• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.143-148
• /
• 2013

Well-distributed $SnO_2$-Sn-$Ag_3Sn$ nanoparticles embedded in carbon nanofibers were fabricated using a co-electrospinning method, which is set up with two coaxial capillaries. Their formation mechanisms were successfully demonstrated. The structural, morphological, and chemical compositional properties were investigated by field-emission scanning electron spectroscopy (FESEM), bright-field transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In particular, to obtain well-distributed $SnO_2$ and Sn and $Ag_3Sn$ nanoparticles in carbon nanofibers, the relative molar ratios of the Ag precursor to the Sn precursor including 7 wt% polyacrylonitrile (PAN) were controlled at 0.1, 0.2, and 0.3. The FESEM, bright-field TEM, XRD, and XPS results show that the nanoparticles consisting of $SnO_2$-Sn-$Ag_3Sn$ phases were in the range of ~4 nm-6 nm for sample A, ~5 nm-15 nm for sample B, ~9 nm-22 nm for sample C. In particular, for sample A, the nanoparticles were uniformly grown in the carbon nanofibers. Furthermore, when the amount of the Ag precursor and the Sn precursor was increased, the inorganic nanofibers consisting of the $SnO_2$-Sn-$Ag_3Sn$ nanoparticles were formed due to the decreased amount of the carbon nanofibers. Thus, well-distributed nanoparticles embedded in the carbon nanofibers were successfully synthesized at the optimum molar ratio (0.1) of the Ag precursor to the Sn precursor after calcination of $800^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.6
• /
• pp.417-421
• /
• 2018

$TiO_2$ has excellent photocatalytic properties and several studies have reported the increase in its specific surface area. The structure of $TiO_2$ nanofibers indicates promising improved photocatalytic properties and these nanofibers can thus potentially be applied in air pollution sensors and pollutant removal filters. In this study, a $TiO_2$ nanofiber was fabricated by the electrospinning method. The fabrication processing factors such as the applied voltage, the distance between nozzle and collector, and the inflow rate of solution were controlled. The precursor was titanium (IV) isopropoxide and as-spun $TiO_2$ nanofibers were heated at $450^{\circ}C$ for 2 h to obtain an anatase crystalline structure. The microstructure was analyzed using field emission scanning electron microscope (FE-SEM) and X-ray diffraction analysis (XRD). The anatase phase was observed in the $TiO_2$ nanofibers after heat treatment. The diameter of $TiO_2$ nanofibers increased with the flow rate, but decreased with decreasing applied voltage and nozzle to collector distance. The diameter of $TiO_2$ nanofibers was controlled in the range of 364 nm to 660 nm. These nanofibers are expected to be very useful in photocatalytic applications.

• Journal of Radiation Industry
• /
• v.9 no.4
• /
• pp.171-180
• /
• 2015

Vascular tissue engineering has been accessed to mimic the natural composition of the blood vessel containing intima, media, and adventitia layers. We fabricated mechanically expanded PLLA/PLCL nanofibers using electrospinning and UTM. The pore size of the meshes was increased the gelatin immobilized AAc-PLLA/PLCL nanofibers ($203.30{\pm}49.62microns$) than PLLA/PLCL nanofibers ($59.99{\pm}8.66microns$) after mechanical expansion. To increase the cell adhesion and proliferation, we introduced carboxyl group, and gelatin was conjugated on them. The properties of the PLLA/PLCL nanofibers were analyzed with SEM, ATR-FTIR, TBO staining, and water contact angle measurement, general cell responses on the PLLA/PLCL nanofibers such as adhesion, proliferation, and infiltration were also investigated using smooth muscle cell (SMC). During the SMC culture, the initial viability of the cells was significantly increased on the gelatin immobilized AAc-PLLA/PLCL nanofibers, and infiltration of the cells was also enhanced on them. Therefore, gelatin immobilized AAc-PLLA/PLCL nanofibers and mechanically expanded meshes may be a good tool for vascular tissue engineering application.

• Journal of Radiation Industry
• /
• v.5 no.4
• /
• pp.365-370
• /
• 2011

Electrospun nanofibers prepared with synthetic biodegradable polymer have some limitations in regulating adhesion, proliferation, and spreading of cells because of their surface hydrophobicity and absence of cell-interaction. In this study, we functionalized the electrospun poly(L-lactide-co-${\varepsilon}$-caprolactone) (PLCL) nanofibers with acrylic acid (AAc) to modulate their surface hydrophilicity using electron-beam irradiation method and then measured grafting ratio of AAc, water contact angle, and ATR-FTIR of AAc-grafted nanofibers. A grafting ratio of AAc on the nanofibers was increased as irradiation dose and AAc concentration were increased. AAc-grafted nanofibers also have higher wettability than non-modified nanofibers. In conclusion, those surface-modified nanofibers may be an essential candidate to regulate cell attachment in tissue engineering applications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.8
• /
• pp.650-653
• /
• 2009

Hybrid nanofibers made of $Cu_2O$ and polyvinyl pyrrolidone were fabricated by electrospinning on glass substrates. The current magnitude of the $Cu_2O$-PVP hybrid nanofibers is 10 times larger than that of pure PVP nanofibers. In addition, $Cu_2O$-PVP nanofibers possess high sensitivity to air at room temperature than pure PVP nanifibers.

• Journal of Forest and Environmental Science
• /
• v.33 no.2
• /
• pp.154-159
• /
• 2017

Enzymatic treatment was conducted to hydrolyze pure cellulose nanofiber (PCNF), holocellulose nanofiber (HCNF), and lignocellulose nanofiber (LCNF) for 6, 24 and 72 hours and thus-obtained nanofibers (1, 3, 5, 10 wt%) were used to reinforce polyvinyl alcohol (PVA). Glucose production yield was increased by enzymatic hydrolysis. Tensile strength and elastic modulus of all PVA nanocomposite reinforced three nanofibers were improved by increasing enzymatic hydrolysis time of nanofibers and these values were higher in order of nanocomposite reinforced with PCNF>HCNF>LCNF. Furthermore, tensile properties of nanocomposite with PCNF were increased by nanofiber content. Thermal stability of PVA was improved by adding nanofibers and by increasing nanofiber content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.04b
• /
• pp.33-34
• /
• 2009

Hybrid nanofibers made of $Cu_2O$ and polyvinyl pyrrolidone were fabricated by electrospinning. The current magnitude of the $Cu_2O$-PVP hybrid nanofibers is 10 times larger than that of pure PVP nanofibers. In addition, $Cu_2O$-PVP nanofibers possess high sensitivity to air at room temperature.

• Carbon letters
• /
• v.15 no.1
• /
• pp.71-76
• /
• 2014

Activated carbon nanofibers (ACNF) were prepared from polyacrylonitrile (PAN)-based nanofibers using $CO_2$ activation methods with varying activation process times. The surface and structural characteristics of the ACNF were observed by scanning electron microscopy and X-ray diffraction, respectively. $N_2$ adsorption isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. As experimental results, many holes or cavernous structures were found on the fiber surfaces after the $CO_2$ activation as confirmed by scanning electron microscopy analysis. Specific surface areas and pore volumes of the prepared ACNFs were enhanced within a range of 10 to 30 min of activation times. Performance of the porous PAN-based nanofibers as an electrode for electrical double layer capacitors was evaluated in terms of the activation conditions.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.2
• /
• pp.242-247
• /
• 2004

Using Ar plasama and Fe-phthalocyanine, carbon nanofibers have been synthesized at a low temperature. Fe-phthalocyanine was used as a source material for this process. The carbon nanofibers were grown in random orientation with a diameter of about 100 nm and length up to 10${\mu}{\textrm}{m}$ on Si substrate. The synthesized carbon nanofibers exhibited excellent field emission characteristics. Protrusions with a nanometer size are observed at an angle of 60$^{\circ}$with respect to the nanofiber axis. Furthermore, we found the selective growth of nanofibers on a scratched substrates.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.8
• /
• pp.723-730
• /
• 2003

The CN(carbon nitrogen) nanofibers were formed by HIP(high isostatic pressure) process. From the field emission measurement, CN nanofibers shows an excellent characteristics of emitter, better than CNTs and carbon nanofibers. The structures obtained can be divided into three groups : bamboo-like fibers, corrugated structures and bead necklace-like fib res. Emission properties of CN nanofibers were investigated for spacing, between anode and cathode, variation. Turn-on fields was 1.4 v/$\mu\textrm{m}$. The time reliability and light emission test were carried out for about 100 hours. We suggest that CN nanofibers can be possibly applied to the high brightness flat lamp because of low turn-on field and time reliability