Purpose: This study was performed to investigate mechanical properties of the porous Ti implants according to porosity. Porous Ti implant will be had properties similar to human bone such as microstructure and mechanical properties. Methods: Porous Ti implant samples were fabricated by sintering of spherical Ti powders(below $25{\mu}m$, $25{\sim}32{\mu}m$, $32{\sim}38{\mu}m$, and $38{\sim}45{\mu}m$) in a high vacuum furnace. Specimen's diameter and height were 4mm and 40 mm. Surface and sectional images of porous Ti implants were evaluated by scanning electron microscope(SEM). Porosity and average pore size were evaluated by mercury porosimeter. Young's modulus and tensile strength were evaluated by universal testing machine(UTM). Results: Porosity of Implant was increased according to larger particle size of the powder. Boundary portions of particles are sintered fully and others portions were formed pore. Young's modulus was decreased by formed porous structure. Tensile strength was decreased according to larger the particle size of the powder, but higher than human bone. Conclusion: If prepared by adjust the porosity of the porous Ti implant will be able to resolve the stress shielding phenomenon.

• Journal of Technologic Dentistry
• /
• v.34 no.3
• /
• pp.221-226
• /
• 2012

Purpose: This study was performed to compare mechanical properties for sintering methods of porous Ti implants. Methods: The specimens of Ti implant were fabricated by several sintering methods. One of them is spark plasma sintering(SPS). Another is electro discharge singering(EDS) and the other is high vacuum sintering(HVS). Mechanical properties of porous Ti implants were evaluated by universal testing machine(UTM) and their fracture surface was examined under a sanning electron microscope(SEM). Results: The tensile strength was in a range of 71 to 230 MPa, and Young's modulus was in a range of 11 to 21 Gpa. It matched with range of cortical bone. Conclusion: Mechanical properties of porous Ti implants were similar to human bone. It was shown that sintering methods of spherical powders can efficiently produce porous Ti implants with various porosities. Porous metals will be commonly used in orthopedic and dental application despite of initial focus has been on bioceramics.

• Biomolecules & Therapeutics
• /
• v.22 no.6
• /
• pp.563-569
• /
• 2014

Materials with differing surfaces have been developed for clinical implant therapy in dentistry and orthopedics. This study was designed to evaluate bone response to titanium alloy containing Ti-32Nb-5Zr with nanostructure, anodic oxidation, heat treatment, and ibandronate coating. Rats were randomly assigned to two groups for implantation of titanium alloy (untreated) as the control group and titanium alloy group coated with ibandronate as the experimental group. Then, the implants were inserted in both tibiae of the rats for four weeks. After implantation, bone implant interface, trabecular microstructure, mechanical fixation was evaluated by histology, micro-computed tomography (${\mu}CT$) and the push-out test, respectively. We found that the anodized, heat-treated and ibandronate-coated titanium alloy triggered pronounced bone implant integration and early bone formation. Ibandronate-coated implants showed elevated values for removal torque and a higher level of BV/TV, trabecular thickness and separation upon analysis with ${\mu}CT$ and mechanical testing. Similarly, higher bone contact and a larger percentage bone area were observed via histology compared to untreated alloy. Furthermore, well coating of ibandronate with alloy was observed by vitro releasing experiment. Our study provided evidences that the coating of bisphosphonate onto the anodized and heat-treated nanostructure of titanium alloy had a positive effect on implant fixation.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.19 no.1
• /
• pp.17-25
• /
• 2003

Treatment with implants of single tooth missing cases is both functional and esthetic. Although the success rate of single-tooth implant treatments is increasing, sometimes it makes some problems. Problems with single-tooth implant treatments include soft tissue complications, abutment screw fracture, and most commonly, abutment screw loosening, and these involve the instability of the dental implant-superstructure interface. This study investigated and compared dental implant screw joint micromotion of various implant system with external connection or internal connection when tested under simulated clinical loading, Six groups (N=5) were assessed: (1) Branemark AurAdapt (Nobel Biocare, Goteborg, Sweden), (2) Branemark EsthetiCone (Nobel Biocare, Goteborg, Sweden), (3) Neoplant Conical (Neobiotec, Korea), (4) Neoplant UCLA (Neobiotec, Korea), (5) Neoplant 5.5mm Solid (Neobiotec, Korea), and (6) ITI SynOcta (Institute Straumann, Waldenburg, Switzerland). Six identical frameworks were fabricated. Abutment screws were tightened to 32-35 Ncm and occlusal screw were tightened to 15-20 Ncm with an electronic torque controller. A mechanical testing machine applied a compressive cyclic load of 20kg at 10Hz to a contact point on each implant crown. Strain gauge recorded the micromotion of the screw joint interface once a second. Data were selected at 1, 500, 5,000, 10,000, 20,000, 30,000, 40,000 and 50,000 cycle and 2-way ANOVA test was performed to assess the statistical significance. The results of this study were as follows; The micromotion of the implant-superstructure in the interface increased gradually through 50,000 cycles for all implant systems. In the case of the micromotion according to cycle increase, Neoplant Conical and Neoplant UCLA system exhibited significantly increasing micromotion at the implant-superstructure interface (p<0.05), but others not significant. In the case of the micromotion of the implant-superstructure interface at 50,000 cycle, the largest micromotion were recorded in the Branemark EsthetiCone, sequently followed by Neoplant Conical, Neoplant UCLA, Branemark AurAdapt, ITI SynOcta and Neplant Solid. Internal connection system showed smaller micromotion than external connection system. Specially, Neoplant Solid with internal connection system exhibited significantly smaller micromotion than other implant systems except ITI SynOcta with same internal connection system (p<0.05). In the case of external connection, Branemark EsthetiCone and Neoplant Conical system with abutment showed significantly larger micromotion than Branemark AurAdapt without abutment (p<0.05).

• Journal of Oral Medicine and Pain
• /
• v.46 no.4
• /
• pp.136-142
• /
• 2021

Purpose: Oral and facial sensation is affected by various factors, including trauma and disease. This study assessed the clinical profile of patients diagnosed with sensory dysfunction and investigated their sensory perception using simple qualitative sensory tests. Methods: Based on a retrospective review of the medical records, we analyzed a total of 68 trigeminal nerve branches associated with sensory dysfunction in 52 subjects. We analyzed the frequency and etiology of sensory dysfunction, and the frequency of different types of sensory perception in response to qualitative sensory testing using tactile and pin-prick stimuli. Results: The inferior alveolar nerve branch was the most frequently involved in sensory dysfunction (88.5%). Third molar extraction (36.5%) and implant surgery (36.5%) were the most frequent etiological factors associated with sensory dysfunction. Hypoesthesia was the most frequent sensory response to tactile stimuli (60.3%). Pin-prick stimuli elicited hyperalgesia, hypoalgesia, and analgesia in 32.4%, 27.9%, and 36.8%, respectively. A significant association was found between the two kinds of stimuli (p=0.260). Conclusions: Sensory dysfunction frequently occurs in the branches of the trigeminal nerve, including the inferior alveolar nerve, mainly due to trauma associated with dental treatment. Simple qualitative sensory testing can be conveniently used to screen sensory dysfunction in patients with altered sensation involving oral and facial regions.

• Journal of Technologic Dentistry
• /
• v.32 no.4
• /
• pp.317-325
• /
• 2010

Purpose: The aim of this study is to make some basic materials to find retention force difference based on the total height of CAD/CAM zirconia abutment used for implant, retention force difference based on how to regulate the height of the abutment, retention force difference based on the size and retention force difference based on the design group. Methods: The retention force was measured by being pulled at the speed of 1mm/min after being combined with zirconia block and abutment using Temp-BOND of Kerr. The experiment was done at the research lab of OSTEM in Busan by useing UNIVERSAL TESTING MACHINE on March 3rd, 2010. Results: After analysing the total height and the retention force, p-value had minor difference by 0.01 statistically. Namely, 3mm, 4mm, 5mm had the retention force difference and we could see retention force difference on 3mm and 5mm at the post test. After analyzing how to regulate the height and retention force, p-value had minor difference by 0.000 statistically. Namely, 1mm and 2mm had the retention difference and we could see that 1mm and 2mm with the total height had retention difference. After analyzing the retention force based on the size, p-value had minor retention force difference by 0.000 statistically. Namely, 7 different size had retention force difference and we could see the size 21.9mm, 32.9mm, 32.9mm, 38.4mm, 48.9mm and 54.9mm had retention force difference. Conclusion: Namely 9 different design group had retention difference and we could see that 9 design group with 5.6.7.8 design group and 9 design group with 1.2.3.4. design group had retention force.

• Journal of Periodontal and Implant Science
• /
• v.52 no.3
• /
• pp.242-257
• /
• 2022

Purpose: This study investigated periodontal ligament (PDL) restoration in osseointegrated implants using stem cells. Methods: Commercial pure titanium and zirconium oxide (zirconia) were coated with beta-tricalcium phosphate (β-TCP) using a long-pulse Nd:YAG laser (1,064 nm). Isolated bone marrow mesenchymal cells (BMMSCs) from rabbit tibia and femur, isolated PDL stem cells (PDLSCs) from the lower right incisor, and co-cultured BMMSCs and PDLSCs were tested for periostin markers using an immunofluorescent assay. Implants with 3D-engineered tissue were implanted into the lower right central incisors after extraction from rabbits. Forty implants (Ti or zirconia) were subdivided according to the duration of implantation (healing period: 45 or 90 days). Each subgroup (20 implants) was subdivided into 4 groups (without cells, PDLSC sheets, BMMSC sheets, and co-culture cell sheets). All groups underwent histological testing involving haematoxylin and eosin staining and immunohistochemistry, stereoscopic analysis to measure the PDL width, and field emission scanning electron microscopy (FESEM). The natural lower central incisors were used as controls. Results: The BMMSCs co-cultured with PDLSCs generated a well-formed PDL tissue that exhibited positive periostin expression. Histological analysis showed that the implantation of coated (Ti and zirconia) dental implants without a cell sheet resulted in a well-osseointegrated implant at both healing intervals, which was confirmed with FESEM analysis and negative periostin expression. The mesenchymal tissue structured from PDLSCs only or co-cultured (BMMSCs and PDLSCs) could form a natural periodontal tissue with no significant difference between Ti and zirconia implants, consequently forming a biohybrid dental implant. Green fluorescence for periostin was clearly detected around the biohybrid implants after 45 and 90 days. FESEM showed the invasion of PDL-like fibres perpendicular to the cementum of the bio-hybrid implants. Conclusions: β-TCP-coated (Ti and zirconia) implants generated periodontal tissue and formed biohybrid implants when mesenchymal-tissue-layered cell sheets were isolated from PDLSCs alone or co-cultured BMMSCs and PDLSCs.

• Journal of Periodontal and Implant Science
• /
• v.31 no.1
• /
• pp.41-57
• /
• 2001

It is well known that the apposition of bone at implant surface would be influenced by the microstructure of titanium implants. The purpose of this study was to compare bone healing around the screw-shaped titanium implant with three different surface topographies in the canine mandibles by histological and biomechanical evaluation. All mandibular premolars of six mongrel dogs were extracted and implants were placed one month later. The pure titanium implants had different surface topographies: smooth and machined ($Steri-OSS^{(R)}$: Group II); sandblasted and acid-etched ($ITI^{(R)}$, SLA: Group III) surface. The fluorescent dyes were injected on the 2nd (calcein), 4th (oxytetracycline HCI) and 12th (alizarin red) weeks of healing. Dogs were sacrificed at 4 and 12 weeks after implantation. The decalcified and undecalcified specimens were prepared for histological and histo-metrical evaluation of implant-bone contact. Some specimens at 12 weeks after implantation were used for removal torque testing. Histologically, direct bone apposition to implant surface was found in all of the treated groups. More mature and dense bone was observed at the implant-bone interface at 12 weeks than that at 4 weeks after implantation. Under the fluorescent microscope, thick regular green fluorescent lines which mean early bone apposition were observed at the implant-bone interface in Group III, while yellow and red fluorescent areas were found at the implant-bone interface in Group I and II. The average implant-bone contact ratios at 4 weeks of healing were 54.3% in Group I, 57.7% in Group II and 66.2% in Group III. In Group I, implant-bone contact ratio was significantly lower than Group II and III(p<0.05). The average implant-to-bone contact ratios at 12 weeks after implantation were 64.3% in Group I, 66.7% in Group II and 71.2% in Group III. There was no significant difference among the three groups. In Group I and II, the implant-bone contact ratio at 12 weeks increased significantly in comparison to ratio at 4 weeks(p<0.05). The removal torque values at 12 weeks after implantation were 90.9 Ncm in Group I, 81.6 Ncm in Group II and 77.1 Ncm in Group III, which were significantly different(p<0.05). These results suggest that bone healing begin earlier and be better around the surface-treated implants compared to the smooth surface implants. The sandblasted and acid-etched implants showed the most favorable bone response among the three groups during the early healing stage and could reduce the waiting period prior to implant loading.

• Journal of Technologic Dentistry
• /
• v.30 no.1
• /
• pp.57-63
• /
• 2008

The purpose of this study was to ascertain the effect of different abutment height and different taper of abutment on retention force of cemented implant-supported prostheses. Test specimens consisted of different abutment height group(3mm, 4mm, 5mm, 6mm, 7mm) and different taper(degrees) abutment group($4^{\circ},\;5^{\circ},\;6^{\circ},\;7^{\circ},\;8^{\circ}$). The surfaces of abutments and crowns were manufactured and finished by automatic lathe(CNC). Luting cement(Tokuso Ionomer) was prepared according to the manufacturer's instruction. And the cylinders were sealed onto the abutments and loaded in compression at 5kg for 10minutes. Excess cement was removed from the abutment-cylinder junction and the specimens were stored at room temparature for 24 hours. Specimens were tested in tension using a universal testing machine. Within the limits of this study, the following conclusions were drawn: 1. The increase in abutment height result in improvement in retention strength(P<0.05). 2. The increase in taper of abutment result in decrease in retention strength(P<0.05). 3. The decrease in abutment height result in decrease in retention strength, besides has a significantly lower retention strength at 3mm abutment height. 4. The increase in taper of abutment result in decrease in retention strength, besides has a significantly lower retention strength at $7^{\circ}$ abutment.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.5
• /
• pp.388-395
• /
• 2016

PURPOSE. The purpose of this study was to evaluate the resistance to deformation under static overloading by measuring yield and fracture strength, and to analyze the failure characteristics of implant assemblies made of different titanium grades and connections. MATERIALS AND METHODS. Six groups of implant assemblies were fabricated according to ISO 14801 (n=10). These consisted of the combinations of 3 platform connections (external, internal, and morse tapered) and 2 materials (titanium grade 2 and titanium grade 4). Yield strength and fracture strength were evaluated with a computer-controlled Universal Testing Machine, and failed implant assemblies were classified and analyzed by optical microscopy. The data were analyzed using the One-way analysis of variance (ANOVA) and Student's t-test with the level of significance at P=.05. RESULTS. The group $IT4_S$ had the significantly highest values and group IT2 the lowest, for both yield strength and fracture strength. Groups $IT4_N$ and ET4 had similar yield and fracture strengths despite having different connection designs. Group MT2 and group IT2 had significant differences in yield and fracture strength although they were made by the same material as titanium grade 2. The implant system of the similar fixture-abutment interfaces and the same materials showed the similar characteristics of deformation. CONCLUSION. A longer internal connection and titanium grade 4 of the implant system is advantageous for static overloading condition. However, it is not only the connection design that affects the stability. The strength of the titanium grade as material is also important since it affects the implant stability. When using the implant system made of titanium grade 2, a larger diameter fixture should be selected in order to provide enough strength to withstand overloading.