• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.6
• /
• pp.153-159
• /
• 2004

In this study, a new process to pattern directly on a thin metal layer using improved nano replication printing (nRP) process is suggested to evaluate the possibilities of fabricating a stamp for nano-imprinting. In the nRP process, any figure can be replicated from a bitmap figure file in the range of several micrometers with nano-scaled details. In the process, liquid-state resins are polymerized by two-photon absorption which is induced by femto-second laser. A thin gold layer was sputtered on a glass plate and then, designed patterns or figures were developed on the gold layer by newly developed top-down building approach. Generally, stamps fur nano-imprinting have been fabricated by using the costly electron-beam lithography process combined with a reactive ion-etching process. Through this study, the effectiveness of the improved nRP process is evaluated to make a stamp with the resolution of around 200nm with reduced cost.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.5
• /
• pp.206-210
• /
• 2018

Two kinds of bioactive glass were coated on the Ti6Al4V alloy by the enameling technique. In order to reduce the thermal stress due to the difference in expansion coefficient with the alloy with the secondary coating forming hydroxyapatite, the difference in expansion coefficient between the alloy and the two glasses was adjusted at $2{\times}10^{-6}/^{\circ}C$ intervals. FE-SEM and EDS analysis showed that good adhesion was formed between the Ti6Al4V alloy and the primary coating by diffusion bonding. After immersion in SBF solution, it was confirmed from FT-IR that hydroxycarbonate apatite formed in the secondary coating was not different from bulk bioactive glass.

• Journal of the Korean Vacuum Society
• /
• v.21 no.1
• /
• pp.12-16
• /
• 2012

Although silver is used for T-OLED (Top emitting organic Light-Emitting Diode) as reflective anode, it is not an ideal material due to its low work function. Thus, we study the effect of annealing and atmospheric pressure plasma treatment on Ag film that increases its work function by forming the thin silver oxide layer on its surface. In this study, we deposited silver on glass substrate using RF sputtering. Then we treated the Ag samples annealing at $300^{\circ}C$ for 30 minutes in atmosphere or treating the atmospheric plasma treatment for 30, 60, 90, 120s, respectively. We measured the change of the mechanical properties and the potential value of surface with each one at a different treatment type and time. We used nano-indenter system and KPFM (Kelvin Probe Force Microscopy). KPFM method can be measured the change of surface potential. The nanoindenter results showed that the plasma treatment samples for 30s, 120s had very low elastic modulus, hardness and Weibull modulus. However, annealed sample and plasma treated samples for 60s and 90s had better mechanical properties. Therefore, plasma treatment increases the uniformity thin film and the surface potential that is very effective for the performace of T-OLED.

• Tribology and Lubricants
• /
• v.21 no.5
• /
• pp.209-215
• /
• 2005

Nano/micro friction with the contact area was studied on Si-wafer (100) and diamond-like carbon (DLC) film. Borosilicate balls of radii $0.32{\mu}m,\;0.5{\mu}m,\;1.25{\mu}m\;and\;2.5{\mu}m$ mounted on the top of AFM tip (NPS) were used for nano-scale contact and Soda Lime glass balls of radii 0.25mm, 0.5mm, 1mm were used for micro-scale contact. At nano-scale, the friction between ball and surface was measured with the applied normal load using an atomic force microscope (AFM), and at micro scale it was measured using ball-on flat type micro-tribotester. All the experiments were conducted at controlled conditions of temperature $(24\pm1^{\circ}C)$ and humidity $(45\pm5\%)$. Friction was measured as a function of applied normal load in the range of 0-160nN at nano scale and in the range of $1000{\mu}N,\; 1500{\mu}N,\;3000{\mu}N\;and\;4800{\mu}N$ at micro scale. Results showed that the friction at nano scale increased with the applied normal load and ball size for both kinds of samples. Similar behavior of friction with the applied normal load and ball size was observed for Si-wafer at micro scale. However, for DLC friction decreased with the ball size. This difference of in behavior of friction in DLC nano- and microscale was attribute to the difference in the operating mechanisms. The evidence of the operating mechanisms at micro-scale were observed using scanning electron microscope (SEM). At micro-scale, solid-solid adhesion was dominant in Silicon-wafer, while plowing in DLC. Contrary to the nano scale that shows almost a wear-less situation, wear was prominent at micro-scale. At nano- and micro-scale, effect of contact area on the friction was discussed with the different applied normal load and ball size.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.4
• /
• pp.123-130
• /
• 2020

Nano seed incorporated in micro-sized 4BS (Tetrabasic lead Sulfate) seed was applied to the positive electrode active material and compared with Nano 4BS seed (NS). The dispersion of NS decreased due to the aggregation phenomenon, while the nano seed incorporated in micro-sized 4BS seed (INS) could confirm excellent dispersion. As the content of INS increased, the particle size of the active material became small and constant, which was confirmed through SEM and particle size analysis. The specific surface area for the reaction was increased and the high-rate discharge and lifetime characteristics were improved. In order to confirm the variation in particle size distribution in the plate manufacturing process, internal resistance and voltage were measured for 200 AGM lead-acid batteries, and it was confirmed that batteries quality variation decreased.

• Journal of Adhesion and Interface
• /
• v.9 no.4
• /
• pp.17-23
• /
• 2008

In this study, waterborne polyurethane (WPU)/nano ZnO was synthesized from various polyester polyols, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylolpropionic acid (DMPA), triethylamine (TEA) and ethylenediamine (EDA), nano ZnO. The contents of metal oxide were varied from 0 to 1.0 wt% of total solid. The effects of nano ZnO contents and ionic contents in the WPU/nano ZnO on thermal, mechanical properties were studied. The glass transition temperature ($T_g$) of WPU/nano ZnO do not show a distinct tendency with incorporation of nano ZnO and the $T_g$ of WPU/nano ZnO a little increased with increase of DMPA contents. The tensile strength and 100% modulus increase and elongation at break decreases with increase of nano ZnO contents and DMPA contents.

• Transactions on Electrical and Electronic Materials
• /
• v.17 no.2
• /
• pp.98-103
• /
• 2016

The surface morphology of the front transparent conductive oxide (TCO) films plays a vital role in amorphous silicon thin film solar cells (a-Si TFSCs) due to their high transparency, conductivity and excellent light scattering properties. Recently, plasma textured glass surface morphologies received much attention for light trapping in a-Si TFSCs. We report various plasma textured glass surface morphologies for the high efficiency of a-Si TFSCs. Plasma textured glass surface morphologies showed high rms roughness, haze ratio with micro- and nano size surface features and are proposed for future high efficiency of a-Si TFSCs.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.644-651
• /
• 2003

Effects of additives on electrical properties and microstructure of MLCC X7R dielectrics have been investigated. The additives of glass frit or oxide form were added in the same main composition by the different powder processing conditions. As a result of the dielectric property and microstructure analysis, the composition having the glass layer with dopant concentration gradient showed the excellent dielectric properties. The MLCCs were fabricated with the excellent composition and all dielectric properties satisfied the X7R requirements.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.12
• /
• pp.28-32
• /
• 2010

Technical demands for aspheric glass lens formed in market increases its application from simple camera lens module to fiber optics connection module in optical engineering. WC is often used as a metal core of the aspheric glass lens, but the long life time is issued because it fabricated in high temperature and high pressure environment. High hard thin film coating of lens core increases the core life time critically. Diamond Like Carbon(DLC) thin film coating shows very high hardness and low surface roughness, i.e. low friction between a glass lens and a metal core, and thus draw interests from an optical manufacturing industry. In addition, DLC thin film coating can removed by etching process and deposit the film again, which makes the core renewable. In this study, DLC films were deposited on the SiC ceramic core. The process variable in FVA(Filtered Vacuum Arc) method was the substrate bias-voltage. Deposited thin film was evaluated by raman spectroscopy, AFM and nano indenter and measured its crystal structure, surface roughness, and hardness. After applying optimum thin film condition, the life time and crystal structure transition of DLC thin film was monitored.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.1034-1037
• /
• 2004

In this paper we fabricated a test panel for AMOLED on glass and PET substrate. The test panel consisted of the various size of OTFTs and OLEDs and the current driving capability of OTFTs for OLEDs has been investigated. OTFTs were made of the inverted staggered structure and employed polyvinylphenol (PVP) as the gate insulator and pentacene thin film as the active layer. The OTFTs produced the filed effect mobility of 0.3$cm^2$/V.sec and on/off current ratio of $10^5$. OLEDs consisted of TPD for HTL and Alq3 for EML with 35nm thick, generating green monochrome light. We found that OTFT with channel length of 70${\mu}m$and channel width of over 3.5mm provided the sufficient current to OLED to generate the luminescence of 0.3Cd/$m^2$.