• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.3
• /
• pp.1-6
• /
• 2019

Wettability is an important factor to decide solderability of solder, flux, other soldering-related materials and soldering conditions. The wettability also affects the reliability of solder joint. Wetting balance test is a good method for quantitatively measuring wettability between solder and substrate. The wetting balance test is easy to reproduce the wetting experiment and to measure the wetting time and force. And this test provides wetting curve to calculate the surface tension of the molten solder. Development of new solder has been continued in accordance with various and harsh environment in the electronics industry. In this paper, the principle of wetting balance test and recent research issues including nano-composite solder are explained.

• Journal of Welding and Joining
• /
• v.20 no.5
• /
• pp.106-112
• /
• 2002

In the present study, the wettability and interfacial tension between (bare Cu, electroless Ni/cu, immersion Au/Ni/Cu) substrates and indium solder were investigated as a function of soldering temperature, types of flux. The wettability of In solder increased with soldering temperature and solid content of flux. The wettability of In solder was affected by the substrate metal finish used, i.e., nickel, gold and copper. On the bare Cu substrate, In solder wet better than any of the substrate metal finishes tested. Intermetallic compound formation between liquid solder and substrate reduced the interfacial energy and improved wettability. For the identification of intermetallic compounds, X-Ray Diffraction(LRD) were employed. Experimental results showed that the intermetallic compounds, such as Cu11In9 and In27Ni10 are observed f3r different substrates respectively. The wetting kinetics is investigated by measuring wetting time with the wetting balance technique. The activation energy of wetting calculated for the In solder/cu substrate and In solder/electroless Au/Ni/Cu substrate are 36.13 and 27.36 kJ/mol, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.2
• /
• pp.1-9
• /
• 2017

Recently, there has been a continuous researches on solders having sophisticated and improved performance due to demand for high-density and miniaturization of electronics, and development of solder for automotive electronics which can be used in harsh environment. When developing a new solder alloy, there is a wettability of solder on substrate for things to consider, and the wetting balance test is one of the methods for measuring that one. In this paper, the wetting balance test is introduced, and the calculus of the surface tension of solder and the contact angle between solder and substrate using wetting curve obtained is introduced too. In detail, the principle and test method of the wetting balance test, the introduction of the parameters with important meaning in the wetting curve, the method of calculating the contact angle as well as the surface tension of the solder using the shape of the solder meniscus.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.35-41
• /
• 2015

In this study, in order to improve the reliability of ACF interconnections, solder ACF joints were investigated interms of solder joint morphology and solder wetting areas, and evaluated the electrical properties of Flex-on-Board (FOB) interconncections. Solder ACF joints with the ultrasonic bonding method showed excellent solder wetting by broken solder oxide layers on solder surfaces compared with solder joints with remaining solder oxide layer bonded by the conventional thermo-compression (TC) bonding method. When higher target temperature was used, Sn58Bi solder joints showed concave shape due to lower degree of cure of resin at solder MP by higher heating rate. ACFs with epoxy resins and SAC305 solders showed lower degree of resin cure at solder MP due to the slow curing rate resulting in concave shaped solder joints. In terms of solder wetting area, solder ACFs with $25-32{\mu}m$ diameters and 30-40 wt% showed highest wetted solder areas. Solder ACF joints with the concave shape and the highest wetting area showed lower contact resistances and higher reliability in PCT results than conventional ACF joints. These results indicate that solder morphologies and wetting areas of solder ACF joints can be controlled by adjustment of bonding conditions and material properties of solder and polymer resin to improve reliability of ACF joints.

• Korean Journal of Metals and Materials
• /
• v.50 no.8
• /
• pp.563-568
• /
• 2012

The wetting property and reflectivity of Sn-3.5Ag solder which was dip coated on a LED lead frame were investigated. The wettability of molten solder on Cu substrate was evaluated by the wetting balance tester, and surface tension was calculated from maximum withdrawal force and withdrawal time. Temperature of the molten solder in a bath was varied in the range of $250-290^{\circ}C$. With increasing temperature, the surface tension decreased a little. The reflectivity of Sn-3.5Ag coated on a substrate became a little lower than the highest current LED lead frame reflectivity.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.549-554
• /
• 2003

The purpose of this paper is to investigate the solder properties by the change of P mass percentage. Tension test, wetting balance test, spread test, and analysis of intermetallic compound after isothermal aging of Sn-2.5Ag-0.7Cu-0.005P, Sn-2.5Ag-0.7Cu-0.01P, Sn-2.5Ag-0.7Cu-0.02P, Sn-0.7Cu-0.005P were performed. Adding P in the solder alloys resulted in improvement of tensile strength, reduction of intermetallic compound growth, reduction of oxidization in fusible solders under wave soldering. After comparing solder alloy containing P with tin-lead eutectic solder alloy, P contained solders alloys showed much better solder properties than eutectic solder alloy. Furthermore, this solder alloy presented remarkable properties than any other lead-free solder alloy.

• Journal of Welding and Joining
• /
• v.16 no.6
• /
• pp.77-85
• /
• 1998

Effects of non-cleaning and cleaning fluxes on the wetting properties and defects at flow soldered joints were investigated. Non-cleaning flux (R-type of 3.3% solid content) and cleaning flux (RMA-type of 15% solid content) were used. Wetting test was accomplished by wetting balance method with changing surface state of wetting specimen, CU. Sn-37%Pb solder was used for wetting test and flow soldering. As experimental results, the wetting time for vertical force from the surface tension being zero was mainly affected by surface state of the wetting specimen. Non-cleaning flux had a good wettability compared with cleaning flux. In case of non-cleaning flux, conveyor speed had a great affection to defects of bridge, icicle, and poor solder.

• Journal of Welding and Joining
• /
• v.25 no.6
• /
• pp.78-83
• /
• 2007

The wettability of Sn-Xwt%Cu(X=$0{\sim}3wt%$) solder was evaluated with wetting balance tester. And, the intermetallic compounds(IMCs) which were formed at the interface between solders and pads were investigated by using scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS). The wetting force of Sn-0.7wt%Cu solder was higher than that of 100wt%Sn and Sn-3.0wt%Cu solder. The value of $\gamma_{fl}$ and ($\gamma_{fs}-\gamma_{ls}$) had a tendency to increase with increasing the wetting temperature. The activation energy with bare Cu pad and flux with 15% solid content was increased in the following order: Sn-0.7Cu (68.42 kJ/mol) ; Sn-3.0Cu(72.66 kJ/mol) ; Sn solder(94.53 kJ/mol). It was identified that the Cu6Sn5 phase was formed at the interface between Sn-Xwt%Cu solder and Cu pad.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.11-16
• /
• 2002

As environmental concerns increasing, the electronics industry is focusing more attention on lead free solder alternatives. In this research, we have researched wettability of intermediate solder of Sn3Ag9Bi5In, which include In and Bi and has similar melting temperature to Sn37Pb eutectic solder. We investigated the wetting property of Sn3Ag9Bi5In. To estimate wettability of Sn3Ag9Bi5In solder on various substrates, the wettability of Sn3Ag9Bi5In solder on high-pure Cu-coupon was measured. Cu-coupon that plated Sn, Ni and Au/Ni and Si-wafer adsorbed Ni/Cu under bump metallurgy on one side. As a result, the wetting property of Sn3Ag9Bi5In solder is a little better than that of Sn37Pb and Sn3.5Ag.

• Korean Journal of Materials Research
• /
• v.28 no.2
• /
• pp.89-94
• /
• 2018

The properties of 18 K red gold solder alloys were investigated by changing the content of In up to 10.0 wt% in order to replace the hazardous Cd element. Cupellation and energy dispersive X-ray spectroscopy (EDS) were used to check the composition of each alloy, and FE-SEM and UV-VIS-NIR-Colormeter were employed for microstructure and color characterization. The melting temperature, hardness, and wetting angle of the samples were determined by TGA-DTA, the Vickers hardness tester, and the Wetting angle tester. The cupellation result confirmed that all the samples had 18K above 75.0wt%-Au. EDS results showed that Cu and In elements were alloyed with the intended composition without segregation. The microstructure results showed that the amount of In increased, and the grain size became smaller. The color analysis revealed that the proposed solders up to 10.0 wt% In showed a color similar to the reference 18 K substrate like the 10.0 wt% Cd solder with a color difference of less than 7.50. TGA-DTA results confirmed that when more than 5.0 wt% of In was added, the melting temperature decreased enough for the soldering process. The Vickers hardness result revealed that more than 5.0 wt% In solder alloys had greater hardness than 10.0 wt% Cd solder, which suggested that it was more favorable in making a wire type solder. Moreover, all the In solders showed a lower wetting angle than the 10.0 wt% Cd solder. Our results suggested that the In alloyed 18 K red gold solders might replace the conventional 10.0 wt% Cd solder with appropriate properties for red gold jewelry soldering.