• Korean Journal of Materials Research
• /
• v.18 no.4
• /
• pp.204-210
• /
• 2008

$1.5\;{\mu}m$-thick copper films deposited on silicon wafers were successfully bonded at $415^{\circ}C$/25 kN for 40 minutes in a thermo-compression bonding method that did not involve a pre-cleaning or pre-annealing process. The original copper bonding interface disappeared and showed a homogeneous microstructure with few voids at the original bonding interface. Quantitative interfacial adhesion energies were greater than $10.4\;J/m^2$ as measured via a four-point bending test. Post-bonding annealing at a temperature that was less than $300^{\circ}C$ had only a slight effect on the bonding energy, whereas an oxygen environment significantly deteriorated the bonding energy over $400^{\circ}C$. This was most likely due to the fast growth of brittle interfacial oxides. Therefore, the annealing environment and temperature conditions greatly affect the interfacial bonding energy and reliability in Cu-Cu bonded wafer stacks.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.155-161
• /
• 2000

BN films composed of c-BN(70%) and h-BN(30%) phases have been synthesized by the ion beam assisted deposition (IBAD) process and stabilized by post-annealing. Boron was e-beam evaporated at 1.2 $\AA$/sec and nitrogen was ionized and accelerated at about 100 eV by the end-hall type ion gun. Substrates were negatively biased by DC 400 and 500 V, respectively, and heated at $700^{\circ}C$. Synthesized BN films were in-situ post-annealed at 700 or $800^{\circ}C$, respectively, for 1 hr without breaking vacuum. BN films without post-annealing were peeled off from substrates immediately when they were exposed to the air while those with post-annealing at $800^{\circ}C$ were stabilized. Post annealing reduced the film stress from 4.9 GPa to 3.4 GPa, but no considerable stress release in the c-BN phase was observed, contrary to previous reports that the stress relaxation in the c-BN phase is the main mechanism for the stabilization. Structural and chemical relaxation of non c-BN phase is supposed to be responsible for the film stress reduction and, in turn, stabilization, especially when the c-Bn content of the film is not high.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.8
• /
• pp.734-739
• /
• 2005

Zinc oxide films were deposited on Si (111) substrates by radio-frequency (rf)sputtering at a room temperature and post annealed in Na, air, and $H_2O$ ambient at temperatures between $800{\circ}C$ for 2 hrs. The properties were investigated by atomic force microscope (AFM), X-ray diffraction (XRD), Auger electron spectroscopy (AES) and photoluminescence (PL). Our experiments demonstrated that ZnO films have the better crystal quality for post thermal annealing and especially in $H_2O$ ambient. Even though thermal annealing reduced deep level emission somewhat, for further getting rid off deep level emission, oxygen contents should be adjusted. In our results, $H_2O$ ambient gave the best structural and optical properties.

• Journal of the Semiconductor & Display Technology
• /
• v.19 no.2
• /
• pp.55-59
• /
• 2020

Copper Oxide (CuO) films were deposited on the n-type silicon wafer by rf magnetron sputtering for heterojunction solar cells. And then the samples were treated as a function of the annealing temperature (300-600℃) in a vacuum. Their electrical, optical and structural properties of the fabricated heterojunction solar cells were then investigated and the power conversion efficiencies (PCE) of the fabricated p-type copper oxide/n-type Si heterojunction cells were measured using solar simulator. After being treated at temperature of 500℃, the solar cells with CuO film have PCE of 0.43%, Current density of 5.37mA/㎠, Fill Factor of 39.82%.

• New & Renewable Energy
• /
• v.17 no.4
• /
• pp.36-45
• /
• 2021

To remove the Cu secondary phase remaining on the surface of a CIGSSe absorber layer manufactured by the two-step process, KCN etching was applied before depositing the CdS buffer layer. In addition, it was possible to increase the conversion efficiency by air annealing after forming the CdS buffer layer. In this study, various pre-treatment/post-treatment conditions wereapplied to the S-containing CIGSSe absorber layerbefore and after formation of the CdS buffer layer to experimentally confirm whether similareffects as those of Se-terminated CIGSe were exhibited. Contrary to expectations, it was noted that CdS air annealing had negative effects.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.668-671
• /
• 2001

The Sr$\_$0.8/Si$\_$2.4/Ta$_2$O$\_$9/(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO$_2$/SiO$_2$/Si) using RF magnetron sputtering method. With increasing post-annealing temperature from 600[$^{\circ}C$] to 850[$^{\circ}C$], Bi-layered perovskite phase was crystallized above 650[$^{\circ}C$]. The maximum remanent polarization and the coercive electric field is 11.60[${\mu}$C/$\textrm{cm}^2$], 48[kV/cm] respectively. The leakage current density of SBT capacitor at post-annealing temperature of 750[$^{\circ}C$] is 1.01${\times}$10$\^$-8/ A/$\textrm{cm}^2$ at 100[kV/cm]. The fatigue characteristics of SBT thin films did not change up to 10$\^$10/ switching cycles.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.2
• /
• pp.93-98
• /
• 2020

We investigated the effect of a post-annealing process using ultraviolet (UV) light on the electrical properties of solution-processed InZnO (IZO) thin-film transistors (TFTs). UV light was irradiated on IZO TFTs for different time periods of 0s, 30s, and 90s. We measured transfer and retention stability curves to evaluate the performance of the fabricated TFTs. In addition, we measured height, amplitude, and phase AFM images to analyze changes in the surface and morphology of the devices. AFM measurements were performed by setting the drive amplitude of the cantilever tip to 47.9 mV in tapping mode, then dividing the device surface into 500 nm × 500 nm. In the case of IZO TFT irradiated with UV for 30s, the electron mobility and I_on/I_off ratio were improved, the threshold voltage was reduced by approximately 2 V, and the subthreshold swing also decreased form 1.34 V/dec to 1.11 V/dec.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1988.05a
• /
• pp.27-30
• /
• 1988

This paper is investigated on the sublimation in obliguely deposited a-$Se_{75}Ge_{25}$ films. With varying the treatment conditions, the transmittance in each of $0^{\circ}$, $60^{\circ}$, and $80^{\circ}$-deposited films and the absorbance in $80^{\circ}$-deposited film were measured. By increasing the angle of deposition, the variation of transmittance in post-exposure annealing film showed the characteristic different from that in only exposed film or annealed film. And the changes of thickness in $80^{\circ}$-deposited film were measured. The results showed that the changing rate of thickness was 1.4% in exposed film and 9.4% in post-exposure annealing film. Therefore, in $80^{\circ}$-deposited film, the possibility for sublimatin due to physical and chemical change by post-exposure annealing can be suggested.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1992.02a
• /
• pp.93-94
• /
• 1992

2X1018 ions/cmz at 180 keV and post-implantation annealing at 12500C for 6 hours in nitrogen ambient. The oxygen redistribution process during post-implantation annealing was examined by AES and TEM. The electrical property of the structure was investigated by SRP method. We could find oxygen precipitates in SOl layer after high temperature annealing. The influence of the precipitates to the electrical property of the SOl layer was discussed. And the Iimiting factor to the decrease of the precipi tates during post-implantation anneal ing was discussed also.

• Journal of the Korean Vacuum Society
• /
• v.8 no.3A
• /
• pp.224-230
• /
• 1999

$SrBi_{2x}Ta_2O_9$ (SBT) thin films were prepared on platinized silicon substrates by MOD process, and their ferroelectric and leakage current characteristics were investigated. The grain size of the MOD derived SBT films increased with increasing the BI/Ta mole ration. Although the SBT films with x of 0.8~1.2 were composed of the equiaxed grains, the elongated grains were also observed for the SBT films with x of 1.4 and 1.6. The SBT film with x of 1.2 exhibited the optimum ferroelectric properties of 2PR : 9.79 $\muC/\textrm{cm}^2$ and Ec : 24.2kV/cm at applied voltage of 5V. The leakage current density of the SBT films increased with increasing the BI/Ta mole ratio. With post annealing process, 2Pr and $E_c$of the SBT film with x of 1.2 increases 11.3 $\muC/\textrm{cm}^2$ and 39.6kV/cm, respectively. decrement of the leakage current density by post annealing process increased remarkably with increasing the Bi/ta mole ratio, and the SBT film with x=1.6 exhibited the lowest leakage current density after post annealing process.