto 300 nm-thick oxidized Si substrates and glass substrates by direct current (DC) magnetron sputtering of IGZO targets at room temperature. FESEM and XRD analyses indicate that non-annealed and annealed IGZO thin films exhibit an amorphous structure. To investigate the effect of an annealing treatment, the films were thermally treated at $300^{\circ}C$ for 1hr in air. The IGZO TFTs structure was a bottom-gate type in which electrodes were deposited by the DC magnetron sputtering of Ti and Au targets at room temperature. The non-annealed and annealed IGZO TFTs exhibit an $I_{on}/I_{off}$ ratio of more than $10^5$. The saturation mobility and threshold voltage of nonannealed IGZO TFTs was $4.92{\times}10^{-1}cm^2/V{\cdot}s$ and 1.46V, respectively, whereas these values for the annealed TFTs were $1.49{\times}10^{-1}cm^2/V{\cdot}$ and 15.43V, respectively. It is believed that an increase in the surface roughness after an annealing treatment degrades the quality of the device. The transmittances of the IGZO thin films were approximately 80%. These results demonstrate that IGZO thin films are suitable for use as transparent thin film transistors (TTFTs).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.3
• /
• pp.177-182
• /
• 2013

Transparent thin film transistors (TTFT) were fabricated on $N^+$ Si wafers. $SiO_2$, $Si_3N_4/SiO_2$ and $Al_2O_3/SiO_2$ grown on the wafers were used as gate insulators. The rf magnetron sputtered zinc tin oxide (ZTO) films were adopted as active layers. $N^+$ Si wafers were wet-oxidized to grow $SiO_2$. $Si_3N_4$ and $Al_2O_3$ films were deposited on the $SiO_2$ by plasma enhanced chemical vapor deposition (PECVD) and atomic layer deposition (ALD), respectively. The mobility, $I_{on}/I_{off}$ and subthreshold swing (SS) were obtained from the transfer characteristics of TTFTs. The properties of gate insulators were analyzed by comparing the characteristics of TTFTs. The property variation of the ZTO TTFTs with time were observed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.127-127
• /
• 2011

We investigate the transparent TFTs using a transparent ZnSnO3 (ZTO)/Ag/ZTO multilayer electrode as S/D electrodes with low resistivity of $3.24{\times}10^{-5}$ ohm-cm, and high transparency of 86.29% in ZTO based TFTs. The Transparent TFTs (TTFTs) are prepared on glass substrate coated 100 nm of ITO thin film. On atomic layer deposited $Al_2\;O_3$, 50 nm ZTO layer is deposited by RF magnetron sputtering through a shadow mask for channel layer using ZTO target with 1 : 1 molar ratio of ZnO : $SnO_2$. The power of 100W, the working pressure of 2mTorr, and the gas flow of Ar 20 sccm during the ZTO deposition. After channel layer deposition, a ZTO (35 nm)/Ag (12 nm)/ZTO(35 nm) multilayer is deposited by DC/RF magnetron sputtering to form transparent S/D electrodes which are patterned through the shadow mask. Devices are annealed in air at 300$^{\circ}C$ for 30 min following ZTO deposition. Using UV/Visible spectrometer, the optical transmittances of the TTFT using ZTO/Ag/ ZTO multilayer electrodes are compared with TFT using Mo electrode. The structural properties of ZTO based TTFT with ZTO/Ag/ZTO multilayer electrodes are analyzed by high resolution transmission electron microscopy (HREM) and X-ray photoelectron spectroscopy (XPS). The transfer and output characterization of ZTO TTFTs are examined by a customized probe station with HP4145B system in are.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.309-309
• /
• 2009

In-Ga-Zn-O (IGZO) has drawn much attention as a compatible material for transparent thin film transistors (TTFT) channel layer due to its high mobility and optical transparency at low processing temperatures. In this work, we investigated the effect of oxygen ambient on structural, electrical and optical properties of amorphous In-Ga-Zn-O (IGZO) thin films by using pulsed laser deposition (PLD). The films were deposited at various oxygen pressures and the structural, electrical and optical properties were investigated. X-ray diffraction (XRD) analysis showed that amorphous IGZO films were grown at all oxygen pressures. The surface morphology and optical properties with various oxygen pressures were studied by field emission scanning electron microscopy (FE-SEM) and UV-VIS spectroscopy, respectively. The grain boundary was observed more apparently and the calculated optical band gap became larger as oxygen pressure increased. To examine the electrical properties, Hall-effect measurements were carried out. The films showed high mobility.