• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.63-68
• /
• 2000

This paper introduces the partial melting process for solder application and characterization of its possibility using off-eutectic Pb-Sn alloy. In order to show that the liquid phase in the semi-liquid state maintains the wettability as the single-phase liquid, the wetting balance test are conducted with varying temperatures and compositions. The results are then compared with the surface tension of liquid, both measured and calculated, to examine the correlation. The results from this investigation indicate that the partial melting can yield satisfactory solder joints as long as the liquid phase acquires sufficient chemical activity. At a condition where the partial melting is effective, a direct correlation between the wettability and the surface tension is found to exist. All alloys are found to show a reasonable wettability in semi-liquid state.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.23 no.3
• /
• pp.237-242
• /
• 2014

Recently much research are has been done into the compositions of lead-free solders. As a result, there has been a rapid increase in the number of new compositions. In the past, the properties of these new compositions were determined and verified through drop-impact tests. However, these drop tests were expensive and it took a long time to obtain a result. The main goal of this study was to establish an analytical method capable of predicting the impact life-time of a new solder composition for board-level flip chips though the application of drop simulations using LS-DYNA. Based on the reaction load obtain with LS-DYNA, the drop-impact fracture cycles were predicted. The study was performed using a Sn-3.0Ag-0.5Cu solder (305 composition). To verify the reliability of the proposed analytical method, the results of the drop-impact tests and life-time analysis were compared, and were found to be in good agreement. Thus, the new analytical method was shown to be very useful and effective.

• Journal of Welding and Joining
• /
• v.21 no.7
• /
• pp.59-64
• /
• 2003

Microstructure and shear strength of Sn-Zn lead-free solders and Au/Ni/Cu UBM joint under thermal aging conditions was investigated. The samples were aged isothermally at 10$0^{\circ}C$ and 15$0^{\circ}C$ for 300, 600, and 900 hours. The IMCs(Intermetallic Compound) at the interface between solder and UBM were examined by FESEM and TEM. The results showed that the shear strength was decreased with aging time and temperature. The solder ball with high activated RA flux had about 8.2% higher shear strength than that of RMA flux. Poor wetting and many voids were observed in the fractured solder joint with of RMA flux. The decreased shear strengths were caused by IMC growth and Zn grain coarsening. Zn reacted with Au and then was transformed to the $\beta$ -AuZn compound. Although AuZn grew first, $r-Ni_5Zn_{21}$ compounds were formed with aging time. The layers indicated by $Ni_5Zn_{21}(1)$, (2), and (3) were formed with the thickness of ∼0.7 ${\mu}{\textrm}{m}$, ∼4 ${\mu}{\textrm}{m}$, and ∼2 ${\mu}{\textrm}{m}$, respectively.

• Journal of Korean society of Dental Hygiene
• /
• v.12 no.5
• /
• pp.1007-1015
• /
• 2012

Objectives : The purpose of this study was to survey Korean solders' oral healthcare recognition and perceived oral health concern. Methods : The data was collected from a questionnaire given 157 soldiers in Chungcheongnamdo. The data was analyzed into t-test, one-way ANOVA and Pearson's correlation analysis. Results : 25.5% replied that they were concerned about oral health. Soldiers who have received oral healthcare education exhibited higher recognition on the prevention of dental caries and periodontal disease. Moreover, those who have used oral hygiene devices also showed higher recognition on the prevention of dental caries and periodontal disease. The recognition of preventive effects on dental caries, in particular, showed a statistically significant difference (p<0.05). In regard to the relationship between oral health concern and recognition of oral healthcare, those who were more concerned about oral health were higher recognition of periodontal disease prevention(r=0.254, p<0.01). Conclusions : To improve concern and recognition of oral health for the members, the soldiers needs to develop oral health education and policy.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.475-480
• /
• 2002

The reliability of the solder joint is affected by type and extent of the interfacial reaction between solder and substrates. Therefore, understanding of intermetallic compounds produced by soldering in electronic packaging is essential. In-based alloys have been favored bonding devices that demand low soldering temperatures. For photonic and fiber optics packaging, m-based solders have become increasingly attractive as a soldering material candidate due to its ductility. In the present work, the interfacial reactions between indium solder and bare Cu Substrate are investigated. For the identification of intermetallic compounds, both Scanning Electron Microscopy(SEM) and X-Ray Diffraction(XRD) were employed. Experimental results showed that the intermetallic compounds, such as Cu$_{11}$In$_{9}$ was observed for bare Cu substrate. Additionally, the growth rate of these intermetallic compounds was increased with the reaction temperature and time. We found that the growth of the intermetallic compound follows the parabolic law, which indicates that the growth is diffusion-controlled.d.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.481-486
• /
• 2002

We have investigated the effects of plating materials for Cu lead (Sn-lOPb, AwPdJNi, Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu) on properties of QFP joints using a Sn-8Zn-3Bi solder. The results were compared with the joints using Sn-3. 5Ag-0. 7Cu and Sn-37Pb solders. As a result, the joints with the Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu plated Cu lead had the reliability comparable to those of the Sn-3.5Ag-0.7Cu and Sn-37Pb soldered joints with respect to the joint strength after the high temperature holding tests at 348K to 423k. In particular, the joint with the Sn-3.5Ag plated Cu lead had the best reliability. This is caused by the low growth rate of a Cu-Sn interfacial reaction layer that degrades the joint strength of the soldered joints. Consequently, the Sn-3.5Ag plating was found to be most feasible plating for the Sn-8Zn-3Bi soldered joint.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.89-96
• /
• 2000

As solder becomes small and fine, the reliability and solderability of solder joint are the critical issue in present electronic packaging industry. Besides the use of lead(Pb) containing solders for the interconnections of microelectronic subsystem assembly and packaging has enviromental problem. In this study, using Sn/Pb and Sn/Ag eutectic solder paste, in order to obtain decrease of solder joint strength with increasing aging time, initial solder joint strength and aging strength after 1000 hour aging at $100^{\circ}C$ were measured by peel test. And in order to obtain the growth of intermetallic compound(IMC) layer thickness, IMC layer thickness was measured by scanning electron microscope(SEM). As a result, solder joint strength was decreased with increasing aging time. The mean IMC layer thickness was increased linearly with the square root of aging time. The diffusion coefficient(D) of IMC layer was found to $1.29{\times}10^{-13}{\;}cm^2/s$ at using Sn/Pb solder paste, 7.56{\times}10^{-14}{\textrm}{cm}^2/s$ at using Sn/Ag solder paste.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.2
• /
• pp.119-125
• /
• 2017

We have studied the effects of Ag on the characteristics of $Sn_{43}Bi_{57}Ag_x$(wt%) lead-free solders for photovoltaic ribbon. Ag atoms in the solder formed an alloy phase of Ag3Sn after reacting with some part of Sn atoms, while they did not react with Bi atoms, but decreased the mean size of Bi solid phase and the thickness of solder. When Ag atoms of 3.0 wt% was added to eutectic $Sn_{43}Bi_{57}$(wt%) solder, it showed the optimally useful results that the peel strength of photovoltaic ribbon greatly increased and the sheet resistance of the solder decreased. In the meanwhile, the eutectic $Sn_{43}Bi_{57}$(wt%) solder showed a low melting temperature of $138.9^{\circ}C$, and showed a very similar result regardless of the added amount of Ag atoms.

• Journal of Welding and Joining
• /
• v.27 no.1
• /
• pp.85-89
• /
• 2009

Reflow process conditions were investigated for 0402 electric parts with Sn-3.0Ag-0.5Cu solders. Circle hole shape metal mask with 100 m thickness showed excellent printability. Self alignment abilities were 71% for 1005 chips, 52% for 0603 chips, and 3% for 0402 chips. Average joining strengos were 1990 gf for 1005 chips, 867 gf for 0603 chips, and 525 gf for 0402 chips. As mis-mounting angle increased, joining strength decreased. Considering self-alignment ability, mounting angle had to be under $5^{\circ}$ and contact area of the chips had to be over 40% for Pb-free soldering process for 0402 chips.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.74-80
• /
• 2014

Due to environmental regulations (RoHS, WEEE and ELV) of the European Union, electronics and automotive electronics have to eliminate toxic substance from their devices and system. Especially, reliability issue of lead-free solder joint is increasing in car electronics due to ELV (End-of-Life Vehicle) banning from 2016. We have prepared engine control unit (ECU) modules soldered with Sn-40Pb and Sn-3.0Ag-0.5Cu (SAC305) solders, respectively. Degradation characteristics of solder joint strength were compared with various conditions of automobile environment such as cabin and engine room. Thermal cycle test (TC, $-40^{\circ}C$ ~ ($85^{\circ}C$ and $125^{\circ}C$), 1500 cycles) were conducted with automotive company standard. To compare shear strength degradation rate with eutectic and Pb-free solder alloy, we measured shear strength of chip components and its size from cabin and engine ECU modules. Based on the TC test results, finally, we have known the difference of degradation level with solder alloys and use environmental conditions. Solder joints degradation rate of engine room ECU is superior to cabin ECU due to large CTE (coefficient of thermal expansion) mismatch in field condition. Degradation rate of engine room ECU is 50~60% larger than cabin room electronics.