• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.223-226
• /
• 1999

The purpose of this study is no examine the combination effect on strength preperties of water-permeable concretes mixed with redispersible polymer, silica fume and polypropylene fibers for overlay in pavement. The water-permeable concrete with a water-cement ration of 25%, polymer-cement ratios of 0 to 10%, silica fume contents of 0 to 10% and polypropylene fiver contents of 0 to 1.5% are prepared, and tested for flexural strength, compressive strength and water permeability. It is concluded concretes are obtained at a polypropylene fiber content of 1.0% and a silica fume content of 10% with a void filling ratio of 50%. And the water-permeable concretes with a flexural strength of 14.1~28.0kgf/$\textrm{cm}^2$, a compressive strength of 71.2~128.0kgf/$\textrm{cm}^2$, and a coefficient of permeability of 1.22~2.52cm/s at a void filling ratio of 30% can be prepared. Also water-permeable concretes having flexural strength of 24.9~57.9kgf/$\textrm{cm}^2$, a compressive strength of 83.8~268.5kgf/$\textrm{cm}^2$, and a coefficient of permeability of 0.24~1.04cm/s at a void filling ratio of 50% can be prepared in the consideration of the mix proportioning factors.

• Carbon letters
• /
• v.19
• /
• pp.1-11
• /
• 2016

In efforts to characterize and understand the properties and processing of phenylethynyl-terminated imide (LaRC PETI-5, simply referred to as PETI-5) oligomers and polymers as a high-temperature sizing material for carbon fiber-reinforced polymer matrix composites, PETI-5 imidization and thermal curing behaviors have been extensively investigated based on the phenylethynyl end-group reaction. These studies are reviewed here. In addition, the use of PETI-5 to enhance interfacial adhesion between carbon fibers and a bismaleimide (BMI) matrix, as well as the dynamic mechanical properties of carbon/BMI composites, are discussed. Reports on the thermal expansion behavior of intercalated graphite flake, and the effects of exfoliated graphite nanoplatelets (xGnP) on the properties of PETI-5 matrix composites are also reviewed. The dynamic mechanical and thermal properties and the electrical resistivity of xGnP/PETI-5 composites are characterized. The effect of liquid rubber amine-terminated poly(butadiene-co-acrylonitrile) (ATBN)-coated xGnP particles incorporated into epoxy resin on the toughness of xGnP/epoxy composites is examined in terms of its impact on Izod strength. This paper provides an extensive overview from fundamental studies on PETI-5 and xGnP, as well as applied studies on relevant composite materials.

• KSTLE International Journal
• /
• v.8 no.1
• /
• pp.1-6
• /
• 2007

Chromatic device was developed using light emitting diodes, optic fibers and photodiodes. Chromatic ratio and total contamination parameters based on transmitted light intensity in Red, Green, and Blue wavelengths were used for oil chemical and particulate contamination assessment. Chromatic ratio criterion was found independent of the particulate contamination of oil; but depended on chemical degradation, being more sensitive for synthetic than mineral hydraulic oil. Total contamination index of the sensor depended on both the chemical degradation and particulate contamination of the oil; being most sensitive in blue wavelength, and least in the red. Test results for synthetic hydraulic oils monitored corroborated with results of other tests such as viscosity, total acid number, elemental optical emission spectroscopy, particulate counts and UV-VIS photospectrometry. Chromatic ratio showed a clearer indication of oil degradation, compared to key monitoring parameters such as total acid number, viscosity and particle counts. The results showed that these parameters are effective criteria for the condition monitoring of synthetic hydraulic oils.

• Structural Engineering and Mechanics
• /
• v.67 no.4
• /
• pp.403-415
• /
• 2018

In the present study, nonlinear dynamic response of polymer-CNT-fiber multiscale nanocomposite plate resting on elastic foundations in thermal environments using the finite element method is performed. In this regard, the governing equations are derived based on Inverse Hyperbolic Shear Deformation Theory and von $K{\acute{a}}rm{\acute{a}}n$ geometrical nonlinearity. Three type of distribution of temperature through the thickness of the plate namely, uniform linear and nonlinear are considered. The considered element is C1-continuous with 15 DOF at each node. The effective material properties of the multiscale composite are calculated using Halpin-Tsai equations and fiber micromechanics in hierarchy. The carbon nanotubes are assumed to be uniformly distributed and randomly oriented through the epoxy resin matrix. Five types of impulsive loads are considered, namely the step, sudden, triangular, half-sine and exponential pulses. After examining the validity of the present work, the effects of the weight percentage of SWCNTs and MWCNTs, nanotube aspect ratio, volume fraction of fibers, plate aspect, temperature, elastic foundation parameters, distribution of temperature and shape of impulsive load on nonlinear dynamic response of CNT reinforced multi-phase laminated composite plate are studied in details.

• Polymer(Korea)
• /
• v.24 no.2
• /
• pp.174-181
• /
• 2000

The ACF/PP-g-AN copolymers were synthesized by the irradiational grafting of acrylonitrile onto ACF/PP hybrid fabric. The synthesis of the ACF/PP-g-AN copolymer was evidenced by the band of -C=N absorption peak at 2250 $cm^{-1}$ / and amidoximation was evidenced by the band of -OH and -NH$_2$ peak at 3450 $cm^{-1}$ / on FT-IR spectrum. The optimal time for the uranium ion adsorption equilibrium on ACF/PP-g-AN copolymers was 8 days and the optimal pH was 8. The adsorption capacities of ACF/PP-g-AN copolymers increased according to the content of amidoxime and were not varied even after more than 10 times of regeneration.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.512-517
• /
• 2007

The grafting of styrene, glycidylmethacrylate (GMA) or acrylic acid (AAc) onto kapok fiber were performed by $Co_{60}\;{\gamma}-ray$ radiation-induced graft copolymerization. Degree of grafting (DG) of copolymers were increased with increasing monomer concentration and radiation dose. In addition to we confirmed the introduced functional group and measured ion exchange capacity. Morphology of the ion exchange fibers and their structures were analyzed by SEM and FT-IR.

• Fibers and Polymers
• /
• v.4 no.1
• /
• pp.27-31
• /
• 2003

A major concern in solvent extraction process is the loss of extractant into the aqueous phase due to its slight solubility in the aqueous phase. Similarly, in membrane extraction processes, extractant loss through extractant leakage from the membrane into the aqueous phase is also a concern. Several published membrane extraction studies using Aliquat 336 ai the extractant, have expressed this concern, but none has studied extractant leakage quantitatively. It is the authors' opinion that the extractant leakage should be considered at a technical parameter of a membrane. In our laboratory active progress has been made in using Aliquat 336 ‘entangled’ into the polymer membranes to remove heavy metal ions from wastewater samples. In this work, we studied the loss of Aliquat 336 from the point of view of its solubility in aqueous solutions. The results showed that the solubilities or Aliquat 3,36 in an aqueous phase acidified with 2 M HCI it about 0.1 g/100 m/ of the solution. This figure provides a useful guideline for evaluating the leakage of the Aliquatoat 336 extractant from the membranes.

• Fibers and Polymers
• /
• v.5 no.3
• /
• pp.198-203
• /
• 2004

Composite films were prepared by casting the solution of polyacrylonitrile (PAN) and single wall nanotube (SWNT) in DMF subsequent to sonication. The SWNTs in the films are well dispersed as ropes with 20-30 nm thickness. Moreover, AFM surface image of the composite film displays an interwoven fibrous structure of nanotubes which may give rise to conductive passways and lead to high conductivity. The polarized Raman spectroscopy is an ideal characterization technique for identification and the orientation study of SWNT. The well-defined G-peak intensity at 1580 $cm^{-1}$shows a dependency on the draw ratio under cross-Nicol. The degree of nanotube orientation in the drawn film was measurable from the sine curve obtained by rotating the drawn film on the plane of cross-Nicol of polarized Raman microscope. The threshold loading of SWNT for electrical conductivity in PAN is found to be lower than 1 wt% in the composite film. The electrical conductivity of the SWNT/PAN composite film decreased with increasing of draw ratio due to the collapse of the interwoven fibrous network of the nanotubes with uniaxial orientation.

• Fibers and Polymers
• /
• v.2 no.2
• /
• pp.92-97
• /
• 2001

New film forming aromatic poly(amide-imide)s containing isoindoloquinazolinedione (IQ) unit in the backbone chain (polymer XIV) have been successfully synthesized by preparing prepolymers of poly(amic acid-carbonamide). followed by subsequent thermal cyclization of the prepolymers. 4,4-Diamino-3-carbamoylbenzanilide (DACB) V has been synthesized by reduction of 3-carbamoyl-4-amino-4-nitrobenzanilide IV. The prepolymers of poly(amic-acid-carbonamide) (polymers VII and VIII) which exhibit viscosities ranging from 1.4 to 1.7 dl/g have been prepared by a condensation polymerization of monomers such as BPDA, ODA, and DACB. Polymer XIV has been obtained by thermal cyclization of the polymers VII and VIII. During the thermal cyclization reaction, imide ring structure was first introduced and then transformed to the structure of IQ unit. The thermal degradation rate of the resultant polymers were influenced by the cleavage of amide bond but the final char yield was comparable to that of poly(BPDA-ODA).

• Fibers and Polymers
• /
• v.2 no.4
• /
• pp.203-211
• /
• 2001

Residual stresses were predicted by a flow analysis in the mold cavity and residual stress distribution in the injection molded product was measured. Flow field was analyzed by the hybrid FEM/FDM method, using the Hele Shaw approximation. The Modified Cross model was used to determine the dependence of the viscosity on the temperature and the shear rate. The specific volume of the polymer melt which varies with the pressure and temperature fields was calculated by the Tait\`s state equation. Flow analysis results such as pressure, temperature, and the location of the liquid-solid interface were used as the input of the stress analysis. In order to calculate more accurate gap-wise temperature field, a coordinate transformation technique was used. The residual stress distribution in the gap-wise temperature field, a coordinate transformation technique was used. The residual stress distribution in the gap-wise direction was predicted in two cases, the free quenching, under the assumption that the shrinkage of the injection molded product occurs within the mold cavity and that the solid polymer is elastic. Effects of the initial flow rate, packing pressure, and mold temperature on the residual stress distribution was discussed. Experimental results were also obtained by the layer removal method for molded polypropylene.