• Elastomers and Composites
• /
• 제42권4호
• /
• pp.201-208
• /
• 2007

본 연구에서는 충전된 고무재료의 온도 변화에 대한 치수 안정성을 고찰하기 위해 카본블랙 또는 실리카가 충전된 NR과 SBR의 열변화시 발생하는 수축력과 팽창력을 측정하였다. 일정 길이로 인장된 시편의 온도를 올렸을 때 고무사슬의 엔트로피적 변화에 의해 수축력이 발생하였다. 카본블랙이나 실리카가 첨가된 NR의 경우 충전제 함량이 증가함에 따라 최대 열수축력 값이 감소하였으나, SBR의 경우는 30 phr 함량에서 미충전 고무보다 높은 열수축력 값을 보였다. 압축된 시편의 열팽창력 측정의 경우, 카본블랙을 첨가한 NR의 열팽창력은 거의 변화가 없었으나, SBR은 카본블랙 양의 증가와 함께 최대 팽창력 값이 증가하였다. 실리카를 첨가했을 경우 NR, SBR시편 모두 첨가량이 증가할수록 최대 열팽창력 값이 증가하였다.

• 대한금속재료학회지
• /
• 제48권10호
• /
• pp.884-892
• /
• 2010

To modify the physical properties of Cu thin films, gelatin is generally used as an additive. In this study, we assessed the effect of gelatin on the mechanical properties of electrodeposited Cu films. For this purpose, Cu/gelatin composite films were fabricated by adding 100 ppm of gelatin to an electrolyte, and tension and indentation tests were then performed. Additional tests based on pure Cu films were also performed for comparison. The Cu films containing gelatin presented a smaller grain size compared to that of pure Cu films. This increased the hardness of the Cu films, but addition of gelatin did not significantly affect the elastic modulus of the films. Cu films prepared at room temperature showed no significant change in the yield strength and tensile strength with an addition of gelatin, but we observed a dramatic decrease in the elongation. In contrast, Cu films prepared at $40^{\circ}C$ with gelatin presented a significant increase in the yield strength and tensile strength after the addition of gelatin. Elongation was not affected by adding gelatin. Presumably, the results would be closely related to the preferred orientation of the Cu thin film with the addition of gelatin and at temperatures that lead to a change in the microstructure of the Cu thin films.

• Composites Research
• /
• 제35권5호
• /
• pp.328-333
• /
• 2022

본 연구에서는 CFRP rebar의 휨강도와 기공 특성과의 상관성을 도출하기 위해 CFRP rebar의 제조 조건을 제어하였다. 이때 CFRP rebar의 제조 조건은 리브 유무, 수지 온도 및 경화로 온도 등을 조정하였으며, 제조된 CFRP rebar의 휨강도와 기공특성을 분석하였다. CFRP rebar의 휨강도는 리브 유무, 경화로 온도 및 수지 온도 등, 제조 조건에 따라 변화되었다. 특히 리브가 감겨지지 않은 경우, CFRP rebar의 휨강도 값이 크게 낮아진다는 것도 확인하였다. Nano X-Ray CT 분석 결과, 수지 온도가 60℃인 CFRP rebar에서 최대 기공 지름을 나타내었다. 광학현미경 분석 결과, 최대 기공율은 No. 1에서 6.89%, 최소 기공율은 No. 7의 2.88%이었다. 광학현미경을 통한 기공율과 휨강도의 상관관계계수는 -0.64이었으며, 이는 Nano X-Ray CT 기공율 및 기공크기와의 상관관계계수 보다 높은 값이었다.

• Composites Research
• /
• 제20권5호
• /
• pp.49-55
• /
• 2007

반도체 쿼츠 웨이퍼 다이싱용 블레이드는 마이크로/나노 디바이스와 부품을 제조하기 위해 고정밀도의 가공성을 요구한다. 따라서 균일한 마이크로/나노 선폭의 가공을 위해서는 블레이드의 제작 단계에서 균일한 두께와 밀도를 유지하는 것이 중요하다. 기존의 실리콘웨이퍼 가공을 위해서는 금속의 블레이드가 사용되고 있지만 쿼츠 웨이퍼 가공을 위해서는 고분자 복합재가 사용된다. 이러한 복합재는 가공성, 전기전도성, 그리고 적절한 강도와 연성 및 마모저항성이 있어야 한다. 그러나 기존의 건식성형 공정으로는 균일성을 유지하기 위해 많은 공정과 비용이 소비되고 있다. 본 연구에서는 도전성 나노 세라믹스 분말, 연마재 세라믹스 분말에 열경화성 수지, 전도성 고분자를 혼합한 복합재 분말을 습식성형 공정에 의해 제조, 평가하는 연구를 수행하였다. 먼저 복합재 분말을 액상과 혼합하여 블레이드를 제작하였으며, 액상의 종류, 액상 건조공정의 영향을 고찰하였다. 평가는 마이크로미터 측정기와 현미경을 이용하여 두께를 측정하였다. 두께편차와 기공률, 밀도, 경도, 등의 특성을 비교, 평가하였다. 그 결과 습식성형에 의해 블레이드의 두께편차를 감소시킬 수 있었으며, 경도 등의 특성을 향상시킬 수 있었다.

• 공업화학
• /
• 제26권3호
• /
• pp.239-246
• /
• 2015

나노 탄소재료를 복합화하면 기존 재료의 특성을 유지하면서 그 효율을 극대화할 수 있다. 여기에 이종원소를 부가하면 전기화학적인 특성이 디자인되므로, 나노 탄소재료의 복합화를 통해 한 종류의 나노 재료로부터 여러 강점을 얻을 수 있다. 특히 탄소나노섬유와 금속산화물을 복합화하면 탄소나노섬유의 전기이중층 뿐만 아니라 금속산화물의 산화 환원 반응을 이용하여 비축전 용량, 고율 특성, 수명 특성이 향상되고 높은 수준의 출력밀도가 유지되는 고용량 슈퍼 캐퍼시터용 전극 소재를 개발할 수 있다. 본 총설에서는 탄소의 고출력특성과 금속산화물의 고에너지 특성이 동시에 발현되는 금속산화물계 탄소나노섬유복합체의 제법과 응용에 대한 최신연구를 다루도록 하겠다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2009년도 제40회 하계학술대회
• /
• pp.1449_1450
• /
• 2009

Surface contamination and leakage current have caused operating problems. A flashover in a substation may result in destruction of an insulator or many others electrical equipment. Engineering plastics have good characteristic (light weight, good productivity and little of void) as compare with epoxy or porcelain insulators. Outdoor insulator must have resistance to contamination. However, they are not suited to outdoor insulator by reason of being not good hydrophobic. RTV has a good property of hydrophobic and ATH has characteristic obstructing exothermic reaction. In order to reduce the incidence of insulator flashover and damage, the silicon rubber contained nano size ATH coat on surface of engineering plastics. In this paper, it compares resistance tracking of the engineering plastic coated RTV with that of non-coated engineering plastic and ATH filled composites performed much better than non-filled composites.

• 한국분말재료학회지
• /
• 제21권1호
• /
• pp.50-54
• /
• 2014

A powder-in-sheath rolling method was applied to a fabrication of a carbon nano tube (CNT) reinforced aluminum composite. A STS304 tube with an outer diameter of 34 mm and a wall thickness of 2 mm was used as a sheath material. A mixture of pure aluminum powders and CNTs with the volume contents of 1, 3, 5 vol was filled in the tube by tap filling and then processed to 73.5% height reduction by a rolling mill. The relative density of the CNT/Al composite fabricated by the powder-in-sheath rolling decreased slightly with increasing of CNTs content, but exhibited high value more than 98. The grain size of the aluminum matrix was largely decreased with addition of CNTs; it decreased from $24{\mu}m$ to $0.9{\mu}m$ by the addition of only 1 volCNT. The average hardness of the composites increased by approximately 3 times with the addition of CNTs, comparing to that of unreinforced pure aluminum. It is concluded that the powder-in-sheath rolling method is an effective process for fabrication of CNT reinforced Al matrix composites.

• 한국재료학회지
• /
• 제14권10호
• /
• pp.696-700
• /
• 2004

The reduction behavior of $Al_{2}O_3/CuO$ powder mixtures, prepared from $Al_{2}O_3/CuO$ or $Al_{2}O_3/Cu-nitrate$, was investigated by using thermogravimetry and hygrometry. The powder characteristics were examined by BET, XRD and TEM. Also, the influence of powder characteristics on the microstructure and properties of hot-pressed composites was analyzed. The formation mechanism of nano-sized Cu dispersions was explained based on the powder characteristics and reduction kinetics of oxide powders. In addition, the dependence of the microstructure and mechanical properties of hot-pressed composites on powder characteristics is discussed in terms of the initial size and distribution of Cu particles. The practical implication of these results is that an optimum processing condition for the design of homogeneous microstructure and required properties can be established.

• 한국세라믹학회지
• /
• 제51권1호
• /
• pp.1-6
• /
• 2014

Here we report improved photo-catalytic effect of $Ag_2S$ under visible light using carbon nano-tubes (CNT) modified with $Ag_2S$ nanoparticles. The optical properties, structural properties and compositional analysis, as well as the photo-electrochemical properties of the prepared composites were investigated. It was found that the photocurrent density, and the photo-catalytic effect, was increased by modification of CNT in this way. Compared with the separate effects of $Ag_2S$ and CNT nanoparticles, the photocatalytic effect of CNT-modified-with-$Ag_2S$ composites, increased significantly due to a synergistic effect between the CNT and the $Ag_2S$ nanoparticles.

• 한국분말재료학회지
• /
• 제21권6호
• /
• pp.415-421
• /
• 2014

W-10vol.%ZrC composites reinforced by micrometric and nanosized ZrC particles were prepared by hot-pressing of 25 MPa for 2 h at $1900^{\circ}C$. The effect of ZrC particle size on microstructure and mechanical properties at room temperature and elevated temperatures was investigated by X-ray diffraction analysis, scanning electron microscope and transmission electron microscope observations and the flexural strength test of the W-ZrC composite. Microstructural analysis of the W-ZrC composite revealed that nanosized ZrC particles were homogeneously dispersed in the W matrix inhibiting W grain growth compared to W specimen with micrometric ZrC particle. As a result, its flexural strength was significantly improved. The flexural strength at room temperature for W-ZrC composite using nanosized ZrC particle being 740 MPa increased by around 2 times than that of specimen using micrometric ZrC particle which was 377 MPa. The maximum strength of 935 MPa was tested at $1200^{\circ}C$ on the W composite specimen containing nanosized ZrC particle.