• Korean Journal of Crystallography
• /
• v.6 no.2
• /
• pp.111-117
• /
• 1995

TiO2 thin films were prepared on a (100)silicon wafer using a chemical vapor deposition(CVD) method. The deposition experiments were performed using the TTIP in the deposition temperature ransing from 200 content. The deposition rate of TiO2 was increased with the substrate temperature and the oxygen content. The thickness of the deposited thin film and the compositional analysis of this thin films with theoxygen content were measured using Ellipsometry, SEM and ESCA, respectively. The deposited thin film was composed of a bilayer, external TiO2 and internal Ti. Carbon as a residual impurity was found to remain when zero sccm O2 was purged into a reaction chamber and the composition of the deposited thin film was found to change Ti into TiO in a deeper layer. However, when 600sccm O2 was supplied to a reaction chamber, it has been found to reside less carbon content than without O2. Finally, in the condition of 1200sccm O2, no impurity level of carbon was observed and a deeper layer consisted of the Ti composite, even though the deposited surface was composed of TiO2.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.39.1-39.1
• /
• 2009

본 실험은 연성과 광 투명도가 뛰어난 아크릴 (PMMA) 과 폴리카보네이트 (Polycabonate) 기판의 축전 결합형 플라즈마 (CCP) 건식 식각 연구에 관한 것이다. 특히 식각 반응기 내부의 압력 변화에 따른 두 기판의 건식 식각 특성 분석에 초점을 맞추었다. 실험에 사용된 기판은 두께 1mm의 아크릴 (PMMA) 과 폴리카보네이트 (Polycabonate)를 $1.5\times1.5\;cm^2$로 절단하여 Photo-lithography 공정을 통하여 감광제 (Photo-resist)로 패턴하였다. 식각 반응기 내부에 패턴 된 아크릴(PMMA) 과 폴리카보네이트 (Polycabonate)를 넣은 후 반응기 내부 진공 상태로 만들었다. 그 후 5 sccm $O_2$ 가스를 유량조절기 (Mass flow controller)를 통하여 식각 반응기 내부로 유입하여 실험을 하였다. 이때 식각 공정 변수는 식각 반응기 내부 압력과 샘플 척 파워이다. 특성평가 항목은 식각 후 기판 (Substrate)의 식각율 (Etch rate), 식각 선택비 (Selectivity) 그리고 기판 표면 거칠기 (RMS roughness)이다. 실험 결과는 표면 단차 분석기(Surface profiler)를 이용하여 기판 (Substrate)의 표면을 분석 하였다. 또한 OES (Optical Emission Spectroscopy) 를 이용하여 식각 중 내부 플라즈마의 상태를 분석하였다. 본 실험 결과에 따르면 5 sccm $O_2$ 가스와 100 W 척 파워를 고정한 후 반응기 내부의 압력을 25 mTorr에서 180 mTorr까지 변화시켜 실험한 결과 40 mTorr의 반응기 내부 압력에서 실험 자료 중 가장 높은 식각율로 아크릴 (PMMA)은 $0.46\;{\mu}m/min$, 폴리카보네이트 (Polycabonate)는 $0.28\;{\mu}m/min$의 결과를 얻었다. 또한 이 자료를 바탕으로 5 sccm $O_2$ 가스와 반응기 내부 압력을 40 mTorr로 고정시키고 RIE 척 파워를 25 W에서 150 W로 증가시켰을 때 아크릴 (PMMA)의 식각율은 $0.15\;{\mu}m/min$에서 $0.72\;{\mu}m/min$까지 증가하였고, 폴리카보네이트 (Polycabonate) 의 식각율은 $0.1\;{\mu}m/min$에서 $0.36\;{\mu}m/min$까지 증가하였다.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.13 no.4
• /
• pp.82-86
• /
• 1999

Electron Energy Distribution Function(EEDF) were treasured In Radio-Frequency Inductively Coupled Plasma(RFlCP) using a probe rrethocl Measurerrents were conducted in argon discharge for pressure from 10[mTorr] to 4O[mTorr] and input rf power from 100[W] to 600[W] and flow rate from 3[sccm] to 12[sccm]. Spatial distribution of electron energy distribution function were measured for discharge with same aspoct ratio (R/L=2). Electron energy distribution function strongly depended on both pressure and power. Electron energy distribution function increased with increasing flow rate. Radial distribution of the electron energy distribution function were peaked in the plasma center. Normal distribution of the electron energy distribution function were peaked in the center between quartz plate and substrate. From the results, we can find out the generation mechanism of Radio Frequency Inductively Coupled Plasma. And these results contribute the application of a simple Inductively Coupled Plasma(ICP).a(ICP).

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.3
• /
• pp.157-161
• /
• 2012

In this study, we investigated the etching characteristics of ITO thin films and the effects of inert gases added to $Cl_2/BCl_3$ inductivity coupled plasma. The maximum etch rate of ITO thin film was 130.0 nm/min upon the addition of Ar (6 sccm) to the $Cl_2/BCl_3$ (4:16 sccm) plasma, which was higher than that with He or $N_2$ added to the plasma. The ion bombardment by $Ar^+$ sputtering was due to the relatively low volatility of the by-products formed in the $Cl_2/BCl_3$ (4:16 sccm) plasma. The surface of the etched ITO thin film was characterized by x-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). From the XPS results, it is concluded that the proper addition of Ar and He to the $Cl_2/BCl_3$ plasma removes carbon and by-products from the surface of the etched ITO thin film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.10
• /
• pp.662-667
• /
• 2014

B-doped Si nanoparticles were synthesized by using inductive coupled plasma and specially designed double tube reactor, and their microstructures were investigated. 0~10 sccm of $B_2H_6$ gas was injected during the synthesis of Si nanoparticles from $SiH_4$ gas. Highly crystalline Si nanoparticles were synthesized, and their crystallinity did not change with increase of $B_2H_6$ flow rates. From SEM measurement, their particle sizes were approximately 30 nm regardless of $B_2H_6$ flow rates. From SIMS analysis, almost saturation of B in Si nanoparticles was detected only when 1 sccm of $B_2H_6$ was injected. When $B_2H_6$ flow rate exceeded 5 sccm, higher concentration of B than solubility limit was detected even if any secondary phase was not detected in XRD or HR-TEM results. Due to their high electronic conductivity, those heavily B-doped Si nanoparticles can be a potential candidate for an active material in Li-ion battery anode.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.149-149
• /
• 2010

The double-layer antireflection (DLAR) coatings have significant advantages over single-layer antireflection (SLAR) coatings. This is because they will be able to cover a broad range of the solar spectrum which would enhance the overall performance of solar cells. Moreover films deposited at high frequency are expected to show excellent and UV-stable passivation in the refractive index that we adopted. In this work, we present a novel DLAR coating using SiNx:H thin films with refractive indices 1.9 and 2.3 as the top and bottom layers. This approach is cost effective when compared to earlier DLAR coatings with two different materials. SiNx:H films were deposited by Plasma enhanced chemical vapor deposition (PECVD) technique using $SiH_4$, $NH_3$ and $N_2$ gases with flow rates 20~80sccm, 200sccm and 85 sccm respectively. The RF power, plasma frequency and substrate temperature for the deposition were 300W, 13.56 MHz and $450^{\circ}C$, respectively. The optimum thickness and refractive indices values for DLAR coatings were estimated theoretically using Macleod simulation software as 82.24 nm for 1.9 and 68.58 nm for 2.3 respectively. Solar cells were fabricated with SLAR and DLAR coatings of SiNx:H films and compared the cell efficacy. SiNx:H> films deposited at a substrate temperature of $450^{\circ}C$ and that at 300 W power showed best effective minority carrier lifetime around $50.8\;{\mu}s$. Average reflectance values of SLAR coatings with refractive indices 1.9, 2.05 and 2.3 were 10.1%, 9.66% and 9.33% respectively. In contrast, optimized DLAR coating showed a reflectance value as low as 8.98% in the wavelength range 300nm - 1100nm.

• Journal of the Semiconductor & Display Technology
• /
• v.9 no.3
• /
• pp.53-58
• /
• 2010

In this study, we have investigated the effect of the ambient gases on the characteristics of IZO thin films for the OLED (organic light emitting diodes) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering under various ambient gases (Ar, $Ar+O_2$ and $Ar+H_2$) at $150^{\circ}C$. In order to investigate the influences of the oxygen and hydrogen, the flow rate of oxygen and hydrogen in argon mixing gas has been changed from 0.1sccm to 0.5sccm, respectively. All the samples show amorphous structure regardless of ambient gases. The electrical resistivity of IZO film increased with increasing flow rate of $O_2$ under $Ar+O_2$ while under $Ar+H_2$ atmosphere the electrical resistivity showed minimum value near 0.5sccm of $H_2$. All the films showed the average transmittance over 85% in the visible range. The OLED device was fabricated with different IZO substrates made by configuration of IZO/${\alpha}$-NPD/DPVB/$Alq_3$/LiF/Al to elucidate the performance of IZO substrate. OLED devices with the amorphous-IZO (a-IZO) anode film show better current densityvoltage-luminance characteristics than that of OLED devices with the commercial crystalline-ITO (c-ITO) anode film. It can be explained that very flat surface roughness and high work function of a-IZO anode film lead to more efficient hole injection by reduction of interface barrier height between anode and organic layers. This suggests that a-IZO film is a promising anode materials substituting conventional c-ITO anode in OLED devices.

• Korean Journal of Metals and Materials
• /
• v.46 no.10
• /
• pp.683-690
• /
• 2008

In order to develop transparent electrodes for high efficiency GaN-based light emitting diodes (LEDs), the electrical and optical properties of the electron beam evaporated ITO contacts have been investigated as a function of the deposition temperature and flow rate of oxygen during the deposition. As the deposition temperature increases from $140^{\circ}C$ to $220^{\circ}C$, the resistivity of the ITO films decreases slightly from $4.0{\times}10^{-4}{\Omega}cm$ to $3.3{\times}10^{-4}{\Omega}cm$, meanwhile the transmittance of the ITO films significantly increases from 67% to 88% at the wavelength of 470 nm. When the flow rate of oxygen during the deposition increases from 2 sccm to 4 sccm, the resistivity of the ITO films increases from $3.6{\times}10^{-4}{\Omega}cm$ to $7.4{\times}10^{-4}{\Omega}cm$, meanwhile the transmittance of the ITO films increases from 86% to 99% at 470 nm. Blue LEDs fabricated with the electron beam evaporated ITO electrode show that the ITO films deposited at $200^{\circ}C$ and 3 sccm of the oxygen flow rate give a low forward-bias voltage of 3.55 V at injection current of 20 mA with a highest output power.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.260-264
• /
• 2012

We have investigated the effect of ambient gases on the structural, electrical, and optical characteristics of IZO thin films intended for use as anode contacts in the organic light emitting diodes (OLED) devices. These IZO thin films were deposited on the PES film by radio frequency (RF) magnetron sputtering under different ambient gases (Ar, Ar + O2, and Ar + H2) at room temperature. In order to investigate the influences of the ambient gases, the flow rate of oxygen and hydrogen in argon has been changed from 0.1 sccm to 0.5 sccm, respectively. All the IZO thin film has an (222) preferential orientation regardless of ambient gases. The electrical resistivity of the IZO film increased with increasing O2 flow rate, whereas the electrical resistivity decreased sharply under an Ar + H2 atmosphere and was nearly similar regardless of the H2 flow rate. The change of electrical resistivity with changes in the ambient gas composition was mainly interpreted in terms of the charge carrier concentration rather than the charge carrier mobility. All the films showed the average transmittance over 85% in the visible range. The OLED device was fabricated with different IZO substrates made with the configuration of IZO/α-NPD/DPVB/Alq3/LiF/Al in order to elucidate the performance of the IZO substrate. The current density and the luminance of OLED devices with IZO thin films deposited in 0.5 sccm H2 ambient gas are the highest amongst all other films.

• Journal of the Korean Vacuum Society
• /
• v.18 no.2
• /
• pp.141-146
• /
• 2009

PLZT ferroelectric thin films were deposited on Pt/Ti/$SiO_2$/Si substrate with $TiO_2$ buffer layer in between by rf magnetron sputtering method. In order to investigate the effect of Ar/$O_2$ partial pressure ratio on the ferroelectric properties of PLZT thin films, PLZT thin films were deposited at various Ar/$O_2$ partial pressure ratio ; 27/1.5 seem, 23/5.5 seem, 21/7.5 seem and 19/9.5 seem. The crystallinities of PLZT thin films were analyzed by XRD. The surface morphology was observed using FE-SEM. The P-E hysteresis loops, the remanent polarization characteristics and the leakage current characteristics were obtained using a Precision LC. The crystallinity and elaborateness of PLZT thin films were decreased as increasing the oxygen partial pressure ratio. And preferred orientation of PLZT thin films changed from (110) plane to (111) plane. The oxygen partial pressure ratio affects the thin film surface morphology and the ferroelectric properties.