• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.228.2-228.2
• /
• 2015

We have developed a TOF-MEIS system using 70~100 keV He+. A TOF-MEIS system was designed and constructed to minimize the ion beam damage effect by utilizing a pulsed ion beam with a pulse width < 1 ns and a TOF delay-line-detector with an 120 mm diameter and a time resolution of 180 ps. The TOF-MEIS is an useful tool for interfacial analysis of the composition and structure of nano and bio systems. Our recent applications are reported. We investigated the effect with Polyaspartic Acid (pAsp) and Osteocalcin on the initial bone growth of calcium hydroxyl appatite on a carboxyl terminated surface. When pAsp is not added to the self-assembled monolayers of Ca 2mM with Phosphate 1.2 mM, the growth procedure of calcium hydroxyl appatite cannot be monitored due to its rapid growth. When pAsp is added to the SAMs, the initial grow stage of the Ca-P can be monitored so that the chemical composition and their nucleus size can be analyzed. Firstly discovered the existence of 1-nm-sized abnormal calcium-rich clusters (Ca/P ~ 3) comprised of three calcium ions and one phosphate ion. First-principles studies demonstrated that the clusters can be stabilized through the passivation of the non-collagenous-protein mimicking carboxyl-ligands, and it progressively changes their compositional ratio toward that of a bulk phase (Ca/P~1.67) with a concurrent increase in their size to ~2 nm. Moreover, we found that the stoichiometry of the clusters and their growth behavior can be directed by the surrounding proteins, such as osteocalcin.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.135-136
• /
• 2012

Carbon atoms near the surface of W(110) induce reconstructions such as $R(15{\times}12)$ -C/W(110) which consists of two characteristic parts, one square shaped and bright protrusion and two smaller ones. In the atomic resolution STM image, the bigger protrusion shows the periodicities of clean W(110), indicating that it is almost carbon poor region. The smaller protrusion contains hexagonal carbide surface layer of ${\alpha}$-W2C on W(110). Employing this carburized W(110) as templates, we grow Co and Fe clusters of less than ten atoms. Due to the selectivity of bonding sites, growth of larger cluster is highly unfavorable for Co and the size of clusters is very uniform. Since Co atoms prefer to sit on the bigger protrusion rather than smaller one, Co cluster can be arranged one-dimensionally in $R(15{\times}12)$-C/W(110) with quite uniform size distribution. However, Fe clusters sit on both sites without favored site, but still with uniform size distribution. On the other hand, Fe clusters can be grown with quasi one-dimensional order in $R(15{\times}3)$-C/W(110), which consists of only smaller protrusions. We investigate the magnetic properties of the ordered nano-sized clusters. Experiments using XMCD reveals little magnetic moment of Co cluster on $R(15{\times}12)$-C/W(110). This observation is consistent with the predictions of our first principles calculations that small Co clusters can be nonmagnetic or antiferromagnetic with low mean magnetic moment per atom.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.252-258
• /
• 2002

Transparent $TiO_2$ thin films prepared by sol-gel process using the modification of titanium(IV) alkoxide showed improved thermal stability and high refraction index. Compared to the pure $TiO_2$ film, the modified $TiO_2$ films show the increased index of refraction under proper condition at pH 2.5. Transparency of these $TiO_2$ thin films were more than 80% in the visible region. It has been demonstrated that the reaction occurs in the amorphous phase: an exchange of phase results in anatase before and after 400$^{\circ}C$, in rutile over 700$^{\circ}$C form the XRD results. The particle sizes, shapes and structures of these nanoclusters in the $TiO_2$ films have been identified through a SEM and XRD. The physical properties and structures of their powders have also been studied through a SEM, XRD, TGA and DSC. The thickness and index of refraction have been determined by the analysis of ellipsometric spectra.

• Polymer(Korea)
• /
• v.29 no.3
• /
• pp.266-270
• /
• 2005

Iron oxide nanoparticles were prepared by the thermal decomposition of iron pentacarbonyl (Fe(CO)$_5$) Poly(vinylpyrrolidone) (PVP) was used as surface-modifying agent to control the size of the iron oxide nanoparticles. The crystalline structure of PVP coated iron oxide nanoparticles was determined by XRD. The size of PVP coated iron oxide nanoparticles was determined by TEM and ELS. The particle sizes of PVP coated iron oxide nanoparticles were controlled by adjusting the molar ratio of PVP/Fe (CO)$_5$, solvent and molecular weight of PVP Particle sizes increased with increasing PVP content. Spherical $50\~100$ nm sized iron oxide nanoclusters were produced when dimethylformamide was used as a solvent. And well-defined 10 nm iron oxide nanoparticles were produced in Carbitol. The prepared PVP coated iron oxide nanoparticles exhibited a well-dispersed property in water. The results obtained in this study confirmed the feasibility of the PVP-coated iron oxide nanoparticles as a biomaterial for MRI contrast agent.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.133-140
• /
• 2017

This study investigates the oxidation properties of Fe-14Cr ferritic oxide-dispersion-strengthened (ODS) steel at various high temperatures (900, 1000, and $1100^{\circ}C$ for 24 h). The initial microstructure shows that no clear structural change occurs even under high-temperature heat treatment, and the average measured grain size is 0.4 and $1.1{\mu}m$ for the as-fabricated and heat-treated specimens, respectively. Y-Ti-O nanoclusters 10-50 nm in size are observed. High-temperature oxidation results show that the weight increases by 0.27 and $0.29mg/cm^2$ for the as-fabricated and heat-treated ($900^{\circ}C$) specimens, and by 0.47 and $0.50mg/cm^2$ for the as-fabricated and heat-treated ($1000^{\circ}C$) specimens, respectively. Further, after 24 h oxidation tests, the weight increases by 56.50 and $100.60mg/cm^2$ for the as-fabricated and heat-treated ($1100^{\circ}C$) specimens, respectively; the latter increase is approximately 100 times higher than that at $1000^{\circ}C$. Observation of the surface after the oxidation test shows that $Cr_2O_3$ is the main oxide on a specimen tested at $1000^{\circ}C$, whereas $Fe_2O_3$ and $Fe_3O_4$ phases also form on a specimen tested at $1100^{\circ}C$, where the weight increases rapidly. The high-temperature oxidation behavior of Fe-14Cr ODS steel is confirmed to be dominated by changes in the $Cr_2O_3$ layer and generation of Fe-based oxides through evaporation.

• Journal of Photoscience
• /
• v.12 no.1
• /
• pp.17-23
• /
• 2005

Application of a new photocatalyst has been attempted to improve the efficiency and rates of photocatalytic degradation of azo dyes by using a model dye such as Methyl Orange. As a new photocatalyst, $TiO_2$ encapsulated EFAL-removed zeolite Y ($TiO_2$ /EFAL-removed zeolite Y) has been synthesized by ion-exchange in the mixture of EFAL-removed zeolite Y with 0.05 M aqueous [$(NH_4)_2 TiO(C_2O_4)_2.H_2O$] [$TiO(C_2O_4)_2.H_2O$]. This new photocatalyst has been characterized by measuring XRD, IR and reflectance absorption spectra as well as ICP analysis, and it was found that the framework structure of $TiO_2$ /EFAL-removed zeolite Y is not changed by removing the extra-framework aluminum (EFAL) from the normal zeolite Y and the $TiO_2$ inside the photocatalyst exists in the form of $(TiO^{2+})_n$ nanoclusters. Based on the ICP analysis, the Si/Al ratio of the $TiO_2$ /EFAL-removed zeolite Y and the weight of $TiO_2$ were determined to be 23 and 0.061g in 1.0g photocatalyst, respectively. It was also found that adsorption of the azo dye in the $TiO_2$ /EFAL-removed zeolite is very effective (about 80 % of the substrate used). This efficient adsorption contributes to the synergistic photocatalytic activities of the $TiO_2$ /EFAL-removed zeolite by minimizing the required flux diffusion of the substrate. Thus, the photocatalytic reduction of methyl orange (MO) was found to be 8 times more effective in the presence of $TiO_2$ /EFAL-removed zeolite Y than in the presence of $TiO_2$ /normal zeolite Y. Furthermore, the photocatalytic reduction of MO by using 1.0 g of the $TiO_2$ /EFAL-removed zeolite Y containing 0.061g of $TiO_2$ is much faster than that carried out by using 1.0 g of Degussa P-25.

• Journal of the Korean Vacuum Society
• /
• v.18 no.4
• /
• pp.302-309
• /
• 2009

We fabricated a Si nano floating gate memory with Schottky barrier tunneling transistor structure. The device was consisted of Schottky barriers of Er-silicide at source/drain and Si nanoclusters in the gate stack formed by LPCVD-digital gas feeding method. Transistor operations due to the Schottky barrier tunneling were observed under small gate bias < 2V. The nonvolatile memory properties were investigated by measuring the threshold voltage shift along the gate bias voltage and time. We obtained the 10/50 mseconds for write/erase times and the memory window of $\sim5V$ under ${\pm}20\;V$ write/erase voltages. However, the memory window decreased to 0.4V after 104seconds, which was attributed to the Er-related defects in the tunneling oxide layer. Good write/erase endurance was maintained until $10^3$ write/erase times. However, the threshold voltages moved upward, and the memory window became small after more write/erase operations. Defects in the LPCVD control oxide were discussed for the endurance results. The experimental results point to the possibility of a Si nano floating gate memory with Schottky barrier tunneling transistor structure for Si nanoscale nonvolatile memory device.