• Journal of the Korean Institute of Gas
• /
• v.17 no.5
• /
• pp.75-80
• /
• 2013

In this study, the effect of phosphorus flame retardants on the flame retardancy of the rigid polyurethane foam(PUF) was studied. Tetramethylene bis(orthophos-phorylurea)[TBPU] and Tris(2-chloroethyl) phosphate[TCEP], Tris(2-chloropropyl)phosphate [TCPP], Triethyl phosphate[TEP] were used as flame retardant. It was found that TBPU added PUF exhibits low mean heat release rate(HRR), peak HRR, effective heat of combusion(EHC), mass loss rate (MLR), CO yield and $CO_2$ compared other flame retardants.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.3
• /
• pp.257-269
• /
• 2005

This study was focused on the maximization of flame-retardancy of polyesters by a synergism of simultaneously introduced chlorine and phosphorus into polymer chains of modified polyesters. To prepare modified polyesters, reaction intermediates, TD-adduct (prepared from trimethylolpropane /2,4-dichlorobenzoic acid (2,4-DCBA)) and TMBO (prepared from tetramethlene bis (orthophosphate)), were prepared first, then condensation polymerization of the prepared intermediates, adipic acid, and 1,4-butanediol were carried out. In the condensation polymerization, the content of phosphorus was fixed to be 2wt%, and the content of 2,4-DCBA that provides chlorine component was varied to be 10, 20, and 30wt%, and we designated the prepared modified polyesters containing chlorine and phosphorus as ABTTs. The prepared intermediates and modified polyesters were characterized with FT-IR, NMR, GPC, and TGA analysis. Average molecular weight and polydipersity index of the preparation of ABTTs were decreased with increasing 2,4-DCBA content because of the incease in hydroxyl group that retards reaction. We found that the thermal stability of the prepared ABTTs increased with chlorine content at high temperatures.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1678-1686
• /
• 2021

In this study, we prepared phosphorous flame-retarding coating solutions by mixing triphosphate (3 phosphonate), phytic acid (6 phosphonate), or ammonium polyphosphate (10 phosphonate) with boric acid as a crosslinking agent and acryl resin binder. Prepared phosphorous flame-retarding coating solutions were coated onto non-woven fabrics, respectively, to obtain high flame-retarding effects. These prepared flame-retardant non-woven fabrics were evaluated using smoke density standard test (ASTM E662), limit oxygen index standard test (ISO E622), and vertical burning standard test (UL 94). Their flame-retarding effects were affected by the number of phosphonate groups. Regardless of natural or synthetic binder resins, their effects showed the following order: ammonium polyphosphate > phytic acid > triphosphate. Natural hydrocarbon compounds were also examined to determine the possible retardancy of binder resins. Results showed that natural hydrocarbon binder resins could be used for preparing fire-retardant nonwoven fabrics.

• Fire Science and Engineering
• /
• v.20 no.4 s.64
• /
• pp.110-115
• /
• 2006

Polyurethane(PU) was mixtured by the treatment with flame retardants such as Tri(chloroisopropyl) phosphate(TCPP), Triethyl phosphate(TEP) and Trimethyl phosphate(TMP) at about $90^{\circ}C$. Rigid polyurethane foam was produced using the mixured products as flame retardants. The mechanical property and flammability of rigid polyurethane was investigated. The mixtured polyurethane shows reduced flammability over virgin polyurethane. Mechanical strength of mixtured polyurethane also shows as high as that of virgin polyurethane. In order to evaluate flame retardant properties of the mixtured polyurethane foams, heat release rate(HRR) of the foam was measured by cone calorimeter. Scanning electron micrograph of mixtured PU shows uniform cell morphology as virgin PU.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.25 no.4
• /
• pp.36-42
• /
• 2021

In this study, the impregnation of Lyocell fabrics was performed using phosphoric acid, ammonium phosphate, diammonium hydrogen, triammonium phosphate as phosphorus flame retardant, to fabricate continuous graphite fabrics using lyocell fiber. The physical and chemical structure changes were investigated by thermogravimetric, Fourier-transform infrared spectroscopy, C-nuclear magnetic resonance, X-ray diffraction, and weight analyses, By analyzing the thermal behavior of phosphorus flame retardant, conditions for the temperature, gas, and residual time of the pyrolysis process were set. Graphite fabrics with a tensile strength of 1,007.19±11.47 N/5 cm and yield of 25.3% were fabricated using continuous pyrolysis, carbonization and graphitization process.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.04a
• /
• pp.31-33
• /
• 2008

The study related that Red Phosphorus is surface coated by Al(OH)$_3$ using the proportion 1:1, 1:3, 1:5 respectively, and then take the coated red phosphorus as the core material, at the same time, use Melamine-Formaldehyde resin as the capsule materials for microcapsule processing. According to the TG analysis, the coated red phosphorus with the proportion 1:3 has the tiptop temperature of thermal decomposition, it reaches 376.20^{\circ}C$$. The same to the ratio of burning incomplete carbon it reaches 26.5%. The lowest moisture absorption ratio of the red phosphorus that used coated red phosphorus for microcapsule processing can reach 0.5% with the condition that thermal decomposition temperature decline 3.6%.

• Composites Research
• /
• v.33 no.4
• /
• pp.177-184
• /
• 2020

Flame retardant(FR) clothes prohibit additional fire diffusion and make the personnel do their tasks without a hitch in a flammable environment. The existing FR clothes, however, are heavy and give high thermal fatigue. Therefore, it is strongly demanded to develop a light, convenient, and eco-friendly clothes. Recently, many works have been reported to make FR fabrics with phosphorus compounds, but their performance could not satisfy the specified criteria in appraisal standards of domestic and American FR clothes or combat uniforms. In this paper, two kinds of phosphorus compounds were applied to cotton fabric. Graphene oxide functionalized with a phosphorus-rich deep eutectic solvent and ammonium polyphosphate were coated on cotton fabric by eco-friendly padding procedure. The coated fabrics were analyzed with thermogravimetric analysis, vertical flame resistance test(ASTM D6413), cone calorimeter test(ISO 5660-1), and method of test for limited flame spread(ISO 15025). It was revealed that the as-made cotton with those two materials simultaneously had better flame resistance than the cottons with each one. Furthermore, an additional coating for hydrophobicity on the FR cotton was tried for better washing fastness.

• Applied Chemistry for Engineering
• /
• v.24 no.2
• /
• pp.208-213
• /
• 2013

In this study, the effect of phosphorus flame retardants on the flame retardancy of the flexible polyurethane foam (PUF) was investigated. Tetramethylene bis(orthophosphorylurea) [TBPU] and phosphinyl alkylphosphate ester [CR-530], resorcinol bis diphenylphosphate [RDP], triethyl phosphate [TEP] were used as flame retardants. The results of thermogravimetric analysis (TGA) indicate that TBPU added PUF produces more charred residues than the other flame retardant added PUF. It was found that TBPU added PUF exhibits low mean heat release rate (HRR), peak HRR, effective heat of combusion (EHC), mass loss rate (MLR), CO yield and $CO_2$ compared to those other flame retardants.

• Journal of Adhesion and Interface
• /
• v.20 no.2
• /
• pp.61-65
• /
• 2019

In this study, phosphorus polyols, having a molecular weight of 880 to 1,560 g/mol, were synthesized by reacting phenylphosphonic dichloride (PPDC), allylphosphonic dichloride (APDC), and ethylene glycol (EG) in solvent, to enhance flame retardance of polyurethane. Phosphorus polyurethanes were polymerized using the synthesized phosphorus polyols, polycarbonate diol (PCD), and 4,4'-diphenylmethane diisocyanate (MDI) by a melt polymerization method. As increasing phosphorus contents of the phosphorus polyurethanes, we observed that the remaining char amount increased. This tendency was also confirmed in the following UL-94V test. We found that when the synthesized phosphorus polyols were applied, the resulting phosphorus polyurethanes show UL-94V0 grade at above 0.5 wt% phosphorus contents.

• Elastomers and Composites
• /
• v.37 no.3
• /
• pp.159-169
• /
• 2002

The improvement of flame retardancy of the foams based on NBR/GTR compounds was conducted by formulating various materials i.e. NBR, GTR, inorganic and phosphorus containing flame retardants, foaming agent, cross-linking agent and activator. The foaming properties, morphology, smoke density and flame retardancy of the specimens were investigated using SEM, LOI tester, smoke density control system and cone calorimeter. The phosphorus containing flame retardant reduces heat release rate, increases the limiting oxygen index and a char formation. The inorganic flame retardant increases the limiting oxygen index and reduces heat release rate with an increased CO yield by char formation, and smoke suppressing effect. The formed char seemed to intercept the oxygen transport and heat transfer into the core area. When the composition ratios of the compounds of NBR/GTR were $100{\sim}80/0{\sim}20 wt.%$, and the ratios of the rubbers/flame retardants were $1/1.55{\sim}3.60 wt.%$, we could developed foams with low heat release rate, high limiting oxygen index($28.0{\sim}39.3$), closed or semi-closed cell of uniformity and reasonable expandability($225{\sim}250 %$).